Magister Chirurgiae Dentium (MChD) / Background: Lack of appropriate bone thickness is a common clinical limitation for tooth replacement, often requiring narrow implants, which have shown better results when combined with Morse taper connections. Little is known about the sealing of the abutment-implant interface of narrow implants with Morse taper connections against oral bacteria. Aims: To investigate the in vitro ability of four commercially available narrow diameter implant (< 3.5 mm) with Morse-taper type implant abutment connections to impede bacterial penetration of their implant abutment interface (IAI). Material and Methods: Four commercially available narrow implant systems with Morse taper connections were subjected to Streptococcus sanguinis cultures in vitro and evaluated for contamination and microgaps through Scanning Electron Microscopy (SEM). Results: Bacterial penetration of the IAI was observed in all systems (n=12), ranging from 65 to >300 CFU. There were no statistically significant differences in the average log CFU between the four implant groups (χ2= 5.244, P=0.155). Microgaps ranging from 5-10 μm were observed in all assemblies when analyzed under SEM, with no statistically significant differences between the different systems (P>0.05). Conclusions: Despite the advantages of Morse taper systems, the evaluated narrow diameter implants using this type of abutment geometry failed to provide bacterial sealing. The observed microgaps can form reservoirs and potentially lead to inflammation in the peri-implant tissues and micromovements.

Os implantes cone morse apresentam um travamento e vedamento por meio de atrito entre as paredes do implante e do pilar protético. Nos sistemas convencionais do tipo Hexágono externo e interno, para reduzir o afrouxamento dos parafusos protéticos, são utilizados materiais de cobertura de superfície, como carbono e ouro. Não foram encontradas referências na literatura da utilização desse tipo de deposição em componentes do sistema cone morse. O propósito desse estudo é mensurar, registrar e avaliar os valores do torque de desaperto em pilares protéticos dos tipos sólido e parafuso passante do sistema cone morse com a deposição de carbono na zona de atrito do pilar protético. Foram utilizados 40 implantes cone morse com seus respectivos pilares divididos em 4 grupos (n=10): G1- pilar sólido; G2- pilar sólido com deposição de carbono na zona de atrito do sistema morse; G3- estudo somente do parafuso do pilar passante; G4- estudo somente do parafuso do pilar passante com deposição de carbono na ponta ativa; G5- estudo somente do pilar passante sem ação do parafuso; G6- estudo somente do pilar passante revestido em carbono na zona de atrito do sistema morse sem ação do parafuso. Cada pilar recebeu uma seqüência de 5 apertos e desapertos (20Ncm para o pilar sólido e 10Ncm para o parafuso passante). Os resultados mostraram no teste estatístico ANOVA para dois fatores de variação (desaperto e carbono), haver diferença estatística significante entre os grupos: G1 maior que G2 (p < 0,01); G4 maior que G3 (p < 0,01); G6 maior que G5 (p < 0,01). Esse estudo concluiu que o grupo controle G1 mostrou maior valor através da media aritmética (23,706 Ncm) em relação ao grupo experimental G2 (22,114 Ncm); o grupo experimental G4 mostrou maior valor através da media aritmética (8,218 Ncm) em relação ao grupo controle G3 (7,354 Ncm) e o grupo experimental G6 mostrou maior valor através da media aritmética (10,268 Ncm) em relação ao grupo controle G5 (6,906 Ncm), mostrou também que não houve diferença significativa (p > 0,01) para o fator desaperto em todos os grupos estudados, ou seja, não houve interferência da deformação do material com a repetição dos ciclos de aperto e desaperto. / The morse taper implants present a locking and sealing by means of the attrition between implants internal walls and the abutment. In the external and internal conventional hexagon system, to reduce the prosthetic screw loosing, its used covering surface materials, as carbon and gold. Literature reference using these kind of surface deposition were not found in morse taper abutment implants. The aim of this study is to measure, register and evaluate the removal torque values in morse taper solid abutment and passing screw abutment with carbon deposition in attrition zone. They were used 40 morse taper implants with their respective abutments divided in 4 groups (n = 10): G1 solid abutment; G2 - solid abutment with carbon deposition in attrition zone; G3 evaluation only in the screw of the passing abutment; G4 - evaluation only in the screw of the passing abutment with carbon deposition in the screw thread; G5 - evaluation only in the passing abutment without the screw action; G6 - evaluation only in the passing abutment with carbon deposition in attrition zone without the screw action. Each abutment received a sequence of 5 tightening and removal torque (20Ncm in solid abutment and 10Ncm in passant screw abutment). The results of ANOVA statistic test for two factors of variation (removal torque and carbon), showed that there is significant statistic difference between the groups: G1 higher than G2 (p < 0.01); G4 higher than G3 (p < 0.01); G6 higher than G5 (p < 0.01). This study concluded that control group G1 showed a higher value through the arithmetical media (23.706Ncm) in relation of the experimental group G2 (22.114Ncm); the experimental group G4 showed higher value through the arithmetical media (8.218Ncm) in relation of the control group G3 (7.354Ncm) and the experimental group G6 showed higher values through the arithmetical media (10.268Ncm) in relation of the control group G5 (6.906Ncm), and also showed that there was not significant difference (p < 0.01) to the removal torque factor in all the groups studied, that is, there was not a material deformation interference with the tightening and removal torque cycles repetition.

