Made available in DSpace on 2014-06-11T19:33:02Z (GMT). No. of bitstreams: 0 Previous issue date: 2000-12-06Bitstream added on 2014-06-13T19:43:59Z : No. of bitstreams: 1 silva_vo_dr_arafo.pdf: 540803 bytes, checksum: 7326794dd51a361dd48b2e7c4b355170 (MD5) / O objetivo desse trabalho foi avaliar a influência da forma do preparo cavitário na microinfiltração marginal em restaurações em dentes decíduos. Foram preparadas canaletas medindo 2,0 mm nas faces vestibular e lingual de molares decíduos que foram divididas aleatoriamente em 3 grupos de acordo com a técnica de preparo cavitário: Grupo I - alta rotação associado à ponta diamantada; Grupo II - sistema de abrasão a ar; e Grupo III - laser Er:YAG. Após o condicionamento com ácido fosfórico por 15 segundos, foi utilizado o adesivo Single Bond (3M) e a resina Filtek Flow (3M) para restaurar as canaletas. Os espécimes foram então mantidos em estufa a 37ºC por 6 dias, termociclados (500 ciclos com temperatura variando entre 5 e 55ºC), isolados e colocados em solução de fucsina básica à 0,5% durante 24 horas. Após serem seccionados a microinfiltração foi avaliada em microscópio ótico ligado a uma câmera de vídeo com 10 X de aumento. Para se avaliar a forma das cavidades medimos os ângulos oclusal, cervical e de abertura das cavidades, bem como a largura e a profundidade das mesmas por meio de fotomicrografias obtidas em MEV. Os resultados demonstraram semelhança estatística entre as larguras dos preparos cavitários, porém os ângulos oclusal, cervical e de abertura das cavidades apresentaram-se diferentes estatisticamente e que não houve microinfiltração marginal em nenhum dos grupos avaliados e que a diferença na forma de preparo das cavidades não influenciou na microinfiltração marginal dos espécimes estudados. / The aim of this research was the evaluation of the cavity prepare technique on the marginal microleakage in deciduous teeth. Cavities measuring 2.0 mm were prepared on the buccal and lingual faces and were divided into three groups according to the cavity prepare technique: Group I - High speed associated to diamond bur; Group II - air abrasion system; and Group III - Er:YAG laser. After the phosphoric acid etching for 15 seconds, the Single Bond (3M) adhesive and te Filtek Flow (3M) were used for the restoration of the cavities. Then the sample was stored at 37ºC for 6 days, termocycled (500 cycles with temperature varying from 5 to 55º C), isolated and immersed in a 0.5% funcsin solution for 24 hours. After being sectioned the microleakage was examined with a magnification optical microscope connected to a color video camera. In order to evaluate the shape of the cavities the occlusal, cervical and cavity opening angles were measured, as well as the width and depth of then, using SEM photographs. The results showed that there was no marginal microleakage in any of the evaluated groups and that the difference in the cavity shape did not influence the marginal infiltration on the studied samples.

Orientador: Milton Carlos Kuga / Resumo: O selamento dentinário na câmara pulpar é frequentemente executado após o tratamento endodôntico, o qual é chamado de selamento endodôntico tardio (SET). A irrigação com Hipoclorito de Sódio (NaOCl) tem mostrado uma redução na resistência de união entre o dente e a resina. Porém, uma nova técnica denominada Selamento Endodôntico Imediato (SEI) tem sido proposta. O objetivo deste estudo foi comparar a eficácia da técnica do SEI, avaliando a adaptação interna de vários sistemas adesivos na dentina. Para isso 48 molares humanos foram instrumentados e distribuídos em seis grupos (n = 8), de acordo com o tipo de sistema adesivo utilizado e o momento de execução do SEI sendo esse antes da execução do tratamento endodôntico e SET após o tratamento endodôntico. Nos grupos G1-SBM- SEI / G4-SBM-SET foi utilizado um sistema adesivo "condiciona-e-lava" de três passos (Adper Scotchbond Multi-Purpose-SBM; 3M ESPE, St. Paul, MN, EUA), nos grupos G2-CF-SEI / G5-CF-SET sistema adesivo autocondicionante de dois passos (Clearfil SE Bond-CF; Kuraray, Osaka, Japão) e nos grupos G3-SBU-SEI / G6-SBU- SET) sistema adesivo autocondicionante de passo único (Scotchbond Universal- SBU; 3M ESPE, St. Paul, MN, EUA). Os dados obtidos na mensuração da penetrabilidade dos sistemas adesivos na dentina, por meio de microscopia confocal a laser, foram inicialmente submetidos ao teste de Shapiro-Wilk e, na sequência, aos testes de ANOVA e Tukey (P = 0.05). Por outro lado, os d... