Dissertação (mestrado)—Universidade de Brasília, Instituto de Geociências, 2014. / Submitted by Ana Cristina Barbosa da Silva (annabds@hotmail.com) on 2015-03-05T19:22:44Z No. of bitstreams: 1 2014_JoaoPauloGomesdeSouza_Parcial.pdf: 6871163 bytes, checksum: 89cc3d442e6b314dfedc53ed12ab0b7d (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2015-03-06T17:25:38Z (GMT) No. of bitstreams: 1 2014_JoaoPauloGomesdeSouza_Parcial.pdf: 6871163 bytes, checksum: 89cc3d442e6b314dfedc53ed12ab0b7d (MD5) / Made available in DSpace on 2015-03-06T17:25:38Z (GMT). No. of bitstreams: 1 2014_JoaoPauloGomesdeSouza_Parcial.pdf: 6871163 bytes, checksum: 89cc3d442e6b314dfedc53ed12ab0b7d (MD5) / As formações ferríferas do Depósito do Pelado estão inseridas na sequência vulcânica-sedimentar do Grupo Vila Nova no domínio geológico conhecido como Terreno Antigo Cupixi-Tartarugal Grande, no estado do Amapá. A imagem de intensidade magnética mostra uma anomalia com forte magnetização remanescente localizado em baixa latitude magnética, o que dificulta a aplicação da redução ao polo e consequentemente uma inversão por propriedade física, devido a direção da magnetização total não ser conhecida. Optou-se por aplicar transformações de campo com fraca dependência da direção de magnetização como amplitude do campo magnético anômalo (AMCA), sinal analítico da integral vertical (ASVI) e a integral vertical de sinal analítico (VIAS) com o objetivo de obter a correta distribuição da susceptibilidade para a formação ferrífera em sub-superfície atraves da inversão magnética. Foi-se utilizado o software MAG3D e AMP3D para a realização de três inversões sintéticas e três inversões (com dados reais),com as transformações de campo mencionadas anteriormente. Os resultados dos dados reais foram comparados com os dados de furos da sondagem exploratória e os dados de susceptibilidade magnética obtidos por perfilagem dos testemunhos de sondagem. Os resultados mostram que as transformações de campo AMCA, ASVI VIAS e é capaz de delinear a formação de ferro em planta (2D). Em 3D, os métodos AMCA e ASVI possibilitaram o mapeamento das formações ferríferas mineralizadas como mapeado pelas sondagens exploratórias. Propõe-se que, para os corpos de formações ferríferas, com forte magnetização remanescente, em baixas latitudes magnéticas onde o campo magnético da Terra é três vezes menor do que no polo magnético, o uso das técnicas de AMCA e ASVI para o mapeamento de corpos magnéticos mineralizados sub-superfície e localização dos furos. / The banded iron formations from the Pelado deposit are hosted in the vulcanic-sedimentary sequence of the Vila Nova Group at the geological domain known as Terreno Antigo Cupixi-Tartarugal Grande, in the state of Amapá. The image of total magnetic intensity shows an anomaly with strong remanent magnetization located at low magnetic latitude, which makes difficult the reduction of data to the pole and an inversion by physical propriety due the direction of the total magnetization is not known. We opted to apply field transformations with weak dependence on magnetization direction as amplitude of the anomalous magnetic field (AMCA), analytic signal of vertical integral (ASVI) and the vertical integral of analytic signal (VIAS) aiming to obtain the correct distribution of the susceptibility for the sub-surface by magnetic inversion. Utilizing the software MAG3D and AMP3D three synthetic inversions were carried out and three inversions for the iron deposit of the Pelado. The results of the real data were compared to the data from exploration drill holes and magnetic susceptibility data obtained in the well logging. The results show that the field transformations AMCA, ASVI and VIAS are able to outline the iron formation in 2D. In 3D, the methods AMCA and ASVI have mapped the mineralized banded iron formations as mapped by the exploration drilling. It is proposed that for the mineralized bodies of banded iron formations, with strong remanent magnetization, in low magnetic latitudes where the Earth’s magnetic field is three times less than in the magnetic pole, the use of the AMCA techniques and the ASVI for the mapping of sub-surface mineralized bodies and location of drill holes.