Orientadores: Wagner dos Santos Oliveira, Leila Peres / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-12T08:56:57Z (GMT). No. of bitstreams: 1 Paiva_VanessaGiusti_M.pdf: 3847622 bytes, checksum: 3b220ff7426435a8efb069e376425300 (MD5) Previous issue date: 2008 / Resumo: O objetivo deste trabalho foi avaliar a resistência mecânica e a morfologia de fratura de resinas acrílicas sem e com reforço, processadas por microondas. Foram confeccionados 20 cp, sendo eles, Sem Reforço (SR), P246 5%, P246 8%, FSR 5%, FSR 8%, 688 5%, 688 8%, M14P 5% e M14P 8%, medindo 65 x 10 x 2,5mm, sendo os cp SR o grupo controle e os outros com os reforços de filamentos de fibra de vidro e microfibra de vidro. Utilizou-se para confecção das formulações estudadas a resina Vipi Wave, preparadas numa potência de 20 minutos/180W e 5 minutos/450W. Para as análises mecânicas foram feitas análises de variância e teste de Tukey, p<0,05. Constatou-se um aumento significativo para todos os cp reforçados submetidos aos ensaios de resistência à flexão e ao módulo de elasticidade, destacando-se os reforços (P246 5%, P246 8%, 688 5% e 688 8%). Para a análise da dureza (Esquerda, Central e Direita) e para resistência ao impacto não foi observada diferença estatística significante entre o grupo controle e os demais cp reforçados. Para a análise morfológica microestrutural da fratura foram utilizados fragmentos resultantes dos testes de impacto. Verificou-se uma melhor adesão entre a matriz polimérica e os reforços (P246 5%, P246 8%, 688 5% e 688 8%). Comparando-se os resultados dos ensaios mecânicos e a análise morfológica, concluiu-se que os reforços (P246 5%, P246 8%, 688 5% e 688 8%) apresentaram os melhores resultados, p<0,05. Mesmo não sendo observada uma melhora na adesão entre os reforços (FSR 5% e FSR 8%) e a matriz polimérica, estes apresentaram resultados estatisticamente significantes, p<0,05, em relação aos ensaios de resistência à flexão e ao módulo de elasticidade. / Abstract: The purpose of the present study is to evaluate the mechanical resistance and the fracture morphology of acrylic resins reinforced with glass fiber filaments and glass microfiber. 20 proof bodies (PB) were produced from each group, namely, no reinforcement (NR - control), P246 5%, P246 8%, FSR 5%, FSR 8%, 688 5%, 688 8%, M14P 5% and M14P 8%, measuring 65 x 10 x 2,5mm. These were made of a Vipi Wave microwave polymerized resin. Potencies employed were 20 minutes/180W and 5 minutes/450W. In order to perform the mechanical analysis, variation analysis and Tukey test p<0,05 were used. It was evidenced a significant improvement for all cp reinforcements submitted for flexion resistance analysis and the elasticity module analysis, evidencing the reinforcements (P246 5%, P246 8%, 688 5% e 688 8%). For the hardness tests (Left, Right and Center) and for impact. it was not observed significant differences between the control group and the reinforced PBs. For microstructure morphology characterization were used fragments origned from impact tests. Through this technique, it was evidenced some positive interaction between the polymeric matrix and the reinforced PBs. Comparing the results of the mechanic analysis and morphologic analysis, is was concluded that that reinforcements (P246 5%,P246 8%, 688 5% e 688 8%) presented the best results, p<0,05. Even that a better adhesion was not observed between reinforcement (FSR 5% e FSR 8%) and polymeric matrix, these presented significant improvements results, p<0,05, in relation to flexion resistance analysis and elasticity module analysis. / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

