Realizou-se, no contexto deste trabalho, o estudo de espécies tropicais de madeira e a qualificação destas a partir de suas características físicas, de resistência e rigidez. Os ensaios para a determinação das propriedades foram realizados no Laboratório de Madeiras e de Estruturas de Madeira, do Departamento de Engenharia de Estruturas, Escola de Engenharia de São Carlos, seguindo as recomendações do anexo B da NBR 7190/1997 - Projeto de Estruturas de Madeira. O objetivo fundamental é gerar informações que possam fornecer suporte para um direcionamento e perspectiva de novas possibilidades de aplicação na construção civil: construção de estruturas para diferentes finalidades (coberturas, pontes, cimbramentos); industriais para componentes de edificações (pisos, caixilhos); armazenamento; obras portuárias; entre outras. / It was realized, in the context of this work, a study about tropical wood species and their qualification, based on the physical and mechanical properties. The tests to the determination of such properties were realized in Wood and Timber Structures Laboratory, Structural Engineering Departament, São Carlos Engineering School, according to the recommendations of the Annex B, NBR 7190/1997 - Timber Structures Design. The mean subject is to generate information to permit new application in civil construction: structures for different purposes (roofs, bridges, formwork); industrial to building components; storage; among others.

Realizou-se, no contexto deste trabalho, o estudo de espécies tropicais de madeira e a qualificação destas a partir de suas características físicas, de resistência e rigidez. Os ensaios para a determinação das propriedades foram realizados no Laboratório de Madeiras e de Estruturas de Madeira, do Departamento de Engenharia de Estruturas, Escola de Engenharia de São Carlos, seguindo as recomendações do anexo B da NBR 7190/1997 - Projeto de Estruturas de Madeira. O objetivo fundamental é gerar informações que possam fornecer suporte para um direcionamento e perspectiva de novas possibilidades de aplicação na construção civil: construção de estruturas para diferentes finalidades (coberturas, pontes, cimbramentos); industriais para componentes de edificações (pisos, caixilhos); armazenamento; obras portuárias; entre outras. / It was realized, in the context of this work, a study about tropical wood species and their qualification, based on the physical and mechanical properties. The tests to the determination of such properties were realized in Wood and Timber Structures Laboratory, Structural Engineering Departament, São Carlos Engineering School, according to the recommendations of the Annex B, NBR 7190/1997 - Timber Structures Design. The mean subject is to generate information to permit new application in civil construction: structures for different purposes (roofs, bridges, formwork); industrial to building components; storage; among others.

A preservação química visa proteger a madeira contra quaisquer ações deterioradoras, sejam elas consequências de fenômenos físico-químicos, como a ação do intemperismo, ou de fenômenos biológicos, como os organismos xilófagos. No Brasil, os preservativos mais utilizados nas usinas de preservação são o Arseniato de Cobre Cromatado (CCA) e o Borato de Cobre Cromatado (CCB). Ambos são aplicados na madeira através do processo de vácuo-pressão, método que em tese poderia aumentar a quantidade de defeitos superficiais e diminuir os valores das propriedades físico-mecânicas das madeiras. Atualmente, em decorrência da disponibilização no mercado (devida à implantação de áreas certificadas no Brasil) de espécies de madeira de média a baixa densidade, a questão da necessidade da preservação contra a demanda biológica se constitui em aspecto de fundamental importância para que se garantam as alternativas de oferta desse material para a construção de estruturas, cuja durabilidade seja equivalente à da madeira de espécies de uso consagrado, como Jatobá, Sucupira, Garapa e Itaúba, por exemplo. Neste contexto, o presente trabalho teve como objetivo investigar a influência dos tratamentos com os preservativos CCA e CCB nas propriedades físico-mecânicas das seguintes espécies de madeiras tropicais brasileiras: Simarouba amara (C20), Cedrelinga catenaeformis (C30) e Erisma uncinatum Warm (C40), escolhidas