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Samples of Bi 2Fe4O9 mullite and ReFe 0.5M0.5O3 (Re = Nd, Sm, Eu, Gd, Dy; M = Mn, Al) complex perovskites were successfully synthesized by using the combustion synthesis method. While the mullite was obtained after thermal treatment at temperatures below 1000ºC, complex perovskites are produced after thermal treatments between 1250ºC and 1500ºC for at most 24 h. The X-ray diffraction data analysis suggests the formation of single phase orthorhombic structure, after suitable heat treatment. Scanning electron microscopy (SEM) revealed the formation of micrometric grain size, giving to the sample the relative density. EDS spectra confirmed the homogeneity and purity of complex perovskites. Magnetization measurements as a function of field and temperature showed the diversity of magnetic behavior of the samples. Among the behaviors we can highlight the reorientation of spin for ortoferritas ReFe0.5Mn0.5O3 (Re = Dy, Gd, Eu, Sm, Eu) and ReFe0.5Al0.5O3 (Re = Dy, Nd). Another interesting finding was the effect of magnetic reversal of the samples ReFe0.5Al0.5O3 (Re = Nd, Gd) and EuFe0.5Mn0.5O3. Raman spectra show anomalous bands of second order in the perovskite DyFe0.5Al0.5O3 with characteristics of resonant effects. The evolution of the band associated with the symmetric vibrational mode of the octahedron shows hardening at the temperature range of ordered magnetic phase, thus suggesting a possible spin-phonon coupling. Depolarization current measurements highlights a relaxation process due to charge carriers in the samples ReFe0.5Mn0.5O3 (Re = Dy, Gd). The application of magnetic field profoundly influences the depolarization current behavior of DyFe0.5Mn0.5O3. Dielectric permittivity measurements showed no anomalies between 10 K and 300 K, that could can be associated to a ferroelectric phase. / Amostras da mulita Bi2Fe4O9 e das perovskitas complexas ReFe0.5M0.5O3 (Re= Nd, Sm, Eu, Gd, Dy; M = Mn, Al) foram sintetizadas com sucesso utilizando o método de síntese por reação de combustão. Enquanto a mulita foi obtida após tratamento térmico com temperaturas abaixo de 1000ºC, as perovskitas complexas foram produzidas após tratamentos térmicos entre 1250ºC e 1500ºC por, no máximo, 24 h. A análise de dados de difração de raios X sugerem a formação de estruturas ortorrômbicas de fase única, após os tratamento térmico apropriado. Medidas de microscopia evidenciaram formação de grãos micrométricos conferindo às amostras relativa densidade. Os espectros EDS confirmaram a homogeneidade e pureza das perovskitas complexas. As medidas de magnetização em função do campo e da temperatura evidenciaram a diversidade de comportamentos magnéticos das amostras estudadas. Entre os comportamentos destacamos reorientação de spin para as ortoferritas ReFe0.5Mn0.5O3 (Re = Dy, Gd, Eu, Sm, Eu) e ReFe0.5Al0.5O3 (Re = Dy,Nd). Outro interessante achado foi o efeito de inversão magnética das amostras ReFe0.5Al0.5O3 (Re = Nd, Gd) e EuFe0.5Mn0.5O3. Espectros Raman demonstram bandas anômalas de segunda ordem na perovskita DyFe0.5Al0.5O3 com características de efeitos ressonantes. A evolução da banda associada ao modo vibracional simétrico do octaedro apresenta endurecimento em temperaturas na faixa da fase magnética ordenada, sugerindo assim, um possível acoplamento spin-f onon. Medidas de corrente de despolarização destaca um processo de relaxação devido aos portadores de cargas nas amostras ReFe0.5Mn0.5O3 (Re=Dy,Gd). A aplicação de campo magnético influencia profundamente o comportamento da corrente de despolarização do DyFe0.5Mn0.5O3. Medidas de permissividade dielétrica não exibiram anomalias entre 10 K e 300 K que possam a ser associadas a uma fase ferroelétrica.