• Refine Query
  • Source
  • Publication year
  • to
  • Language
  • 11
  • 6
  • Tagged with
  • 17
  • 13
  • 12
  • 12
  • 11
  • 9
  • 9
  • 9
  • 7
  • 7
  • 5
  • 5
  • 5
  • 5
  • 5
  • About
  • The Global ETD Search service is a free service for researchers to find electronic theses and dissertations. This service is provided by the Networked Digital Library of Theses and Dissertations.
    Our metadata is collected from universities around the world. If you manage a university/consortium/country archive and want to be added, details can be found on the NDLTD website.
11

Nitrogen Without Oxygen : The effect of ferroalloys added after vacuum treatment on cleanliness of nitrogen-alloyed tool steel

Nilsson Hultén, Leo January 2021 (has links)
Nitrogen-alloyed tool steel is made at Uddeholms AB by adding high-nitrogen ferroalloy after vacuum degassing where introduced impurities are hard to remove. In this thesis two types of high-nitrogen ferrochromium are compared, a solid version and a powder cored wire. They are examined in crossection and 16 samples from four charges are examined with Pulse Distribution Analysis as well as systematic microscopy of polished cross sections. The PDA results missed smaller spinel inclusions shown in previous research to be detrimental. The wire form shows promise but more charges need to be evaluated before a conclusion is drawn. / Kvävelegerat verktygsstål tillverkas hos Uddeholms AB genom tillsats av kväverika ferrolegeringar efter vakumavgasning, och orenheter som introduceras i detta steg är svåra att avskilja. I den har uppsatsen jämförs två typer av kväverikt ferrokrom varav en i form av stycken och en i form av tråd med pulverkärna. De undersöks i tvärsnitt och totalt 16 prov från fyra charger undersöks med PDA (pulsfördelningsanalys) och systematisk mikroskopering i tvärsnitt. Resultaten från PDA missade mindre inneslutningar av spinell vilka tidigare har visat sig problematiska. Trådformen verkar lovande men fler charger behöver undersökas för att kunna dra en definitiv slutsats.
12

Evaluation of 25 MHz Ultrasonic Testing for Detection of Non-Metallic Inclusions in Steel

Isaksson, Henrietta January 2021 (has links)
Quantification of inclusions is important since it is correlated to the steel’s fatigue properties. One method that could be further developed for detection of inclusions in steel is ultrasonic testing (UST). The aim of this study is to investigate what type of inclusions, in terms of size, morphology and chemical composition, that can be detected with 25 MHz UST, and what type of inclusion that cannot be detected. This was done by firstly scanning 74 steel samples with 25 MHz UST, and then fatigue test the same samples until fracture. The inclusion that caused the fracture was then analysed with microscopy and compared with the results from the 25 MHz UST. It was found that Mn-Mg-sulphides, Ca-sulphides, oxy sulphides and complex oxides are difficult to detect with 25 MHz UST. Globular oxides can be detected with 25 MHz UST, at least down to an area of 8300 μm2 and if they are not too fragmented due to rolling. The results indicate that oxy sulphide stringers can be detected with 25 MHz UST if the inclusion have oxides in direct contact with the steel matrix, rather than oxides encapsulated by sulphides. / Kvantifiering av inneslutningar är viktigt då det korrelerar med stålets utmattningsegenskaper. En metod som kan utvecklas för detektering av inneslutningar i stål är ultraljudstestning (UT). Syftet med den här studien är att undersöka vilken typ av inneslutningar, med avseende på storlek, morfologi och kemisk sammansättning, som kan detekteras med 25 MHz UT, och vilken typ av inneslutningar som inte kan detekteras. Detta gjordes genom att först skanna 74 stålprover med 25 MHz UT och sedan utmattningstesta samma prover tills de gick till brott. Inneslutningen som orsakade brottet analyserades sedan med mikroskopi och jämfördes med resultaten från 25 MHz UT. Det visade sig att Mn-Mg-sulfider, Ca-sulfider, oxisulfider och komplexa oxider är svåra att upptäcka med 25 MHz UT. Globulära oxider kan upptäckas, åtminstone ner till en area på 8300 μm2 och om den inte har blivit för fragmenterad av valsning. Resultaten indikerar att oxisulfider kan detekteras om oxiderna är i direkt kontakt med stålmatrisen, i stället för att oxiderna är inkapslade av sulfider.
13

