Issues of major relevance to the n-type conductivity of Al0.77Ga0.23N associated with Si and O incorporation, their shallow donor or deep donor level behavior, and carrier compensation are elucidated by allying (i) study of Si and O incorporation kinetics at high process temperature and low growth rate, and (ii) electron paramagnetic resonance measurements. The Al0.77Ga0.23N composition correlates to that Al content for which a drastic reduction of the conductivity of AlxGa1−xN is commonly reported. We note the incorporation of carbon, the role of which for the transport properties of AlxGa1−xN has not been widely discussed.

Capacitance-voltage-frequency measurements on n+-GaN/AlxGa1−xN UV/IR dual-band detectors are reported. The presence of shallow Si-donor, deep Si-donor, and C-donor/N-vacancy defect states were found to significantly alter the electrical characteristics of the detectors. The barrier Al fraction was found to change the position of the interface defect states relative to the Fermi level. The sample with Al fraction of 0.1 shows a distinct capacitance-step and hysteresis, which is attributed to C-donor/N-vacancy electron trap states located above the Fermi level (200 meV) at the heterointerface; whereas, the sample with Al fraction of 0.026 shows negative capacitance and dispersion, indicating C-donor/N-vacancy and deep Si-donor defect states located below the Fermi level (88 meV). When an i-GaN buffer layer was added to the structure, an anomalous high-frequency capacitance peak was observed and attributed to resonance scattering due to hybridization of localized Si-donor states in the band gap with conduction band states at the i-GaN/n+-GaN interface.

In this work, multi-band (multi-color) detector structures considering different semiconductor device concepts and architectures are presented. Results on detectors operating in ultraviolet-to-infrared regions (UV-to-IR) are discussed. Multi-band detectors are based on quantum dot (QD) structures; which include quantum-dots-in-a-well (DWELL), tunneling quantum dot infrared photodetectors (T-QDIPs), and bi-layer quantum dot infrared photodetectors (Bi-QDIPs); and homo-/heterojunction interfacial workfunction internal photoemission (HIWIP/HEIWIP) structures. QD-based detectors show multi-color characteristics in mid- and far-infrared (MIR/FIR) regions, where as HIWIP/HEIWIP detectors show responses in UV or near-infrared (NIR) regions, and MIR-to-FIR regions. In DWELL structures, InAs QDs are placed in an InGaAs/GaAs quantum well (QW) to introduce photon induced electronic transitions from energy states in the QD to that in QW, leading to multi-color response peaks. One of the DWELL detectors shows response peaks at ∼ 6.25, ∼ 10.5 and ∼ 23.3 µm. In T-QDIP structures, photoexcited carriers are selectively collected from InGaAs QDs through resonant tunneling, while the dark current is blocked using AlGaAs/InGaAsAlGaAs/ blocking barriers placed in the structure. A two-color T-QDIP with photoresponse peaks at 6 and 17 µm operating at room temperature and a 6 THz detector operating at 150 K are presented. Bi-QDIPs consist of two layers of InAs QDs with different QD sizes. The detector exhibits three distinct peaks at 5.6, 8.0, and 23.0 µm. A typical HIWIP/HEIWIP detector structure consists of a single (or series of) doped emitter(s) and undoped barrier(s), which are placed between two highly doped contact layers. The dual-band response arises from interband transitions of carriers in the undoped barrier and intraband transitions in the doped emitter. Two HIWIP detectors, p-GaAs/GaAs and p-Si/Si, showing interband responses with wavelength thresholds at 0.82 and 1.05 µm, and intraband responses with zero response thresholds at 70 and 32 µm, respectively, are presented. HEIWIP detectors based on n-GaN/AlGaN show an interband response in the UV region and intraband response in the 2-14 µm region. A GaN/AlGaN detector structure consisting of three electrical contacts for separate UV and IR active regions is proposed for simultaneous measurements of the two components of the photocurrent generated by UV and IR radiation.