na tentativa de abranger as três classes de resistência mais baixas, de acordo com o que prescreve a ABNT NBR 7190:1997. Foi realizada a caracterização completa de cada espécie nos três tipos de tratamento (Sem tratamento – Ref; CCA; CCB) para posterior aplicação do teste de comparações múltiplas de Tukey, avaliado ao nível de 5% de significância. Para avaliar o comportamento dos preservativos a nível celular, foram geradas fotomicrografias por Microscopia Eletrônica de Varredura (MEV) e seus respectivos espectros de EDS. Os resultados obtidos mostraram que ambos os tratamentos químicos não afetaram significativamente os valores das propriedades físico-mecânicas das espécies estudadas. / The chemical preservation aims to protect the wood against any deteriorating actions, be they consequences of physical-chemical phenomena, such as weathering, or biological phenomena, such as xylophagous organisms. In Brazil, the most used preservatives in the preservation plants are Chromated Copper Arsenate (CCA) and Chromated Copper Borate (CCB). Both are applied to the wood through the vacuum-pressure process, which in theory could increase the amount of surface defects and decrease the values of the physical-mechanical properties of the wood. Currently, due to the availability in the market (due to the implantation of certified areas in Brazil) of medium to low density wood species, the question of the need for preservation against biological demand is an aspect of fundamental importance to ensure the alternatives of supply of this material for the construction of structures, whose durability is equivalent to the wood of species of consecrated use, such as Jatobá, Sucupira, Garapa and Itaúba, for example In this context, the present work had as objective to investigate the influence of the treatments with the preservatives CCA and CCB on physical-mechanical properties of the following species of Brazilian tropical woods: Simarouba amara (C20), Cedrelinga catenaeformis (C30) e Erisma uncinatum Warm (C40), chosen in an attempt to cover the three lower resistance classes, according to what ABNT NBR 7190:1997 prescribes. The complete characterization of each species in the three types of treatments (No treatment - Ref: CCA; CCB) was performed for the subsequent application of the Tukey\'s multiple comparison test, evaluated at the 5% level of significance. To evaluate the behavior of the preservatives at the cellular level, photomicrographs were generated by Scanning Electron Microscopy (SEM) and their respective EDS spectra. The results obtained showed that both chemical treatments did not affect significantly the values of the physical-mechanical properties of the studied species.

O presente trabalho teve como objetivo principal avaliar a utilização dos resíduos gerados pelo processamento mecânico das madeiras amazônicas Caryocar villosum, Hymenolobium excelsum, Mezilaurus itauba, Erisma uncinatum, Tachigali myrmecophyla e Qualea paraensis na produção de painéis aglomerados de alta densificação. Os painéis foram produzidos com massa específica nominal de 850 kg.m-3, espessura nominal de 15,7 mm e adesivo fenol-formaldeído. Foram adotados 16 tratamentos, analisados por meio de quatro experimentos consecutivos, os quais avaliaram as propriedades físico-mecânicas dos painéis produzidos a partir de cada espécie e de uma mistura entre todas elas em partes iguais, o efeito da remoção dos finos no processo de produção, a influência da alteração do teor de adesivo de 8% para 11% sobre as propriedades dos painéis e a utilização da proporção de 50% de mistura com resíduos de lâminas de Schizolobium amazonicum. A partir dos painéis produzidos, foram confeccionados corpos-de-prova para a realização de ensaios físicos (massa específica, teor de umidade, absorção de água e inchamento em espessura) e mecânicos (flexão estática - MoR e MoE, ligação interna, arrancamento de parafuso e dureza Janka), conduzidos conforme a norma ABNT NBR 14810-3 (2006b). Foi realizada, também, a avaliação do perfil de densidade dos painéis pela metodologia de atenuação de raios X. Observou-se que os painéis aglomerados manufaturados com os resíduos das madeiras Caryocar villosum, Hymenolobium excelsum e Tachigali myrmecophyla apresentaram, de maneira geral, propriedades tecnológicas superiores às