Extremvärdesanalys (SEV) av högkvalitativt verktygsstål : Uppskattning av maximal inneslutningsstorlek i pulverstål / Extreme values analysis (SEV) of high performance tool steel : Prediction of maximum inclusion size in powder steel

Pernefur, Emil January 2017 (has links)
This work were requested by Uddeholms AB. Uddeholm is the worldś leading manufacturer of high performance tool steel for industrial tools. The company exists worldwide and is present in over 100 countries. One of the company’s main production processes is manufacturing powder steels with extremely high quality. In this work, one of these steels has been analyzed to evaluate the presence and distribution of non-metallic inclusions. Higher demands on quality and more global competition worldwide means that you always have to strive towards perfection in the manufacturing processes. Non-metallic inclusions have severe effects on the mechanical properties of steels. That's why it's of utmost importance to investigate their presence in the tool steel and especially their size. The reason for this is because it's the largest inclusions that's the most dangerous for the material. To obtain a statistically number of certainty of the largest of inclusions, very vast areas of steel have to be examined. Therefore a theoretical method of extrapolation is often used instead to approximate the distribution of the largest inclusions. The precision of this method is still very uncertain. Different methods of this kind of analysis do exist. The method applied in this work of degree is extreme values analysis by statistics of extreme values (SEV). To ensure the pre-conditions of the extreme values analysis, a large quantity of powder steel was analyzed. This was done by light-optic microscopy (LOM) and exclusively performed by Uddeholms AB at their R&D-facility (Research and development-facility) in Hagfors. At Karlstad Universityś test-facility specimens were subjected to ultrasonic fatigue testing at 20 kHz. The specimens derived from the same material as the ones examined in LOM. The result from the ultrasonic fatigue testing were that the largest inclusions in the material were found. This was done by applying very high cycle fatigue (VHCF). To calculate the maximum theoretical inclusion size, SEV was used. The extreme values analysis was performed on gathered data from both LOM and VHCF. All fracture surfaces from the ultrasonic fatigue testing were then examined in scanning electron microscope (SEM) at Karlstad University. In SEM, the largest inclusion in every fractured surface was identified and measured. The maximum real inclusion size from the fractured surfaces was then compared to the maximum theoretically calculated inclusion size from the extreme values analysis. As it turned out the real inclusion size proved to be slightly larger than the theoretical. The difference between them was found to be 3,25 µm. Conclusions drawn were that Uddeholms powder steel exhibits very high purity and that extreme values analysis as an analytical method is recommended. However, the analysis should be repeated to underline the chosen solution methodology.
14