O objetivo deste estudo foi comparar, in vitro, a resistência à compressão de 30 raízes bovinas, tratadas endodonticamente, divididas em 3 grupos com 10 raízes cada e restauradas com pino metálico fundido (Grupo 1), pino pré-fabricado de fibra de vidro (Grupo 2) e pino anatômico (Grupo 3). Todas as raízes, com comprimentos de 15mm, foram preparadas internamente para que a espessura dentinária cervical ficasse com 1,5mm, com o objetivo de aumentar a largura do canal radicular. O espaço para o pino foi preparado com 10mm de comprimento. O diâmetro do pino de fibra de vidro escolhido foi o número 2, do sistema utilizado, para que houvesse um espaço entre ele e a estrutura radicular. O Grupo 1 recebeu pino e núcleo metálico fundido cimentado com cimento de fosfato de zinco. O Grupo 2 recebeu pino préfabricado de fibra de vidro cimentado com cimento resinoso Panavia F e núcleo de resina composta Z100. O Grupo 3 recebeu um pino de fibra de vidro modelado no interior do canal com resina composta Z100, cimentado com cimento resinoso Panavia F e núcleo de resina composta Z100. Em todas as raízes dos grupos, um coping metálico foi cimentado com cimento de fosfato de zinco. As raízes foram incluídas em resina acrílica quimicamente ativada, previamente inserida no interior de tubos de PVC e submetidas a testes de compressão em máquina de ensaio Kratos, modelo k2000MP. A carga de compressão foi aplicada a um ângulo de 135 graus ao longo eixo do dente, na face palatina, até que ocorresse uma trinca ou and analysed. The results revealed a statistical difference among groups. Group 1 presented a stronger resistance to fracture than the other groups, which did not present statistical difference. The roots restored with post and cast metallic core were the only ones that presented radicular fracture in the apical root third. The roots that were restored with fibre glass posts presented similar fractures, from the cervical root third to the middle root third. / The aim of this study was to compare, in vitro, the resistance to compression strength of 30bovine roots among canines and incisors endodontically treated, divided into 3 groups with 10 roots each and restored with cast metallic post (Group 1), prefabricated fibre glass post (Group 2), and anatomical post (Group 3). All the roots, with a length of 15mm, were internally prepared so as to their cervical dentin wall thickness would be of 1,5mm, in order to enhance the width of the radicular canal. The space for the post was prepared with 10mm. The diameter of the glass fibre post chosen was the number 2, of the adopted system, so as to create a space between the glass fibre post and the radicular structure. Group 1 received post and cast metallic core cemented with zinc phosphate cement. Group 2 received prefabricated fibre glass post cemented with resin cement Panavia F and composite resin core Z100. Group 3 received a fibre glass post modeled inside the canal with composite resin Z100, cemented with resin cement Panavia F and composite resin core Z100. In all groups, all the roots were cemented with a metallic coping with zinc phosphate cement. The roots were mounted inside pvc pipes with chemically activated acrylic resin, and submitted to compression tests in a universal testing machine Kratos, model k2000MP. The compressive load was done in an angle of 135o in relation to the long axes of the roots, until the occurrence of failure or fracture. The amount of load correspondent to the occurrence of failure or fracture was statistically registered and analysed. The results revealed a statistical difference among groups. Group 1 presented a stronger resistance to fracture than the other groups, which did not present statistical difference. The roots restored with post and cast metallic core were the only ones that presented radicular fracture in the apical root third. The roots that were restored with fibre glass posts presented similar fractures, from the cervical root third to the middle root third.