demais espécies, atendendo um ou mais requisitos mínimos indicados pela norma ANSI A208.1 (2009) para painéis de alta densidade (classificação H-1) e painéis destinados a produção de pisos (classificação PBU). A remoção dos finos na produção dos painéis resultou em tendência de aumento dos valores de MoR, MoE, ligação interna e dureza Janka e contribuiu para reduzir a AA2h, AA24h e IE2h, além de formar perfis de densidade mais homogêneos. O aumento do teor de adesivo de 8% para 11% resultou em tendência de redução dos valores de AA2h, AA24h, IE2h e IE24h e aumento dos valores de dureza Janka, bem como interações significativas para o MoE e ligação interna, além de formar perfis com picos mais elevados de massa específica nas faces e aumento dos valores de massa específica no miolo. A utilização da proporção de 50% de mistura com partículas de Schizolobium amazonicum resultou em tendência de aumento dos valores de MoE e AP topo e redução dos valores de dureza Janka. Houve interação significativa entre os fatores para as propriedades AA24h, IE2h, IE24h, MoR e ligação interna, resultando em tendência de aumento dos valores obtidos. A mistura de 50% originou perfis com picos mais elevados de massa específica nas faces. Os painéis aglomerados manufaturados com resíduos de madeiras amazônicas apresentaram potencial de utilização e se revelaram uma alternativa viável do ponto de vista tecnológico para o aproveitamento de resíduos. / The purpose of this research was to evaluate the potential use of Amazonian wood residues from the mechanical processing of Caryocar villosum, Hymenolobium excelsum, Mezilaurus lindaviana, Erisma uncinatum, Tachigali myrmecophyla and Qualea paraensis in the high density particleboard production. The panels were produced with nominal density of 850 kg.m-3, nominal thickness of 15.7 mm and phenol formaldehyde adhesive. Sixteen treatments were analyzed by four consecutive experiments, which evaluated the physical and mechanical properties of the boards produced from the six species and an equal mix of all six, the effect of removing the fines in the production process, the influence of the change of 8% adhesive content to 11% on the properties of the panels and the use of the mixture proportion of 50% with veneers residues of Schizolobium amazonicum. Their performance was evaluated with respect to their physical (apparent density, moisture content, water absorption and thickness swelling) and mechanical (static bending - modulus of elasticity and modulus of rupture, internal bond, direct screw withdrawal and Janka hardness) properties, conducted according to ABNT NBR 14810-3 (2006b). The evaluation of the density profile of the panels was also performed by X-ray attenuation methodology. It was observed that the particleboard manufactured with wood residues from Caryocar villosum, Hymenolobium excelsum and Tachigali myrmecophyla presented, in general, technological properties superior to other species, according one or more minimum requirements specified by ANSI A208.1 (2009) for high density panels (H-1 grade) and panels for the production of floors (PBU grade). The removal of the fine in the production of panels resulted in a tendency to increase the values of MoR, MoE, internal bond and Janka hardness and contributed to reduce the WA2h, WA24h and TS2h, besides formed more homogeneous density profiles. The increase from 8% adhesive content to 11% resulted in a tendency to reduce the values of WA2h, WA24h, TS2h and TS24h and increased Janka hardness values, as well as presented significant interactions for the MoE and internal bond, besides formed profiles with higher peak density in the faces and lowest density values in the core. The utilization of 50% mixture proportion with Schizolobium amazonicum particles resulted in a tendency to increase the values of MoE and direct screw withdrawal from the edge and reduced the values of Janka hardness. There were significant interactions between the factors for WA24h, TS2h, TS24h, MoR and internal bond properties, resulting in a tendency to increase the values. The mixture of 50% originated profiles with higher peak density in the faces. The particleboard manufactured with Amazonian wood residues showed potential use and viable alternative from a technological point of view for residues recovery.

