Made available in DSpace on 2013-12-27T01:01:19Z (GMT). No. of bitstreams: 1 000452974-Texto+Completo-0.pdf: 3097525 bytes, checksum: fb30a932f49f0911b5cf750d9aaf97e9 (MD5) Previous issue date: 2013 / The aims of this study were: (a) establish, through a review of the literature, the state of the art regarding the use of photodynamic therapy for the disinfection of the root canal system as well as future prospects, (b) evaluate the periapical tissues response on rats’ teeth with apical periodontitis, to photodynamic therapy as an adjunct to endodontic treatment through histological, microbiological and radiological analysis. Therefore, 32 left lower rats’ molars were exposed to the oral environment for 21 days to induce apical periodontitis. The animals were randomly divided into four groups according to proposed treatment: endodontic treatment in one session (G1); endodontic treatment in two sessions with with calcium hydroxide [Ca(OH)2] dressing for 14 days (G2) ; endodontic treatment in one session associated with photodynamic therapy (PDT) (G3) and endodontic treatment in two sessions with Ca(OH)2 for 14 days, associated with PDT (G4). After 28 days, the animals were killed and the jaws prepared for evaluation. For microbiological analysis samples were collected before and after each treatment step. Quantification of CFU/mL were analyzed using linear mixed models, showing significant microbial reduction after all proposed treatments, compared to the initial collection, although no significant difference between groups were found. The radiographic results were submitted to ANOVA, showing no statistically significant difference between groups. For histological data, Kruskal-Wallis test were used, followed by Mann-Whitney U test for those cases where differences were detected. These differences were found in neutrophils and eosinophils populations in groups where PDT was used and macrophages and giant cells when Ca(OH)2 was used, with or without PDT. These data seem to point to a better repair quality when PDT is applied, caused by laser biomodulator effect in periapical tissues. The association of PDT with an interappointment dressing with Ca(OH)2 produces better conditions to stimulate repair, being more research needed to determine this relationship. / Os objetivos deste estudo foram: (a) estabelecer, através de revisão da literatura, o estado da arte na aplicabilidade da terapia fotodinâmica para a desinfecção do sistema de canais radiculares bem como as perspectivas futuras; (b) avaliar a resposta dos tecidos periapicais de dentes de ratos, portadores de periodontite apical, à terapia fotodinâmica como coadjuvante ao tratamento endodôntico, através de análise histológica, microbiológica e radiográfica. Para tanto, 32 molares inferiores esquerdos de ratos foram expostos ao meio bucal por 21 dias, para indução da periodontite apical. Após, foram divididos aleatoriamente em quatro grupos conforme o tratamento proposto: tratamento endodôntico em sessão única (G1); tratamento endodôntico em duas sessões com medicação intracanal à base de hidróxido de cálcio [Ca(OH)2] por 14 dias (G2); tratamento endodôntico em sessão única, associado à terapia fotodinâmica (PDT) (G3) e tratamento endodôntico em duas sessões com Ca(OH)2 por 14 dias, associado à PDT (G4). Após 28 dias, os animais foram mortos e as mandíbulas preparadas para avaliação. Para avaliação microbiológica foram realizadas coletas antes e após cada etapa de tratamento. As quantificações de UFC/mL foram analisadas através de modelos mistos lineares, mostrando significativa redução microbiana após todos os tratamentos propostos, quando comparados à coleta inicial, não havendo porém diferença significativa entre os grupos. Os resultados radiográficos foram submetidos a ANOVA, não havendo diferença estatisticamente significativas entre os grupos. Para os dados histológicos, foi utilizado o teste de Kruskall-Wallis seguido por Mann-Whitney U para aqueles casos onde diferenças foram detectadas. Estas diferenças foram encontradas nas populações de neutrófilos e eosinófilos nos grupos onde a PDT foi utilizada e para macrófagos e células gigantes quando o Ca(OH)2 foi utilizado, independentemente da PDT. Os dados parecem apontar para uma melhor condição de reparo quando da utilização da PDT, pelo efeito biomodulador do laser nos tecidos periapicais. A associação da PDT com MIC com Ca(OH)2 parece propiciar os melhores resultados, sendo necessários mais estudos para determinar esta relação.