O objetivo deste estudo foi comparar, in vitro, a resistência à compressão de 30 raízes bovinas, tratadas endodonticamente, divididas em 3 grupos com 10 raízes cada e restauradas com pino metálico fundido (Grupo 1), pino pré-fabricado de fibra de vidro (Grupo 2) e pino anatômico (Grupo 3). Todas as raízes, com comprimentos de 15mm, foram preparadas internamente para que a espessura dentinária cervical ficasse com 1,5mm, com o objetivo de aumentar a largura do canal radicular. O espaço para o pino foi preparado com 10mm de comprimento. O diâmetro do pino de fibra de vidro escolhido foi o número 2, do sistema utilizado, para que houvesse um espaço entre ele e a estrutura radicular. O Grupo 1 recebeu pino e núcleo metálico fundido cimentado com cimento de fosfato de zinco. O Grupo 2 recebeu pino préfabricado de fibra de vidro cimentado com cimento resinoso Panavia F e núcleo de resina composta Z100. O Grupo 3 recebeu um pino de fibra de vidro modelado no interior do canal com resina composta Z100, cimentado com cimento resinoso Panavia F e núcleo de resina composta Z100. Em todas as raízes dos grupos, um coping metálico foi cimentado com cimento de fosfato de zinco. As raízes foram incluídas em resina acrílica quimicamente ativada, previamente inserida no interior de tubos de PVC e submetidas a testes de compressão em máquina de ensaio Kratos, modelo k2000MP. A carga de compressão foi aplicada a um ângulo de 135 graus ao longo eixo do dente, na face palatina, até que ocorresse uma trinca ou and analysed. The results revealed a statistical difference among groups. Group 1 presented a stronger resistance to fracture than the other groups, which did not present statistical difference. The roots restored with post and cast metallic core were the only ones that presented radicular fracture in the apical root third. The roots that were restored with fibre glass posts presented similar fractures, from the cervical root third to the middle root third. / The aim of this study was to compare, in vitro, the resistance to compression strength of 30bovine roots among canines and incisors endodontically treated, divided into 3 groups with 10 roots each and restored with cast metallic post (Group 1), prefabricated fibre glass post (Group 2), and anatomical post (Group 3). All the roots, with a length of 15mm, were internally prepared so as to their cervical dentin wall thickness would be of 1,5mm, in order to enhance the width of the radicular canal. The space for the post was prepared with 10mm. The diameter of the glass fibre post chosen was the number 2, of the adopted system, so as to create a space between the glass fibre post and the radicular structure. Group 1 received post and cast metallic core cemented with zinc phosphate cement. Group 2 received prefabricated fibre glass post cemented with resin cement Panavia F and composite resin core Z100. Group 3 received a fibre glass post modeled inside the canal with composite resin Z100, cemented with resin cement Panavia F and composite resin core Z100. In all groups, all the roots were cemented with a metallic coping with zinc phosphate cement. The roots were mounted inside pvc pipes with chemically activated acrylic resin, and submitted to compression tests in a universal testing machine Kratos, model k2000MP. The compressive load was done in an angle of 135o in relation to the long axes of the roots, until the occurrence of failure or fracture. The amount of load correspondent to the occurrence of failure or fracture was statistically registered and analysed. The results revealed a statistical difference among groups. Group 1 presented a stronger resistance to fracture than the other groups, which did not present statistical difference. The roots restored with post and cast metallic core were the only ones that presented radicular fracture in the apical root third. The roots that were restored with fibre glass posts presented similar fractures, from the cervical root third to the middle root third.

