The content of analytical part of this thesis is the study of airborne dust samples collected in places with its higher concentration: by the Prague Ring (D0 motorway) and near the Ostrava's iron-mills. In both places, automobile transportation or industrial production are the primary sources of particulate matter emissions in the air. Received samples of PM1, PM2, PM10 a TSP filters were obtained by a standard air pollution monitoring procedure. This study examines the relationship between the magnetic parameters of the samples, their level of concentration of metals frequently present in emissions from these sources, the total mass of the dust fraction in the samples and the meteorological parameters (for Ostrava samples). The magnetic properties of the filters were investigated by magnetometric analyzes using a vibration sampling magnetometer. The concentrations of the metals were monitored by X-ray fluorescence spectrometer, the weight of parts of dust filtres was measured on laboratory scales.

No description available.

Dans les systèmes des télécommunications, beaucoup d’études ont été entreprises pour intégrer des composants passifs non réciproques. Le bon fonctionnement des circulateurs exige souvent des aimants volumineux et lourds qui assurent une orientation uniforme des moments magnétiques du matériau ferrite. Pour tendre vers l’intégration et la miniaturisation des circulateurs, les nanotechnologies peuvent offrir des solutions intéressantes. L’objectif de cette thèse a été de développer un circulateur coplanaire auto-polarisé. L'approche choisie est fondée sur la réalisation de substrats composites à «nano-fil ferrimagnétiques». Elle consiste à faire un dépôt par magnétophorèse ou dip-coating de nanoparticules de ferrite de cobalt dans des membranes d’alumine poreuses et de les orienter sous champ magnétique de manière uniforme. Des substrats composites magnétiques ont été fabriqués à partir de nanoparticules CoFe2O4 dispersées dans une matrice sol-gel de silice en utilisant la technique de Dip-coating avec et sans un champ magnétique appliqué. De nombreuses études ont été faites afin d'étudier le comportement magnétique et diélectrique de ces substrats : VSM, polarimétrie spectrale, MFM et autres. Les cycles d'hystérésis montrent une forte différence des valeurs des champs coercitifs (μ0Hc) et rémanents (Mr/Ms) si, durant la fabrication, un champ magnétique est appliqué ou non, démontrant ainsi l'orientation (ou non) des nanoparticules. Ce nano-composite est un candidat intéressant pour la fabrication de circulateurs même si la concentration et l’orientation des particules sont insuffisantes. Des circulateurs ont été conçus, modélisés et simulés à l'aide du logiciel HFSS. Suite à des résultats de simulation intéressants; un premier prototype a été fabriqué et caractérisé en hautes fréquences. Les résultats de mesure ont montré un phénomène de circulation, qui reste très faible en raison du faible pourcentage de nanoparticules magnétiques dans le composite et de leur orientation imparfaite. Les verrous technologiques ont été clairement identifiés et ne permettent pas, pour l’instant, de réaliser un circulateur opérationnel / In telecommunications systems, many studies have been undertaken to integrate non-reciprocal passive components. The proper functioning of circulators often requires large and heavy magnets that ensure a uniform orientation of the magnetic moments of the ferrite material. To work towards the integration and miniaturization of circulators, nanotechnology can offer interesting solutions. The aim of this thesis was to develop a self-biased coplanar circulator. The approach is based on the production of composite substrates "ferrimagnetic nanowire." It consists in a magnetophoresis or a dip-coating deposition of cobalt ferrite nanoparticles in porous alumina membranes and orienting them in a magnetic field uniformly. Magnetic composite substrates were made from CoFe2O4 nanoparticles dispersed in a matrix of silica sol-gel using the dip-coating technique with and without an applied magnetic field. Many studies have been made to study the magnetic and dielectric behavior of these substrates: VSM, spectral polarimetry, MFM and others. The hysteresis loops show a strong difference in the values of coercive fields (μ0Hc) and persistent (Mr / Ms) if, during the fabrication, a magnetic field is applied or not, therefore showing the orientation (or not) of nanoparticles. This nano-composite is an interesting candidate for the fabrication of circulators even if the concentration and the particle orientation are insufficient. Circulators were designed, modeled and simulated using the HFSS software. Following the interesting results of simulation; a first prototype was fabricated and characterized at high frequencies. The measurement results showed a circulation phenomenon, which is very low due to the small percentage of magnetic nanoparticles in the composite and their imperfect orientation. Technological barriers have been clearly identified and do not allow for the time to achieve an operational circulator

