The crystal structures of the LnAgAs2 and LnAuAs2 compounds were reinvestigated by single-crystal diffraction experiments. Contrary to the respective copper compounds, no stuffed variant of the HfCuSi2 type was found. For CeAuAs2, GdAuAs2 and TbAuAs2, a slight under-occupation of the gold position was determined, the other compounds crystallize in a 1:1:2 ratio. Additionally, LaCuAs2 was synthesized for the first time in a 1:1:2 ratio. Due to the fact that imaging plate diffraction systems were used instead of four-circle diffractometers, satellite reflections could be observed for most of the LnCuAs2 compounds (Ln = Ce, Nd, Sm, Gd, Tb, Ho), CeAuAs2, GdAuAs2 and TbAuAs2. Structure models of GdCuAs2, CeAuAs2, GdAuAs2 and TbAuAs2 were developed, rod and layer groups of the respective structural motives were determined and approximants were presented. / Die Kristallstrukturen der LnAgAs2 und LnAuAs2 Verbindungen wurden mittels Einkristallbeugungsexperimenten neu untersucht. Im Gegensatz zu den jeweiligen Kupferverbindungen wurde keine gefüllte Variante des HfCuSi2-Typs gefunden. Im Falle von CeAuAs2, GdAuAs2 und TbAuAs2 wurde eine geringfügige Unterbesetzung der Gold-Position bestimmt, die anderen Verbindungen kristallisieren in einem 1:1:2-Verhältnis. Weiterhin wurde erstmals LaCuAs2 in diesem Verhältnis synthetisiert. Aufgrund der Verwendung von Bildplattensystemen an Stelle von Vierkreisdiffraktometern konnten Satellitenreflexe für den Großteil der LnCuAs2-Verbindungen (Ln = Ce, Nd, Sm, Gd, Tb, Ho), CeAuAs2, GdAuAs2 and TbAuAs2 beobachtet werden. Strukturmodelle von GdCuAs2, CeAuAs2, GdAuAs2 und TbAuAs2 wurden entwickelt, Stab- und Ebenengruppen der einzelnen Strukturmotive wurden bestimmt und Approximanten präsentiert.

The crystal structures of the LnAgAs2 and LnAuAs2 compounds were reinvestigated by single-crystal diffraction experiments. Contrary to the respective copper compounds, no stuffed variant of the HfCuSi2 type was found. For CeAuAs2, GdAuAs2 and TbAuAs2, a slight under-occupation of the gold position was determined, the other compounds crystallize in a 1:1:2 ratio. Additionally, LaCuAs2 was synthesized for the first time in a 1:1:2 ratio. Due to the fact that imaging plate diffraction systems were used instead of four-circle diffractometers, satellite reflections could be observed for most of the LnCuAs2 compounds (Ln = Ce, Nd, Sm, Gd, Tb, Ho), CeAuAs2, GdAuAs2 and TbAuAs2. Structure models of GdCuAs2, CeAuAs2, GdAuAs2 and TbAuAs2 were developed, rod and layer groups of the respective structural motives were determined and approximants were presented. / Die Kristallstrukturen der LnAgAs2 und LnAuAs2 Verbindungen wurden mittels Einkristallbeugungsexperimenten neu untersucht. Im Gegensatz zu den jeweiligen Kupferverbindungen wurde keine gefüllte Variante des HfCuSi2-Typs gefunden. Im Falle von CeAuAs2, GdAuAs2 und TbAuAs2 wurde eine geringfügige Unterbesetzung der Gold-Position bestimmt, die anderen Verbindungen kristallisieren in einem 1:1:2-Verhältnis. Weiterhin wurde erstmals LaCuAs2 in diesem Verhältnis synthetisiert. Aufgrund der Verwendung von Bildplattensystemen an Stelle von Vierkreisdiffraktometern konnten Satellitenreflexe für den Großteil der LnCuAs2-Verbindungen (Ln = Ce, Nd, Sm, Gd, Tb, Ho), CeAuAs2, GdAuAs2 and TbAuAs2 beobachtet werden. Strukturmodelle von GdCuAs2, CeAuAs2, GdAuAs2 und TbAuAs2 wurden entwickelt, Stab- und Ebenengruppen der einzelnen Strukturmotive wurden bestimmt und Approximanten präsentiert.

No description available.