Foram avaliadas algumas propriedades físico-químicas, como o pH, liberação de íons cálcio, tempo de presa, solubilidade e radiopacidade de 3 cimentos a base do agregado de trióxido mineral, clínquer do cimento Portland e um epóxico experimental. Foram avaliados os cimentos MTA Angelus branco, MTA Bio, cimentos experimentais, MTA fotopolimerizável e Sealepox RP e o Clínquer de cimento Portland acrescido de 20% de óxido de bismuto e 5% de sulfato de cálcio. Para as avaliações do pH e da liberação de íons cálcio foram utilizados tubos de polietileno com 1,0 mm de diâmetro interno e 10,0 mm de comprimento, com apenas uma das extremidades aberta. Esses tubos foram preenchidos com os cimentos e imediatamente imersos em tubos de ensaio contendo 10 mL de água deionizada, onde permaneceram durante todo o período experimental. Realizaram-se avaliações nos períodos de 3, 24, 72 e 168 horas, sempre se renovando a água deionizada ao final de cada período. Os ensaios de tempo de presa, solubilidade e radiopacidade, foram realizados conforme a norma #57 da ADA. Em relação ao tempo de presa, também foi utilizada a agulha de Gilmore de 453,6 g, para a presa final, conforme recomenda a norma #C266-03 da ASTM. Os resultados demonstraram que todos os cimentos apresentaram pH alcalino e liberaram íons cálcio em todos os períodos, com tendência de redução nos períodos finais. Quanto aos tempos de presa, os cimentos MTA Angelus branco e o cimento experimental MTA Bio apresentaram os menores tempos. Já o Clínquer apresentou valores intermediários, e o Sealepox RP, apresentou os tempos mais longos. O cimento MTA fotopolimerizável, por suas características próprias, não foi submetido a esse teste. Em relação ao ensaio de solubilidade, o cimento que mais se aproximou das recomendações da ADA, foi o Sealepox RP, com valores próximos a 1%, enquanto que os cimentos MTA Angelus branco, MTA Bio e o Clínquer acrescido ao radiopacificador e sulfato de cálcio apresentaram valores maiores. O MTA fotopolimerizável apresentou valores menores. Em relação à radiopacidade, a maioria dos cimentos estudados apresentou valores superiores à da dentina, com resultados semelhantes entre si, com exceção do MTA fotopolimerizável, que apresentou valor próximo ao da dentina. / Some properties had been evaluated physicochemical, such as pH, release of calcium ions, setting time, solubility and radiopacity of 3 retrograde filling the base of the aggregate of mineral trioxide, to clínquer of the Portland cement and an experimental epoxy sealer. Experimental cements MTA white Angelus, MTA Bio, light-curing MTA and Sealepox RP and the Clínquer of cement Portland increased of 20% of bismuth oxide and 5% of calcium sulphate had been evaluated. For the evaluations of pH and the release of calcium ions had been used polyethylene pipes with 1,0 mm of internal diameter and 10,0 mm of length, with only one of the extremities open. These pipes had been filled with cements and immediately immersed in pipes of 10 assay I contend mL of distilled water, where they had remained all during the experimental period. Evaluations in the periods of 3, 24, 72 and 168 hours, always if renewing the distilled water to the end of each period. The assays of setting time, solubility and radiopacity, had been carried through in agreement the norm #57 of the ADA. In relation to the setting time, also g was used the needle of Gilmore of 453,6, for the final canine tooth, as it recommends to the norm #C266-03 of the ASTM. The results had demonstrated that all the cements had presented pH alkaline and had liberated calcium ions in all the periods, with trend of reduction in the final periods. How much to the setting time, cements MTA white Angelus and experimental cement MTA Bio had presented the lesser times. Already the Clínquer presented intermediate values, and Sealepox RP, presented the times longest. Light-curing cement MTA, by its proper characteristics, was not submitted to this test. In relation to the solubility assay, the cement that more was come close to the recommendations of the ADA, was Sealepox RP, with next values 1%, whereas cements MTA white Angelus, MTA Bio and the Clínquer increased to the bismuth oxide and calcium sulphate had presented bigger values. The light-curing MTA presented less resulted . In relation to the radiopacity, the majority of studied cements presented more values to the one of the dentine, with similar results between itself, exception of the light-curing MTA, that presented value next to the one to the dentine.