Os implantes cone morse apresentam um travamento e vedamento por meio de atrito entre as paredes do implante e do pilar protético. Nos sistemas convencionais do tipo Hexágono externo e interno, para reduzir o afrouxamento dos parafusos protéticos, são utilizados materiais de cobertura de superfície, como carbono e ouro. Não foram encontradas referências na literatura da utilização desse tipo de deposição em componentes do sistema cone morse. O propósito desse estudo é mensurar, registrar e avaliar os valores do torque de desaperto em pilares protéticos dos tipos sólido e parafuso passante do sistema cone morse com a deposição de carbono na zona de atrito do pilar protético. Foram utilizados 40 implantes cone morse com seus respectivos pilares divididos em 4 grupos (n=10): G1- pilar sólido; G2- pilar sólido com deposição de carbono na zona de atrito do sistema morse; G3- estudo somente do parafuso do pilar passante; G4- estudo somente do parafuso do pilar passante com deposição de carbono na ponta ativa; G5- estudo somente do pilar passante sem ação do parafuso; G6- estudo somente do pilar passante revestido em carbono na zona de atrito do sistema morse sem ação do parafuso. Cada pilar recebeu uma seqüência de 5 apertos e desapertos (20Ncm para o pilar sólido e 10Ncm para o parafuso passante). Os resultados mostraram no teste estatístico ANOVA para dois fatores de variação (desaperto e carbono), haver diferença estatística significante entre os grupos: G1 maior que G2 (p < 0,01); G4 maior que G3 (p < 0,01); G6 maior que G5 (p < 0,01). Esse estudo concluiu que o grupo controle G1 mostrou maior valor através da media aritmética (23,706 Ncm) em relação ao grupo experimental G2 (22,114 Ncm); o grupo experimental G4 mostrou maior valor através da media aritmética (8,218 Ncm) em relação ao grupo controle G3 (7,354 Ncm) e o grupo experimental G6 mostrou maior valor através da media aritmética (10,268 Ncm) em relação ao grupo controle G5 (6,906 Ncm), mostrou também que não houve diferença significativa (p > 0,01) para o fator desaperto em todos os grupos estudados, ou seja, não houve interferência da deformação do material com a repetição dos ciclos de aperto e desaperto. / The morse taper implants present a locking and sealing by means of the attrition between implants internal walls and the abutment. In the external and internal conventional hexagon system, to reduce the prosthetic screw loosing, its used covering surface materials, as carbon and gold. Literature reference using these kind of surface deposition were not found in morse taper abutment implants. The aim of this study is to measure, register and evaluate the removal torque values in morse taper solid abutment and passing screw abutment with carbon deposition in attrition zone. They were used 40 morse taper implants with their respective abutments divided in 4 groups (n = 10): G1 solid abutment; G2 - solid abutment with carbon deposition in attrition zone; G3 evaluation only in the screw of the passing abutment; G4 - evaluation only in the screw of the passing abutment with carbon deposition in the screw thread; G5 - evaluation only in the passing abutment without the screw action; G6 - evaluation only in the passing abutment with carbon deposition in attrition zone without the screw action. Each abutment received a sequence of 5 tightening and removal torque (20Ncm in solid abutment and 10Ncm in passant screw abutment). The results of ANOVA statistic test for two factors of variation (removal torque and carbon), showed that there is significant statistic difference between the groups: G1 higher than G2 (p < 0.01); G4 higher than G3 (p < 0.01); G6 higher than G5 (p < 0.01). This study concluded that control group G1 showed a higher value through the arithmetical media (23.706Ncm) in relation of the experimental group G2 (22.114Ncm); the experimental group G4 showed higher value through the arithmetical media (8.218Ncm) in relation of the control group G3 (7.354Ncm) and the experimental group G6 showed higher values through the arithmetical media (10.268Ncm) in relation of the control group G5 (6.906Ncm), and also showed that there was not significant difference (p < 0.01) to the removal torque factor in all the groups studied, that is, there was not a material deformation interference with the tightening and removal torque cycles repetition.