Made available in DSpace on 2013-10-11T13:35:45Z (GMT). No. of bitstreams: 1 000451353-Texto+Completo-0.pdf: 20017308 bytes, checksum: 296ffb9862c776426e68e43169d40c26 (MD5) Previous issue date: 2013 / The goal of this thesis was the development and analysis of crystalline silicon solar cells processed by laser radiation. Solar cells with n+pp+ structure on p-type, CZ-Si solar grade substrate were developed, analysed, and evaluated, based on two laser processing techniques: laser-fired rear contacts (LFC) and laser ablation of the front surface silicon nitride by means of laser chemical processing (LPC) or using a mirror galvanometer laser system (SCA). The LFC method was employed to form the rear contacts of crystalline silicon solar cells after the deposition of an aluminium layer. The LCP and SOA methods were used to develop a silicon nitride ablation process. The laser ablation process was employed to open regions of the devices antireflection coating, followed by selective chemical deposition of Ni/Ag to form the front metal grid. The best laser processing parameters found for LFC solar cells were: 33. 0 A pumping lamp current, 20. 0 kHz q-switch frequency, and 0. 50 mm contact distance. LFC solar cells with screen printed front metallization and Si02 rear passivation layer achieved an average efficiency of 14. 4 % and best value of 15. 3 %, after an annealing step at 400 00 with a belt speed of 50 cm/min. lncreasing the rear aluminium layer thickness from 2 um to 4 um did not improve the performance of the devices significantly. The best laser processing parameters found for the silicon nitride laser ablation process based on the LCP technique were: 15. 3 uJ laser pulse energy, 16. 0 kHz q-switch frequency, and 100 mm/s processing speed. The best laser processing parameters found for the silicon nitride laser ablation process based on the SOA technique were: 5. 0 uJ laser pulse energy, 130. 0 kHz q-switch frequency, and 813 mm/s processing speed. Solar cells with silicon nitride laser ablation, front side metallization by Ni/Ag selective electrochemical deposition, and screen-printed rear side metallization achieved an average efficiency of 16. 1 % and best value of 16. 8 % for the LCP technique and an average efficiency of 16. 3 % and best value of 16. 6% for the SOA technique. / O objetivo desta tese foi o desenvolvimento e análise de células solares em substrato de silício cristalino com processamento por radiação laser. Células solares com estrutura n+pp+ em substrato de CZ-Si tipo p foram fabricadas, analisadas e comparadas, com base em duas técnicas de processamento laser: contatos posteriores formados por laser (CFL) e ablação do filme antirreflexo frontal de nitreto de silício por processamento químico com laser (PQL) ou por processamento com laser guiado por galvanômetro de espelhos (SCA). O método CFL foi utilizado na formação dos contatos posteriores de células solares, após a deposição de uma camada de alumínio. Os métodos PQL e SCA foram usados no desenvolvimento de um processo de ablação a laser do filme frontal de nitreto de silício. Trilhas foram abertas no filme antirreflexo e posteriormente metalizadas seletivamente por deposição química de níquel e prata, para formar a malha de metalização frontal. Os melhores parâmetros de processamento laser encontrados para células solares CFL foram: corrente da lâmpada de bombeamento óptico de 33,0 A, freqüência q-swttch de 20,0 kHz e distância entre contatos posteriores de 0,50 mm. Células solares CEL com metalização frontal por serigrafia e passivação posterior com SiO2 alcançaram uma eficiência média de 14,4 % e melhor valor de 15,3 %, após tratamento térmico a 400 °C com velocidade de esteira de 50 cm/min.O aumento da espessura da camada de alumínio posterior de 2 um para 4 um não resultou em melhora significativa da performance das células solares. Os melhores parâmetros de processamento encontrados para o processo de ablação a laser de nitreto de silício pela técnica PQL foram: energia do pulso laser de 15,3 uJ, frequência q-switch de 16,0 kHz e velocidade de processamento de 100 mm/s. Os melhores parâmetros de processamento encontrados para o processo de ablação a laser de nitreto de silicio pela técnica SCA foram: energia do pulso laser de 5,0 uJ, freqüência q-switch de 130,0 kHz e velocidade de processamento de 813 mm/s. Células solares com ablação a laser de nitreto de silicio, metalização frontal seletiva por deposição química de níquel e prata e metalização posterior por serigrafia atingiram a eficiência média de 16,1 % e o melhor valor de 16,8 % com a técnica PQL e a eficiência média de 16,3 % e melhor valor de 16,6 % com a técnica SCA.