Corrosion protection is very significant for metals in modern society from the view of industrial development. This thesis work project involves a research study that is aimed to investigate the effect of corrosion on the mechanical strength and magnetic properties of four no treated or treated Somaloy® component samples (Somaloy®700 1P,  Somaloy®700 3P, Somaloy®700HR 5P and Somaloy®110i 5P) provided by Höganäs AB and laminated steel sheets by salt spray test. The coatings for protection are phosphoric acid coating, sodium silicate coating, DCA-Modified silicone conformal coating and water-borne single coat paint respectively. Then the protective properties are evaluated by Electrochemical Impedance Spectroscopy (EIS) in 0.1 mol/L NaCl solution after 7 days exposure.   From transverse rupture strength (TRS) and hysteresis loop measurements by salt spray test, although the bar samples are treated coating, the corrosion decreases the mechanical strength to a certain extent more or less over time. For the magnetic properties, the corrosive environments hardly influence the magnetic parameters of the no treated or four types of coatings treated Somaloy® components. But the all kinds of magnetic parameters for laminated ring samples have a great variation after salt spray test.   In the EIS measurements, for the no treated samples, the initial corrosion resistance is only several hundred ohms and decreases after 1 hour, 8 hours and 1day exposure, then increases to a certain extent with time due to the corrosion products formed on the surface. For the sodium silicate coating, the initial corrosion resistance is approximately several ten thousands ohms and decreases rapidly only after 1 day exposure to several hundred ohms due to the sodium silicate film dissolves in the electrolyte solution and has no effective protective property. Then the following corrosion process is almost same as the no treated samples. For the water-borne single coat paint, the initial corrosion resistance can reach to several Giga-ohms and decreases over time, but can still stay at  level, indicating that this coating has a very good and effective protective properties.   EIS experiments indicate that water-borne single coat paint has a more effective protection than sodium silicate coating and can apply a better corrosion protection for the Somaloy® components   Key words: corrosion protection, soft magnetic composites, phosphoric acid coating, sodium silicate coating, DCA-Modified silicone conformal coating , water-borne single coat paint, salt spray test, TRS, hysteresis loop, EIS

Superaustenitická korozivzdorná ocel typu 22Cr25NiWCoCu určená pro vysokoteplotní aplikace v energetickém průmyslu byla studována za podmínek nízkocyklové únavy při pokojové a zvýšené teplotě. Jednotlivé vzorky byly podrobeny různým zátěžným procedurám, což umožnilo studium materiálové odezvy spolu s mechanismem poškození. Křivky cyklického zpevnění/změkčení, cyklického napětí a Coffin-Mansonovy křivky byly vyhodnoceny. Únavová životnost materiálu byla diskutována s ohledem na uplatňované mechanismy poškození, které se vyvinuly za specifických zátěžných podmínek. Standardní izotermální únavové experimenty byly provedeny při pokojové a zvýšené teplotě. Hysterezní smyčky zaznamenané během cyklického zatěžování byly analyzovány pomocí zobecněné statistické teorie hysterezní smyčky. Pro různé amplitudy napětí byla určena jak distribuce hustoty pravděpodobnosti interních kritických napětí (dále PDF), tak rovněž zjištěn její vývoj během cyklického namáhání. Zjištěné průběhy PDF byly korelovány s vývojem povrchového reliéfu a vnitřního dislokačního uspořádání zdokumentované pro obě teploty pomocí rastrovací elektronové mikroskopie (SEM) vybavené technikou fokusovaného iontového svazku (FIB), která umožnila rovněž efektivní studium nukleace povrchových únavových trhlin. Při cyklickém zatížení při pokojové teplotě byla pozorována lokalizace cyklické plastické deformace do perzistentních skluzových pásů (PSP). V místech, kde tyto PSP vystupují na povrch materiálu byly pozorovány perzistentní skluzové stopy (PSS) tvořené extruzemi a intruzemi. Postupné prohlubování intruzí, zejména na čele nejhlubší intruze, vede k iniciaci únavové trhliny. Odlišný mechanismus tvorby trhlin byl zjištěn při únavové zkoušce při zvýšené teplotě, kde zásadní roli hrál vliv prostředí. Rychlá oxidace hranic zrn a jejich následné popraskání představuje dominantní mechanismus v I. stádiu nukleace trhlin. Aplikace desetiminutové prodlevy v tahové části zátěžného cyklu vedlo k vývoji vnitřního (kavitačního) poškozování. Mechanismy vnitřního poškozování byly studovány na podélných řezech rovnoběžných s napěťovou osou zkušebních vzorků. Trhliny a jejich vztah k hranicím zrn a dvojčat byly studovány pomocí difrakce zpětně odražených elektronů (EBSD). Vliv prodlevy na únavovou životnost byl korelován s vývojem povrchového reliéfu a vnitřního poškození. Vzorky z uvedené oceli byly rovněž podrobeny zkouškám termomechanické únavy (TMF), při nichž se v čase mění jak zátěžná síla tak i teplota. Termomechanické únavové zkoušky v režimu soufázném (in-phase) a protifázném (out-of-phase) byly provedeny jak s prodlevou, tak i bez ní. Ve všech případech bylo pozorováno rychlé cyklické zpevnění bez ohledu na použitou amplitudu deformace, u vzorků testovaných v out-of-phase režimu byla zjištěna tendence k saturaci. Zkoumáním povrchového reliéfu za pomocí technik SEM a FIB byla odhalena přednostní oxidace hranic zrn a následné praskání těchto hranic kolmo k ose zatížení. Prodlevy v cyklech při maximálním napětí vedly ke zvýšení amplitudy plastické deformace a následně ke creepovému poškození ve formě vnitřních kavit a trhlin. Interkrystalické šíření trhlin bylo pozorováno na vzorcích testovaných v režimu in-phase. Vývoj poškození v režimu out-of-phase nebyl principiálně ovlivněn zařazením prodlevy do zátěžného cyklu. Charakteristickým znakem namáhání v režimu out-of-phase je nukleace několika trhlin v homogenní oxidické vrstvě jdoucích napříč zrny kolmo k ose zatěžování.