Na implantodontia visa-se dois grandes resultados para os desdentados parciais e totais, função mastigatória e estética. Ambos têm o mesmo grau de importância, para tanto se deve pensar no que se tem de mais seguro e prático nos dias de hoje. O cone Morse, na implantodontia oral, é um sistema de estabilidade entre o implante dentário e o parafuso intraósseo de sustentação. Para seu correto uso se faz necessário uma série de análise de suas características e condições. No presente trabalho focou-se em desenvolver protocolo de validação de torque, além de analisar parâmetros de acabamento, deformação e estabilidade précarga e pós-carga dentro de protocolos já recomendados. Avaliou-se sua condição antes e após os efeitos de carga mastigatória simulada por ensaio de fadiga. Concluiu-se que o uso do cone Morse dentro dos protocolos indicados deve ser revisto quanto a padrões similares de torque nos pilares sólidos e indexados, cada um possui limites e indicações diferentes para se manter estável. Concluiu-se também que não é um sistema totalmente livre de trânsito de bactérias e que esse trânsito aumenta de forma proporcional ao uso e força mastigatória, indicando que melhorias no acabamento entre as peças devem ser implementadas e/ou adição de material que afaste crescimento bacteriano priorizando a saúde do periodonto e do tecido ósseo de sustentação mantendo o sistema seguro em longevidade. / In implantology it is aimed two major outcomes for the partial and total toothless persons, mastigatory function and aesthetics. Both have the same degree of importance, therefore it must be thought about what is safer and more practical these days. Morse taper in oral implantology is a system of stability between the dental implant and the intraosseous screw support. For its correct use a series of analysis of its features and conditions is required. This work was focused on developing torque validation protocol, and analyzing surface finishing parameters, deformation and stability as before load and after load in recommended protocols. The implants condition before and after the effects of habitual masticatory load was simulated by fatigue testing. It was concluded that the Morse taper use within the specified protocols should be reviewed for similar patterns of torque in solids and indexed pillars, each has different limits and signs to remain stable. It was also concluded that it is not a traffic totally free system of bacteria and that this influence increases in proportion to the use and masticatory forces, improvements in the surface finish between parts and / or addition of material that hinders bacterial growth is needed if it is prioritized the health of the periodontium and the bone tissue keeping the system safe in the long therm.

