OBJECTIVE: The purpose of this in vitro study was to evaluate the cutting performance and accuracy of CAD/CAM diamond burs in different chemo-mechanical conditions when machining yttria-stabilized zirconia (YTZ), lithium-disilicate, feldspathic porcelain, and double network hybrid ceramic material. The study also examined bur wear mechanisms. MATERIALS AND METHODS: Two experiments were performed. Experiment 1: 45 samples of each material were milled, and four criteria were tested: milling time; surface roughness; change in bur weight after machining, and total cement space. Experiment 2: Four different coolant liquids were used while machining 15 samples of lithium-disilicate, feldspathic porcelain, and double network hybrid ceramic material. The four criteria in Experiment 1, plus marginal adaptation, were measured. Burs and ceramic materials used were examined with SEM before and after machining. RESULTS: Experiment 1: All burs milled 15 crowns of each material successfully, with a general increase in milling time and decrease in weight. Four wear patterns were identified: grit cracks, micro-fractures, dislodgement, and matrix abrasion. Sequential milling time increased for all of the ceramic materials. Surface roughness (Ra) decreased in general for all materials used in the study except YTZ, which showed an increase in Ra by the end of the machining series. Experiment 2: Additives used in this study had no significant effect on IPS e.max CAD milling efficiency or Ra. Boric acid reduced Vita MarkII machining time significantly and Ra. CONCLUSIONS: The cutting rate of diamond burs differed when machining different ceramic materials. In sequential machining, every consecutive milling demonstrated lower cutting efficacy. The surface roughness of consecutive machined samples differed. Some cooling liquids affected the quality of the machined surface. The bur wear mechanism was the same when different ceramic materials were machined, and their microstructure affected their machinability. / 2019-09-26T00:00:00Z

Made available in DSpace on 2014-06-11T19:33:02Z (GMT). No. of bitstreams: 0 Previous issue date: 2000-12-06Bitstream added on 2014-06-13T19:43:59Z : No. of bitstreams: 1 silva_vo_dr_arafo.pdf: 540803 bytes, checksum: 7326794dd51a361dd48b2e7c4b355170 (MD5) / O objetivo desse trabalho foi avaliar a influência da forma do preparo cavitário na microinfiltração marginal em restaurações em dentes decíduos. Foram preparadas canaletas medindo 2,0 mm nas faces vestibular e lingual de molares decíduos que foram divididas aleatoriamente em 3 grupos de acordo com a técnica de preparo cavitário: Grupo I - alta rotação associado à ponta diamantada; Grupo II - sistema de abrasão a ar; e Grupo III - laser Er:YAG. Após o condicionamento com ácido fosfórico por 15 segundos, foi utilizado o adesivo Single Bond (3M) e a resina Filtek Flow (3M) para restaurar as canaletas. Os espécimes foram então mantidos em estufa a 37ºC por 6 dias, termociclados (500 ciclos com temperatura variando entre 5 e 55ºC), isolados e colocados em solução de fucsina básica à 0,5% durante 24 horas. Após serem seccionados a microinfiltração foi avaliada em microscópio ótico ligado a uma câmera de vídeo com 10 X de aumento. Para se avaliar a forma das cavidades medimos os ângulos oclusal, cervical e de abertura das cavidades, bem como a largura e a profundidade das mesmas por meio de fotomicrografias obtidas em MEV. Os resultados demonstraram semelhança estatística entre as larguras dos preparos cavitários, porém os ângulos oclusal, cervical e de abertura das cavidades apresentaram-se diferentes estatisticamente e que não houve microinfiltração marginal em nenhum dos grupos avaliados e que a diferença na forma de preparo das cavidades não influenciou na microinfiltração marginal dos espécimes estudados. / The aim of this research was the evaluation of the cavity prepare technique on the marginal microleakage in deciduous teeth. Cavities measuring 2.0 mm were prepared on the buccal and lingual faces and were divided into three groups according to the cavity prepare technique: Group I - High speed associated to diamond bur; Group II - air abrasion system; and Group III - Er:YAG laser. After the phosphoric acid etching for 15 seconds, the Single Bond (3M) adhesive and te Filtek Flow (3M) were used for the restoration of the cavities. Then the sample was stored at 37ºC for 6 days, termocycled (500 cycles with temperature varying from 5 to 55º C), isolated and immersed in a 0.5% funcsin solution for 24 hours. After being sectioned the microleakage was examined with a magnification optical microscope connected to a color video camera. In order to evaluate the shape of the cavities the occlusal, cervical and cavity opening angles were measured, as well as the width and depth of then, using SEM photographs. The results showed that there was no marginal microleakage in any of the evaluated groups and that the difference in the cavity shape did not influence the marginal infiltration on the studied samples.