Além da secagem convencional, a aplicação de tratamentos térmicos a altas temperaturas é um dos processos mais empregados para potencializar a estabilidade da madeira, porém necessitam de estrutura e equipamentos próprios. Diante disto, a proposta desta pesquisa fundamenta-se no estudo da aplicação de tratamentos estabilizadores para redução da higroscopicidade do material madeira, mediante temperaturas mais brandas (abaixo de 150°C) e que permitam a aplicação prática em equipamentos de secagem utilizados na indústria nacional. O objetivo geral deste trabalho foi avaliar os efeitos dos tratamentos estabilizadores nas propriedades físicas e componentes químicos da madeira para sua viabilização prática. O trabalho consistiu em duas etapas, na primeira: foram utilizadas três espécies de folhosas: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba), foi realizada a caracterização anatômica das espécies utilizando Microscopia Ótica e Microscopia Eletrônica de Varredura (MEV), e análise da composição química e propriedades físicas. As amostras destinadas aos tratamentos estabilizadores, inicialmente, foram secas em estufa convencional e em seguida passaram pelos tratamentos estabilizadores em autoclave a 90°C (24 e 96h) e 120°C (2h e 8h). Em seguida, foram realizados os condicionamentos higroscópicos (adsorção e dessorção) nas umidades relativas de 30, 60 e 90% para avaliação do potencial higroscópico e das variações dimensionais. Na segunda etapa, a partir dos resultados obtidos na primeira etapa, foi possível aplicar o tratamento propriamente dito, o piloto em escala industrial, utilizando uma estufa de secagem convencional (90°C por 24 horas); e em escala laboratorial (90°C por 24 e 96 horas), em uma câmara de climatização simulando um secador convencional. Para o tratamento piloto, foi levado em consideração a disponibilidade de matéria prima da empresa e tendo como foco o trabalho concomitante entre laboratório e aplicação industrial, a espécie utilizada foi o Cumarú (Dipterix sp), uma vez que essa espécie é considerada pela indústria como uma das mais problemáticas e, portanto, uma das espécies prioritárias para receber um tratamento que contribua para reduzir a variação dimensional após secagem. Os principais resultados permitiram observar que os tratamentos estabilizadores na forma em que foram aplicados na presente pesquisa, não causaram alterações na composição química na madeira das espécies e quando realizados em ambiente com alta umidade relativa, não apresentam redução significativa da higroscopicidade e da variação dimensional na maioria dos condicionamentos. Com aplicação do tratamento piloto foi possível observar que com o controle da umidade relativa do ar, tanto no início quanto no final do processo, é possível reduzir o potencial higroscópico da madeira mediante aplicação de tratamentos estabilizadores. / Besides conventional drying, the application of heat treatment at high temperatures is one of the processes employed to improve the stability of wood, however they require its own structure and equipment. Therefore, the purpose of this research is based on the application of the stabilizers treatments studies of wood material hygroscopicity reduction, using low temperatures (below 150°C) and that allows practical application in drying equipment used in the domestic industry. The aim of this study was to evaluate the effects of stabilizing treatments on the physical properties and chemical components of wood for its practical feasibility. The research was comprised for two steps, the first: a total of three species of hardwoods had been used: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba). The characterization of this three species was made by anatomical description, using Optical Microscope and Scanning Electron Microscopy (SEM), the chemical composition analysis and the physical properties. Samples of the stabilizing treatment, initially, were dried in a conventional kiln dryer and then the stabilizing treatment was applied in an autoclave at 90°C (24 e 96h) e 120°C (2h e 8h). Next, the hygroscopic conditioning were conducted (adsorption and desorption) in relative humidity (RH) of 30, 60 and 90% for evaluation of hygroscopic potential and dimensional changes. In the second stage, from the results obtained in the first step, it was possible to apply the treatment itself, the industrial scale pilot, using a conventional kiln dryer (90°C for 24 hours); and laboratory scale (90°C for 24 and 96 hours) in a climate chamber simulating a conventional dryer. For the pilot treatment, the availability of raw materials in the company was taken into account and focusing on the concurrent work between laboratory and industrial application, the selected specie was Cumarú (Dipterix sp), considered by the industry as one of the most problematic and, therefore a priority species to receive a treatment that can help to reduce the dimensional change after drying. The main results allowed to observe that the stabilizing treatments in the way that were applied in this study, did not cause changes in the chemical composition and when performed in an environment with high relative humidity, show no significant reduction of hygroscopicity and dimensional variation in most of conditionings. From the implementation of pilot treatment was observed that adopting the control of relative humidity, both in the beginning and the end of the process, is possible to reduce hygroscopic potential of wood by applying stabilizers treatments.