Problemas com desenho de conexões protéticas sobre implantes, microfendas, afrouxamento e, consequentemente, perdas das estruturas protéticas reabilitadoras são tópicos frequentes do estudo odontológico. Conexões do tipo Cone Morse, devido às suas características, diminuíram o índice desses problemas, abrindo uma nova perspectiva para o sucesso da prótese sobre implante. Contudo, ainda é frequente encontrar componentes que falham no desempenho, levando à falência da restauração, especialmente quando esses componentes não são bem ajustados, bem fixados ou, ainda, não possuem, na sua geometria, características suficientes para suportar as forças laterais e oclusais de um ciclo mastigatório. O objetivo deste estudo é avaliar a influência do jateamento com óxido de alumínio sobre a superfície externa dos componentes protéticos, separadamente e em conjunto, com um adesivo industrial, em uma tentativa de aumentar os valores de torque de abertura de componentes apertados em seu torque recomendado, pelo fabricante ou menor. Neste ensaio, foram utilizados 36 implantes da marca Straumann®, de 10mm de comprimento com diâmetro de 4,8 mm, os quais foram divididos em 6 grupos: Grupo 1 = controle, torque de 35 N.cm; Grupo 2 = superfície jateada com óxido de alumínio (# 320) e torque de 35 N.cm; Grupo 3 = superfície jateada com óxido de alumínio (# 320) e torque de 25 N.cm; Grupo 4 = superfície jateada com óxido de alumínio (# 100) e torque de 25 N.cm; Grupo 5 = superfície jateada com óxido de alumínio (# 320), aplicação de adesivo e torque de 25 N.cm; Grupo 6 = superfície jateada com óxido de alumínio (# 100), aplicação de adesivo e torque de 25 N.cm, que receberam componentes protéticos sólidos de 5,5 mm de altura, regulares e alterados. As modificações incluídas foram o jateamento com partículas de óxido de alumínio (100 e 320 micra) e o uso de Loctite® 277 como adesivo industrial. Os conjuntos implante-componente foram levados até uma máquina de controle de tração, Instron®, e, após a sua calibração, as amostras dos grupos foram apertadas em 35 e 25 N.cm, com um conjunto catraca-torquímetro, com checagem visual e registro no software acoplado à máquina de ensaio. Após trinta dias, os grupos foram levados à máquina novamente e o conjunto abutment-implante foi desapertado, agora somente com registro no software da máquina de ensaio. Os valores e porcentagens da diferença entre torque de aperto e desaperto foram avaliados estatisticamente, e comparados entre os grupos. Para todas as associações, o valor de p deveria ser menor ou igual 0,05, para relevância. O grupo Jateado 35 N.cm, 320 micra, não apresentou valores mais altos do que o grupo Controle no momento do torque de desaperto, assim como os grupos Jateados 25 N.cm 100 e 320 micra. Os grupos Jateados 25 N.cm, 100 e 320 micra, com adesivo, mostraram uma resistência por volta de uma vez e meia maior, no torque de desaperto do que o grupo Controle 35 N.cm. / Problems with design of prosthetic implant connections, microleakage,! loosening which leads to loss of rehabilitative prosthetic structures are frequent topics of dental study. Morse taper connections, due to its characteristics, decreased the rate of these problems opening a new perspective to the success of the prosthesis supported over implant. However, it is still frequent to find components that fail in performance leading to failure of restoration especially when these components are not well adjusted, tightened or do not have in its geometry enough characteristics to support the occlusal and lateral forces in a masticatory cycle. The aim of this study is to evaluate the influence of blasting with aluminum oxide on the outer surface of the prosthetic components separately and in conjunction with an industrial adhesive in an attempt to increase the opening torque values of components tightened on their recommended torque by the manufacturer or less, therefore allowing the dentist an early intervention in the prosthetic rehabilitation. In this test, 36 Straumann® implants of 10mm high and 4,8mm wide were used. They were divided into six groups: Group 1 Solid abutments control group - 35 N.cm tightened; Group 2 - Solid sandblasted abutments, 35 N.cm aluminum oxide 320 microns size particles; Group 3 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles; Group 4 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles; Group 5 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles with glue application; Group 6 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles with glue application, which received 5,5 mm high regular and modified solid abutments. The included modifications were sandblasting with aluminum oxide particles (100 and 320 microns) and the use of Loctite® 277 as an industrial adhesive. The samples were taken to a traction control test machine, Instron ®, and after calibration the group samples were tightened on 35 and 25 N.cm with a ratchet-wrench set with visual check. The data was recorded in a software coupled to the test machine. After thirty days the groups were brought again to the test machine and the samples were untightened. At this point the resulting data was recorded only in the testing machine software. The values and percentages of the changes between the tightening and loosening torques were recorded and compared among the study groups. For all associations a p-value < 0.05 was considered significant. The group blasted 35 N.cm, 320 microns did not show higher values than the control group at the time of loosening torque as well as groups blasted 25 N.cm 100 and 320 microns. The groups blasted 25 N.cm, 100 and 320 microns with adhesive showed a resistance around one and a half times greater in the loosening torque than the control group 35 N.cm.

