Dissertação (mestrado)—Universidade de Brasília, Instituto de Química, 2015. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2016-05-16T15:31:15Z No. of bitstreams: 1 2015_DanielAndradeMoreira.pdf: 5936294 bytes, checksum: b47ddee8b1d7d84f7efbd5f3de0d31e3 (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2016-07-21T18:34:08Z (GMT) No. of bitstreams: 1 2015_DanielAndradeMoreira.pdf: 5936294 bytes, checksum: b47ddee8b1d7d84f7efbd5f3de0d31e3 (MD5) / Made available in DSpace on 2016-07-21T18:34:08Z (GMT). No. of bitstreams: 1 2015_DanielAndradeMoreira.pdf: 5936294 bytes, checksum: b47ddee8b1d7d84f7efbd5f3de0d31e3 (MD5) / Este trabalho baseia-se na síntese e caracterização de compósitos a partir de nanocristais de NaYF4:Eu ou NaYF4:Tb e nanopartículas de carbono conhecidas como carbon-dots ou carbon-nanodots, também chamados de C-Dots, afim de desenvolver e estudar novos materiais luminescentes. Os compósitos são sintetizados por dois métodos, via coprecipitação, onde foram obtidos materiais nanométricos com diâmetros a partir de 25 nm, com baixa cristalinidade, tempos de vida próximos de 1 ms e rendimentos quânticos abaixo de 1%, para a via hidrotermal, foram obtidos compósitos micrométricos com diâmetro a a partir de 300 nm, cristais de fase hexagonal tempos de vida próximos a 1 ms e rendimentos quânticos abaixo de 1%, os compósitos coprecipitados apresentaram luminescência superior aos tratados hidrotermalmente. Houve variação de concentração de C-Dots nas sínteses, visando morfologias e tamanhos distintos e a relação destes com as propriedades luminescentes do material, maiores concentrações de C-Dots indicaram maior agregação dos compósitos, baixa intensidade luminescente e menores tempos de vida, baixas concentrações geraram compósitos dispersos, com intensidade luminescente e tempos de vida superiores as demais concentrações. / This work is about the synthesis and characterization of composites from nanocrystals of NaYF4:Eu or NaYF4:Tb and nanoparticles of carbon, known as carbon-dot or carbon-nanodots, also called of C-Dots to develop and study new luminescent materials. The composites are sintherized by two differents methods co-precipitation and hydrothermal. Using co-precipitation the materials obtained are nanomerics, with diameter from 25 nm, They have low crystallinity and lifetime next to 1 ms and quantum yeld bellow 1%. Using the hydrothermal method the materials obtained are micrometric composites of hexagonal phase, with diameter from 300 nm, lifetime next to 1 ms and quantum yeld bellow 1%. The co-precipitates composts shows more luminescence than hydrothermal composts. To obtained sizes and differents morphologies and to determine the relation of this and the luminescence properties the concentration of C-Dots in the sinthezys had been varied. Higher concentrations of C-Dots indicates greater aggregation of composites, low luminescent intensity, shorter lifetime and low concentration produced dispersed composites, with intense luminescence and higher lifetime than with others concentration.