A preservação química visa proteger a madeira contra quaisquer ações deterioradoras, sejam elas consequências de fenômenos físico-químicos, como a ação do intemperismo, ou de fenômenos biológicos, como os organismos xilófagos. No Brasil, os preservativos mais utilizados nas usinas de preservação são o Arseniato de Cobre Cromatado (CCA) e o Borato de Cobre Cromatado (CCB). Ambos são aplicados na madeira através do processo de vácuo-pressão, método que em tese poderia aumentar a quantidade de defeitos superficiais e diminuir os valores das propriedades físico-mecânicas das madeiras. Atualmente, em decorrência da disponibilização no mercado (devida à implantação de áreas certificadas no Brasil) de espécies de madeira de média a baixa densidade, a questão da necessidade da preservação contra a demanda biológica se constitui em aspecto de fundamental importância para que se garantam as alternativas de oferta desse material para a construção de estruturas, cuja durabilidade seja equivalente à da madeira de espécies de uso consagrado, como Jatobá, Sucupira, Garapa e Itaúba, por exemplo. Neste contexto, o presente trabalho teve como objetivo investigar a influência dos tratamentos com os preservativos CCA e CCB nas propriedades físico-mecânicas das seguintes espécies de madeiras tropicais brasileiras: Simarouba amara (C20), Cedrelinga catenaeformis (C30) e Erisma uncinatum Warm (C40), escolhidas na tentativa de abranger as três classes de resistência mais baixas, de acordo com o que prescreve a ABNT NBR 7190:1997. Foi realizada a caracterização completa de cada espécie nos três tipos de tratamento (Sem tratamento – Ref; CCA; CCB) para posterior aplicação do teste de comparações múltiplas de Tukey, avaliado ao nível de 5% de significância. Para avaliar o comportamento dos preservativos a nível celular, foram geradas fotomicrografias por Microscopia Eletrônica de Varredura (MEV) e seus respectivos espectros de EDS. Os resultados obtidos mostraram que ambos os tratamentos químicos não afetaram significativamente os valores das propriedades físico-mecânicas das espécies estudadas. / The chemical preservation aims to protect the wood against any deteriorating actions, be they consequences of physical-chemical phenomena, such as weathering, or biological phenomena, such as xylophagous organisms. In Brazil, the most used preservatives in the preservation plants are Chromated Copper Arsenate (CCA) and Chromated Copper Borate (CCB). Both are applied to the wood through the vacuum-pressure process, which in theory could increase the amount of surface defects and decrease the values of the physical-mechanical properties of the wood. Currently, due to the availability in the market (due to the implantation of certified areas in Brazil) of medium to low density wood species, the question of the need for preservation against biological demand is an aspect of fundamental importance to ensure the alternatives of supply of this material for the construction of structures, whose durability is equivalent to the wood of species of consecrated use, such as Jatobá, Sucupira, Garapa and Itaúba, for example In this context, the present work had as objective to investigate the influence of the treatments with the preservatives CCA and CCB on physical-mechanical properties of the following species of Brazilian tropical woods: Simarouba amara (C20), Cedrelinga catenaeformis (C30) e Erisma uncinatum Warm (C40), chosen in an attempt to cover the three lower resistance classes, according to what ABNT NBR 7190:1997 prescribes. The complete characterization of each species in the three types of treatments (No treatment - Ref: CCA; CCB) was performed for the subsequent application of the Tukey\'s multiple comparison test, evaluated at the 5% level of significance. To evaluate the behavior of the preservatives at the cellular level, photomicrographs were generated by Scanning Electron Microscopy (SEM) and their respective EDS spectra. The results obtained showed that both chemical treatments did not affect significantly the values of the physical-mechanical properties of the studied species.

O presente trabalho teve como objetivo principal avaliar a utilização dos resíduos gerados pelo processamento mecânico das madeiras amazônicas Caryocar villosum, Hymenolobium excelsum, Mezilaurus itauba, Erisma uncinatum, Tachigali myrmecophyla e Qualea paraensis na produção de painéis aglomerados de alta densificação. Os painéis foram produzidos com massa específica nominal de 850 kg.m-3, espessura nominal de 15,7 mm e adesivo fenol-formaldeído. Foram adotados 16 tratamentos, analisados por meio de quatro experimentos consecutivos, os quais avaliaram as propriedades físico-mecânicas dos painéis produzidos a partir de cada espécie e de uma mistura entre todas elas em partes iguais, o efeito da remoção dos finos no processo de produção, a influência da alteração do teor de adesivo de 8% para 11% sobre as propriedades dos painéis e a utilização da proporção de 50% de mistura com resíduos de lâminas