Na implantodontia visa-se dois grandes resultados para os desdentados parciais e totais, função mastigatória e estética. Ambos têm o mesmo grau de importância, para tanto se deve pensar no que se tem de mais seguro e prático nos dias de hoje. O cone Morse, na implantodontia oral, é um sistema de estabilidade entre o implante dentário e o parafuso intraósseo de sustentação. Para seu correto uso se faz necessário uma série de análise de suas características e condições. No presente trabalho focou-se em desenvolver protocolo de validação de torque, além de analisar parâmetros de acabamento, deformação e estabilidade précarga e pós-carga dentro de protocolos já recomendados. Avaliou-se sua condição antes e após os efeitos de carga mastigatória simulada por ensaio de fadiga. Concluiu-se que o uso do cone Morse dentro dos protocolos indicados deve ser revisto quanto a padrões similares de torque nos pilares sólidos e indexados, cada um possui limites e indicações diferentes para se manter estável. Concluiu-se também que não é um sistema totalmente livre de trânsito de bactérias e que esse trânsito aumenta de forma proporcional ao uso e força mastigatória, indicando que melhorias no acabamento entre as peças devem ser implementadas e/ou adição de material que afaste crescimento bacteriano priorizando a saúde do periodonto e do tecido ósseo de sustentação mantendo o sistema seguro em longevidade. / In implantology it is aimed two major outcomes for the partial and total toothless persons, mastigatory function and aesthetics. Both have the same degree of importance, therefore it must be thought about what is safer and more practical these days. Morse taper in oral implantology is a system of stability between the dental implant and the intraosseous screw support. For its correct use a series of analysis of its features and conditions is required. This work was focused on developing torque validation protocol, and analyzing surface finishing parameters, deformation and stability as before load and after load in recommended protocols. The implants condition before and after the effects of habitual masticatory load was simulated by fatigue testing. It was concluded that the Morse taper use within the specified protocols should be reviewed for similar patterns of torque in solids and indexed pillars, each has different limits and signs to remain stable. It was also concluded that it is not a traffic totally free system of bacteria and that this influence increases in proportion to the use and masticatory forces, improvements in the surface finish between parts and / or addition of material that hinders bacterial growth is needed if it is prioritized the health of the periodontium and the bone tissue keeping the system safe in the long therm.

In this master thesis the connection between the two major parts of an osseointegrated prosthesis system for lower limb amputees has been investigated by finite element (FE) analysis. The prosthesis system is developed by Integrum and the current design consists of a fixture, which is integrated in the residual bone, an abutment that penetrates the skin and an abutment screw that holds the parts together. The connection between the fixture and the abutment has a hexagonal section and a press-fit section that together form the connection. Due to wear and fracture problems it is desired to improve the connection. A tapered connection could be an alternative and three different taper angles, the effect of the length of the taper and the smoothness of the outer edge of a tapered fixture have been investigated. The results show that the taper has potential to function well and that a longer connection will give lower stresses in the system, but further investigations are needed.

