Orientador: Eliermes Arraes Meneses / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Física Gleb Wataghin / Made available in DSpace on 2018-08-26T09:54:15Z (GMT). No. of bitstreams: 1 Gazoto_AndreLuis_M.pdf: 15242675 bytes, checksum: ac4c94e41838cf002e9c0e1f968e4b63 (MD5) Previous issue date: 2004 / Resumo: Neste trabalho realizamos um estudo sobre a influência da espessura nominal do poço quântico de InP nas propriedades ótica e estrutural de pontos quânticos de InP crescidos sobre InGaP. Foram utilizadas técnicas de espectroscopia ótica como fotoluminescência (PL), microfotoluminescência (?-PL) e fotoluminescência de excitação (PLE), assim como técnicas de caracterização estrutural Reflection High Energy Electron Diffraction (RHEED) e Atomic Force Microscopy (AFM). As questões envolvidas na evolução de um crescimento bidimensional para um tridimensional são investigadas em amostras crescidas pela técnica de Chemical Beam Epitaxy (CBE), utilizando-se o método Stranski-Krastanov de crescimento. Os resultados dessa investigação mostraram que as propriedades ótica e estrutural são fortemente correlacionadas e dependentes da espessura nominal do poço quântico de InP. Por AFM foi possível observar a formação de pontos quânticos a partir da rugosidade superficial do InP. Com o incremento na espessura nominal do poço quântico de InP o sistema evolui para uma configuração bimodal de ilhas pseudomórficas e com forma de tronco de pirâmide, formando assim duas famílias. A transição entre estas famílias se dá com o facetamento das ilhas pseudomórficas a partir de um volume crítico VC de cada ilha. O ponto em que essa transição ocorre pode ser determinado com o aparecimento de estruturas tipo chevron no padrão de difração do RHEED. Ficou claro que a transição de um crescimento bi para tridimensional não é abrupta, mas sim contínua. Foi encontrado também, um comportamento autolimitante para o raio desses pontos quânticos. A rica evolução do crescimento epitaxial de pontos quânticos de InP, observada pelas técnicas estruturais, pôde ser acompanhada também pelas técnicas óticas. A correlação dos dados estrutural e ótico confirmou uma evolução contínua de um crescimento 2D para um 3D com a coexistência destes dois modos de crescimento durante um certo intervalo de espessura do poço quântico de InP. Mostramos assim, que uma transição de fase de primeira ordem, comumente utilizada para descrever a transição entre os crescimentos bi e tridimensional, não descreve corretamente o crescimento epitaxial de pontos quânticos de InP/InGaP pelo método Stranski-Krastanov / Abstract: In this work we study the influence of the thickness of InP quantum well on the optical and structural properties of the InP quantum dots that were grown on the InGaP barrier. For this study we have used optical spectroscopy techniques such as Photoluminescence (PL), Micro-Photoluminescence (?-PL), Excitation Photoluminescence (PLE); as well as structural characterization techniques such as Reflection High Energy Electron Diffraction (RHEED) and Atomic Force Microscopy (AFM). The evolution of the bi-dimensional to tri-dimensional growth was investigated in the InP/InGaP samples grown by Stranski-Krastanov method in a Chemical Beam Epitaxy Reactor (CBE). The results show that the optical and structural properties are strongly correlated and depend of the InP thickness. Through the AFM technique was possible to observe the formation of quantum dots from the surface rougeness of the InP layer. By increasing the nominal thickness of the InP quantum well, the system evolves to a bimodal configuration, one of pseudomorfic islands, and other, of truncated pyramidal shapes, thus creating two structure families. The transition between these two families occurs with the facing of these pseudomorfic islands after a Vc critical volume is reached. The point where the transition occurs can be determined by the appearance of structures chevron like in the RHEED diffraction pattern. It became clear that the transition from the bi-dimensional to tri-dimensional growth is not abrupt, but continuous. The rich evolution of the epitaxial growth of the InP quantum dots, observed through the structural techniques, was also able to be followed through the optical techniques. The correlation between the structural and optical data confirmed a continuous evolution of the growth process of the quantum dots, with the coexistence of the two modes of growth, during a certain thickness interval of the InP. We thus demonstrate that a first order phase transition, used commonly to describe the transition between the bi and tri-dimensional growths, does not describe correctly the growth of the InP/InGaP quantum dots by Stranki-Krastanov method / Mestrado / Física / Mestre em Física

This work studied the rheological and mechanical properties of polyamide 12 modified montmorillonite clays and bentonita (the organo-modified commercial montmorillonite and a bentonite modified by various routes. Two polyamides 12 were used for the polyamide matrix, a virgin and another reprocessed. The polyamide 12 reprocessed was derived from tailings lines of fluid transport in automotive vehicles. Ten different compositions were prepared in single-screw extruder, and subsequently molded test specimens by injection. For formulations reprocessed polyamide 12, were added 5 to 7 wt.% of a commercial organo-modified montmorillonite ( I44P ) and the virgin polyamide 12 , 3 and 5 wt.%. For virgin polyamide matrix, also formulations were studied with 3 and 5% by weight of bentonite treated with Agent Titanate. The nanocomposite structure formation was evaluated by X-ray diffraction. For all developed formulations, mechanical and rheological tests, and their results were correlated performed: polyamide matrices, the content and the treatments of the clays. Clay dispersion and morphology of the fracture surface were analyzed by SEM. The analysis results showed distinct mechanical and rheological behaviors depending on the type of matrix, the degree of dispersion of clay, content and type of treatment of clays. There was formation of nanocomposites for polyamide 12 modified with I44P clay and composites for polyamide 12 modified bentonite. The rheological properties confirm the increase of the elastic properties of the nanocomposites due to the restriction to macromolecular mobility. The addition of organophilic commercial montmorillonite (I44P) promoted the increased stiffness of the nanocomposites without significant loss of toughness. / Este trabalho estudou as propriedades reológicas e mecânicas de poliamida 12 modificadas com montmorilonitas, sendo uma montmorilonita organofilica comercial (I44P) e montmorilonita sódica (bentonita) modificada por diversas rotas. Para a matriz de poliamida, foram utilizadas duas poliamidas 12, sendo uma virgem e a outra reprocessada oriunda de rejeito de linhas de transporte de fluídos em veículos automotores. Foram preparadas dez composições diferentes em extrusora monorrosca e, posteriormente, moldados corpos de prova por injeção. Para as formulações de poliamida 12 reprocessada, foram adicionados 5 e 7% em massa de montmorilonita organofílica comercial e para a poliamida 12 virgem, 3 e 5%. Para esta mesma matriz de poliamida virgem, também foram estudadas formulações com 3 e 5% em massa das bentonitas tratadas com agente titanato. A formação de estrutura de nanocompósitos foi avaliada por difração de raios-X. Para todas as formulações desenvolvidas, foram realizados ensaios mecânicos e reológicos, e seus resultados correlacionados com: as matrizes de poliamida, o teor e os tratamentos das argilas. A dispersão da argila e a morfologia da superfície de fratura foram avaliadas por MEV. Os resultados das análises mostraram comportamentos mecânicos e reológicos distintos em função do tipo de matriz, grau de dispersão das argilas, o teor e o tipo de tratamento das argilas. Houve formação de nanocompósitos para poliamida 12 modificada com a argila I44P e de compósitos para poliamida 12 modificada com bentonitas. As propriedades reológicas confirmam o aumento das propriedades elásticas dos nanocompósitos devido à restrição a mobilidade macromolecular. A adição da montmorilonita organofilica comercial (I44P) promoveu o aumento da rigidez dos nanocompósitos sem perdas significativas da tenacidade.