O uso de pinos de fibra de vidro são cada vez mais comuns em reabilitação oral, dessa forma vários sistemas de adesão são encontrados no mercado. Porém ainda há o desafio de manter assepsia do conduto para cimentação do pino sem contaminação. O objetivo deste trabalho foi avaliar a interação de soluções irrigantes na adesão de cimento auto-adesivo em casos de cimentação de pinos de fibra de vidro. Foram utilizados 75 caninos superiores humanos hígidos seccionados transversalmente, de modo que restaram16mm de comprimento radicular partindo do ápice. Estes dentes foram tratados endodonticamente e receberam preparo com profundidade de 12 mm. Após a inclusão das raízes em resina acrílica receberam irrigação com as soluções: G1 - Soro fisiológico; G2 - Extrato Alcoólico de Neem; G3 - EDTA 17%; G4 Hipoclorito de Sódio 2,5%; G5 - Gluconato de Clorexidina 2%. Após a cimentação dos pinos de fibra de vidro com cimento auto-adesivo estes foram submetidos a teste de tração pull out. Foram obtidos slices das raízes em corte transversal para análise em microscópio confocal a laser e microscopia eletrônica de varredura. Realizou-se teste ANOVA e Tukey para análise estatística. As seguintes médias em Newtons foram observadas: G1 - 334,0; G2 - 265,9; G3 - 281,7; G4 - 205,7; G5 - 303,1.Pela microscopia eletrônica de varredura notou-se que G4 apresentou maior degradação da dentina, G2 mostrou maior deposição de debris. Pela análise confocal observou-se prevalência de falhas adesivas. Após análise dos dados concluiu-se que o gluconato de clorexidina foi a solução que apresentou melhor força de adesão comparada às demais, além de não degradar a dentina e não deixar resíduos. Conclui-se que a Clorexidina ainda é um interessante irrigante prévio a cimentação de pinos de fibra de vidro devido às propriedades apresentadas. / The use of glass fiber posts are increasingly common in oral rehabilitation thus various adhesion systems are found on the market. But there is still the challenge of maintaining the root canal aseptic for luting post without contamination. The objective of this study was to evaluate the interaction between irrigating solutions in the selfadhesive cement in cases of luting glass fiber post. A total of 75 human maxillary canines healthy were sectioned, so that remaining 16 mm of root length from the apex. The roots were endodontic treated and post space preparation were12mm. Then, after inclusion in acrylic resin they were separated in groups according to irrigation protocol: G1 - Saline Solution; G2 - Neem Alcoholic Extract; G3 - EDTA 17%; G4 Sodium Hipocloryte 2,5%; G5 - Chlorhexidine Gel 2%. After luting of glass fiber posts with self adhesive cement these were subjected to tensile test pull out. Slices were obtained in the root cross section for analysis in confocal microscopy and scanning electron microscopy. The statistical analysis was performed by ANOVA and Tukey tests. The following averages in Newtons were observed: G1 - 334,0; G2 - 265,9; G3 - 281,7; G4 - 205,7; G5 - 303,1. By scanning electron microscopy it was noted that G4 showed higher degradation of dentin, G2 showed greater deposition of debris. By confocal analysis showed a prevalence of adhesive failures. After analyzing the data it is concluded that the G5 group showed the best bond strength compared to the others, and does not degrade the dentine and not leaving residue. It follows that the chlorhexidine is still an interesting prior irrigating cementing glass fiber post due to the properties presented.

Made available in DSpace on 2017-07-24T19:22:27Z (GMT). No. of bitstreams: 1 Adriana de Oliveira Silva.pdf: 854698 bytes, checksum: 0fe1099b901133907165a1d0a216a8e3 (MD5) Previous issue date: 2004-07-27 / The aim of this study was to evaluate the flexural strength of two fibers glass and two ceramics systems used like substructure of prosthesis fixed partial using a three point bending test. Four groups, with ten specimens and dimensions of 25+ 2mm X 2+ 0,1mm X 2+ 0,1mm (ISO 10477) to fibers glass and 25+ 5 mm X 4+ 0,25 mm X 1,2+ 0,2 mm (ISO 6872) to ceramics were prepared according to the manufacturer’s instructions, where: GI-Vectris Pontic® (Ivoclar/Vivadent), GII-Fibrex Medial® (Angelus Soluções Odontológicas), GIII- IPS Empress ®2(Ivoclar/Vivadent) e GIV- VITA In- Ceram® Zircônia. The specimens were dry stored, in plastic recipient, without light on room temperature and submitted on three point test at universal machine Instron® Corp. 2KN(crosshead speed of 0,75mm/min) and the results of the mean values of flexural strength were 516,04 + 58,44 MPa to GI , 505,23 + 85,57 MPa to GII, 182,73+ 50,33 MPa to the GIII and 442,37 + 99,89 MPa to GIV. The predominance of failure was incomplete fracture to fibers glass and complete fracture to ceramics. The results were submitted on statistical analysis, Anova (p<0,05) and there were observed differences statistically insignificant among the fibers’ group (p=0.7460) and differences statistically significant among the ceramics’ group. Concluded that fibers tested presented similar performance of flexural strength and the result suggested the possibility of fibers glass be used like alternative of alloy in good indication of clinical situation of prosthesis fixed partial. The ceramics presented not similar performance of flexural strength being VITA In-Ceram® Zircônia system able to support more load when compared with IPS Empress® 2 Ivoclar/Vivadent system. / O objetivo deste estudo foi avaliar a resistência flexural de dois sistemas de fibras de vidro unidirecionais e duas cerâmicas utilizadas como subestrutura de próteses parciais fixas, através do teste de três pontos. Quatro grupos, com 10 corpos-deprova cada, e dimensões de 25+2mm X 2+0,1mm X 2+0,1mm (ISO 10477) para as fibras de vidro e 25+ 5 mm X 4+ 0,25 mm X 1,2+ 0,2 mm (ISO 6872) para as cerâmicas, foram obtidos seguindo as orientações dos fabricantes, sendo: GIVectris Pontic® (Ivoclar/Vivadent), GII- Fibrex Medial® (Angelus Soluções Odontológicas), GIII- IPS Empress ®2(Ivoclar/Vivadent) e GIV- VITA In-Ceram® Zircônia. Os corpos-de-prova foram armazenados, secos, à temperatura ambiente, em recipientes plásticos, sem interferência de luz e submetidos ao teste de três pontos em uma máquina de ensaio Instron® Corp. 2KN (velocidade de 0,75mm/min) obtendo-se valores médios de resistência à flexão de 516,04 + 58,44 MPa para GI, 505,23 + 85,57 MPa para GII, 182,73+ 50,33MPa para o GIII e 442,37 + 99,89 MPa para o GIV. O padrão de falha observado foi de fratura incompleta para as fibras de vidro e fratura completa para as cerâmicas. Os valores médios de resistência foram submetidos à análise estatística, teste Anova (p<0,05) e verificou-se a inexistência de diferenças estatísticas significantes entre os grupos de fibras de vidro (p=0.7460) e a existência de diferenças estatísticas significantes entre os grupos de cerâmicas. Concluiu-se que as fibras de vidro utilizadas no experimento apresentaram desempenhos de resistência flexural semelhantes e os resultados sugeriram a possibilidade da utilização das fibras de vidro como alternativa às ligas metálicas em situações clínicas bem indicadas de próteses parciais fixas. As cerâmicas apresentaram diferentes desempenhos de resistência flexural, sendo o sistema VITA In-Ceram® Zircônia capaz de resistir a maior carga aplicada comparada ao sistema IPS Empress® 2 Ivoclar/Vivadent.

Este trabalho apresenta o estudo da incorporação de fibra de vidro curta em composto rígido de poli(cloreto de vinila) - PVC - por meio de equipamentos e técnicas de processamento convencionais da indústria brasileira. Foram avaliadas as influências de: a) tamanho de fibra de vidro (tipo E), b) dosagem de fibra de vidro, c) dosagem de dióxido de titânio (TiO2) e d) a temperatura de processamento nas propriedades físicas, térmicas, mecânicas e na adesão entre matriz polimérica e fibra de vidro (analisada por Microscopia Eletrônica de Varredura). O custo-benefício dos compósitos foi calculado por meio de Índices de Mérito para os modos de carregamento mecânico encontrados nos tubos pressurizados para água fria (Cilindro com Pressão Interna) e perfis rígidos utilizados em construção civil (Barra em Flexão), dado o grande uso de PVC nestas aplicações. Entre os resultados obtidos, destaca-se o aumento de 45% no módulo de elasticidade para os compósitos com 20% de fibra de vidro moída que, para algumas aplicações, pode apresentar uma relação custo-benefício bastante favorável. / This work presents the impact of the short glass fiber incorporation in rigid PVC compound through conventional processing techniques currently employed in the Brazilian industry. It were studied the influences of a) glass fiber geometry (E type), b) glass fiber content, c) titanium dioxide content and d) processing temperature in the physical, mechanical and thermal properties. The adhesion conditions between polymeric matrix and glass fiber was analyzed by scanning electron microscopy (SEM). Cost-benefit relation of composites was evaluated using materials index technique for mechanical conditions found in pressurized water pipes (cylinder with internal pressure) and in building construction profiles (beam loaded in bending). The results attained suggested that, in some cases, the mechanical properties enhancement (such as the increase of 45% in the modulus of elasticity for composites containing 20% of glass fiber) and the processing techniques required to produce it can present an interesting cost-benefit relation.

