Made available in DSpace on 2016-06-02T20:15:18Z (GMT). No. of bitstreams: 1 1960.pdf: 10381131 bytes, checksum: 5638ec0c0a5f463febc74da13a4f7c30 (MD5) Previous issue date: 2006-08-02 / Financiadora de Estudos e Projetos / The fundamental magnetic properties of chromium and its alloys Cr(1¡x)Nb(x) and Cr(1¡x)V(x), were investigated with the aim to achieve a better comprehension about the nature of the spin density waves. Was dened the edge between the AF1 and AF2 phases on the Cr(1¡x)Nb(x) alloys as function of niobium concentration. Using x-rays di®raction techniques was studied de formation of antiferromagnetic domains in the surfaces with [001] direction of chromium samples. As observed, cooling the sample under applied magneticeld do not create new magnetic domains, actuating only on its reorien- tation. The magnetic history of sample does not in°uence the surface magnetic domains formation, been an exclusive property of the sample surface crystalographic orientation. Was observed the formation of localized magnetic moment on paramagnetic phase of Cr(1¡x)Nb(x) alloys. This phenomenon early studied in Cr(1¡x)V(x) alloys, shown important qualitative di®erences which are explained on Friedel oscillations picture generated by impurity atoms. Was realized x-rays di®raction experiments which provided evidences of the existence of Friedel oscillations in Cr(1¡x)V(x) alloys. / As propriedades magnéticas fundamentais do cromo e de suas ligas de Cr(1¡x)Nb(x) e Cr(1¡x)V(x), foram investigadas com o objetivo de melhorar a compreensão sobre a natureza das ondas de densidade de spin (spin-density-wave). Foi determinada a fronteira entre as fases AF1 e AF2 nas ligas Cr(1¡x)Nb(x) em função da concentração de nióbio. Utilizando tecnica de difração de raios-x foi estudada a formação dos dominios antiferro-magnéticos nas superfícies paralelas às direções [001] e [111] de uma amostra de cromo crescida por transporte qumico de vapor (chemical vapor deposition method). Os resultados obtidos com o estado de monodomínio volumétrico preparado por resfriamento das amostras com campo magnético aplicado, comparados com aqueles das amostras em estado multi-domínio volumétrico e monodomínio de superfície, levam a conclusão de que a aplicação de campo magnético ou de outra maneira, a história magnética da amostra, não implica na formação de novos domínios magnéticos na superfície do cromo e que o campo magnético atua especificamente na reorientação do domínios existentes. Portanto, a formação de monodomínios superficiais e uma propriedade exclusiva da orientação cristalografica da superfície da amostra. Foi observada a formação de momento magnético localizado na fase paramagnética das ligas de Cr(1¡x)Nb(x). Esse fenômeno, anteriormente estudado nas ligas Cr(1¡x)V(x), apresentou diferenças qualitativas importantes na sua manifestação nas ligas de Cr(1¡x)Nb(x), que são explicadas a partir das oscilações de Friedel que se formam na região dos átomo de vanadio e nióbio. Foram realizados experimentos de difração de raios-x que forneceram evidências da existência das oscilações de Friedel nas ligas Cr(1¡x)V(x).

Made available in DSpace on 2016-06-02T20:16:44Z (GMT). No. of bitstreams: 1 2351.pdf: 2530597 bytes, checksum: 2dabbfba073a037a84cb55dab0c7bba2 (MD5) Previous issue date: 2009-03-30 / Financiadora de Estudos e Projetos / In this work we present the results of characterization of Cr-Ti alloys with small quantities of Ti. The samples were prepared in a melting arc furnace, using hight purity Cr and Ti. The magnetic phase diagram was determined from critical temperatures obtained by eletrical resistivity and DC magnetic susceptibility measurements, delimiting the boundaries between the transverse and longitudinal SDW (Spin Density Wave) and paramagnetic phases. We have observed that the Band Rigid Model is valid only for concentrations below 1.5%Ti. Above this concentration, a possible structural phase transition explain the disappearance of antiferromagnetic phase. From the observation of anomalies in resistivity ratio, magnetic susceptibilty and Hall effect measurements at low temperature, we have concluded that the system exhibits a quantum critical point in 1.2%Ti. / Neste trabalho realizamos um estudo sobre as propriedades magnéticas das ligas de Cr-Ti com baixas concentrações de Ti. As amostras foram preparadas por fusão de grânulos de Cr e Ti de alta pureza em forno a arco voltaico. O diagrama de fases magnéticas foi determinado a partir das temperaturas de transição obtidas por medidas de resistividade elétrica e suscetibilidade magnética, delimitando as fronteiras entre as fases antiferromagnéticas de polarização de SDW ( spin density waves ) transversal e longitudinal e a fase paramagnética. Observamos que o Modelo de Banda Rígida é válido apenas para concentrações inferiores a 1,5%Ti, acima da qual possivelmente há uma transição de fase estrutural, que pode explicar o desaparecimento da fase antiferromagnética. A partir de anomalias observadas em medidas de razão de resistividade elétrica, suscetibilidade magnética e efeito Hall em baixas temperaturas, concluímos que a liga apresenta uma Transição de Fase Quântica, com um ponto crítico quântico em 1,2% Ti.