Study of Non-metallic Inclusion in Alloy 825

Kellner, Hans January 2017 (has links)
It is well known that inclusions affect the properties of steels and alloys. Therefore, it is important to understand what type of inclusions that exist and how they behave and especially with a focus on large size inclusions. Thus, the large size non-metallic inclusions in ferroalloy FeTi70R were investigated in two dimensions (2D) by using scanning electron microscopy (SEM) in combination with an energy dispersive technique (EDS). It was found that the FeTi70R ferroalloy contain complex oxide inclusions consisting mostly of CaO, SiO2 and TiOx. Furthermore, experimental trials were performed to investigate how these inclusions behaved when entering a melt. More specifically, a comparison between pure Fe and an Alloy 825 grade were made. These results determined the parameters effect on the transformation of the inclusions in the melt. The large size non-metallic inclusions in Alloy 825 during the ladle treatment were investigated during industrial trials by using both two dimensional (2D) and three dimensional (3D) microscopic investigations. The results showed that inclusions consisted of spherical oxides and clusters made up of oxides and nitrides. Further investigations found that the spherical inclusions were transformed from existing NMI in the FeTi70R ferroalloy and slag particles. As for the clusters, they originate from deoxidation products. Furthermore, small inclusions precipitated in the local zones around the added FeTi70R ferroalloy and titanium nitrides. Investigations also found that only Al2O3-MgO and TiN clusters exist after casting. Industrial trials were performed during the last period of the ladle treatment and using a combined electromagnetic (EMS) and gas (GS) stirring. The purpose to investigate the effect of different EMS directions on the agglomeration and on the removal of Al2O3-MgO and TiN clusters. The investigations were then performed in 3D after an electrolytic extraction of the metal samples. The results show that electromagnetic stirring in the upwards direction is best for the agglomeration of the Al2O3-MgO and TiN clusters. However, electromagnetic stirring in the downwards direction is more effective to remove clusters from the melt. This is in agreement with the theoretical predictions based on Stokes’, Brownian and Turbulent collisions. Also, the calculations showed that for Al2O3-MgO clusters with sizes &lt;20 μm the Turbulent collision is the defining factor for agglomeration. However, both Stokes’ and Turbulent collisions are dominant for larger inclusions. For the TiN clusters, turbulent collisions is the dominant factor. Further investigations with more heats and stirring modes were done by using 2D microscopic investigations. More specifically, the number, size, composition and morphology of different inclusions were determined by using SEM in combination with EDS and Inca Feature analyses. The results show that the EMS in downwards direction with a 0.04 m3 min-1 gas flow rate promotes a general removal of Al2O3-MgO and TiN inclusions. Furthermore, that the upwards EMS direction promotes a drastically increase of inclusions having an equivalent size smaller than 11.2 μm. Moreover, the stirring with a 0.02 m3 min-1 gas flow rate has a better removal rate for both downwards and upwards stirring directions compared to the stirring with a 0.04 m3 min-1 gas flow rate. However, no influence on the inclusion composition and morphology could be seen from the different stirring modes. / Det är välkänt att inneslutningar påverkar egenskaperna i