Problemas com desenho de conexões protéticas sobre implantes, microfendas, afrouxamento e, consequentemente, perdas das estruturas protéticas reabilitadoras são tópicos frequentes do estudo odontológico. Conexões do tipo Cone Morse, devido às suas características, diminuíram o índice desses problemas, abrindo uma nova perspectiva para o sucesso da prótese sobre implante. Contudo, ainda é frequente encontrar componentes que falham no desempenho, levando à falência da restauração, especialmente quando esses componentes não são bem ajustados, bem fixados ou, ainda, não possuem, na sua geometria, características suficientes para suportar as forças laterais e oclusais de um ciclo mastigatório. O objetivo deste estudo é avaliar a influência do jateamento com óxido de alumínio sobre a superfície externa dos componentes protéticos, separadamente e em conjunto, com um adesivo industrial, em uma tentativa de aumentar os valores de torque de abertura de componentes apertados em seu torque recomendado, pelo fabricante ou menor. Neste ensaio, foram utilizados 36 implantes da marca Straumann®, de 10mm de comprimento com diâmetro de 4,8 mm, os quais foram divididos em 6 grupos: Grupo 1 = controle, torque de 35 N.cm; Grupo 2 = superfície jateada com óxido de alumínio (# 320) e torque de 35 N.cm; Grupo 3 = superfície jateada com óxido de alumínio (# 320) e torque de 25 N.cm; Grupo 4 = superfície jateada com óxido de alumínio (# 100) e torque de 25 N.cm; Grupo 5 = superfície jateada com óxido de alumínio (# 320), aplicação de adesivo e torque de 25 N.cm; Grupo 6 = superfície jateada com óxido de alumínio (# 100), aplicação de adesivo e torque de 25 N.cm, que receberam componentes protéticos sólidos de 5,5 mm de altura, regulares e alterados. As modificações incluídas foram o jateamento com partículas de óxido de alumínio (100 e 320 micra) e o uso de Loctite® 277 como adesivo industrial. Os conjuntos implante-componente foram levados até uma máquina de controle de tração, Instron®, e, após a sua calibração, as amostras dos grupos foram apertadas em 35 e 25 N.cm, com um conjunto catraca-torquímetro, com checagem visual e registro no software acoplado à máquina de ensaio. Após trinta dias, os grupos foram levados à máquina novamente e o conjunto abutment-implante foi desapertado, agora somente com registro no software da máquina de ensaio. Os valores e porcentagens da diferença entre torque de aperto e desaperto foram avaliados estatisticamente, e comparados entre os grupos. Para todas as associações, o valor de p deveria ser menor ou igual 0,05, para relevância. O grupo Jateado 35 N.cm, 320 micra, não apresentou valores mais altos do que o grupo Controle no momento do torque de desaperto, assim como os grupos Jateados 25 N.cm 100 e 320 micra. Os grupos Jateados 25 N.cm, 100 e 320 micra, com adesivo, mostraram uma resistência por volta de uma vez e meia maior, no torque de desaperto do que o grupo Controle 35 N.cm. / Problems with design of prosthetic implant connections, microleakage,! loosening which leads to loss of rehabilitative prosthetic structures are frequent topics of dental study. Morse taper connections, due to its characteristics, decreased the rate of these problems opening a new perspective to the success of the prosthesis supported over implant. However, it is still frequent to find components that fail in performance leading to failure of restoration especially when these components are not well adjusted, tightened or do not have in its geometry enough characteristics to support the occlusal and lateral forces in a masticatory cycle. The aim of this study is to evaluate the influence of blasting with aluminum oxide on the outer surface of the prosthetic components separately and in conjunction with an industrial adhesive in an attempt to increase the opening torque values of components tightened on their recommended torque by the manufacturer or less, therefore allowing the dentist an early intervention in the prosthetic rehabilitation. In this test, 36 Straumann® implants of 10mm high and 4,8mm wide were used. They were divided into six groups: Group 1 Solid abutments control group - 35 N.cm tightened; Group 2 - Solid sandblasted abutments, 35 N.cm aluminum oxide 320 microns size particles; Group 3 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles; Group 4 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles; Group 5 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles with glue application; Group 6 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles with glue application, which received 5,5 mm high regular and modified solid abutments. The included modifications were sandblasting with aluminum oxide particles (100 and 320 microns) and the use of Loctite® 277 as an industrial adhesive. The samples were taken to a traction control test machine, Instron ®, and after calibration the group samples were tightened on 35 and 25 N.cm with a ratchet-wrench set with visual check. The data was recorded in a software coupled to the test machine. After thirty days the groups were brought again to the test machine and the samples were untightened. At this point the resulting data was recorded only in the testing machine software. The values and percentages of the changes between the tightening and loosening torques were recorded and compared among the study groups. For all associations a p-value < 0.05 was considered significant. The group blasted 35 N.cm, 320 microns did not show higher values than the control group at the time of loosening torque as well as groups blasted 25 N.cm 100 and 320 microns. The groups blasted 25 N.cm, 100 and 320 microns with adhesive showed a resistance around one and a half times greater in the loosening torque than the control group 35 N.cm.