Este trabalho apresenta o estudo da incorporação de fibra de vidro curta em composto rígido de poli(cloreto de vinila) - PVC - por meio de equipamentos e técnicas de processamento convencionais da indústria brasileira. Foram avaliadas as influências de: a) tamanho de fibra de vidro (tipo E), b) dosagem de fibra de vidro, c) dosagem de dióxido de titânio (TiO2) e d) a temperatura de processamento nas propriedades físicas, térmicas, mecânicas e na adesão entre matriz polimérica e fibra de vidro (analisada por Microscopia Eletrônica de Varredura). O custo-benefício dos compósitos foi calculado por meio de Índices de Mérito para os modos de carregamento mecânico encontrados nos tubos pressurizados para água fria (Cilindro com Pressão Interna) e perfis rígidos utilizados em construção civil (Barra em Flexão), dado o grande uso de PVC nestas aplicações. Entre os resultados obtidos, destaca-se o aumento de 45% no módulo de elasticidade para os compósitos com 20% de fibra de vidro moída que, para algumas aplicações, pode apresentar uma relação custo-benefício bastante favorável. / This work presents the impact of the short glass fiber incorporation in rigid PVC compound through conventional processing techniques currently employed in the Brazilian industry. It were studied the influences of a) glass fiber geometry (E type), b) glass fiber content, c) titanium dioxide content and d) processing temperature in the physical, mechanical and thermal properties. The adhesion conditions between polymeric matrix and glass fiber was analyzed by scanning electron microscopy (SEM). Cost-benefit relation of composites was evaluated using materials index technique for mechanical conditions found in pressurized water pipes (cylinder with internal pressure) and in building construction profiles (beam loaded in bending). The results attained suggested that, in some cases, the mechanical properties enhancement (such as the increase of 45% in the modulus of elasticity for composites containing 20% of glass fiber) and the processing techniques required to produce it can present an interesting cost-benefit relation.

Made available in DSpace on 2014-06-11T19:24:41Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-09-01Bitstream added on 2014-06-13T18:52:28Z : No. of bitstreams: 1 baggio_a_me_botfca.pdf: 559829 bytes, checksum: e12ab3a17570794b47bb229f375ebfb5 (MD5) / Universidade Estadual Paulista (UNESP) / Nesta pesquisa estudou-se o aproveitamento dos resíduos de compósitos a base de resina poliéster insaturado e fibra de vidro provenientes dos processos de transformação: Moldagem por contato manual Hand lay-up, moldagem por projeção simultânea Spray-up e moldagem por injeção de resina Resin Transfer Moulding - RTM. As rebarbas de compósitos, oriundas das empresas transformadoras, são descartadas como lixo em aterros industriais ou clandestinos e levam décadas para se degradarem, poluindo, desta forma, o meio ambiente. A utilização destes resíduos pode conduzir ao desenvolvimento de uma nova tecnologia competitiva e sustentável. Este trabalho propõe a moagem e micronização das rebarbas de compósitos dando origem a um pó fino, contendo resina mais vidro, e substituição da carga mineral (calcita - CaCO3), tradicionalmente utilizada no processo RTM, por este pó, denominado pó de rebarba de compósito a base de resina poliéster e fibra de vidro. Confeccionaram-se placas de ensaios variando o tipo de carga, entre calcita e pó de rebarba, e a porcentagem em peso da carga na mistura com a resina. Em corpos-de-prova retirados das placas foram realizados ensaios de resistência à tração, resistência à flexão, resistência ao impacto e dureza. Complementarmente, foram realizados ensaios de densidade aparente das cargas, viscosidade da mistura, contração linear, exame microscópico e ensaio prático operacional, contribuindo para avaliar a proposta apresentada. Os resultados obtidos mostraram, que em alguns casos, ocorreram variações de propriedades. Em contrapartida expressaram-se fatores limitantes como por exemplo a viscosidade da mistura contendo pó de rebarba. Entretanto, pode-se afirmar que, tanto tecnicamente quanto operacionalmente, é possível a substituição do pó de calcita pelo pó de rebarba de compósito no processo de moldagem por injeção... / In this research the exploitation of the residues of composites was studied the resin polyester not saturated and fiber glass proceeding from the transformation processes: Molding for manual contact Hand lay-up, molding for simultaneous projection Spray-up and molding for resin injection Resin Transfer Moulding - RTM. The barbs of composites, deriving of the transforming companies, they are discarded as garbage in appropriate or clandestine places and take decades to be degraded, contaminating, of this form, the environment. The use it of these residues can lead to the development of a new competitive and sustainable technology. This work considers the milling and particle's formation of the barbs of composites giving origin to a fine dust, contend