Materiais auto-organizados constituídos de V2O5 xerogel, poli(etilenoimina) (PEI) e nanopartículas de carbono (NpCs) foram obtidos por meio da técnica camada-por-camada (LbL). A metodologia aplicada permitiu a obtenção de filmes finos com elevado controle de espessura além de permitir um crescimento linear dos filmes, denominados neste trabalho V2O5/PEI e V2O5/PEI/NpCs. Além disso, o desempenho eletroquímico dos materiais auto-organizados foi comparado a um eletrodo de V2O5. Análises de FTIR mostraram que interações específicas entre os grupos amina do PEI e os grupos carboxila do V2O5 são responsáveis pelo crescimento do filme. Estas interações permitem a formação de um campo eletrostático capaz de blindar as interações entre os íons lítio e os oxigênios da vanadila (V=O) e, por consequência, são responsáveis pelo aumento na mobilidade iônica dos íons lítio no interior da matriz hospedeira e, portanto, um aumento na capacidade de armazenamento de carga. Resultados obtidos através de medidas de carga/descarga mostram que o V2O5/PEI/NpCs apresenta uma melhor desempenho do que os demais materiais estudados neste trabalho. Estes resultados mostram que a capacidade específica do V2O5/PEI/NpCs foi de 137 mA h g-1 para a menor densidade de corrente aplicada e aproximadamente 1,6 vezes maior do que os valores de capacidade específica para os outros materiais para a maior densidade de corrente aplicada. Além disso, estas medidas permitiram a observação de uma menor variação na razão estequiométrica máxima (xmáx) em função das densidades de corrente aplicadas para os filmes auto-organizados, fato este relacionado a uma maior mobilidade iônica dos íons lítio no interior dessas matrizes. Os resultados obtidos a partir de espectroscopia de impedância eletroquímica (EIS) mostraram que a difusão dos íons lítio no interior das matrizes auto-organizadas é maior do que no caso do V2O5, cujos valores do coeficiente de difusão foram de 1,64 x 10-15, 1,21 x 10-14 e 2,26 x 10-14 cm2 s-1 para os filmes V2O5, V2O5/PEI e V2O5/PEI/NpCs, respectivamente. Sendo assim, o polímero e as NpCs promoveram novos caminhos condutores e permitiram a conexão elétrica entre camadas isoladas da matriz V2O5. Dessa forma, novos nanocompósitos foram obtidos visando demonstrar o método de auto-organização empregado para melhorar o transporte de carga em matrizes hospedeiras. / Self-assembled materials constituted of V2O5 xerogel, poly (ethyleneimine) (PEI), and carbon nanoparticles (CNPs) were obtained by the layer-by-layer (LbL) technique. The applied methodology permitted the obtainment of thin films with high thickness control and also permitted a linear growth of the films, which will be named V2O5/PEI and V2O5/PEI/CNPs. Besides, the electrochemical performance of the self-assembled materials was compared to a V2O5 electrode. FTIR analyses showed that the specific interactions between the amine groups of PEI and the vanadyl groups of the V2O5 are responsible for the film growth. These interactions permitted the formation of an electrostatic shield capable of hindering the interactions between the lithium ions and the vanadyl oxygen atoms (V=O) and are consequently responsible for the enhancement on the ionic mobility of the lithium ions within the host matrix, leading to a higher energy storage capability. Results obtained by the charge/discharge measurements showed that V2O5/PEI/CNPs presents a better performance than the other materials studied for this research. These results demonstrated that the specific capacity of the V2O5/PEI/CNPs was 137 mA h g-1 under the lowest current density applied and approximately 1.6 times higher than the specific capacity values obtained for the other materials under the highest current density applied. Moreover, it was observed that the variation of the maximum stoichiometric ratio (xmax) as a function of the current density is lower for the self-assembled materials than for the V2O5 electrode, which can be related to the higher ionic mobility of the lithium ion within the self-assembled materials. Electrochemical Impedance Spectroscopy (EIS) data demonstrated that the diffusion of the lithium ions within the self-assembled materials is higher than within the V2O5 electrode, and the diffusion coefficients were 1.64 x 10-15, 1.21 x 10-14 e 2.26 x 10-14 cm2 s-1 for V2O5, V2O5/PEI and V2O5/PEI/CNPs, respectively. Thus, the polymer and the CNPs provided new conducting pathways and connected isolated V2O5 chains in the host matrix. Therefore, novel spontaneous nanocomposites were formed, aiming to demonstrate the self-assembled method adopted for improving charge transport within host matrices.

