Submitted by Marco Antônio de Ramos Chagas (mchagas@ufv.br) on 2017-06-26T12:57:42Z No. of bitstreams: 1 texto completo.pdf: 2127724 bytes, checksum: 89bc8ec500331342f75a21279e25866b (MD5) / Made available in DSpace on 2017-06-26T12:57:42Z (GMT). No. of bitstreams: 1 texto completo.pdf: 2127724 bytes, checksum: 89bc8ec500331342f75a21279e25866b (MD5) Previous issue date: 2017-03-09 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este trabalho tem como objetivo estudar as propriedades mecânicas e de durabilidade da alvenaria estrutural de blocos de concreto utilizando ensaios recomendados pela norma de desempenho ABNT NBR 15575:2013. Para tanto, foram avaliados blocos inteiros e meios blocos da família (15 x 40) cm com resistência nominal à compressão de 4,5 MPa, 8 MPa e 12 MPa. Utilizando os métodos de avaliação estabelecidos pela ABNT NBR 12118: 2014, os blocos foram adquiridos e avaliados quanto à: análise dimensional, absorção de água, área líquida, resistência à compressão, módulo de deformação e aplicação do modelo de previsão do avanço de frentes de carbonatação, este último solicitado como parâmetro na ABNT NBR 15575-2: 2013. Executou-se blocos, de todos os lotes, grauteados com grautes de resistência (15, 20, 25 MPa), produzindo também corpos de prova de graute, que foram ensaiados quanto ao avanço da frente de carbonatação, resistência à compressão e módulo de deformação. Por meio dessas avaliações foi possível estabelecer o desempenho estrutural e durabilidade do material analisado de acordo com os parâmetros estabelecidos pela norma de desempenho. / This work aims to study the mechanical properties and durability of structural masonry of concrete blocks using tests recommended by the performance standard ABNT NBR 15575: 2013. For that, the family blocks (15 x 40) cm with nominal compressive strength of 4.5 MPa, 8 MPa and 12 MPa were evaluated. Using the evaluation methods established by ABNT NBR 12118: 2014, the blocks were acquired and evaluated for: dimensional analysis, water absorption, net area, compressive strength, modulus of deformation and application of the forward frontier prediction model Carbonation, the latter being requested as a parameter in ABNT NBR 15575-2: 2013. Blocks of all portion were grouting with resistance groute (15, 20, 25 MPa), also producing groute specimens, which were tested for carbonation front advancement, compressive strength and modulus of deformation. Through these evaluations it was possible to establish the structural performance and durability of the material analyzed according to the parameters established by the performance standard.

Orientador: Margarete Cristiane de Costa Trindade Amorim / Banca: José Tadeu Garcia Tommaselli / Banca: João Lima Sant'Anna Neto / Banca: Maria Elisa Zanella / Banca: Emerson Galvani / Resumo: Os estudos e discussões sobre o ambiente construído e suas relações com os seres humanos são muitos, mas são poucas as suas aplicações para os projetos arquitetônicos escolares, assim, este estudo buscou compreender se a composição dos materiais construtivos das unidades escolares, associada ao uso e ocupação do solo presentes no entorno das escolas estaduais de Presidente Prudente/SP, comprometem as condições do conforto térmico das pessoas que frequentam esses espaços, especialmente os alunos. Estudos dessa natureza se tornam relevantes, pois a escola é um dos principais lugares em que os seres humanos adquirem competências e habilidades, que serão utilizadas na vida pessoal e profissional. A pesquisa teve como base teórica a proposta do Sistema Clima Urbano (Monteiro, 1976) com ênfase no canal de termodinâmico, que compreende o conforto térmico a partir do estudo das características da temperatura e umidade nas suas variações diurnas e sazonais no espaço urbano e os seus elementos construtivos. Para a... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The studies and discussions on the built environment and its relationship with human beings are many, but few applications for the architectural school, thus, this study sought to understand the composition of building materials of school units, associated with the use and occupation of land surrounding the present state schools in Presidente Prudente / SP, undertake the conditions of thermal comfort of people who attend these spaces, especially students. Studies of this nature become relevant, because the school is one of the main places where humans acquire skills and abilities that will be used in personal and professional life. The research was based on the theoretical proposal of the urban climate system (Monteiro, 1976) with emphasis on thermodynamic channel, comprising the thermal comfort from the study of the characteristics of temperature and humidity in its diurnal and seasonal variations in the urban space and the its... (Complete abstract click electronic access below) / Doutor