stål och legeringar. Därför är det viktigt att förstå vilken sorts inneslutningar som existerar samt hur de beter sig, särskilt stora inneslutningar. Således undersöktes de stora icke-metalliska inneslutningarna i ferrolegeringen FeTi70R i två dimensioner (2D) genom att använda svepelektronmikroskopi (SEM) i kombination med energidispersionsteknik (EDS). Det visade sig att ferrolegeringen FeTi70R innehåller komplexa oxidinneslutningar bestående huvudsakligen av CaO, Si02 och TiOx. Vidare utfördes laborativa försök för att undersöka hur dessa inneslutningar uppträder när de kommer ner i det smälta stålet. Mer specifikt så gjordes en jämförelse mellan rent Fe och Alloy 825 legeringen. Dessa resultat fastställde hur olika parametrar påverkade inneslutningarnas omvandling i smältan. De stora icke-metalliska inneslutningarna i Alloy 825 legeringen under skänkugnsbehandlingen undersöktes vid industriella försök med hjälp av både tvådimensionella (2D) och tredimensionella (3D) mikroskopiska undersökningar. Resultaten visade att inneslutningarna bestod av sfäriska oxider och kluster uppbyggda av oxider och nitrider. Ytterligare undersökningar visade att de sfäriska inneslutningarna omvandlades från befintliga icke-metalliska inneslutningar i ferrolegeringen FeTi70R och slaggpartiklar. När det gäller kluster härrör de från desoxidationsprodukter. Vidare så bildades små inneslutningar i de lokala zonerna kring den tillsatta FeTi70R legeringen och kring titanitriderna. Undersökningarna fann också att endast Al2O3-MgO och TiN-kluster existerar efter gjutning. De industriella försöken utfördes under den sista perioden av skänkugnsbehandlingen och med en kombinerad elektromagnetisk (EMS) och gas (GS) omröring. Syftet med detta var att undersöka effekten av olika riktningar på EMS omrörningen på agglomerationen och avskiljningen av Al2O3-MgO- och TiN klustren. Undersökningarna utfördes sedan i 3D efter en elektrolytisk extraktion av metallproverna. Resultaten visar att en uppåtriktad elektromagnetisk omröring är bäst för agglomereringen av Al2O3-MgO inneslutningar och TiN kluster. Emellertid så är en nedåtriktad elektromagnetisk omröring effektivare för att avlägsna kluster från smältan. Dessa resultat överensstämmer med de teoretiska förutsägelserna baserade på Stokes, Brownian och Turbulent kollisionsvolymer. Dessutom visade beräkningarna att för Al2O3-MgO kluster med storlekar &lt;20 μm är det turbulenta kollisioner som är den avgörande faktorn för agglomerering. Dock är det både Stokes och de Turbulenta kollisionerna som dominerar för större inneslutningar. För TiN klustren är det de turbulenta kollisionerna som är den dominerande faktorn. Ytterligare undersökningar med fler charger av Alloy 825 och olika omrörningsmetoder gjordes baserade på 2D mikroskopiska undersökningar. Mer specifikt så bestämdes antalet, storleken, sammansättningen och morfologin för olika inneslutningar med användning av SEM i kombination med EDS och Inca Feature analyser. Resultaten visar att en nedåtriktad EMS i kombination med ett gasflöde på 0,04 m3 min-1 främjar ett generellt avlägsnande av Al2O3-MgO och TiN inneslutningar. Vidare främjar den uppåtriktade EMS omrörningen en drastisk ökning av inneslutningar med en ekvivalent storlek av 11,2 μm eller mindre. Vidare har omröringen med ett gasflöde på 0,02 m3 min-1 en bättre avskiljningshastighet för inneslutningar i både nedåt och uppåtgående omrörningsriktningar jämfört med omrörningen med ett gasflöde på 0,04 m3 min-1. Emellertid kunde inget inflytande på sammansättningen och morfologin ses från de olika omrörningssätten. / <p>QC 20171122</p>
15

