Fabrication of current generation integrated circuits involves the creation of multilevel copper/low-k dielectric structures during the back end of line processing. This is done by plasma etching of low-k dielectric layers to form vias and trenches, and this process typically leaves behind polymer-like post etch residues (PER) containing copper oxides, copper fluorides and fluoro carbons, on underlying copper and sidewalls of low-k dielectrics. Effective removal of PER is crucial for achieving good adhesion and low contact resistance in the interconnect structure, and this is accomplished using wet cleaning and rinsing steps. Currently, the removal of PER is carried out using semi-aqueous fluoride based formulations. To reduce the environmental burden and meet the semiconductor industry's environmental health and safety requirements, there is a desire to completely eliminate solvents in the cleaning formulations and explore the use of organic solvent-free formulations.The main objective of this work is to investigate the selective removal of PER over copper and low-k (Coral and Black Diamond®) dielectrics using all-aqueous dilute HF (DHF) solutions and choline chloride (CC) - urea (U) based deep eutectic solvent (DES) system. Initial investigations were performed on plasma oxidized copper films. Copper oxide and copper fluoride based PER films representative of etch products were prepared by ashing g-line and deep UV photoresist films coated on copper in CF4/O2 plasma. PER removal process was characterized using scanning electron microscopy and X-ray photoelectron spectroscopy and verified using electrochemical impedance spectroscopy measurements.A PER removal rate of ~60 Å/min was obtained using a 0.2 vol% HF (pH 2.8). Deaeration of DHF solutions improved the selectivity of PER over Cu mainly due to reduced Cu removal rate. A PER/Cu selectivity of ~20:1 was observed in a 0.05 vol% deaerated HF (pH 3). DES systems containing 2:1 U/CC removed PER at a rate of ~10 and ~20 Å/min at 40 and 70oC respectively. A mixture of 10-90 vol% de-ionized water (W) with 2:1 U/CC in the temperature range of 20 to 40oC also effectively removed PER. Importantly, etch rate of copper and low-k dielectric in DES formulations were lower than that in conventional DHF cleaning solutions.