This work investigates the defect energies, band alignments, and charge carrier recombination in polycrystalline Cu(In1-xGax)(Se1-ySy)2 chalcopyrite thin films and the interrelationship with the alloy composition. Photoluminescence spectroscopy of investigated Cu-poor Cu(In,Ga)(Se,S)2 layers generally shows broad emission lines with the corresponding maxima shifting towards higher energies under decreasing temperature or under increasing excitation power. Admittance spectroscopy of Cu-poor ZnO/CdS/Cu(In,Ga)(Se,S)2 chalcopyrite devices shows that the activation energies of the dominant defect distributions involving donors at the CdS/absorber interface and deep acceptors in the chalcopyrite bulk, increase upon alloying CuInSe2 with S. The band alignments within the Cu(In1-xGax)(Se1-ySy)2 system are determined using the energy position of the bulk acceptor state as a reference. The band gap enlargement under Ga alloying is accommodated almost exclusively in the rise of the conduction band edge, whereas the increase of band gap upon alloying with S is shared between comparable valence and conduction band offsets. The extrapolated band discontinuities [delta]EV(CuInSe2/CuInS2) = -0.23 eV, [delta]EC(CuInSe2/CuInS2) = 0.21 eV, [delta]EV(CuInSe2/CuGaSe2) = 0.036 eV, and [delta]EC(CuInSe2/CuGaSe2) = 0.7 eV are in good agreement with theoretical predictions. Current-voltage analysis of Cu-poor ZnO/CdS/Cu(In,Ga)(Se,S)2 devices reveals recombination barriers which follow the band gap energy of the absorber irrespective of alloy composition, as expected for dominant recombination in the chalcopyrite bulk. In turn, the recombination at the active junction interface prevails in Cu-rich devices which display substantially smaller barriers when compared to the band gap energy of the absorber. The result indicates that the Cu-stoichiometry is the driving compositional parameter for the charge carrier recombination in the chalcopyrite heterojunctions under investigations.

This work investigates the defect energies, band alignments, and charge carrier recombination in polycrystalline Cu(In1-xGax)(Se1-ySy)2 chalcopyrite thin films and the interrelationship with the alloy composition. Photoluminescence spectroscopy of investigated Cu-poor Cu(In,Ga)(Se,S)2 layers generally shows broad emission lines with the corresponding maxima shifting towards higher energies under decreasing temperature or under increasing excitation power. Admittance spectroscopy of Cu-poor ZnO/CdS/Cu(In,Ga)(Se,S)2 chalcopyrite devices shows that the activation energies of the dominant defect distributions involving donors at the CdS/absorber interface and deep acceptors in the chalcopyrite bulk, increase upon alloying CuInSe2 with S. The band alignments within the Cu(In1-xGax)(Se1-ySy)2 system are determined using the energy position of the bulk acceptor state as a reference. The band gap enlargement under Ga alloying is accommodated almost exclusively in the rise of the conduction band edge, whereas the increase of band gap upon alloying with S is shared between comparable valence and conduction band offsets. The extrapolated band discontinuities [delta]EV(CuInSe2/CuInS2) = -0.23 eV, [delta]EC(CuInSe2/CuInS2) = 0.21 eV, [delta]EV(CuInSe2/CuGaSe2) = 0.036 eV, and [delta]EC(CuInSe2/CuGaSe2) = 0.7 eV are in good agreement with theoretical predictions. Current-voltage analysis of Cu-poor ZnO/CdS/Cu(In,Ga)(Se,S)2 devices reveals recombination barriers which follow the band gap energy of the absorber irrespective of alloy composition, as expected for dominant recombination in the chalcopyrite bulk. In turn, the recombination at the active junction interface prevails in Cu-rich devices which display substantially smaller barriers when compared to the band gap energy of the absorber. The result indicates that the Cu-stoichiometry is the driving compositional parameter for the charge carrier recombination in the chalcopyrite heterojunctions under investigations.

No description available.