Orientador: Jorge Luís Akasaki / Co-orientador: Mauro Mitsuuchi Tashima / Banca: José Luiz Pinheiro Melges / Banca: Jorge Juan Payá Bernadeu / Resumo: O Brasil é o maior produtor mundial de cana-de-açúcar, devido a sua alta produção, enormes quantidades de cinza de bagaço cana-de-açúcar são geradas após a fabricação de álcool e açúcar. A fim de encontrar uma aplicação sustentável para este material residual, este trabalho avalia a produção e utilização de cinza de bagaço cana-de - açúcar (CBC), tanto na produção de aglomerantes com cimento Portland e também em aglomerantes ativados alcalinamente. As propriedades físicas e químicas de CBC foram avaliadas e, os resultados obtidos demonstraram que a CBC apresentou um baixo teor de matéria orgânica (4,4 %) e um elevado teor de SiO2 (78,6 %). A análise por meio do DRX mostrou a presença de fases cristalinas na CBC, sendo o quartzo a fase principal cristalina e a sua presença pode ser atribuída contaminação do bagaço por impurezas do solo. O uso de CBC em substituição parcial ao cimento Portland foi analisado para diferentes porcentagens e tempos de cura. A Reatividade pozolânica da CBC também foi determinada em pastas hidróxido de cálcio / CBC e pastas de cimento Portland / CBC por meio de análise termogravimétrica (TGA). Os resultados confirmaram a reatividade pozolânica da CBC. Para a produção de argamassas e pastas ativadas alcalinamente, trabalhou-se com uma mistura de escória de alto-forno / CBC. Diferentes porcentagens de CBC na faixa de 0-50 % e diferentes tipos de soluções ativadoras foram usadas neste estudo, tais como: hidróxido de sódio, hidróxido de potássio e solução de silicato de sódio. As argamassas ativadas alcalinamente apresentaram resistência à compressão variando de 15-50 MPa, após 90 dias de cura à temperatura ambiente. A análise microestrutural para pastas e argamassas ativadas alcalinamente foram realizadas utilizando diversas técnicas instrumentais, tais como: TGA, FTIR, DRX, SEM e PIM. Para a análise da durabilidade ... / Abstract: Brazil is the biggest worldwide sugar cane productor and, due to its high production, huge amounts of sugar cane bagasse ash are generated after alcohol and sugar manufacture. In order to find out a sustainable application for this waste material, this work assess the production and use of sugar cane bagasse ash (SCBA) both in Portland cement blended and also in alkali-activated binders. Physical and chemical properties of SCBA were assessed and, obtained results showed that SCBA presented low organic matter (4.4%) and a high SiO2 content (78.6%). XRD pattern showed the presence of crystalline phases in the SCBA, mainly quartz assigned to the soil impurities. The use of SCBA in Portland cement blended mortars was achieved in different percentages and for different curing time. Pozzolanic reactivity of SCBA was also determined in calcium hydroxide/SCBA pastes and Portland cement/SCBA pastes by means of thermogravimetric analysis (TGA) for different curing time. The results confirmed the pozzolanic reactivity of SCBA. SCBA was also used in binary systems blast furnace slag/SCBA for the production of alkali-activated binders. Different percentages of SCBA in the range 0-50% and different types of activating solutions such as sodium hydroxide, potassium hydroxide and sodium silicate solution were used in this study. Compressive strength mortars in the range 15-50 MPa were yielded after 90 curing days at room temperature. Microstructural analyses for alkali-activated binders were performed using several instrumental techniques such as TGA, FTIR, XRD, SEM and MIP. The durability of selected alkali-activated mortars were tested both in acid attack (HCl, HAc and HN4Cl) and sulfate attack (Na2SO4 and MgSO4). The obtained results were compared to a Portland cement mortars and depending on the attack and on the activating solution, alkali-activated binders can present increment on the compressive strength even ... / Mestre

Orientador: Mauro Mitsuuchi Tashima / Co-orientador: Jorge Luís Akasaki / Banca: José Luiz Pinheiro Melges / Banca: Lourdes Soriano Martinez / Resumo: O concreto de alto desempenho (CAD) possui uma densa microestrutura que lhe proporciona ao mesmo, alta resistência e redução de sua permeabilidade. Com isso, apresenta alta durabilidade, sendo maior que a do concreto convencional. Esse fato mostra que a utilização deste concreto está crescendo rapidamente em diversas obras. Este produto tem como base a cinza de bagaço de cana-de-açúcar (CBC), que possui grande potencial para ser utilizada como aditivo mineral em concretos, uma vez que é composta por dióxido de silício. A partir dessas afirmações, esta pesquisa apresenta a finalidade de analisar o desempenho da adição de CBC sem sofrer o processo de moagem, na fabricação do concreto de alto desempenho. Para tanto, foi feita a substituição de CBC na proporção de 5%, 10%, 15% e 20%, sendo esta substituída na quantidade de agregado miúdo em massa. Os ensaios realizados foram: absorção, módulo de elasticidade, resistência à compressão e resistência à tração por compressão diametral para as idades de 7, 28, 60 e 90 dias. Chegou-se, portanto, à conclusão que o CAD com CBC de substituição em 20% de agregado miúdo em massa foi o que obteve o melhor desempenho, por isso foi o traço escolhido para os ensaios de durabilidade, tais como: resistência ao ataque