de Schizolobium amazonicum. A partir dos painéis produzidos, foram confeccionados corpos-de-prova para a realização de ensaios físicos (massa específica, teor de umidade, absorção de água e inchamento em espessura) e mecânicos (flexão estática - MoR e MoE, ligação interna, arrancamento de parafuso e dureza Janka), conduzidos conforme a norma ABNT NBR 14810-3 (2006b). Foi realizada, também, a avaliação do perfil de densidade dos painéis pela metodologia de atenuação de raios X. Observou-se que os painéis aglomerados manufaturados com os resíduos das madeiras Caryocar villosum, Hymenolobium excelsum e Tachigali myrmecophyla apresentaram, de maneira geral, propriedades tecnológicas superiores às demais espécies, atendendo um ou mais requisitos mínimos indicados pela norma ANSI A208.1 (2009) para painéis de alta densidade (classificação H-1) e painéis destinados a produção de pisos (classificação PBU). A remoção dos finos na produção dos painéis resultou em tendência de aumento dos valores de MoR, MoE, ligação interna e dureza Janka e contribuiu para reduzir a AA2h, AA24h e IE2h, além de formar perfis de densidade mais homogêneos. O aumento do teor de adesivo de 8% para 11% resultou em tendência de redução dos valores de AA2h, AA24h, IE2h e IE24h e aumento dos valores de dureza Janka, bem como interações significativas para o MoE e ligação interna, além de formar perfis com picos mais elevados de massa específica nas faces e aumento dos valores de massa específica no miolo. A utilização da proporção de 50% de mistura com partículas de Schizolobium amazonicum resultou em tendência de aumento dos valores de MoE e AP topo e redução dos valores de dureza Janka. Houve interação significativa entre os fatores para as propriedades AA24h, IE2h, IE24h, MoR e ligação interna, resultando em tendência de aumento dos valores obtidos. A mistura de 50% originou perfis com picos mais elevados de massa específica nas faces. Os painéis aglomerados manufaturados com resíduos de madeiras amazônicas apresentaram potencial de utilização e se revelaram uma alternativa viável do ponto de vista tecnológico para o aproveitamento de resíduos. / The purpose of this research was to evaluate the potential use of Amazonian wood residues from the mechanical processing of Caryocar villosum, Hymenolobium excelsum, Mezilaurus lindaviana, Erisma uncinatum, Tachigali myrmecophyla and Qualea paraensis in the high density particleboard production. The panels were produced with nominal density of 850 kg.m-3, nominal thickness of 15.7 mm and phenol formaldehyde adhesive. Sixteen treatments were analyzed by four consecutive experiments, which evaluated the physical and mechanical properties of the boards produced from the six species and an equal mix of all six, the effect of removing the fines in the production process, the influence of the change of 8% adhesive content to 11% on the properties of the panels and the use of the mixture proportion of 50% with veneers residues of Schizolobium amazonicum. Their performance was evaluated with respect to their physical (apparent density, moisture content, water absorption and thickness swelling) and mechanical (static bending - modulus of elasticity and modulus of rupture, internal bond, direct screw withdrawal and Janka hardness) properties, conducted according to ABNT NBR 14810-3 (2006b). The evaluation of the density profile of the panels was also performed by X-ray attenuation methodology. It was observed that the particleboard manufactured with wood residues from Caryocar villosum, Hymenolobium excelsum and Tachigali myrmecophyla presented, in general, technological properties superior to other species, according one or more minimum requirements specified by ANSI A208.1 (2009) for high density panels (H-1 grade) and panels for the production of floors (PBU grade). The removal of the fine in the production of panels resulted in a tendency to increase the values of MoR, MoE, internal bond and Janka hardness and contributed to reduce the WA2h, WA24h and TS2h, besides formed more homogeneous density profiles. The increase from 8% adhesive content to 11% resulted in a tendency to reduce the values of WA2h, WA24h, TS2h and TS24h and increased Janka hardness values, as well as presented significant interactions for the MoE and internal bond, besides formed profiles with higher peak density in the faces and lowest density values in the core. The utilization of 50% mixture proportion with Schizolobium amazonicum particles resulted in a tendency to increase the values of MoE and direct screw withdrawal from the edge and reduced the values of Janka hardness. There were significant interactions between the factors for WA24h, TS2h, TS24h, MoR and internal bond properties, resulting in a tendency to increase the values. The mixture of 50% originated profiles with higher peak density in the faces. The particleboard manufactured with Amazonian wood residues showed potential use and viable alternative from a technological point of view for residues recovery.