Made available in DSpace on 2015-02-13T01:00:51Z (GMT). No. of bitstreams: 1 000465177-Texto+Completo-0.pdf: 2199385 bytes, checksum: 7e39de6eac33d2dfd74591983c10103d (MD5) Previous issue date: 2015 / This work was focused on the development of silicon solar cells with laser fired contacts and rear face passivation. Several processes were developed based on two different p-type silicon substrates. The objective was to develop a solar cell manufacturing process with laser fired contacts and aluminum deposited by evaporation, as well as to assess the rear passivation. In Si-Cz wafers, the phosphorus diffusion was performed at 865 °C. From the power and the frequency experimental optimization in Si-Cz wafers, it was found that the efficiency of 13. 1 % was obtained with 15 W of power and 80 kHz of frequency. The efficiency of 14. 5 % was achieved from the annealing temperature of 350 °C and belt speed of 66 cm/min. The experimental optimization of the distance between the dots and the contact area of the dots resulted on 14. 1 % efficiency, for the distance between dots of 0. 5 mm and the dot area contact of 7230 μm2. For the PV-Si-FZ substract, with the best diffusion temperature of 875 °C, the efficiency of 14. 0 % was obtained. It was found that the efficiency for Si-Cz and Si-FZ solar cell was similar, due to the low minority charge carrier lifetime. The deposition of a TiO2 film on the rear side resulted in an increase of the fill factor and efficiency, however the increase of the silicon oxide layer reduced the efficiency of the devices. / Neste trabalho foram desenvolvidas células solares de silício com contatos formados por radiação laser e passivação na face posterior. Para isso, foram desenvolvidos processos para produção de células solares a partir de lâminas de silício tipo p de dois tipos diferentes de substrato. O objetivo foi desenvolver um processo de fabricação de células solares com contato e difusão posterior formado em pontos por radiação laser e alumínio depositado por evaporação bem como avaliar a passivação na face posterior. Em lâminas de Si-Cz, a difusão de fósforo foi realizada a 865 °C. Da otimização experimental da potência e da frequência do sistema laser em lâminas de Si-Cz, constatou-se que a eficiência de 13,1 % foi obtida com a potência de 15 W e frequência de 80 kHz. Obteve-se a eficiência de 14,5 % para a temperatura de recozimento 350 °C e a velocidade de esteira de 66 cm/min. A otimização experimental da distância entre pontos e da área dos pontos de contato, resultou na eficiência de 14,1 %, para a distância entre pontos de 0,5 mm e área dos pontos de contato de 7230 μm2. Para substratos de PV-Si-FZ, a melhor temperatura de difusão de fósforo foi de 875 °C e obteve-se a eficiência de 14,0 %. Constatou-se que a eficiência foi similar para células solares processadas em lâminas de Si-Cz e PV-Si-FZ, devido o baixo tempo de vida dos portadores de carga minoritários. A deposição de um filme de TiO2 na face posterior resultou em um aumento no fator de forma e da eficiência, porém o aumento da camada de óxido de silício reduziu a eficiência dos dispositivos.