Made available in DSpace on 2015-04-14T13:58:35Z (GMT). No. of bitstreams: 1 422849.pdf: 6410464 bytes, checksum: ccd93368032fc92429c59317d9dbf9fe (MD5) Previous issue date: 2010-03-30 / Este estudo prop?e a caracteriza??o estrutural, por meio de ensaios mec?nicos, de postes de eucalipto em servi?o usados na rede el?trica. Os testes de flex?o est?tica foram realizados em uma ?rea de teste em campo constru?da de acordo com a NBR 6231 (ABNT, 1980) e ASTM D 1036-americanos (1990), enquanto os testes de compress?o paralela as fibras foram feitos de acordo com a NBR 7190 (ABNT1997). As propriedades mec?nicas, densidade e umidade ao longo de tr?s postes novos, de diferentes esp?cies de eucalipto, tamb?m foram avaliadas, levando em conta a quantidade de cerne e alburno presentes nas amostras. Correla??es entre os ensaios de compress?o e flex?o foram obtidos considerando-se a as diferentes faixas de densidade da madeira. Os resultados indicaram que a quantidade de cerne e alburno nas amostras afeta as propriedades mec?nicas, especialmente se o corpo de prova for composto de apenas um desses componentes. Foi poss?vel encontrar, dentre as esp?cies, a mais adequada para a fabrica??o poste. Al?m disso, ensaios de compress?o realizados tanto em postes em servi?o como novos, flexionados ou n?o, indicaram propriedades mec?nicas semelhantes quando classificados na mesma faixa de densidades. As correla??es estabelecidas s?o ?teis para obter uma estimativa das propriedades mec?nicas dos postes com a vantagem de ser um teste semi destrutivo, ao contr?rio dos testes de flex?o.

Made available in DSpace on 2015-04-14T13:58:58Z (GMT). No. of bitstreams: 1 447106.pdf: 3203948 bytes, checksum: ee13ebac3cdb25bab02611e4cd2d6c1e (MD5) Previous issue date: 2013-01-25 / The objective of the present work is to develop a study of abrasive wear a specific component of a grain harvester, the bars of unit threshing the combines. For this study it was designed and built a test bench that simulates two types of materials, an ABNT/SAE 1045 steel and an ABNT/SAE 1518 steel underwent a forced to wear an abrasive that simulates the size and condition of a grain at a accelerated rate. This bench is in turn composed of parts used in systems threshing on harvesters in order to bring the test closer to the real. The general condition of the abrasive was compared with the literature in order to obtain better data with respect to wear on the condition. After the wear test was designed to better characterize this wear, where it is noted that medium carbon steel (SAE 1045) had a good initial performance with respect to wear, however the material with manganese (SAE 1518) showed a better resistance at the end of the tests when compared to SAE 1045. Finally, the tests was conducted to validate the bench, and characterization of abrasive wear in relation to which it was possible to sense the increased wear of the samples was performed when adding the SiO2 abrasive to simulate rice hull. / O presente trabalho tem como objetivo desenvolver um estudo de desgaste abrasivo de um componente espec?fico de uma colheitadeira de gr?os, no caso as barras da unidade de trilha da colhedora. Para este estudo foi projetada e constru?da uma bancada de testes para utiliza??o de dois tipos de materiais, um a?o ABNT/SAE 1045 e um a?o ABNT/SAE 1518, submetidos ao desgaste for?ado de abrasivos que simulem o tamanho e condi??o mais pr?xima de um gr?o em ritmo acelerado. Esta bancada por sua vez foi constitu?da de pe?as utilizadas em sistemas de trilha de colheitadeiras, a fim de tornar o teste o mais pr?ximo do real. A condi??o geral do abrasivo foi comparada com a literatura, a fim de se obter melhores dados em rela??o ao desgaste nessa condi??o. A an?lise de dados posterior teve a finalidade de caracterizar melhor este desgaste, onde foi poss?vel perceber que o a?o de m?dio carbono (SAE 1045) teve um desempenho inicial bom em rela??o ao desgaste, no entanto a liga com mangan?s (SAE 1518) apresentou uma resist?ncia ao final dos ensaios melhor quando comparada ao SAE 1045. Por fim nos testes executados, foi realizada a valida??o da bancada, e a caracteriza??o do desgaste em rela??o aos abrasivos onde foi poss?vel perceber o aumento do desgaste das amostras quando se realizava a adi??o de SiO2 no abrasivo para simular a casca do arroz.