Orientador: Cecilia Gatti Guirado, Milton Fernando de Andrade Silva / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-06T02:24:33Z (GMT). No. of bitstreams: 1 Vieira_KarllaAlmeida_M.pdf: 1454696 bytes, checksum: 54211a0f6cbc569a73706cdd1e4ef1f0 (MD5) Previous issue date: 2006 / Resumo: A Azadirachta indica A. Juss. (Nim) é uma planta tropical nativa do continente indiano. É utilizada na Índia e na Ásia há muitos anos como principal utensílio na manutenção da saúde dos dentes e gengivas. O presente estudo in vitro avaliou o potencial anticariogênico de extratos obtidos da semente e da folha da Azadirachta indica (Nim). Para tanto, 80 fragmentos dentais bovinos foram divididos aleatoriamente em 9 grupos de 9 réplicas cada, com exceção do último grupo, que apresentava 8 réplicas: grupo 1 ¿ Água destilada estéril; grupo 2 ¿ Colutório de gluconato de clorexidina (0,12%); grupo 3 ¿ Dentifrício com Nim; grupo 4 ¿ Emulsão do óleo de Nim a 0,5%; grupo 5 ¿ Emulsão do óleo de Nim a 1%; grupo 6 ¿ Extrato da folha do Nim a 5%; grupo 7 ¿ Extrato da folha do Nim a 10%; grupo 8 - Extrato da folha do Nim a 25%; grupo 9 ¿ Controle (Tween 80 + Tween 20 + água). Os blocos de esmalte foram submetidos a um modelo bacteriano de desmineralização com estreptococos mutans (cepa PS14) por 18 horas e, então, analisados quanto à perda mineral (microdureza e análise de Fósforo) e pH. Para microdureza, não houve diferença significante entre o Colutório de gluconato de clorexidina, a Água, o Dentifrício com Nim e o Extrato da folha de Nim a 10% e 25%. Para o pH, observou-se que o Colutório de gluconato de clorexidina e o Dentifrício com Nim não diferiram estatisticamente. Para a análise de Fósforo, o grupo do Dentifrício com Nim não mostrou diferença estatística entre o grupo da Água e o Extrato da folha a 10% e 25%. No entanto, todos os grupos apresentaram diferença significante em relação ao grupo do Colutório de gluconato de clorexidina (p < 0,05%). Os resultados mostram que os extratos de Nim utilizados neste estudo in vitro não apresentam atividade anticariogênica / Abstract: The Azadirachta indica A. Juss. (Neem) is a tropical tree native to the Indian continent. It is used in India and Asia for many years as a tool for keeping teeth and gums healthy. This in vitro study evaluated the anticariogenic potential of seed and leaf extracts of Azadirachta indica (Neem). For this purpose, 80 bovine dental fragments were randomly divided in 9 groups of 9 specimens (with the exception of the group 9 which had 8 specimens): group 1 ¿ Sterile distilled water; group 2 - Chlorhexidine gluconate mouthwash (0.12%); group 3 ¿ Neem dentifrice; group 4 ¿ 0.5% Neem Emulsion; group 5 ¿ 1% Neem Emulsion; group 6 ¿ 5% Neem leaf extract ; group 7 - 10% Neem leaf extract; group 8 ¿ 25% Neem leaf extract; group 9 ¿ Control (Tween 80 + Tween 20 + water). The blocks were submitted to a demineralization bacterial model using a Streptococcus mutans (PS14 strain) for 18 hours. Then, the blocks were analyzed for surface mineral loss (microhardness and Phosphorus analysis) and pH. For microhardness, no statistical difference was observed between Chlorhexidine gluconate mouthwash, Water, Neem dentifrice, 10% and 25% Neem leaf extracts. For pH, no statistical difference was observed between Chlorhexidine gluconate mouthwash and Neem dentifrice. For the Phosphorus analysis, the Neem dentifrice not displayed a statistical difference between Water, 10% and 25% Leaf extracts groups. Nevertheless, all groups were differently from Chlorhexidine gluconate mouthwash (p<0.05%). The results shows that the Neem extracts used in this in vitro study do not show anticariogenic activity / Mestrado / Odontopediatria / Mestre em Odontologia

