Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-07Bitstream added on 2014-06-13T18:35:10Z : No. of bitstreams: 1 barca_dc_me_sjc.pdf: 4808947 bytes, checksum: 238892d410325de1d23eb76694cb9763 (MD5) / Este estudo avaliou a influência da espessura da cerâmica, do tempo e tipo de fotopolimerização do cimento resinoso na resistência da união entre uma cerâmica vítrea e a dentina coronária humana. A hipótese é a de que o tipo e o tempo de fotopolimerização do agente cimentante e a espessura da cerâmica influenciem na resistência de união entre cimento e dentina. Foram selecionados cento e doze dentes molares humanos hígidos que foram incluídos em resina acrílica e tiveram a superfície oclusal cortadas em máquina Labcut, expondo a dentina planificada. Dois grupos foram tiveram a dentina condicionada com ácido fosfórico 37% lavada e aplicado adesivo (Excite, Ivoclar) fotopolimerizando por 20s. No grupo controle (n=16), utilizou-se cimento auto-adesivo. Foram confeccionados cento e doze blocos (6 x 6 mm) de cerâmica feldspática (Vita PM9) com três espessuras: 1, 2 e 3 mm que tiveram a superfície de cimentação tratad a com ácido fluorídrico 10%, lavada, seca e silanizada. Os blocos cerâmicos foram cimentados, de acordo com o grupo experimental: Variolink II (Ivoclar Vivadent); e fotopolimerizados com LED por 40 ou 80 segundos de fotopolimerização ou cimento Multilink II (no grupo controle). Assim, formaram-se sete grupos (n=16). Os espécimes foram armazenados em água destilada (37°C) por 24 horas e seccionados em dois eixos, X e Y, para a obtenção dos espécimes. Cada grupo (N=16) foi subdividido em 2 (n=8) onde um grupo foi termociclado e o outro submetido ao ensaio de microtração 24 horas após a cimentação. Esse palito (cerâmica/dente) foi fixado no dispositivo de microtração Erios, levado à máquina de ensaio universal e testado com velocidade de 1 mm/min. Os valores médios obtidos (MPa) foram à análise de Variáveis ANOVA 3- fatores, teste de Dunnett e ao teste de Tukey (5%). A resistência adesiva foi significantemente influenciada pelos fatores... / This study evaluated the influence of the thickness of the ceramic, time and type of light curing resin cement on bond strength between a ceramic and glass human dentin. The hypothesis is that the type and time of curing luting agent and the thickness of the ceramic bearing on the bond strength between cement and dentin. We selected one hundred and twelve healthy human molar teeth were embedded in acrylic resin and were cut in the occlusal surface Labcut machine, exposing the dentin. Two groups have had to dentin conditioned with 37% phosphoric acid washed applied adhesive (Excite, Ivoclar) light cured for 20s. In the control group (n = 16), we used self-adhesive cement. We made one hundred and twelve blocks (6 x 6 mm) ceramic feldspathic (Vita PM9) with three thicknesses: 1, 2 and 3 mm that had cement surface treated with hydrofluoric acid 10%, washed, dried, and silanized. The ceramic blocks were cemented according to the experimental group: Variolink II (Ivoclar Vivadent) and cured with LED for 40 or 80 seconds of curing cement Multilink or II (control group). Thus, they formed seven groups (N = 16). The specimens were stored in distilled water (37 ° C) for 24 hours and sectioned in two axes, X and Y, to obtain the specimens. Each group (N = 16) was subdivided into two (n = 8) where a group was thermocycled and another test by microtensile 24 hours after cementation. This toothpick (ceramic / tooth) was mounted in microtensile Erios, led to a universal testing machine and tested at a speed of 1 mm / min. The average values (MPa) were the ANOVA analysis of three variables - factors, Dunnett test and Tukey test (5%). The bond strength was significantly influenced by light irradiation time, thickness of the ceramic thermal cycling

Lesões dentais por erosão têm sido cada vez mais presentes na prática clínica. A restauração direta com resina composta é uma das opções de tratamento para lesões severas, em que há comprometimento estético/funcional. Com o aprimoramento da tecnologia, a utilização do laser para pré-tratamento da superfície dentinária, antes do condicionamento ácido, tem sido considerada como método alternativo para melhorar a adesão das resinas compostas às superfícies erodidas. Assim, o objetivo deste estudo in vitro foi avaliar a influência da irradiação com laser de Er:YAG (2,94 ?m), de pulso super-curto, na adesão da resina composta à superfície dentinária erodida. Quarenta e seis discos de dentina