resin more glass, e substitution of the mineral load (calcite - CaCO3) traditionally used in process RTM for this dust, called dust of composite barb the resin base polyester and fiber glass. Plates of assays had been confectioned varying the type of load, between calcite and dust of barb, e the percentage in weight of the load in the mixture with the resin. In body-of-test removed of the plates assays of tensile strenght had been carried through, resistance to the flexion, resistance to the impact and hardness. Complementarily, assays of apparent density of loads had been carried through, viscosity of the mixture, linear contraction, microscopical examination and operational practical assay, contributing to evaluate the proposal presented. The gotten results had shown, that in some cases, had occurred variations of properties. On the other hand limitantes factors had been expressed as for example the viscosity of the mixture contends barb dust...(Complete abstract click electronic access below)

Made available in DSpace on 2014-10-09T12:53:10Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T13:58:37Z (GMT). No. of bitstreams: 0 / Dissertação (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Orientador: Alcides Lopes Leão / Banca: Adriano Wagner Ballarin / Banca: José Augusto Marcondes Agnelli / Resumo: Nesta pesquisa estudou-se o aproveitamento dos resíduos de compósitos a base de resina poliéster insaturado e fibra de vidro provenientes dos processos de transformação: Moldagem por contato manual "Hand lay-up", moldagem por projeção simultânea "Spray-up" e moldagem por injeção de resina "Resin Transfer Moulding - RTM". As rebarbas de compósitos, oriundas das empresas transformadoras, são descartadas como lixo em aterros industriais ou clandestinos e levam décadas para se degradarem, poluindo, desta forma, o meio ambiente. A utilização destes resíduos pode conduzir ao desenvolvimento de uma nova tecnologia competitiva e sustentável. Este trabalho propõe a moagem e micronização das rebarbas de compósitos dando origem a um pó fino, contendo resina mais vidro, e substituição da carga mineral (calcita - CaCO3), tradicionalmente utilizada no processo RTM, por este pó, denominado pó de rebarba de compósito a base de resina poliéster e fibra de vidro. Confeccionaram-se placas de ensaios variando o tipo de carga, entre calcita e pó de rebarba, e a porcentagem em peso da carga na mistura com a resina. Em corpos-de-prova retirados das placas foram realizados ensaios de resistência à tração, resistência à flexão, resistência ao impacto e dureza. Complementarmente, foram realizados ensaios de densidade aparente das cargas, viscosidade da mistura, contração linear, exame microscópico e ensaio prático operacional, contribuindo para avaliar a proposta apresentada. Os resultados obtidos mostraram, que em alguns casos, ocorreram variações de propriedades. Em contrapartida expressaram-se fatores limitantes como por exemplo a viscosidade da mistura contendo pó de rebarba. Entretanto, pode-se afirmar que, tanto tecnicamente quanto operacionalmente, é possível a substituição do pó de calcita pelo pó de rebarba de compósito no processo de moldagem por injeção...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: In this research the exploitation of the residues of composites was studied the resin polyester not saturated and fiber glass proceeding from the transformation processes: Molding for manual contact "Hand lay-up", molding for simultaneous projection "Spray-up" and molding for resin injection "Resin Transfer Moulding - RTM". The barbs of composites, deriving of the transforming companies, they are discarded as garbage in appropriate or clandestine places and take decades to be degraded, contaminating, of this form, the environment. The use it of these residues can lead to the development of a new competitive and sustainable technology. This work considers the milling and particle's formation of the barbs of composites giving origin to a fine dust, contend resin more glass, e substitution of the mineral load (calcite - CaCO3) traditionally used in process RTM for this dust, called dust of composite barb the resin base polyester and fiber glass. Plates of assays had been confectioned varying the type of load, between calcite and dust of barb, e the percentage in weight of the load in the mixture with the resin. In body-of-test removed of the plates assays of tensile strenght had been carried through, resistance to the flexion, resistance to the impact and hardness. Complementarily, assays of apparent density of loads had been carried through, viscosity of the mixture, linear contraction, microscopical examination and operational practical assay, contributing to evaluate the proposal presented. The gotten results had shown, that in some cases, had occurred variations of properties. On the other hand limitantes factors had been expressed as for example the viscosity of the mixture contends barb dust...(Complete abstract click electronic access below) / Mestre