Study of Non-metallic Inclusion in Alloy 825

Kellner, Hans January 2017 (has links)
It is well known that inclusions affect the properties of steels and alloys. Therefore, it is important to understand what type of inclusions that exist and how they behave and especially with a focus on large size inclusions. Thus, the large size non-metallic inclusions in ferroalloy FeTi70R were investigated in two dimensions (2D) by using scanning electron microscopy (SEM) in combination with an energy dispersive technique (EDS). It was found that the FeTi70R ferroalloy contain complex oxide inclusions consisting mostly of CaO, SiO2 and TiOx. Furthermore, experimental trials were performed to investigate how these inclusions behaved when entering a melt. More specifically, a comparison between pure Fe and an Alloy 825 grade were made. These results determined the parameters effect on the transformation of the inclusions in the melt. The large size non-metallic inclusions in Alloy 825 during the ladle treatment were investigated during industrial trials by using both two dimensional (2D) and three dimensional (3D) microscopic investigations. The results showed that inclusions consisted of spherical oxides and clusters made up of oxides and nitrides. Further investigations found that the spherical inclusions were transformed from existing NMI in the FeTi70R ferroalloy and slag particles. As for the clusters, they originate from deoxidation products. Furthermore, small inclusions precipitated in the local zones around the added FeTi70R ferroalloy and titanium nitrides. Investigations also found that only Al2O3-MgO and TiN clusters exist after casting. Industrial trials were performed during the last period of the ladle treatment and using a combined electromagnetic (EMS) and gas (GS) stirring. The purpose to investigate the effect of different EMS directions on the agglomeration and on the removal of Al2O3-MgO and TiN clusters. The investigations were then performed in 3D after an electrolytic extraction of the metal samples. The results show that electromagnetic stirring in the upwards direction is best for the agglomeration of the Al2O3-MgO and TiN clusters. However, electromagnetic stirring in the downwards direction is more effective to remove clusters from the melt. This is in agreement with the theoretical predictions based on Stokes’, Brownian and Turbulent collisions. Also, the calculations showed that for Al2O3-MgO clusters with sizes &lt;20 μm the Turbulent collision is the defining factor for agglomeration. However, both Stokes’ and Turbulent collisions are dominant for larger inclusions. For the TiN clusters, turbulent collisions is the dominant factor. Further investigations with more heats and stirring modes were done by using 2D microscopic investigations. More specifically, the number, size, composition and morphology of different inclusions were determined by using SEM in combination with EDS and Inca Feature analyses. The results show that the EMS in downwards direction with a 0.04 m3 min-1 gas flow rate promotes a general removal of Al2O3-MgO and TiN inclusions. Furthermore, that the upwards EMS direction promotes a drastically increase of inclusions having an equivalent size smaller than 11.2 μm. Moreover, the stirring with a 0.02 m3 min-1 gas flow rate has a better removal rate for both downwards and upwards stirring directions compared to the stirring with a 0.04 m3 min-1 gas flow rate. However, no influence on the inclusion composition and morphology could be seen from the different stirring modes. / Det är välkänt att inneslutningar påverkar egenskaperna i stål och legeringar. Därför är det viktigt att förstå vilken sorts inneslutningar som existerar samt hur de beter sig, särskilt stora inneslutningar. Således undersöktes de stora icke-metalliska inneslutningarna i ferrolegeringen FeTi70R i två dimensioner (2D) genom att använda svepelektronmikroskopi (SEM) i kombination med energidispersionsteknik (EDS). Det visade sig att ferrolegeringen FeTi70R innehåller komplexa oxidinneslutningar bestående huvudsakligen av CaO, Si02 och TiOx. Vidare utfördes laborativa försök för att undersöka hur dessa inneslutningar uppträder när de kommer ner i det smälta stålet. Mer specifikt så gjordes en jämförelse mellan rent Fe och Alloy 825 legeringen. Dessa resultat fastställde hur olika parametrar påverkade inneslutningarnas omvandling i smältan. De stora icke-metalliska inneslutningarna i Alloy 825 legeringen under skänkugnsbehandlingen undersöktes vid industriella försök med hjälp av både tvådimensionella (2D) och tredimensionella (3D) mikroskopiska undersökningar. Resultaten visade att inneslutningarna bestod av sfäriska oxider och kluster uppbyggda av oxider och nitrider. Ytterligare undersökningar visade att de sfäriska inneslutningarna omvandlades från befintliga icke-metalliska inneslutningar i ferrolegeringen FeTi70R och slaggpartiklar. När det gäller kluster härrör de från desoxidationsprodukter. Vidare så bildades små inneslutningar i de lokala zonerna kring den tillsatta FeTi70R legeringen och kring titanitriderna. Undersökningarna fann också att endast Al2O3-MgO och TiN-kluster existerar efter gjutning. De industriella försöken utfördes under den sista perioden av skänkugnsbehandlingen och med en kombinerad elektromagnetisk (EMS) och gas (GS) omröring. Syftet med detta var att undersöka effekten av olika riktningar på EMS omrörningen på agglomerationen och avskiljningen av Al2O3-MgO- och TiN klustren. Undersökningarna utfördes sedan i 3D efter en elektrolytisk extraktion av metallproverna. Resultaten visar att en uppåtriktad elektromagnetisk omröring är bäst för agglomereringen av Al2O3-MgO inneslutningar och TiN kluster. Emellertid så är en nedåtriktad elektromagnetisk omröring effektivare för att avlägsna kluster från smältan. Dessa resultat överensstämmer med de teoretiska förutsägelserna baserade på Stokes, Brownian och Turbulent kollisionsvolymer. Dessutom visade beräkningarna att för Al2O3-MgO kluster med storlekar &lt;20 μm är det turbulenta kollisioner som är den avgörande faktorn för agglomerering. Dock är det både Stokes och de Turbulenta kollisionerna som dominerar för större inneslutningar. För TiN klustren är det de turbulenta kollisionerna som är den dominerande faktorn. Ytterligare undersökningar med fler charger av Alloy 825 och olika omrörningsmetoder gjordes baserade på 2D mikroskopiska undersökningar. Mer specifikt så bestämdes antalet, storleken, sammansättningen och morfologin för olika inneslutningar med användning av SEM i kombination med EDS och Inca Feature analyser. Resultaten visar att en nedåtriktad EMS i kombination med ett gasflöde på 0,04 m3 min-1 främjar ett generellt avlägsnande av Al2O3-MgO och TiN inneslutningar. Vidare främjar den uppåtriktade EMS omrörningen en drastisk ökning av inneslutningar med en ekvivalent storlek av 11,2 μm eller mindre. Vidare har omröringen med ett gasflöde på 0,02 m3 min-1 en bättre avskiljningshastighet för inneslutningar i både nedåt och uppåtgående omrörningsriktningar jämfört med omrörningen med ett gasflöde på 0,04 m3 min-1. Emellertid kunde inget inflytande på sammansättningen och morfologin ses från de olika omrörningssätten.
16

