Made available in DSpace on 2014-10-09T12:31:38Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:01:05Z (GMT). No. of bitstreams: 1 02286.pdf: 3044750 bytes, checksum: 753f2e5a876a0a848f90cf7bcb06b0e5 (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

The aim of this study was to investigate rubber toughening of resol type phenol-formaldehyde resin. For this purpose, phenolic resin was first modified by only acrylonitrile butadiene rubber, and then by using nitrile rubber together with 3-aminopropyltriethoxysilane. Test specimens were prepared by mixing and casting of liquid phenolic resin in three groups. In the first one, neat phenolic resin specimens were produced. In the second group, phenolic resin was modified with 0.5, 1, 2, and 3 wt.% nitrile rubber, while in the last group modification was carried out by using 0.5 wt.% nitrile rubber together with 1, 2, and 4wt.% amino silane (with respect to nitrile rubber). All specimens were heat cured in the oven. In order to observe behaviors of the specimens, Three-Point Bending, Charpy Impact, Plane-Strain Fracture Toughness, and Dynamic Mechanical Analysis tests were conducted according to the related ISO standards for all specimens groups. Scanning Electron Microscopy was also used for the fractographic analysis of some samples. It can be concluded that, although there were problems in mixing and casting of liquid resol type phenolic resin, its toughness could be improved by using nitrile rubber and amino silane. Modification by using nitrile rubber and amino silane together was much more effective than by using only nitrile rubber. In this synergistic case for instance, Charpy impact strength and fracture toughness values of the neat phenolic specimens were increased 63% and 50%, respectively. SEM studies indicated that the main rubber toughening mechanism was shear yielding observed as deformation lines especially initiated at the domains of nitrile rubber and amino silane.

Made available in DSpace on 2014-10-09T12:41:41Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:07:06Z (GMT). No. of bitstreams: 0 / Dissertação (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:41:41Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:07:06Z (GMT). No. of bitstreams: 0 / Com a aprovação da Política Nacional de Resíduos Sólidos, a política de sustentabilidade tende ao reaproveitamento de resíduos, em seu ciclo ou destinação final ambientalmente adequada. Neste contexto, são apresentados neste trabalho, estudos do processo de separação de materiais metálicos e não metálicos encontrados em placas de circuito impresso de microcomputadores e a caracterização dos elementos químicos presentes. Para isto efetuou-se a trituração primária (moagem) das placas de circuito impresso, classificação granulométrica, separação de elementos metálicos e não metálicos utilizando separadores, magnético e eletrostático, separação gravimétrica com o uso de clorofórmio e bromofórmio. Para caracterização dos elementos metálicos e não metálicos, foram utilizadas as técnicas de Espectrometria de fluorescência de Raios X e Espectrometria de infravermelho. Os separadores eletrostático e eletromagnético não foram efetivos na separação de placas de circuito impresso para granulometrias inferiores a 9 Mesh. A separação dos elementos metálicos e não metálicos das amostras com granulometrias inferiores a 9 Mesh, teve eficiência parcial utilizando o clorofórmio, mas mostrou-se efetiva com a utilização do bromofórmio. Embora a separação gravimétrica, não tenha sido efetiva, as amostras foram caracterizadas. Para obter uma melhor separação dos elementos presentes na amostra de não metálicos, procedeu-se a trituração secundária (moagem) desta amostra, resultando na desagregação e separação efetiva. / Dissertação (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP