Made available in DSpace on 2014-12-17T14:57:40Z (GMT). No. of bitstreams: 1 OsvaldoCS.pdf: 1194235 bytes, checksum: da247435df103f473806af70be8f1c3e (MD5) Previous issue date: 2007-06-01 / The study of the physical and mechanic properties is an analysis of unquestioned importance on the production of the ceramic materials. In the region of the Rec?ncavo Baiano, there are ceramic and small brick factories, that still use rudimentary techniques, where the necessity of characterization of raw materials is denounced by the quality of the final product. The present work has for objective to study the behavior of the clay proceeding from the region of the Rec?ncavo, between the cities of Candeias and Cama?ari/Ba, with addition of 5, 10 and 15% by weight of brick scraps, trying to optimize the physic and mechanical properties of the final product, aiming a better possibility of being manufactured, mechanic resistance, low linear retraction and water absorption. The brick scraps and the clay were characterized by FRX, DRX, TG, ATD and the granulometric analysis. Samples for testing where prepared by uniaxial pressing at 25Mpa, in 60x20x5mm size. The evaluated technological properties were: linear retraction, water absorption, apparent porosity and flexural strength. The samples were burned in electric oven in the temperatures of 850?, 950? and 1050?C and compared its mechanical properties and the gresification. With addition of 15% by weight of brick scraps and burning at 900?-1000?C the samples showed properties superior to that clay / O estudo das propriedades f?sicas e mec?nicas ? uma an?lise de import?ncia inquestion?vel na produ??o dos materiais cer?micos. Na regi?o do Rec?ncavo Baiano, encontram-se cer?micas e pequenas olarias, que ainda utilizam t?cnicas rudimentares, onde a necessidade de caracteriza??o das mat?rias-primas ? denunciada pela qualidade do produto final. O presente trabalho tem por objetivo estudar o comportamento da argila proveniente da regi?o do Rec?ncavo Baiano, compreendida entre os munic?pios de Candeias e Cama?ari, com adi??o de 5, 10 e 15% em peso de rejeitos cer?micos, procurando otimizar as propriedades f?sico-mec?nicas do produto final, visando uma melhor trabalhabilidade, resist?ncia mec?nica e baixas retra??o linear e absor??o de ?gua. O rejeito cer?mico e a argila foram caracterizados por FRX, DRX, TG, ATD e analise granulom?trica. Foram preparados corpos-de-prova com dimens?es de 60x20x5mm, por prensagem uniaxial a 25MPa. As propriedades tecnol?gicas avaliadas foram: retra??o linear, absor??o de ?gua, porosidade aparente e resist?ncia mec?nica ? flex?o. Os corpos foram sinterizados em forno resistivo nas temperaturas de 850?, 950? e 1050?C e comparadas suas propriedades mec?nicas e a gresifica??o. Obteve-se para os corpos com incorpora??o de 15% em peso de rejeitos cer?micos, propriedades superiores as da argila, nas temperaturas entre 900? e 1000? C

Industry sector is of great importance for economic development in every country. However, increasing discussions about environmental impacts led to strategies to minimize its effects, optimize production and technology, in a search for a process capable of superior production and lesser impact on nature. This thesis proposes development and analysis of supports for production of ceramic plates of a semi-porous kind (BIIb class), with water absorption between 6 -10%, and porcelain plates, with water absorption smaller than 0.5%. Inside the supports, we incorporated solid residues from the primary treatment of brine to be electrolyzed for production of caustic soda, hydrogen, and chlorine, using dry technology. The study was conducted from a partnership between industries from thermoplastic resin and ceramic plates production. Nowadays, Solid Residue from Brine Treatment (SRBT) is reinjected in salt mines which, although environmentally adequate, might not be the best solution. Therefore, we believe that SRBT incorporation at ceramic plate´s support is a viable alternative for better destination of this chemical residue that allows lower consumption of nature´s non-renewable resources and brings advantages to the support. This study generated 954 test subjects to verify the influence of different temperatures and SRBT concentrations in processing and densification using different tests. We test apparent density, linear retraction, water absorption, flexure strength, extraction expansion, black-heart formation, humidity expansion, thermal dilation coefficient and water loss in high temperatures. After the subject characterization, we gather that SRBT did not alter the main features of the material before burning, as presented by apparent density and mechanical strength tests. In all tested concentrations, rejects brought specific gains to mechanical strength especially for subjects of BIIb class. We infer that SRBT application in ceramic plates support is viable if one takes cautionary measures regarding homogenization of the material. / O setor industrial é de grande importância para o desenvolvimento econômico em todos os países. No entanto, discussões crescentes sobre os impactos ambientais levaram a estratégias para minimizar seus efeitos, otimizar a produção e a tecnologia, em busca de um processo capaz de produzir com qualidade superior e menor impacto sobre a natureza. Esta tese propõe o desenvolvimento e análise de suportes para produção de placas cerâmicas semi-porosas (classe BIIb), com absorção de água entre 6-10% e placas de porcelana, com absorção de água menor que 0,5%. Dentro dos suportes, incorporamos resíduos sólidos do tratamento primário de salmoura a ser eletrolisado para produção de soda cáustica, hidrogênio e cloro, utilizando tecnologia seca. O estudo foi realizado a partir de uma parceria entre indústrias de resinas termoplásticas e produção de placas cerâmicas. Atualmente, o Resíduo Sólido de Tratamento de Salmoura (RSTS) é reinjetado em minas de sal que, embora ambientalmente adequadas, podem não ser a melhor solução. Por isso, acreditamos que a incorporação da RSTS no suporte de placas cerâmicas é uma alternativa viável para melhor destinação desse resíduo químico que permite menor consumo dos recursos não renováveis da natureza e traz vantagens ao suporte. Este estudo gerou 954 corpos de teste para verificar a influência de diferentes temperaturas e concentrações de RSTS no processamento e densificação usando diferentes testes. Testamos densidade aparente, retração linear, absorção de água, resistência à flexão, expansão de extração, formação de coração negro, expansão de umidade, coeficiente de dilatação térmica e perda de água em altas temperaturas. Após a caracterização, concluímos que o RSTS não alterou as principais características do material antes da queima, como apresentado pelos testes de densidade aparente e resistência mecânica. Em todas as concentrações testadas, os rejeitos trouxeram ganhos específicos para a resistência mecânica, especialmente para corpos da classe BIIb. Infere-se que a aplicação da RSTS em placas cerâmicas de suporte é viável, caso se tomem medidas de cautela quanto à homogeneização do material.