Evaluation of Non-Metallic Inclusions after Deformation and Their Effect on the Machinability of Steel

GUO, SHUO January 2022 (has links)
The presence of non-metallic inclusions (NMIs) have critical effects on both the mechanical properties and machinability of steels. In the present thesis, one focus is to study the characteristics of deformed sulfides (MnS) for a stainless steel (3R65) and a tool steel (42CrMo4). Three groups of MnS inclusions were detected in the samples taken after deformation of the steel: i) type RS (sulfides with a Rod-like geometry), ii) type PS (sulphides with a plate-like geometry) and iii) type OS (oxy-sulfides). Here, the elongated inclusions present in both stainless and tool steels were studied more in detail using SEM to determine the tendency for the inclusions to break.  The results showed that three types of elongated MnS inclusions could be identified, namely UU, UB and BB. Here, ‘U’ represents the unbroken edge(s) of inclusion and ‘B’ represents the broken edge(s) of an inclusion. The presence of these three types of inclusions in samples collected both before and after a heat treatment was studied and the results showed that the heat treatment had a very small effect on the morphologies of the elongated MnS inclusions for both stainless steels (containing &lt;0.1 mass % C) and tool steels (containing 0.42 mass % C).  In the second part of the thesis, the characteristics of chips after machining of a 157REM Ce-treated steel and a 157C reference steel was studied. Furthermore, the effect of the NMIs on the chip breakability during machining was determined. The results show that a Ce modification of a 157C steel transforms the NMIs from large size elongated inclusions to small size inclusion with a spherical shape. This leads to an improved machinability of 157C steels. In addition, a newly developed weight distribution of chips (WDC) method, based on the chip weight measurements, was used to determine the tendencies for breaking of chips. The results of this investigation showed that the chips that were obtained from the machining of 157C and the 157REM steels could be classified into the following three types: i) type I chips (with a geometry containing one arc) and having a weight of less than 0.08 g, ii) type II chips (with a geometry containing two arcs) and having weights between 0.08 g and 0.15 g, and iii) type III chips (with a geometry containing three or more arcs) and having weights larger than 0.15 g. From industrial experience, it is known that a high amount of small type I chips will lead to a good chip breakability. The results from the machining test show that the fraction of type I chips from machining of the 157REM steel (65 %) is smaller than from machining of the 157C reference steel (80 %) when using a lower feed rate of 0.4 mm/rev. However, when using a higher feed rate of 0.5 mm/rev, 40 % of the chips belong to type I small chips for the 157REM steel and 14 % for the 157C steel. Based on the conditions used in this study and the obtained results, the following is clear in order to reach the best machinability: i) it is most advantageous to use the 157C steel when using a lower feed rate of 0.4 mm/rev and ii) it is most advantageous to use the 157REM steel when using a higher feed rate of 0.5 mm/rev. / Närvaron av icke-metalliska inneslutningar (NMIs) har en betydande påverkan både med avseende på mekaniska egenskaper såväl som skärbarhetsförmågan hos stål. I denna avhandling är ett fokus att studera deformerade sulfider (MnS)  i ett rostfritt stål (3R65) och ett verktygsstål (42CrMo4). Tre grupper av MnS inneslutningar återfanns i stålproverna, som togs efter deformation av stålet: i) RS (sulfider som har en cylindrisk geometri), ii) PS (sulfider som har en platt geometri) och iii) OS (oxy-sulfider). Dessutom så studerades utdragna inneslutningar mer i detalj med användande av SEM undersökningar i syfte att studera tendensen till att dessa inneslutningar bröts sönder. Resultaten visade att tre typer av utdragna inneslutningar kunde identifieras, nämligen UU, UB och BB. Här representerar ‘U’ en ände av en inneslutning som inte brutits sönder och ‘B’ representerar en ände av en inneslutning som brutits sönder. Närvaron av dessa tre typer av utdragna inneslutningar studerades i prover som togs både före och efter en värmebehandling, men resultaten visade att en värmebehandling hade en mycket liten påverkan på morfologin hos de utdragna MnS inneslutningarna för både rostfria stål (innehållande &lt;0.1 mass % C) och verktygsstål (innehållande 0.42 mass % C).  I den andra delen av avhandlingen så studerades karakteristiken hos spånor som bildats efter skärande bearbetning av ett 157REM (Ce-behandlat) modifierat stål och ett 157C referensstål som inte modifierats. Dessutom så studerades inverkan av icke-metalliska inneslutningar på spånbrytningen under den skärande bearbetningen. Resultaten visar att en Ce-modifiering av stålet omvandlar inneslutningarna från stora och utdragna geometrier till små inneslutningar med en sfärisk geometri. Detta leder till en ökad skärbarhet hos 157C stål. Spånbrytbarheten bestämdes också med användande av en nyutvecklad metod (WDC metoden) som baseras sig på att bestämma vikten av spånor. Resultaten av denna utvärdering visade att spånorna som erhölls från bearbetning av 157C och 157REM stål kunde klassificeras enligt följande tre typer: i) typ I spånor (en geometri som består av en bågform) som har en vikt som är mindre än 0.08 g, ii) typ II spånor (en geometri som består av två bågformar) som har en mellan 0.08 g och 0.15 g och iii) typ III spånor (en geometri som består av tre eller fler bågformar) som har en vikt som är större än 0.15 g. Baserat på industriell erfarenhet så är det känt att en stor mängd av små typ I spånor är kopplad till en bra spånbrytbarhet. Resultaten från skärbarhetstesterna visar att andelen typ I spånor från bearbetning av ett 157REM stål (65 %) är mindre än vid bearbetning av ett 157C referens stål (80 %), när en lägre matningshastighet av 0.4 mm/rev används. Däremot så visar resultaten att om en högre matningshastighet av 0.5 mm/rev används vid bearbetning, så är andelen typ I spånor 40 % för 157REM stålet och 14 % för 157C referensstålet. I syfte att erhålla bästa möjliga skärbarhet så är det fördelaktigt att använda ett 157C referensstål för den lägre matningshastigheten av 0.4 mm/rev, men att använda ett 157REM stål för en högre matningshastighet av 0.5 mm/rev.
17