Materiais auto-organizados constituídos de V2O5 xerogel, poli(etilenoimina) (PEI) e nanopartículas de carbono (NpCs) foram obtidos por meio da técnica camada-por-camada (LbL). A metodologia aplicada permitiu a obtenção de filmes finos com elevado controle de espessura além de permitir um crescimento linear dos filmes, denominados neste trabalho V2O5/PEI e V2O5/PEI/NpCs. Além disso, o desempenho eletroquímico dos materiais auto-organizados foi comparado a um eletrodo de V2O5. Análises de FTIR mostraram que interações específicas entre os grupos amina do PEI e os grupos carboxila do V2O5 são responsáveis pelo crescimento do filme. Estas interações permitem a formação de um campo eletrostático capaz de blindar as interações entre os íons lítio e os oxigênios da vanadila (V=O) e, por consequência, são responsáveis pelo aumento na mobilidade iônica dos íons lítio no interior da matriz hospedeira e, portanto, um aumento na capacidade de armazenamento de carga. Resultados obtidos através de medidas de carga/descarga mostram que o V2O5/PEI/NpCs apresenta uma melhor desempenho do que os demais materiais estudados neste trabalho. Estes resultados mostram que a capacidade específica do V2O5/PEI/NpCs foi de 137 mA h g-1 para a menor densidade de corrente aplicada e aproximadamente 1,6 vezes maior do que os valores de capacidade específica para os outros materiais para a maior densidade de corrente aplicada. Além disso, estas medidas permitiram a observação de uma menor variação na razão estequiométrica máxima (xmáx) em função das densidades de corrente aplicadas para os filmes auto-organizados, fato este relacionado a uma maior mobilidade iônica dos íons lítio no interior dessas matrizes. Os resultados obtidos a partir de espectroscopia de impedância eletroquímica (EIS) mostraram que a difusão dos íons lítio no interior das matrizes auto-organizadas é maior do que no caso do V2O5, cujos valores do coeficiente de difusão foram de 1,64 x 10-15, 1,21 x 10-14 e 2,26 x 10-14 cm2 s-1 para os filmes V2O5, V2O5/PEI e V2O5/PEI/NpCs, respectivamente. Sendo assim, o polímero e as NpCs promoveram novos caminhos condutores e permitiram a conexão elétrica entre camadas isoladas da matriz V2O5. Dessa forma, novos nanocompósitos foram obtidos visando demonstrar o método de auto-organização empregado para melhorar o transporte de carga em matrizes hospedeiras. / Self-assembled materials constituted of V2O5 xerogel, poly (ethyleneimine) (PEI), and carbon nanoparticles (CNPs) were obtained by the layer-by-layer (LbL) technique. The applied methodology permitted the obtainment of thin films with high thickness control and also permitted a linear growth of the films, which will be named V2O5/PEI and V2O5/PEI/CNPs. Besides, the electrochemical performance of the self-assembled materials was compared to a V2O5 electrode. FTIR analyses showed that the specific interactions between the amine groups of PEI and the vanadyl groups of the V2O5 are responsible for the film growth. These interactions permitted the formation of an electrostatic shield capable of hindering the interactions between the lithium ions and the vanadyl oxygen atoms (V=O) and are consequently responsible for the enhancement on the ionic mobility of the lithium ions within the host matrix, leading to a higher energy storage capability. Results obtained by the charge/discharge measurements showed that V2O5/PEI/CNPs presents a better performance than the other materials studied for this research. These results demonstrated that the specific capacity of the V2O5/PEI/CNPs was 137 mA h g-1 under the lowest current density applied and approximately 1.6 times higher than the specific capacity values obtained for the other materials under the highest current density applied. Moreover, it was observed that the variation of the maximum stoichiometric ratio (xmax) as a function of the current density is lower for the self-assembled materials than for the V2O5 electrode, which can be related to the higher ionic mobility of the lithium ion within the self-assembled materials. Electrochemical Impedance Spectroscopy (EIS) data demonstrated that the diffusion of the lithium ions within the self-assembled materials is higher than within the V2O5 electrode, and the diffusion coefficients were 1.64 x 10-15, 1.21 x 10-14 e 2.26 x 10-14 cm2 s-1 for V2O5, V2O5/PEI and V2O5/PEI/CNPs, respectively. Thus, the polymer and the CNPs provided new conducting pathways and connected isolated V2O5 chains in the host matrix. Therefore, novel spontaneous nanocomposites were formed, aiming to demonstrate the self-assembled method adopted for improving charge transport within host matrices.