O objetivo deste trabalho foi estudar a ação sobre a dentina humana (in vitro) de vários tratamentos de superfície: Lixa, IADR-GM, CVDt e CVDi e de alguns adesivos dentais: Adper Sigle Bond 2 (SB), Clearfil SE Bond (CF) e Adper Prompt L-Pop (PL) avaliando: rugosidade e resistência adesiva por micro-cisalhamento. Foram utilizados 72 terceiros molares hígidos que foram divididos ao meio. As superfícies oclusais das 144 metades dentais foram removidas e padronizadas com Lixa #600. Após receberem os tratamentos de superfície citados, foi avaliada a rugosidade média superficial (Ra) da dentina. Em seguida realizou-se a hibridização e a confecção dos cilindros de resina composta (RC) para finalizar o preparo dos corpos de prova (cps). Após armazenagem de 24h em água destilada a 370C realizou-se o teste de micro-cisalhamento com velocidade de deslocamento de 1mm/min. Os resultados foram submetidos a testes de analise estatística (ANOVA) onde foi comprovado que a menor Ra foi encontrada nas superfícies instrumentadas com Lixa #600 seguida pelo CVDi, IADR-GM que apresentaram rugosidade intermediaria e se igualaram e pelo CVDt que produziram as superfícies mais rugosas. Já para o tratamento de superfície, o CVDi foi que apontou os piores valores de resistência de adesão que com Lixa e IADR-GM. Nos resultados para os adesivos, o PL apresentou valores de resistência à união inferiores ao SB e CF que se igualaram. Já para a interação entre os tratamentos de superfície e os adesivos não houve diferenças estatisticamente significantes entre os grupos tratados com Lixa #600, IADR-GM e CVDt e hibridizados com SB ou CF. Concluiu-se: que a Ra produzida em dentina pelo CVD variou de acordo com o tipo de movimento (CVDt produz maior rugosidade que o CVDi); que não foi possível estabelecer uma correlação entre Ra e valores de resistência adesiva; que o PL apresentou valores de resistência à adesão inferiores aos obtidos pelos adesivos SB e CF; que a interação dos tratamentos Lixa, IADR-GM e CVDt com os três adesivos (SB, CF, PL) mostrou valores mais altos para o SB e CF que se igualaram e menores para o PL; que o fator tratamento não produziu diferença de resistência adesiva para o adesivo CF e o mesmo ocorreu com o PL. / The aim of this in vitro study was to evaluate the micro-shear bond strength and the roughness to human dentin using different instrumentations (SiC #600, diamond rotary bur, CVDt and CVDi) and three dentin adhesive/composite resin systems: Adper Sigle Bond 2 (SB), Clearfil SE Bond (CF) e Adper Prompt L-Pop (PL). Seventy-two third molars were split in the middle. The oclusal third from the one hundred and forty and four halves were removed and standardized using the SiC #600. After the prepared surfaces, which were analyzed the roughness average (Ra) with a surface perfilometer and hybridization. The specimens were then stored in distillated water for 24 hours at 370C. The specimens were then were attached to a micro-shear apparatus and subjected to a micro-shear strength test at a crosshead speed of 1mm/min until failure occurred. The two-way ANOVA indicated that there was significant differences in average roughness between the instrumentations which SiC #600 was the smoothest surface. No differences were detected between dentin surface prepared with diamond bur and CVDi (intermediate in the roughness assessment) and the CVDt gave the roughest surface. The bond strengths varied slightly, though dentin instrumentations with CVDi showed the lowest values than the surfaces prepared with SiC #600 and diamond bur. The bond strengths varied slightly, though adhesives, PL showed lower micro-shear bond strength than SB and CF, which were no significant relevance. The interaction of SiC #600, diamond bur and CVDt using SB and CF showed no significant difference in micro-shear bond strength and higher than PL. The instrumentation showed no significant differences in micro-shear bond strength using CF and PL.