Investigations of Tool Wear Mechanisms in the Turning of Conventional, Calcium Treated and Ultraclean Steels

Göransson, Milou January 2023 (has links)
Application of clean and ultraclean steels have shown to provide favourable mechanical properties for bearings and transmission components, specifically regarding fatigue performance, compared to conventional steel grades. Clean steels are characterized by containing a very low level of non-metallic inclusions. While this characteristic is beneficial for the fatigue strength, inclusions in steels have shown to be favorable for the machinability and therefore challenges during machining of clean steels can arise. In this thesis the machinability and tool wear mechanisms of ultraclean steel have been evaluated during longitudinal turning. The aim of the study was to determine how steel cleanness and inclusions impact different machinability aspects. This was achieved by performing a comparative study of three steel grades with different level of cleanness and inclusions characteristics. Four machining experiments were executed investigating the chip breakability, cutting force, tool life and cutting tool coating degradation. The machined inserts were then analysed using light optical microscopy, secondary electron microscopy and electron probe microanalysis. The result revealed that the ultraclean steel grade has the overall worst machinability with the lowest chip breakability, highest cutting forces, and lowest tool life for the investigated steels. Additionally, it was found that the inserts that machined the ultraclean steel and the calcium treated steel was exposed to severe crater wear. However, the coating degradation causing the crater wear differs between the two grades. For the ultraclean steel the wear rate of the entire chemical vapor deposition coating is high. In contrast, for the calcium treated steel only the top alumina layer degrades rapidly and the underlying titanium carbonitride layer have a low wear rate. / Användning av rena och ultrarena stål har visat sig ge gynnsamma mekaniska egenskaper för kullager och transmissionskomponenter, speciellt gällande utmattningsprestanda, jämfört med konventionella stålsorter. Rena stål kännetecknas av att de innehåller en mycket låg nivå av icke-metalliska inneslutningar. Denna egenskap är fördelaktig för utmattningshållfastheten, men däremot har inneslutningar i stål visat sig vara gynnsamma för bearbetbarheten och därför kan utmaningar uppstå vid bearbetning av rena stål. I detta arbete har bearbetbarheten och verktygsslitagemekanismerna för ultrarent stål utvärderats under längsgående svarvning. Syftet med studien var att fastställa hur stålets renhet och inneslutningar påverkar olika bearbetningsaspekter. Detta uppnåddes genom att utföra en jämförande studie av tre stålsorter med olika renhetsgrad samt inneslutningar. Fyra bearbetningsexperiment utfördes för att undersöka spånbrytbarheten, skärkraften, verktygets livslängd och nerbrytningen av skärverktygets beläggning. De bearbetade skären analyserades sedan med användning av ljusoptisk mikroskopi, svepelektronmikroskopi och elektronprobmikroanalys. Resultatet visade att den ultrarena stålsorten har den totalt sett sämsta bearbetbarheten med lägst spånbrytbarhet, högsta skärkrafter och lägsta verktygslivslängd av de undersökta stålen. Dessutom upptäcktes att skären som bearbetade det ultrarena stålet och det kalciumbehandlade stålet utsattes för kraftigt kraterslitage. Nedbrytningen av verktygs beläggningen som orsakar kraternötningen skiljer sig dock mellan de två stålkvaliteterna. För det ultrarena stålet är slitagehastigheten för hela beläggningen hög. För det kalciumbehandlade stålet bryts däremot endast det övre aluminiumoxidskiktet ned snabbt och det underliggande titankarbonitridskiktet har en låg nötningshastighet.