Além da secagem convencional, a aplicação de tratamentos térmicos a altas temperaturas é um dos processos mais empregados para potencializar a estabilidade da madeira, porém necessitam de estrutura e equipamentos próprios. Diante disto, a proposta desta pesquisa fundamenta-se no estudo da aplicação de tratamentos estabilizadores para redução da higroscopicidade do material madeira, mediante temperaturas mais brandas (abaixo de 150°C) e que permitam a aplicação prática em equipamentos de secagem utilizados na indústria nacional. O objetivo geral deste trabalho foi avaliar os efeitos dos tratamentos estabilizadores nas propriedades físicas e componentes químicos da madeira para sua viabilização prática. O trabalho consistiu em duas etapas, na primeira: foram utilizadas três espécies de folhosas: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba), foi realizada a caracterização anatômica das espécies utilizando Microscopia Ótica e Microscopia Eletrônica de Varredura (MEV), e análise da composição química e propriedades físicas. As amostras destinadas aos tratamentos estabilizadores, inicialmente, foram secas em estufa convencional e em seguida passaram pelos tratamentos estabilizadores em autoclave a 90°C (24 e 96h) e 120°C (2h e 8h). Em seguida, foram realizados os condicionamentos higroscópicos (adsorção e dessorção) nas umidades relativas de 30, 60 e 90% para avaliação do potencial higroscópico e das variações dimensionais. Na segunda etapa, a partir dos resultados obtidos na primeira etapa, foi possível aplicar o tratamento propriamente dito, o piloto em escala industrial, utilizando uma estufa de secagem convencional (90°C por 24 horas); e em escala laboratorial (90°C por 24 e 96 horas), em uma câmara de climatização simulando um secador convencional. Para o tratamento piloto, foi levado em consideração a disponibilidade de matéria prima da empresa e tendo como foco o trabalho concomitante entre laboratório e aplicação industrial, a espécie utilizada foi o Cumarú (Dipterix sp), uma vez que essa espécie é considerada pela indústria como uma das mais problemáticas e, portanto, uma das espécies prioritárias para receber um tratamento que contribua para reduzir a variação dimensional após secagem. Os principais resultados permitiram observar que os tratamentos estabilizadores na forma em que foram aplicados na presente pesquisa, não causaram alterações na composição química na madeira das espécies e quando realizados em ambiente com alta umidade relativa, não apresentam redução significativa da higroscopicidade e da variação dimensional na maioria dos condicionamentos. Com aplicação do tratamento piloto foi possível observar que com o controle da umidade relativa do ar, tanto no início quanto no final do processo, é possível reduzir o potencial higroscópico da madeira mediante aplicação de tratamentos estabilizadores. / Besides conventional drying, the application of heat treatment at high temperatures is one of the processes employed to improve the stability of wood, however they require its own structure and equipment. Therefore, the purpose of this research is based on the application of the stabilizers treatments studies of wood material hygroscopicity reduction, using low temperatures (below 150°C) and that allows practical application in drying equipment used in the domestic industry. The aim of this study was to evaluate the effects of stabilizing treatments on the physical properties and chemical components of wood for its practical feasibility. The research was comprised for two steps, the first: a total of three species of hardwoods had been used: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba). The characterization of this three species was made by anatomical description, using Optical Microscope and Scanning Electron Microscopy (SEM), the chemical composition analysis and the physical properties. Samples of the stabilizing treatment, initially, were dried in a conventional kiln dryer and then the stabilizing treatment was applied in an autoclave at 90°C (24 e 96h) e 120°C (2h e 8h). Next, the hygroscopic conditioning were conducted (adsorption and desorption) in relative humidity (RH) of 30, 60 and 90% for evaluation of hygroscopic potential and dimensional changes. In the second stage, from the results obtained in the first step, it was possible to apply the treatment itself, the industrial scale pilot, using a conventional kiln dryer (90°C for 24 hours); and laboratory scale (90°C for 24 and 96 hours) in a climate chamber simulating a conventional dryer. For the pilot treatment, the availability of raw materials in the company was taken into account and focusing on the concurrent work between laboratory and industrial application, the selected specie was Cumarú (Dipterix sp), considered by the industry as one of the most problematic and, therefore a priority species to receive a treatment that can help to reduce the dimensional change after drying. The main results allowed to observe that the stabilizing treatments in the way that were applied in this study, did not cause changes in the chemical composition and when performed in an environment with high relative humidity, show no significant reduction of hygroscopicity and dimensional variation in most of conditionings. From the implementation of pilot treatment was observed that adopting the control of relative humidity, both in the beginning and the end of the process, is possible to reduce hygroscopic potential of wood by applying stabilizers treatments.