Low temperature cleavage fracture behaviour was investigated using four experimental microalloyed bainitic plate steels. The four plate samples were produced by different thermomechanical processing (TMP) schedules and had yield strengths in the range 540 - 670 MPa. Microstructures were characterized by optical microscopy (OM), scanning electron microscopy (SEM) and electron back scattered diffraction (EBSD). Quantitative data was obtained for prior austenite grain (PAG) size, volume fractions of two bainite types (conventional bainite and acicular ferrite) and EBSD 15° domain size. Charpy impact tests (using two notch orientations) were carried out over a range of temperatures. Cleavage facet sizes were measured on -196°C Charpy samples. The range of TMP schedules produced variations in PAG width, type of bainite and 15° domain size. The effects of these three microstructural features on cleavage crack propagation are discussed. Results indicate that the microstructures are controlled by i) deformation below TNR and ii) accelerated cooling rate. Domain structure reflects TMP. There is no clear correlation between domain size and cleavage facet size. / Thesis (Master, Mechanical and Materials Engineering) -- Queen's University, 2009-07-30 19:17:01.25

No description available.

For the manufacture of higher strength pipelines to be feasible, a better understanding of the effects of welding on toughness is necessary. Bevel submerged arc welds were performed on X80 grade steel. The subsequent Charpy V-notch (CVN) test results indicated that the notch placement in the various heat affected zone regions, and hence the bead geometry, affected the test results. A series of bead-on-plate (BOP) submerged arc welds then were performed on X70 grade steel plate to determine the effects of current, voltage, heat input, polarity, and waveform manipulation (i.e., balance, offset, and frequency) on both single and tandem weld bead geometry. A new bead profile characteristic, the SP ratio, is proposed to describe weld bead geometry, and its relationship with welding parameters is discussed. Sub-size CVN specimens, pulled from many of the BOP weld coupons, were then tested. The greatest subsize CVN fracture energies were achieved when the bead was produced using lower heat input, and when the bead profile possessed a greater SP ratio. / Materials Engineering