foram obtidos a partir de 46 dentes terceiros molares humanos. A dentina oclusal planificada de 40 molares humanos teve metade de sua face protegida com fita UPVC (dentina hígida), enquanto na outra metade foi produzida uma lesão de erosão através da ciclagem em ácido cítrico (0,05 M, pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Metade das amostras foi irradiada com o laser de Er:YAG (50 ?s, 2 Hz, 80 mJ, 12,6 J/cm2) e a outra não (grupo controle). Em cada grupo de tratamento (laser ou controle) (n=10), um sistema adesivo autocondicionante foi utilizado e, então, confeccionados 2 cilindros de resina composta, tanto do lado erodido como no hígido (total de 4 cilindros), os quais foram submetidos à avaliação da Resistência de União através do ensaio de microcisalhamento (1 mm/min), após armazenamento em saliva artificial por 24 h. A análise do padrão de fratura foi realizada em microscópio óptico (40x). Por meio da Microscopia Eletrônica de Varredura (MEV), a morfologia das superfícies dentinárias hígida e submetida ao desafio erosivo, antes e após o tratamento com laser de Er:YAG (n=3), foi avaliada. Os valores obtidos de resistência de união (MPa) foram submetidos ao teste ANOVA e de comparações múltiplas de Tukey (p<0,05) e as análises das eletromicrografias foram feitas de forma descritiva. A análise morfológica da superfície mostrou alterações significativas na dentina hígida irradiada e na submetida à ciclagem erosiva, irradiada ou não. Quanto à resistência de união, houve diferença entre os 4 substratos analisados, sendo: dentina hígida irradiada (12,77±5,09 A), dentina hígida não irradiada (9,76±3,39 B), dentina erodida irradiada (7,62±3,39 C) e dentina erodida não irradiada (5,12±1,72 D). Houve predominância de padrão de fratura do tipo adesiva. Com base nos resultados e nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que a erosão reduz a adesão em dentina e que o tratamento da superfície dentinária com laser de Er:YAG de largura de pulso super curta aumenta a adesão no substrato erodido ou hígido. / Dental erosion injuries have been increasingly present in clinical practice. Direct restoration with composite resin is one of the treatment options for severe injuries, where there is aesthetic/functional impairment. With the improvement of technology, laser-irradiation for pre-treatment of dentin before surface etching has been considered as an alternative method to improve the adhesion of composite resins to eroded surfaces. The objective of this in vitro study was to evaluate the influence of the irradiation with a super-short pulse Er:YAG (2.94 ?m) laser to the adhesion of composite resin to eroded dentin surface. Forty six dentin discs were obtained from 46 third molars. Forty samples of planned occlusal dentine, obtained from human molars, had half of their surface protected with plastic tape (sound dentin), while the other half was submitted to erosive cycles, consisted on immersion on citric acid (0.05 M, pH 2.3, 10 minutes, 6x/day) and supersaturated solution (pH 7.0, 60 minutes of acid attacks). Half of the samples was irradiated with the Er:YAG laser (50 ?s, 2 Hz, 80 mJ, 12.6 J/cm2) and the other was kept as control. In each treatment group (n = 10), a self-etching adhesive system was used and then two cylinders of composite resin were prepared, on both eroded and sound dentin (total of 4 cylinders). Microshear bond strength test was performed (1 mm/min), after 24 hours storage in artificial saliva. The analysis of the fracture pattern was determined by optical microscopy (40x). The morphology of sound and eroded dentin, before and after treatment with the Er:YAG laser (n = 3) was evaluated under Scanning Electron Microscopy (SEM). Bond strength values (MPa) were subjected to ANOVA and Tukey multiple comparisons test (p<0.05). The analyses of electron micrographs were made descriptively. Morphological analysis of the surface showed significant changes in irradiated and sound dentin subjected to erosive cycling. As for the bond strength, there were differences among the groups, as follows: sound dentin submitted to irradiation (12.77 ± 5.09 A), non-irradiated sound dentin (9.76 ± 3.39 B), eroded dentin submitted to irradiation (7 62 ± 3.39 C) and non-irradiated eroded dentin (5.12 ± 1.72 D). There was a predominance for the adhesive mode of failure. It was concluded that the erosion reduces the adhesion to dentin and that treating the dentin surface with a super-short-pulse Er:YAG laser increases adhesion to both eroded or sound dentin.