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The dentin sealing in the pulp chamber is often performed after the endodontic treatment, which is called late endodontic sealing (SET). Irrigation with sodium hypochlorite (NaOCl) has shown a reduction in bond strength between tooth and resin. However, a new technique called Immediate Endodontic Sealing (SEI) has been proposed. The objective of this study was to compare the efficacy of the SEI technique by evaluating the internal adaptation of several dentin adhesive systems. For this purpose 48 human molars were instrumented and distributed in six groups (n = 8), according to the type of adhesive system used and the moment of execution of the SEI, before the endodontic treatment and SET after the endodontic treatment. In the G1-SBM-SEI / G4-SBM-SET groups a conventional three-step adhesive system (Adper Scotchbond Multi-Purpose-SBM; 3M ESPE, St. Paul, MN, USA) was used. In groups G2-CF-SEI / G5-CF-SET was used as a self-etch adhesive system (Clearfil SE Bond-CF; Kuraray, Osaka, Japan) and G3-SBU-SEI / G6-SBU-SET groups was used a single-step self-etch adhesive system (Scotchbond Universal-SBU; 3M ESPE, St Paul, MN, USA).The data obtained in the measurement of the penetrability of dentin adhesive systems by laser confocal microscopy were initially submitted to the Shapiro-Wilk test and then to the ANOVA and Tukey tests (P = 0.05). On the other hand, the data obtained in the analysis of the scores attributed to the continuity of the hybrid layer were submitted to the Kruskal ... (Complete abstract click electronic access below) / Mestre

Resumo: O objetivo desse trabalho foi avaliar a influência da forma do preparo cavitário na microinfiltração marginal em restaurações em dentes decíduos. Foram preparadas canaletas medindo 2,0 mm nas faces vestibular e lingual de molares decíduos que foram divididas aleatoriamente em 3 grupos de acordo com a técnica de preparo cavitário: Grupo I - alta rotação associado à ponta diamantada; Grupo II - sistema de abrasão a ar; e Grupo III - laser Er:YAG. Após o condicionamento com ácido fosfórico por 15 segundos, foi utilizado o adesivo Single Bond (3M) e a resina Filtek Flow (3M) para restaurar as canaletas. Os espécimes foram então mantidos em estufa a 37ºC por 6 dias, termociclados (500 ciclos com temperatura variando entre 5 e 55ºC), isolados e colocados em solução de fucsina básica à 0,5% durante 24 horas. Após serem seccionados a microinfiltração foi avaliada em microscópio ótico ligado a uma câmera de vídeo com 10 X de aumento. Para se avaliar a forma das cavidades medimos os ângulos oclusal, cervical e de abertura das cavidades, bem como a largura e a profundidade das mesmas por meio de fotomicrografias obtidas em MEV. Os resultados demonstraram semelhança estatística entre as larguras dos preparos cavitários, porém os ângulos oclusal, cervical e de abertura das cavidades apresentaram-se diferentes estatisticamente e que não houve microinfiltração marginal em nenhum dos grupos avaliados e que a diferença na forma de preparo das cavidades não influenciou na microinfiltração marginal dos espécimes estudados. / Abstract: The aim of this research was the evaluation of the cavity prepare technique on the marginal microleakage in deciduous teeth. Cavities measuring 2.0 mm were prepared on the buccal and lingual faces and were divided into three groups according to the cavity prepare technique: Group I - High speed associated to diamond bur; Group II - air abrasion system; and Group III - Er:YAG laser. After the phosphoric acid etching for 15 seconds, the Single Bond (3M) adhesive and te Filtek Flow (3M) were used for the restoration of the cavities. Then the sample was stored at 37ºC for 6 days, termocycled (500 cycles with temperature varying from 5 to 55º C), isolated and immersed in a 0.5% funcsin solution for 24 hours. After being sectioned the microleakage was examined with a magnification optical microscope connected to a color video camera. In order to evaluate the shape of the cavities the occlusal, cervical and cavity opening angles were measured, as well as the width and depth of then, using SEM photographs. The results showed that there was no marginal microleakage in any of the evaluated groups and that the difference in the cavity shape did not influence the marginal infiltration on the studied samples. / Orientador: Rita de Cássia Loiola Cordeiro / Coorientador: Maria Cristina Borsatto / Banca: Lourdes Aparecida Martins dos Santos Pinto / Banca: Ângela Cristina Cilense Zuanon / Banca: Delsa Deise Machetti Kanaan / Banca: Luís José Floriam / Doutor