Experiments on the production of porous metallic materials were performed on Fe-base and Al-base alloys. The method involves dissolution of gases in the liquid state and solidification at various cooling rates. The alloy compositions were selected to induce solidification of primary particles intended to control the pore distribution. For the Fe-base alloys, nitrogen was introduced into the melt by dissolution of chromium nitride powder. Fe-Cr-Mn-Si-C alloys featuring M7C3 carbide particles were selected. For the Al-base alloys, hydrogen gas was dissolved into the melt by decomposition of water vapor. Al-Ti and Al-Fe alloys featuring primary Al3Ti and Al3Fe intermetallic particles, respectively, were considered. In the Fe-base alloys, a homogeneous distribution of gas pores through the specimens’ volume was obtained at high cooling rate (water quenching) and after introduction of external nucleating agents. In the case of the Al-base alloys, a good pore distribution was observed at all cooling rates and without addition of nucleating agents. Calculations of the variation of nitrogen (respectively hydrogen) solubility based on Wagner interaction parameters suggest that pore nucleation and growth occur during precipitation of the primary particles (M7C3 carbides, Al3Ti or Al3Fe intermetallics), due to composition changes in the melt and resultant supersaturation with gas atoms. Microscopic analyses revealed that the primary particles control the pore growth in the melt and act as barriers between adjacent pores, thereby preventing pore coalescence and promoting a fine pore distribution. Uniaxial compression testing of the porous Al-Ti and Al-Fe materials showed the typical compressive behavior of cellular metals. Further work is needed to improve the quality and reproducibility of the porous structures which can possibly be used in energy absorption or load-bearing applications. As a corollary result of the quenching of hypereutectic Fe-Cr-Mn-Si-C alloys in the experiments of synthesis of porous metals, a homogeneous featureless structure was observed in some parts of the samples, instead of the equilibrium structure of M7C3 and eutectic phases. Subsequent investigations on rapid solidification of Fe-base alloys at various alloy compositions and cooling rates led to the formation of a single-phase structure for the composition Fe-8Cr-6Mn-5Mo-5Si-3.2C (wt.%), at relatively low cooling rates (≈103 K/s) and for large sample dimensions (2.85 mm). The single phase, which is likely to be the hcp ɛ-phase, was found to decompose into a finely distributed structure of bainite and carbides at ≈600 °C. The annealed structure showed very high hardness values (850 to 1200 HV), which could be exploited in the development of high-strength Fe-base materials. / QC 20100809

This thesis deals with peritectic reactions and transformations that occur during the solidification of many alloys. Peritectics are believed to be a major cause of crack-formation in many steels, thus, good knowledge of the mechanisms by which these phenomena occur is essential for preventing such defects. The thesis also handles the behaviour of metals, in particular cast structures, during hot forming. Grain size and microstructure are of most importance in determining the strength, toughness and performance of a steel. For achieving enhanced mechanical and microstructural properties, good understanding of the phenomena occurring during hot forming is required. Peritectic reactions and transformations were studied in Fe-base and steel alloys through differential thermal analysis (DTA) experiments and micrographic investigation of quenched DTA samples. The effect of the ferrite/austenite interface strain during the peritectic reaction on equilibrium conditions was thermodynamically analysed, and the results were related to temperature observations from DTA experiments conducted on Fe-base alloys and low-alloy steels. Massive transformations from ferrite to austenite were observed in the micrographs of a number of quenched low-alloy steel samples and it was proposed that these transformations are uncontrolled by diffusion, and occur in the solid state as a visco-plastic stress relief process. DTA study of an austenitic stainless steel indicated that the alloy can exhibit primary precipitations to either ferrite or austenite. A continuously-cast breakout shell of the steel was analyzed and it was suggested that the observed irregularities in growth were due to alternating precipitations of ferrite and austenite; parts of the shell with higher ratios of primary-precipitated ferrite shrink in volume at the peritectic temperature and experience reduced growths. An experimental method for studying the behaviour of metals during hot forming developed, and hot compression tests were conducted on cast copper and ball-bearing steel samples. Flow stress curves were obtained at varying temperatures and strain rates, and the results showed good agreement with earlier observations reported in literature. Micrographic analysis of quenched samples revealed variations in grain size and a model was fitted to describe the grain size as a function of deformation temperature and strain. Solidification growth during continuous casting of stainless steel and copper was numerically modelled. A varying heat transfer coefficient was proposed to approximate the experimentally measured growth irregularities in the continuously-cast stainless steel breakout shell. Solidification growth of pure copper was also modelled in the Southwire continuous casting process. Temperature measurements from the chill mould were used to approximate the temperature gradient and the heat extraction from the solidifying strand, and the results were used in a two-dimensional model of solidification. / QC 20100803