Lesões dentais por erosão têm sido cada vez mais presentes na prática clínica. A restauração direta com resina composta é uma das opções de tratamento para lesões severas, em que há comprometimento estético/funcional. Com o aprimoramento da tecnologia, a utilização do laser para pré-tratamento da superfície dentinária, antes do condicionamento ácido, tem sido considerada como método alternativo para melhorar a adesão das resinas compostas às superfícies erodidas. Assim, o objetivo deste estudo in vitro foi avaliar a influência da irradiação com laser de Er:YAG (2,94 ?m), de pulso super-curto, na adesão da resina composta à superfície dentinária erodida. Quarenta e seis discos de dentina foram obtidos a partir de 46 dentes terceiros molares humanos. A dentina oclusal planificada de 40 molares humanos teve metade de sua face protegida com fita UPVC (dentina hígida), enquanto na outra metade foi produzida uma lesão de erosão através da ciclagem em ácido cítrico (0,05 M, pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Metade das amostras foi irradiada com o laser de Er:YAG (50 ?s, 2 Hz, 80 mJ, 12,6 J/cm2) e a outra não (grupo controle). Em cada grupo de tratamento (laser ou controle) (n=10), um sistema adesivo autocondicionante foi utilizado e, então, confeccionados 2 cilindros de resina composta, tanto do lado erodido como no hígido (total de 4 cilindros), os quais foram submetidos à avaliação da Resistência de União através do ensaio de microcisalhamento (1 mm/min), após armazenamento em saliva artificial por 24 h. A análise do padrão de fratura foi realizada em microscópio óptico (40x). Por meio da Microscopia Eletrônica de Varredura (MEV), a morfologia das superfícies dentinárias hígida e submetida ao desafio erosivo, antes e após o tratamento com laser de Er:YAG (n=3), foi avaliada. Os valores obtidos de resistência de união (MPa) foram submetidos ao teste ANOVA e de comparações múltiplas de Tukey (p<0,05) e as análises das eletromicrografias foram feitas de forma descritiva. A análise morfológica da superfície mostrou alterações significativas na dentina hígida irradiada e na submetida à ciclagem erosiva, irradiada ou não. Quanto à resistência de união, houve diferença entre os 4 substratos analisados, sendo: dentina hígida irradiada (12,77±5,09 A), dentina hígida não irradiada (9,76±3,39 B), dentina erodida irradiada (7,62±3,39 C) e dentina erodida não irradiada (5,12±1,72 D). Houve predominância de padrão de fratura do tipo adesiva. Com base nos resultados e nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que a erosão reduz a adesão em dentina e que o tratamento da superfície dentinária com laser de Er:YAG de largura de pulso super curta aumenta a adesão no substrato erodido ou hígido. / Dental erosion injuries have been increasingly present in clinical practice. Direct restoration with composite resin is one of the treatment options for severe injuries, where there is aesthetic/functional impairment. With the improvement of technology, laser-irradiation for pre-treatment of dentin before surface etching has been considered as an alternative method to improve the adhesion of composite resins to eroded surfaces. The objective of this in vitro study was to evaluate the influence of the irradiation with a super-short pulse Er:YAG (2.94 ?m) laser to the adhesion of composite resin to eroded dentin surface. Forty six dentin discs were obtained from 46 third molars. Forty samples of planned occlusal dentine, obtained from human molars, had half of their surface protected with plastic tape (sound dentin), while the other half was submitted to erosive cycles, consisted on immersion on citric acid (0.05 M, pH 2.3, 10 minutes, 6x/day) and supersaturated solution (pH 7.0, 60 minutes of acid attacks). Half of the samples was irradiated with the Er:YAG laser (50 ?s, 2 Hz, 80 mJ, 12.6 J/cm2) and the other was kept as control. In each treatment group (n = 10), a self-etching adhesive system was used and then two cylinders of composite resin were prepared, on both eroded and sound dentin (total of 4 cylinders). Microshear bond strength test was performed (1 mm/min), after 24 hours storage in artificial saliva. The analysis of the fracture pattern was determined by optical microscopy (40x). The morphology of sound and eroded dentin, before and after treatment with the Er:YAG laser (n = 3) was evaluated under Scanning Electron Microscopy (SEM). Bond strength values (MPa) were subjected to ANOVA and Tukey multiple comparisons test (p<0.05). The analyses of electron micrographs were made descriptively. Morphological analysis of the surface showed significant changes in irradiated and sound dentin subjected to erosive cycling. As for the bond strength, there were differences among the groups, as follows: sound dentin submitted to irradiation (12.77 ± 5.09 A), non-irradiated sound dentin (9.76 ± 3.39 B), eroded dentin submitted to irradiation (7 62 ± 3.39 C) and non-irradiated eroded dentin (5.12 ± 1.72 D). There was a predominance for the adhesive mode of failure. It was concluded that the erosion reduces the adhesion to dentin and that treating the dentin surface with a super-short-pulse Er:YAG laser increases adhesion to both eroded or sound dentin.