Magister Scientiae Dentium - MSc(Dent) / Background: The two-stage implant system has proven to be a successful technique in replacing missing teeth (Nascimento et al., 2008). Nevertheless, the presence of micro-gaps that could entrap microbes at the implant-abutment interface (IAI) is unavoidable. This microbial leakage has been considered as one of the causes of peri-implant infection and bone loss (Scarano et al., 2005). Several companies have attempted to manufacture an implant with a connection design that provides hermetic sealing against bacterial leakage. Studies indicated that implants with internal connection, in particular the conical (Morse taper) design, have better sealing capacity in the implant abutment interface than the external design (Koutouzis et al., 2011, Jaworski et al., 2012). An internal conical implant system with a novel connection design, known as the Grand Morse (GM) connection, is reported to offer secure connection against micro-leakage (Neodent® Implant Systems Inc., 2018). Aims: The aim of this study was to test the sealing ability against bacterial leakage in the implant-abutment interface provided by an implant with a novel deep internal conical (GM) connection design.

Cargas oclusais excessivas podem promover tensões exageradas às estruturas de implantes/pilares/próteses, resultando em deformação, desadaptação ou mesmo fratura dos componentes e do próprio implante. Além disso, tais sobrecargas podem gerar necrose por compressão e perda óssea peri-implantar e, ainda, a ocorrência de microdeslocamentos na interface de conexão implante-pilar (I-P) ocasionando a formação de fendas propícias à colonização bacteriana, o que pode levar ao desenvolvimento de peri-implantite, contribuindo para o insucesso do conjunto. O presente estudo objetivou avaliar, por meio de uma técnica já amplamente utilizada na Engenharia e na Física a Interferometria Eletrônica por Padrões de Speckle (ESPI) as deformações a nível do colar de implantes com conexão cônica interna (cone Morse) de diferentes diâmetros (Kopp 4,3/5,5 mm e Neodent 3,5/5,0 mm), sob dois tipos (cêntrica e excêntrica) e intensidades (50 N e 100 N) de cargas, similares as quais os implantes ficam expostos durante a função mastigatória. Testou-se a hipótese de que a deformação do colar do implante seria inversamente proporcional ao diâmetro do implante. Além disso, discutiu-se vantagens e limitações da técnica ESPI frente a outros métodos comumente utilizados na avaliação de tensões. As maiores deformações foram sempre associadas às cargas excêntricas, com exceção do G1-Kopp. A maior deformação ocorreu no G1-Neodent sob carga excêntrica de 100 N e a menor, no G2-Neodent sob carga cêntrica de 50 N. A técnica ESPI mostrou-se altamente sensível e reprodutível para avaliar deformações a nivel do colar de implantes sendo possível confirmar a hipótese inicial, visto que a maior deformação esteve sempre associada aos implantes de menor diâmetro, em ambos os sistemas de implante pesquisados. / Occlusal overloading may promote excessive stresses to the implants/abutments/prosthesis, resulting in deformation, misfit or fracture of the components, until the implants. Futhermore, strains of the implant-abutment connection can cause the formation of microgaps propitious to bacterial colonization, which leads to the development of peri-implant sites, leading to the failure of the rehabilitation. This study aimed to evaluate, by a technique widely used in the engineering and physics Electronic Speckle Pattern Interferometry (ESPI) the strains related to the implant collar with internal tappered connection (Morse taper) with different diameters (Kopp 4.3/5.5 mm and Neodent 3,5/5,0 mm), under two types (centric and eccentric) and intensities (50 N and 100 N) of loads, similar which implants are exposed during masticatory function. We tested the hypothesis that the strains of the implants collar would be inversely proportional to the diameter of the implant. In addition, the survey discussed the advantages and limitations of the ESPI technique over other methods commonly used to assess strains. The largest strain was always associated with eccentric loads, except for G1-Kopp. The largest strain occurred in the G1-Neodent under the eccentric loads of 100 N and the lowest in the G2-Neodent under the centric loads of 50 N. The ESPI technique was a highly sensitive and reproducible to evaluate the strains at the level of the collar of implants being possible to confirm the initial hypothesis, since most strains was always associated with narrower-diameter implants in both implant systems studied.