O objetivo deste estudo in vitro foi avaliar a perda mineral no esmalte adjacente a cavidades preparadas com laser de Er,Cr:YSGG e restauradas com diferentes materiais, liberadores ou não de flúor, após desafio ácido. Cento e vinte blocos de esmalte dental de terceiros molares humanos (4 x4 mm) foram aleatoriamente divididas em 12 grupos (n=10) de acordo com a técnica de preparo: G1- alta-rotação (AR); G2- Laser de Er,Cr:YSGG (3W, 20Hz, 53,05 J/cm2)(65% ar, 55% água); G3- Laser de Er,Cr:YSGG (4 W, 20 Hz, 70,74 J/cm2); G4- Laser de Er,Cr:YSGG (5 W, 20 Hz, 88,43 J/cm2). Cada grupo experimental foi dividido em subgrupos, conforme o material restaurador utilizado: 1- cimento de ionômero de vidro (CIV), 2- cimento de ionômero de vidro resino modificado (CIVRM), 3- sistema adesivo e resina composta (RC). As amostras foram submetidas a desafio ácido (pH 4,8) por 7 dias. As concentrações do íon cálcio nas soluções desmineralizadoras (ppm/mm2), nos diferentes tempos (1, 3 e 7 dias), foram analisadas por espectrofotometria de emissão atômica. Os dados obtidos foram analisados usando os testes estatísticos ANOVA e LSD (?=5%) mostrando haver diferenças significativas entre Técnica e Material Restaurador no tempo total. Os menores valores médios da perda de cálcio foram obtidos nos grupos G2 + CIV, G2 + CIVRM e G1 + CIVRM; os maiores valores foram observados nos grupos de G1 + RC, G4 + CIV e G4 + RC. As restaurações de RC apresentaram maior perda mineral que as de CIV e CIVRM; os preparos com laser utilizando menor radiância (53,05J/cm2) apresentaram significante menor desmineralização que as maiores radiâncias (70,74 e 88,43J/cm2). Nenhuma técnica ou material impediu a desmineralização do esmalte. Os resultados deste estudo in vitro sugerem que a realização de preparos cavitários com laser de Er,Cr:YSGG (53,05J/cm2) restaurados com CIV e CIVRM ou alta-rotação e CIVRM foram efetivos na redução da perda mineral e aumento da resistência ácida do esmalte adjacente as restaurações após desafio ácido, com importante potencial em prevenir lesões de cárie secundária. / The aim of this study was to evaluate the enamel calcium loss around cavities prepared by Er,Cr:YSGG laser and restored with different materials after an acid challenge. One hundred and twenty enamel samples obtained from third molars (4 x 4 mm) were randomly divided in 12 groups (n=10) using different techniques: G1- high-speed drill (HD); G2- Er,Cr:YSGG laser (3W, 20Hz, 53.05 J/cm2)(air 65% - water 55%); G3- Er,Cr:YSGG laser (4 W, 20 Hz, 70.74 J/cm2); G4- Er,Cr:YSGG laser (5 W, 20 Hz, 88.43 J/cm2). Each experimental group was divided in subgroups, according to the restorative material: 1 - glass ionomer cement (GIC), 2 - resin modified GIC (RMGIC), 3 - adhesive system and composite resin (C). Samples were submitted to an acid challenge (4.8 pH) for 7 days. The Demineralizing solutions were analyzed in relation to the calcium ion contend (ppm/mm2), in different times (1, 3 and 7 days), under atomic emission spectrometry. ANOVA and LSD tests were performed (?=5%). There were significant difference between Technique and Restorative Material on Total Time. The lower average values of calcium loss were observed on G2 + GIC, G2 + RMGIC, G1 + RMGIC groups; the higher values were observed on G1 + C, G4 +GIC, G4 + C. The composite resin showed higher calcium loss than RMGIC and GIC. The lased cavities using lower fluence (53.05J/cm2) showed significant reduced demineralization than higher fluences (70.74 and 88.43J/cm2). Neither the techniques nor the restorative materials used were able to prevent the enamel demineralization. The findings of this in vitro study suggest that the Er,Cr:YSGG lased cavities (53.05J/cm2) restored with GIC or RMGIC or conventional drill cavities with RMGIC were effective on reducing the mineral loss and enhancing the enamel acid resistant around restorations after the acid challenge, showing an important potential in preventing secondary caries.

