Polymeric isoporous membranes have many interesting properties leading to various specific applications in different fields. However, such structures also have one main drawback, namely their poor solvent stability, which should be improved to extend the range of their possible applications. Therefore, this project will focus on the enhancement of solvent stability of polymeric isoporous membranes by UV cross-linking. Stable isoporous films were obtained by creating honeycomb membranes from star polystyrene (PS) and its derivatives. The star PS was synthesized by Atom Transfer Radical Polymerization (ATRP) method and was then functionalized with methacrylate groups. The isoporous films made from these materials maintained the honeycomb structures after curing by UV light and immersion in chloroform. The crosslinking of PS under UV light exposure rather than the cross-linking of the methacrylates groups was responsible for the solvent stability of these membranes. To further investigate the effect of specific end-groups on the film stability, PEG2k-G3-PCL30 linear-dendritic-linear hybrid polymers and its derivatives with allyl, acrylate, methacrylate end-groups were employed to cast films. Functionalized PEG2k-G3-PCL30 linear-dendritic-linear hybrid isoporous films were cross-linked by UV-induced thiol-ene reactions and allyl reactions. However, no significant increase in the solvent stability of these kinds of films was observed. When mixing PEG2k-G3-PCL30 linear-dendritic-linear hybrids with star PS, stable isoporous films could be obtained. The pores became smaller but the isoporous structures were still kept.

Ce travail de thèse de doctorat vise à l’élaboration de surfaces poreuses hiérarchiquement structurées à partir de copolymères aux structures bien définies ainsi qu’à l’étude de leurs propriétés. La chimie des polymères, en constante évolution, a permis dans ce travail de thèse la synthèse de copolymères diblocs de natures diverses par des techniques de polymérisation radicalaire contrôlée tout aussi variées. En effet, la polymérisation radicalaire contrôlée par les nitroxydes (NMP), par transfert d’atome (ATRP), par transfert réversible d’addition/fragmentation (RAFT) et par le Cu(0) ont été utilisées pour la synthèse de copolymères diblocs associant un bloc de poly(styrène) à divers blocs d’acrylates ou de 4-vinylpyridine. Intimement associée à un procédé d’élaboration basé sur l’évaporation de solvant, nommé figure de souffle (trad. Breath Figure), la synthèse de ces copolymères a permis l’élaboration de surfaces poreuses hiérarchiquement structurées aux échelles du micro et nanomètre. Les différentes phases ont conféré à ces matériaux des propriétés particulières d’adhésion, de mouillabilité ou encore de bioactivité. Ces recherches doctorales ont bénéficié de la double compétence du laboratoire en chimie et en physico-chimie des polymères. En effet, des techniques de microscopie (optique, à force atomique ou électronique), de diffusion de rayonnement (neutrons et rayon-X aux petits angles) ainsi que des tests de pégosité et de mouillabilité ont permis l’étude de la structuration des films ainsi que l’étude de leurs propriétés de surface. / The present studies aim at designing hierarchically structured porous surface from copolymers with well defined structures. As a science in constant evolution, polymer chemistry, enable the synthesis of diblock copolymers with different natures by the mean of various radical controlled polymerization techniques. Indeed, radical controlled polymerization with nitroxyde (NMP), by atom transfer (ATRP), by reversible addition/fragmentation transfer (RAFT) or by Cu(0) were used for the synthesis of diblock copolymers based on polystyrene and different acrylates or 4-vinylpyridine blocks. The intimately association between a fast solvent evaporation process named the Breath Figure and the synthesis of the copolymers enable the production of hierarchically structured materials from micro to nanoscale. The nature of the different blocks confers adhesion, wettability or bioactivity properties to these materials. These researches benefit from the chemistry and physico-chemistry laboratory competences. Indeed, microscopy techniques (optical, atomic force and electronic), scattering (small angle neutron or X-ray) as well as tack or wettability measurements enable the complete characterization of films structuration and point up their properties.

Nous évaluons des films polymères poreux structurés en tant que nouveaux supports pour des photosensibilisateurs de l’oxygène singulet. L’objectif de cette association est l’obtention de matériaux photo-actifs à grande surface d’échange. Ces surfaces polymères, structurées ici en nid d’abeille, sont obtenues par la technique « breath figure » (trad. figure de souffle), à partir de polymères bien définis synthétisés par polymérisation radicalaire contrôlée par des nitroxydes (NMP), par transfert d’atome (ATRP) et par transfert réversible par addition/fragmentation (RAFT). Le photosensibilisateur rose Bengale a été greffé de manière covalente au polymère, soit par post-greffage sur un polymère précurseur, soit par modification d’un monomère fonctionnel puis copolymérisation de ce dernier avec du styrène. Ces différentes synthèses conduisent à des films contenant différents taux de rose Bengale. Les films ont été examinés en microscopie (fluorescence, confocale et champ large, électronique à balayage) afin d’établir la structuration des films et la localisation des espèces fluorescentes. L’efficacité des films polymères pour la photo-oxydation a été testée à l’interface liquide/solide en suivant par spectroscopie UV-visible la dégradation du dihydroxynaphtalène (DHN) ou de l’α-terpinène par l’oxygène singulet produit sous irradiation visible. Les films structurés sont environ cinq fois plus efficaces que les films non-poreux de même composition utilisés dans les mêmes conditions, ce qui s’explique par leur surface spécifique et par la localisation préférentielle du rose Bengale à la surface du matériau. / We evaluate structured porous polymer films as new substrates for photosensitizers of singlet oxygen, with a view to obtaining photo-active materials with high specific exchange areas. Here, honeycomb polymer films are obtained by the breath figure process, using well defined polymers synthesized by nitroxide-controlled radical polymerization (NMP), atom transfer polymerization (ATRP) and reversible addition/fragmentation transfer (RAFT). The photosensitizer, rose Bengal, is either post-grafted covalently to the polymer precursor, or pre-grafted to a monomer functional unit which is copolymerized with polystyrene. These syntheses lead to films with different rose Bengal concentrations. We determine the structure of the films and the location of the fluorescent dye by scanning electron microscopy and widefield and confocal microscopy. Efficiency of production of singlet oxygen was tested at a solid/liquid interface by monitoring the oxidation of dihydroxynaphthalene and α-terpinene, using UV-visible absorption spectroscopy. Honeycomb films are about five times more efficient than non-porous films of the same composition used in the same, as may be explained by their higher specific surface area and the preferential location of the photosensitizer at the film surface.