Foram avaliadas algumas propriedades físico-químicas, como o pH, liberação de íons cálcio, tempo de presa, solubilidade e radiopacidade de 3 cimentos a base do agregado de trióxido mineral, clínquer do cimento Portland e um epóxico experimental. Foram avaliados os cimentos MTA Angelus branco, MTA Bio, cimentos experimentais, MTA fotopolimerizável e Sealepox RP e o Clínquer de cimento Portland acrescido de 20% de óxido de bismuto e 5% de sulfato de cálcio. Para as avaliações do pH e da liberação de íons cálcio foram utilizados tubos de polietileno com 1,0 mm de diâmetro interno e 10,0 mm de comprimento, com apenas uma das extremidades aberta. Esses tubos foram preenchidos com os cimentos e imediatamente imersos em tubos de ensaio contendo 10 mL de água deionizada, onde permaneceram durante todo o período experimental. Realizaram-se avaliações nos períodos de 3, 24, 72 e 168 horas, sempre se renovando a água deionizada ao final de cada período. Os ensaios de tempo de presa, solubilidade e radiopacidade, foram realizados conforme a norma #57 da ADA. Em relação ao tempo de presa, também foi utilizada a agulha de Gilmore de 453,6 g, para a presa final, conforme recomenda a norma #C266-03 da ASTM. Os resultados demonstraram que todos os cimentos apresentaram pH alcalino e liberaram íons cálcio em todos os períodos, com tendência de redução nos períodos finais. Quanto aos tempos de presa, os cimentos MTA Angelus branco e o cimento experimental MTA Bio apresentaram os menores tempos. Já o Clínquer apresentou valores intermediários, e o Sealepox RP, apresentou os tempos mais longos. O cimento MTA fotopolimerizável, por suas características próprias, não foi submetido a esse teste. Em relação ao ensaio de solubilidade, o cimento que mais se aproximou das recomendações da ADA, foi o Sealepox RP, com valores próximos a 1%, enquanto que os cimentos MTA Angelus branco, MTA Bio e o Clínquer acrescido ao radiopacificador e sulfato de cálcio apresentaram valores maiores. O MTA fotopolimerizável apresentou valores menores. Em relação à radiopacidade, a maioria dos cimentos estudados apresentou valores superiores à da dentina, com resultados semelhantes entre si, com exceção do MTA fotopolimerizável, que apresentou valor próximo ao da dentina. / Some properties had been evaluated physicochemical, such as pH, release of calcium ions, setting time, solubility and radiopacity of 3 retrograde filling the base of the aggregate of mineral trioxide, to clínquer of the Portland cement and an experimental epoxy sealer. Experimental cements MTA white Angelus, MTA Bio, light-curing MTA and Sealepox RP and the Clínquer of cement Portland increased of 20% of bismuth oxide and 5% of calcium sulphate had been evaluated. For the evaluations of pH and the release of calcium ions had been used polyethylene pipes with 1,0 mm of internal diameter and 10,0 mm of length, with only one of the extremities open. These pipes had been filled with cements and immediately immersed in pipes of 10 assay I contend mL of distilled water, where they had remained all during the experimental period. Evaluations in the periods of 3, 24, 72 and 168 hours, always if renewing the distilled water to the end of each period. The assays of setting time, solubility and radiopacity, had been carried through in agreement the norm #57 of the ADA. In relation to the setting time, also g was used the needle of Gilmore of 453,6, for the final canine tooth, as it recommends to the norm #C266-03 of the ASTM. The results had demonstrated that all the cements had presented pH alkaline and had liberated calcium ions in all the periods, with trend of reduction in the final periods. How much to the setting time, cements MTA white Angelus and experimental cement MTA Bio had presented the lesser times. Already the Clínquer presented intermediate values, and Sealepox RP, presented the times longest. Light-curing cement MTA, by its proper characteristics, was not submitted to this test. In relation to the solubility assay, the cement that more was come close to the recommendations of the ADA, was Sealepox RP, with next values 1%, whereas cements MTA white Angelus, MTA Bio and the Clínquer increased to the bismuth oxide and calcium sulphate had presented bigger values. The light-curing MTA presented less resulted . In relation to the radiopacity, the majority of studied cements presented more values to the one of the dentine, with similar results between itself, exception of the light-curing MTA, that presented value next to the one to the dentine.

Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2014-11-25T10:17:54Z No. of bitstreams: 2 Tese - Omar Zina - 2013.pdf: 1884367 bytes, checksum: ac70615bb4bc9a680a17fead9dac004b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2014-11-25T12:28:09Z (GMT) No. of bitstreams: 2 Tese - Omar Zina - 2013.pdf: 1884367 bytes, checksum: ac70615bb4bc9a680a17fead9dac004b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Made available in DSpace on 2014-11-25T12:28:09Z (GMT). No. of bitstreams: 2 Tese - Omar Zina - 2013.pdf: 1884367 bytes, checksum: ac70615bb4bc9a680a17fead9dac004b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Previous issue date: 2013-09-13 / The aim of this study was to determine the solution-powder ration and to evaluate the setting time, solubility, dimensional change, pH and radiopacity of White structural and non-structural Portland cement, ProRoot MTA® and MTA BIO® associated to 2% glycolic solution of Aloe vera. Five samples of each material were used for each test according to American National Standards Institute/American Dental Association specification 57. Statistical analyses were carried out using ANOVA and Tukey’s test at 5% level of significance. When sample distribution was non-normal, nonparametric analysis of variance were performed with Kruskal-Wallis test (α=0.05). The results revealed no statistical difference in the water-powder ratio among the tested materials. ProRoot MTA® had the longest setting time (116.50 ± 4.08) (P<0.05). White structural and nonstructural Portland cements did not have means values on the radiopacity test (109.76 ± 10.40 and 118.75 ± 15.44, respectively) in accordance with ANSI/ADA, being significantly different from the MTA-based cements (P<0.05), and demonstrated higher mean solubility values (2.30 ± 0.36 and 2.81 ± 0.40, respectively) (P<0.05). The values for dimensional change of all tested materials were considered acceptable by ANSI/ADA. There were no significant differences between the mean pH values recorded for the materials (p>0.05). It was alkaline from the beginning to the end of the tests. MTA BIO presented lower setting time and lower solubility. The cements did not showed a higher solubility than 3%. All the assessed cements showed acceptable values of dimensional variation and high pH during the test time. MTA BIO and ProRoot MTA had adequate radiopacity values. / Esse estudo teve como objetivo determinar propriedades físico-químicas dos cimentos Portland branco estrutural e não estrutural, ProRoot MTA® e MTA BIO® associados à solução glicólica de Aloe vera a 2%. Após o estabelecimento da proporção pó/líquido para cada cimento, foram analisadas as propriedaes físicoquímicas: tempo de endurecimento, alteração dimensional, pH e radiopacidade. Cinco amostras de cada cimento foram usadas para cada teste, seguindo a especificação n. 57 da American National Standards Institute/American Dental Association (ANSI/ADA). A análise estatística foi realizada usando ANOVA e o teste de Tukey em nível de significância de 5%. Quando a distribuição das amostras foi não normal, a análise de variância não paramétrica foi realizada com o teste de Kruskal-Wallis (α=0,05). Os resultados não mostraram diferenças estatisticamente significantes (p>0,05) entre os cimentos em relação à proporção pó/líquido, que variou de 3,14 a 3,52 gramas. O ProRoot MTA® apresentou o tempo de endurecimento mais longo (116,50 min) e o MTA BIO® o menor (66,75 min) (p<0,05). Os cimentos Portland brancos estrutural e não estrutural apresentaram valores médios de solubilidade mais elevados (2,30 e 2,81%, respectivamente) (p<0,05). Todos os cimentos testados apresentaram valores de alteração dimensional semelhantes entre si (1,00%). O pH dos cimentos manteve-se elevado do início ao final do experimento, não havendo diferenças significantes entre os valores médios obtidos (cimento Portland branco estrutural, 11,96; cimento Portland branco não estrutural, 11,80; MTA BIO® 12,07; ProRoot MTA® 11,77) (p>0,05). Os cimentos Portland branco estrutural e não estrutural não apresentaram valores médios em conformidade com ANSI/ADA no teste de radiopacidade (109,76 e 118,75 mmAl, respectivamente), significantemente diferentes dos cimentos MTA BIO® (156,83 mmAl) e ProRoot MTA® (157,95 mmAl) (p<0,05), que apresentaram valores de densidade radiográfica acima do degrau 3 do penetrômetro de alumínio. O MTA BIO® evidenciou menor tempo de endurecimento e menor percentual de solubilidade. Nenhum cimento apresentou solubilidade maior que 3%. Todos os xiv cimentos analisados mostraram valores aceitáveis de alteração dimensional e pH elevado durante todo o período de teste. O MTA BIO® e o ProRoot MTA® apresentaram valores de radiopacidade adequados..