Resumo: O objetivo desse trabalho foi avaliar a influência da forma do preparo cavitário na microinfiltração marginal em restaurações em dentes decíduos. Foram preparadas canaletas medindo 2,0 mm nas faces vestibular e lingual de molares decíduos que foram divididas aleatoriamente em 3 grupos de acordo com a técnica de preparo cavitário: Grupo I - alta rotação associado à ponta diamantada; Grupo II - sistema de abrasão a ar; e Grupo III - laser Er:YAG. Após o condicionamento com ácido fosfórico por 15 segundos, foi utilizado o adesivo Single Bond (3M) e a resina Filtek Flow (3M) para restaurar as canaletas. Os espécimes foram então mantidos em estufa a 37ºC por 6 dias, termociclados (500 ciclos com temperatura variando entre 5 e 55ºC), isolados e colocados em solução de fucsina básica à 0,5% durante 24 horas. Após serem seccionados a microinfiltração foi avaliada em microscópio ótico ligado a uma câmera de vídeo com 10 X de aumento. Para se avaliar a forma das cavidades medimos os ângulos oclusal, cervical e de abertura das cavidades, bem como a largura e a profundidade das mesmas por meio de fotomicrografias obtidas em MEV. Os resultados demonstraram semelhança estatística entre as larguras dos preparos cavitários, porém os ângulos oclusal, cervical e de abertura das cavidades apresentaram-se diferentes estatisticamente e que não houve microinfiltração marginal em nenhum dos grupos avaliados e que a diferença na forma de preparo das cavidades não influenciou na microinfiltração marginal dos espécimes estudados. / Abstract: The aim of this research was the evaluation of the cavity prepare technique on the marginal microleakage in deciduous teeth. Cavities measuring 2.0 mm were prepared on the buccal and lingual faces and were divided into three groups according to the cavity prepare technique: Group I - High speed associated to diamond bur; Group II - air abrasion system; and Group III - Er:YAG laser. After the phosphoric acid etching for 15 seconds, the Single Bond (3M) adhesive and te Filtek Flow (3M) were used for the restoration of the cavities. Then the sample was stored at 37ºC for 6 days, termocycled (500 cycles with temperature varying from 5 to 55º C), isolated and immersed in a 0.5% funcsin solution for 24 hours. After being sectioned the microleakage was examined with a magnification optical microscope connected to a color video camera. In order to evaluate the shape of the cavities the occlusal, cervical and cavity opening angles were measured, as well as the width and depth of then, using SEM photographs. The results showed that there was no marginal microleakage in any of the evaluated groups and that the difference in the cavity shape did not influence the marginal infiltration on the studied samples. / Orientador: Rita de Cássia Loiola Cordeiro / Coorientador: Maria Cristina Borsatto / Banca: Lourdes Aparecida Martins dos Santos Pinto / Banca: Ângela Cristina Cilense Zuanon / Banca: Delsa Deise Machetti Kanaan / Banca: Luís José Floriam / Doutor