químico, absorção por capilaridade, frente à penetração de cloretos, ensaio de abrasão/erosão e permeabilidade à água. Assim, os resultados obtidos nos ensaios foram comparados aos mesmos ensaios realizados com o concreto referência, ou seja, CAD sem nenhuma adição. A partir daí, observou-se que, em determinados casos, o CAD com adição de CBC apresentou resultados iguais ou até mesmo superiores ao do concreto referência / Abstract: The high performance concrete (CAD) has a dense microstructure which provides the same, high strength and reduced permeability. With this, it has high durability, being greater than that of conventional concrete. This fact makes their use is growing rapidly in several works. Regarding bagasse ash cane sugar (CBC), this has great potential to be used as a mineral additive for concrete, since it is composed of silicon dioxide. Thus, this research has the purpose of analyzing the performance of the addition of CBC without undergoing milling, manufacturing of high performance concrete. Replacement of was which is substituted in the proportion of 5%, 10%, 15% and 20%, the amount of aggregate in massa. Os tests were performed: absorption, modulus of elasticity, compressive strength and tensile strength by diametrical compression to the ages of 7, 28, 60 and 90 days. Was reached, so the conclusion that CAD with CBC replacement in 20% of aggregate mass, was what had the best performance, so it was chosen for durability testing trait and which were the following: resistance to chemical attack, wicking, across the penetration of chlorides abrasion test / erosion and water permeability. The results obtained in the tests were compared to tests performed with the same reference concrete, that is, without addition CAD, showing in some cases, the addition of CAD with CBC showed equal or even superior results to the reference concrete / Mestre

Orientador: Haroldo de Mayo Bernardes / Banca: Antonio Anderson da Silva Segantini / Banca: Selmo Chapira Kuperman / Resumo: Diante dos vários casos registrados de anomalias surgidas em concretos de diferentes estruturas devidas às reações deletérias do tipo álcali-agregado (RAA), pesquisadores de todo o mundo têm buscado conhecer melhor o problema, entender seu mecanismo e caracterizar estruturas já afetadas. Realizou-se no presente trabalho um estudo de caso sobre a Tomada d'água (TA) da UHE Jaguari, visando estimar a expansibilidade do concreto dessa estrutura e a reatividade de agregados provenientes da região. Para isto, foram analisados testemunhos extraídos da TA por meio de ensaios de expansão, análises químicas e microestruturais, e um concreto com traço reconstituído em laboratório, reproduzindo o traço utilizado na construção da TA, avaliando a resistência mecânica, a propriedade elástica e a permeabilidade. Realizouse um estudo em separado dos agregados coletados da região (enrocamento da barragem, pedreira comercial e testemunho de sondagem da rocha de fundação da TA) por se tratar de materiais que provavelmente têm a mesma procedência que o empregado na barragem. Foram realizadas análises químicas, usando técnicas como difração de raios X e infravermelho, bem como análises do potencial expansivo, por meio de barras de argamassa e prismas de concreto, conforme as normas NBR 15577-4 e NBR 15577-6, respectivamente. Este conjunto de informações constitui uma contribuição para que venha a ser feita uma avaliação da real situação da estrutura no tocante à RAA, estabelecendo parâmetros iniciais para estimar em qual estágio de expansão a estrutura se encontra. / Abstract: Ahead of some registered cases of anomalies appeared in concrete of different structures due to the deleterious reactions of the alkali-aggregate reaction (AAR) type, researchers of all over the world have studied this problem, to understand its mechanism and to characterize structures which were already affected. In the present work, a characterization of the concrete used in this dam and a study of residual expansion obtained from extracted cores was performed. The case study was the intake of Jaguari Hydra Power plant, because it presents cracks that are characteristic of alkali-aggregate reaction. Tests were made on the same core of Jaguari Hydra Power Plant and in concrete from laboratory, using a local aggregate in order to evaluate: the strength, the elastic property, the permeability and the expansibility; as well as, chemical and micro structural analysis. Another study was made with aggregate collected from the rockfill of the dam, because this aggregate probably has the same origin that the one which were used in the dam construction and collected from soundings of the foundation rock of intake structure of Jaguari Power plant. This study contemplated chemical analysis, using techniques such as X-ray diffraction and infra-red ray, as well as analysis of the expansive potential in mortar bars and concrete prisms, through method NBR 15577-4 e NBR 15577-6, respectively. All this information will be useful to establish initial parameters and estimate what is the stage of the structure expansion due to alkali-aggregate reaction. / Mestre