A study of the behaviour of emulsion explosivesAllum, J. January 2009 (has links)
This study investigated the formulation and characterisation of emulsion explosives. This included the manufacture of more than 120kg of emulsion explosive of which around 105kg was used on the explosive ordnance range in over 350 individual firings. For each emulsion composition, an average of eight firings was undertaken with which to substantiate the explosive performance data. The formulation was varied to determine the effects of water content upon the physical characteristics of the emulsion. These physical effects included thermal conductivity, particle size, viscosity and the explosive performance of the emulsion. In respect of explosive performance, microballoons were added to sensitise the emulsion and the proportions of microballoons added were altered to look at their effect on velocity of detonation, sensitivity and the brisance of the emulsions. Emulsion explosives are commonly referred, in literature, as Type 11 non-ideal explosives. This is due to their non-linear behaviour with respect to the variation of velocity of detonation with density. Traditionally, when an emulsion explosive was commercially manufactured, the water content has been kept at a minimum (12-17%). This was accepted as the way to achieve the best explosive performance, based upon the belief that an emulsion with the highest concentration of active ingredients, ammonium nitrate and oil, would give the best explosive performance. This study examined a wider range of emulsion explosive water contents than has been previously studied, from 12% to 35% water. It was found, during this study, that higher water content emulsions, specifically 25% water, had a marked increase in explosive performance. The highest velocity of detonation recorded was in a 39mm diameter tube, at 25% water content with 3% microballoons, was 5558ms-1. This was some 15% higher than any other VOD recorded in this study. The high velocity of detonation, at 25% water content, was one of a number of physical characteristics in which this water content varied from the other emulsion water contents. This study endeavored to show that emulsion explosives could exhibit two differing types of explosive reaction, thermal explosion and grain burning. This was based on the velocity of detonation and plate dent data, both of which indicated that there was a change in reaction with water content. Emulsion explosives, with a high water and high microballoon content, exhibited a thermal explosion type reaction. They exhibited Type I ideal explosive behaviour, with increasing velocity of detonation with density. Lower water content emulsion explosives, displayed the more commonly expected Type 11 non-ideal behaviour and reacted in a grain burning type detonation.
|
2 |
A Study of the behaviour of emulsion explosives / Department of Environmental and Ordnance SystemsAllum, J 17 November 2009 (has links)
This study investigated the formulation and characterisation of emulsion
explosives. This included the manufacture of more than 120kg of emulsion
explosive of which around 105kg was used on the explosive ordnance range in
over 350 individual firings. For each emulsion composition, an average of eight
firings was undertaken with which to substantiate the explosive performance data.
The formulation was varied to determine the effects of water content upon the
physical characteristics of the emulsion. These physical effects included thermal
conductivity, particle size, viscosity and the explosive performance of the
emulsion. In respect of explosive performance, microballoons were added to
sensitise the emulsion and the proportions of microballoons added were altered to
look at their effect on velocity of detonation, sensitivity and the brisance of the
emulsions.
Emulsion explosives are commonly referred, in literature, as Type 11 non-ideal
explosives. This is due to their non-linear behaviour with respect to the variation
of velocity of detonation with density. Traditionally, when an emulsion explosive
was commercially manufactured, the water content has been kept at a minimum
(12-17%). This was accepted as the way to achieve the best explosive
performance, based upon the belief that an emulsion with the highest
concentration of active ingredients, ammonium nitrate and oil, would give the best
explosive performance.
This study examined a wider range of emulsion explosive water contents than has
been previously studied, from 12% to 35% water. It was found, during this study,
that higher water content emulsions, specifically 25% water, had a marked
increase in explosive performance. The highest velocity of detonation recorded
was in a 39mm diameter tube, at 25% water content with 3% microballoons, was
5558ms-1. This was some 15% higher than any other VOD recorded in this study.
The high velocity of detonation, at 25% water content, was one of a number of
physical characteristics in which this water content varied from the other emulsion
water contents. This study endeavored to show that emulsion explosives could exhibit two differing
types of explosive reaction, thermal explosion and grain burning. This was based
on the velocity of detonation and plate dent data, both of which indicated that there
was a change in reaction with water content. Emulsion explosives, with a high
water and high microballoon content, exhibited a thermal explosion type reaction.
They exhibited Type I ideal explosive behaviour, with increasing velocity of
detonation with density. Lower water content emulsion explosives, displayed the
more commonly expected Type 11 non-ideal behaviour and reacted in a grain
burning type detonation.
|
3 |
Drop size distribution and interfacial area in reactive liquid-liquid dispersionRajapakse, Achula, s9508428@student.rmit.edu.au January 2007 (has links)
Emulsion explosives have become the preferred choice as blasting agents for numerous industries including mining, agriculture, and construction. One of the most important components in such an emulsion is an emulsifier, which controls the emulsification properties of the explosive. The present study involves the production of one such emulsifier, which is produced by reacting two immiscible liquids, PIBSA (polyisobutylene succinic anhydride) and MEA (monoethanolamine). The study examines the effect of design variable such as the impeller speed, impeller type and the dispersed phase volume fraction on interfacial area. Experiments were carried out in a 0.15 m diameter fully baffled stirred tank using a 6-bladed Rushton turbine impeller and a marine propeller. Drop size was determined using a microscope with a video camera and image processing system. The transient concentration of PIBSA was determined using FTIR analysis and used to estimate the volume fraction of the dispersed phase (Ö). The effective interfacial area was calculated using the Sauter mean drop diameter, d32 and Ö. Impeller speeds ranging from 150 to 600 rpm and dispersed phase volume fractions, Ö ranging from 0.01 to 0.028 were examined in the experimental study. It was found that that the evolution of Sauter mean drop diameter, d32 has four different trends depending on Ö and impeller speed. At high impeller speeds and high Ö, d32 values decrease initially and reach constant values after a long period of time. This trend is consistent with the findings in previous investigations. Under certain operating conditions, d32 values increase initially with stirring time to reach a maximum value and then decrease to reach a steady state value. The presence of these trends has been attributed to the effect of changing physical properties of the system as a result of chemical reaction. Results indicate that, in general, Sauter mean drop diameter d32 decreases with an increase in agitation intensity. However a decrease in the dispersed phase volume fraction is found to increase d32. These trends are found to be the same for both impeller types studied. Comparing the drop size results produced by the two impellers, it appears that low-power number propeller produces s ignificantly smaller drops than the Rushton turbine. It was found that the concentrations of reactants decrease with time for all impeller speeds thereby leading to a decrease in interfacial area with the progress of the reaction. Interfacial area values obtained at higher impeller speeds are found to be lower in spite of lower d32 values at these speeds. Also, these values decrease with time and become zero in a shorter duration indicating the rapid depletion of MEA. The interfacial area values obtained with the propeller at a given impeller speed are lower as compared to those for Rushton turbine. They also decrease and become zero in a shorter duration as compared to those for Rushton turbine suggesting propeller¡¦s performance is better in enhancing the reaction rate.
|