O objetivo deste trabalho foi estudar a ação sobre a dentina humana (in vitro) de vários tratamentos de superfície: Lixa, IADR-GM, CVDt e CVDi e de alguns adesivos dentais: Adper Sigle Bond 2 (SB), Clearfil SE Bond (CF) e Adper Prompt L-Pop (PL) avaliando: rugosidade e resistência adesiva por micro-cisalhamento. Foram utilizados 72 terceiros molares hígidos que foram divididos ao meio. As superfícies oclusais das 144 metades dentais foram removidas e padronizadas com Lixa #600. Após receberem os tratamentos de superfície citados, foi avaliada a rugosidade média superficial (Ra) da dentina. Em seguida realizou-se a hibridização e a confecção dos cilindros de resina composta (RC) para finalizar o preparo dos corpos de prova (cps). Após armazenagem de 24h em água destilada a 370C realizou-se o teste de micro-cisalhamento com velocidade de deslocamento de 1mm/min. Os resultados foram submetidos a testes de analise estatística (ANOVA) onde foi comprovado que a menor Ra foi encontrada nas superfícies instrumentadas com Lixa #600 seguida pelo CVDi, IADR-GM que apresentaram rugosidade intermediaria e se igualaram e pelo CVDt que produziram as superfícies mais rugosas. Já para o tratamento de superfície, o CVDi foi que apontou os piores valores de resistência de adesão que com Lixa e IADR-GM. Nos resultados para os adesivos, o PL apresentou valores de resistência à união inferiores ao SB e CF que se igualaram. Já para a interação entre os tratamentos de superfície e os adesivos não houve diferenças estatisticamente significantes entre os grupos tratados com Lixa #600, IADR-GM e CVDt e hibridizados com SB ou CF. Concluiu-se: que a Ra produzida em dentina pelo CVD variou de acordo com o tipo de movimento (CVDt produz maior rugosidade que o CVDi); que não foi possível estabelecer uma correlação entre Ra e valores de resistência adesiva; que o PL apresentou valores de resistência à adesão inferiores aos obtidos pelos adesivos SB e CF; que a interação dos tratamentos Lixa, IADR-GM e CVDt com os três adesivos (SB, CF, PL) mostrou valores mais altos para o SB e CF que se igualaram e menores para o PL; que o fator tratamento não produziu diferença de resistência adesiva para o adesivo CF e o mesmo ocorreu com o PL. / The aim of this in vitro study was to evaluate the micro-shear bond strength and the roughness to human dentin using different instrumentations (SiC #600, diamond rotary bur, CVDt and CVDi) and three dentin adhesive/composite resin systems: Adper Sigle Bond 2 (SB), Clearfil SE Bond (CF) e Adper Prompt L-Pop (PL). Seventy-two third molars were split in the middle. The oclusal third from the one hundred and forty and four halves were removed and standardized using the SiC #600. After the prepared surfaces, which were analyzed the roughness average (Ra) with a surface perfilometer and hybridization. The specimens were then stored in distillated water for 24 hours at 370C. The specimens were then were attached to a micro-shear apparatus and subjected to a micro-shear strength test at a crosshead speed of 1mm/min until failure occurred. The two-way ANOVA indicated that there was significant differences in average roughness between the instrumentations which SiC #600 was the smoothest surface. No differences were detected between dentin surface prepared with diamond bur and CVDi (intermediate in the roughness assessment) and the CVDt gave the roughest surface. The bond strengths varied slightly, though dentin instrumentations with CVDi showed the lowest values than the surfaces prepared with SiC #600 and diamond bur. The bond strengths varied slightly, though adhesives, PL showed lower micro-shear bond strength than SB and CF, which were no significant relevance. The interaction of SiC #600, diamond bur and CVDt using SB and CF showed no significant difference in micro-shear bond strength and higher than PL. The instrumentation showed no significant differences in micro-shear bond strength using CF and PL.