O objetivo deste estudo in vitro foi avaliar a perda mineral no esmalte adjacente a cavidades preparadas com laser de Er,Cr:YSGG e restauradas com diferentes materiais, liberadores ou não de flúor, após desafio ácido. Cento e vinte blocos de esmalte dental de terceiros molares humanos (4 x4 mm) foram aleatoriamente divididas em 12 grupos (n=10) de acordo com a técnica de preparo: G1- alta-rotação (AR); G2- Laser de Er,Cr:YSGG (3W, 20Hz, 53,05 J/cm2)(65% ar, 55% água); G3- Laser de Er,Cr:YSGG (4 W, 20 Hz, 70,74 J/cm2); G4- Laser de Er,Cr:YSGG (5 W, 20 Hz, 88,43 J/cm2). Cada grupo experimental foi dividido em subgrupos, conforme o material restaurador utilizado: 1- cimento de ionômero de vidro (CIV), 2- cimento de ionômero de vidro resino modificado (CIVRM), 3- sistema adesivo e resina composta (RC). As amostras foram submetidas a desafio ácido (pH 4,8) por 7 dias. As concentrações do íon cálcio nas soluções desmineralizadoras (ppm/mm2), nos diferentes tempos (1, 3 e 7 dias), foram analisadas por espectrofotometria de emissão atômica. Os dados obtidos foram analisados usando os testes estatísticos ANOVA e LSD (?=5%) mostrando haver diferenças significativas entre Técnica e Material Restaurador no tempo total. Os menores valores médios da perda de cálcio foram obtidos nos grupos G2 + CIV, G2 + CIVRM e G1 + CIVRM; os maiores valores foram observados nos grupos de G1 + RC, G4 + CIV e G4 + RC. As restaurações de RC apresentaram maior perda mineral que as de CIV e CIVRM; os preparos com laser utilizando menor radiância (53,05J/cm2) apresentaram significante menor desmineralização que as maiores radiâncias (70,74 e 88,43J/cm2). Nenhuma técnica ou material impediu a desmineralização do esmalte. Os resultados deste estudo in vitro sugerem que a realização de preparos cavitários com laser de Er,Cr:YSGG (53,05J/cm2) restaurados com CIV e CIVRM ou alta-rotação e CIVRM foram efetivos na redução da perda mineral e aumento da resistência ácida do esmalte adjacente as restaurações após desafio ácido, com importante potencial em prevenir lesões de cárie secundária. / The aim of this study was to evaluate the enamel calcium loss around cavities prepared by Er,Cr:YSGG laser and restored with different materials after an acid challenge. One hundred and twenty enamel samples obtained from third molars (4 x 4 mm) were randomly divided in 12 groups (n=10) using different techniques: G1- high-speed drill (HD); G2- Er,Cr:YSGG laser (3W, 20Hz, 53.05 J/cm2)(air 65% - water 55%); G3- Er,Cr:YSGG laser (4 W, 20 Hz, 70.74 J/cm2); G4- Er,Cr:YSGG laser (5 W, 20 Hz, 88.43 J/cm2). Each experimental group was divided in subgroups, according to the restorative material: 1 - glass ionomer cement (GIC), 2 - resin modified GIC (RMGIC), 3 - adhesive system and composite resin (C). Samples were submitted to an acid challenge (4.8 pH) for 7 days. The Demineralizing solutions were analyzed in relation to the calcium ion contend (ppm/mm2), in different times (1, 3 and 7 days), under atomic emission spectrometry. ANOVA and LSD tests were performed (?=5%). There were significant difference between Technique and Restorative Material on Total Time. The lower average values of calcium loss were observed on G2 + GIC, G2 + RMGIC, G1 + RMGIC groups; the higher values were observed on G1 + C, G4 +GIC, G4 + C. The composite resin showed higher calcium loss than RMGIC and GIC. The lased cavities using lower fluence (53.05J/cm2) showed significant reduced demineralization than higher fluences (70.74 and 88.43J/cm2). Neither the techniques nor the restorative materials used were able to prevent the enamel demineralization. The findings of this in vitro study suggest that the Er,Cr:YSGG lased cavities (53.05J/cm2) restored with GIC or RMGIC or conventional drill cavities with RMGIC were effective on reducing the mineral loss and enhancing the enamel acid resistant around restorations after the acid challenge, showing an important potential in preventing secondary caries.