Made available in DSpace on 2015-04-14T13:58:34Z (GMT). No. of bitstreams: 1 418870.pdf: 876464 bytes, checksum: a077367c9f6644c00361b5edeb2c3c8b (MD5) Previous issue date: 2009-09-30 / Os poli?steres termopl?sticos v?m apresentando um crescimento significativo nas ?reas automotiva, pl?sticos de engenharia, eletro-eletr?nico, adesivos, etc. Este crescimento vem de encontro com as propriedades que estes materiais apresentam como resist?ncia t?rmica, resist?ncia qu?mica, rigidez, processabilidade, moldabilidade, velocidade de cristaliza??o entre outras. Este estudo tem como objetivo a s?ntese e caracteriza??o de poli?steres utilizando diferentes fontes de ?cido tereft?lico (DMT e PET) e com diferentes composi??es de di?is (hexanodiol e butanodiol). Os poli?steres sintetizados foram caracterizados quanto a sua viscosidade, massa molecular, propriedades t?rmicas e mec?nicas e com rela??o as suas caracter?sticas de adesividade, sendo comparados com um poli?ster comercial utilizado como adesivo termofund?vel. O reagentes de partida DMT e PET mostraram-se eficientes para a obten??o de poli?steres com alta massa molecular (Mw= 46450 g/mol e Mn= 24230 g/mol) compar?veis com a do poli?ster comercial (Mw= 51000 g/mol e Mn= 15350g/mol). A introdu??o do PET na s?ntese de poli?steres diminuiu significativamente o tempo de rea??o que inicialmente era de 12 horas passando para aproximadamente 5 horas. O uso de hexanodiol, butanodiol ou misturas destes na s?ntese produziram poli?steres com viscosidades, propriedades t?rmicas e mec?nicas bem distintas. Os poli?steres obtidos com butanodiol apresentam comportamentos t?rmicos semelhantes ao poli?ster comercial (Tm 178 e 172?C, respectivamente) e poli?steres sintetizados com hexanodiol apresentam propriedades de tens?o versus deforma??es similares ao poli?ster comercial. O uso das misturas de butanodiol/hexanodiol mostra que um maior percentual de hexanodiol na composi??o do poli?ster produz um pol?mero com menor temperatura de fus?o e de transi??o v?trea e com maior percentual de deforma??o.

Made available in DSpace on 2015-04-14T13:59:01Z (GMT). No. of bitstreams: 1 451408.pdf: 2001756 bytes, checksum: 64067e77cbea30ac7596f0d09843bc92 (MD5) Previous issue date: 2013-08-09 / Due to search for different properties in polymeric materials, have increasing studies in the composites and the nanocomposites field, using inorganic fillers. Within this context one this work, which has as main objective to study experimentally the synthesis and characterization of nanocomposites of aromatic polyesters / titanium dioxide (PEA/TiO2), using raw materials trade. To do so, it was used the in situ polymerization technique to prepare the nanocomposites with PEA/TiO2 with different concentrations of the load (0%, 0.5%, 1.0%, 2.0%, 3.0% and 5.0% m/m of the polymer mass). It was used as starting materials: dimethyl terephthalate (DMT), polyethylene terephthalate (PET) and a mixture of 1,4-butanediol and 1,6-hexanediol. The nanocomposites were characterized by Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM), Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA) and Gel Permeation Chromatography (GPC). Shore D hardness, contact angle and X-ray Diffraction (DRX). The results show that there was an interaction filler/polymer evidenced by XRD and FTIR analysis. The thermal properties of nanocomposites suffered no significant changes. It was also possible to observe a change in the surface of the synthesized material indicating good compatibility btween filler and polymeric matrix and a decrease of surface hydrophilicity (measured by the contact angle) as well as an increase in hardness of the material compared to pure polymer. / Devido ? busca de propriedades diferenciadas em materiais polim?ricos, t?m-se um aumento crescente nos estudos de comp?sitos e nanocomp?sitos utilizando cargas inorg?nicas. Dentro deste contexto insere-se este trabalho, que tem como objetivo principal estudar, experimentalmente, a s?ntese e a caracteriza??o de nanocomp?sitos de poli?steres arom?ticos/di?xido de tit?nio (PEA/TiO2), utilizando-se mat?rias-primas comerciais. Para isso, utilizou-se a t?cnica de polimeriza??o in situ para preparar nanocomp?sitos de PEA/TiO2 com diferentes concentra??es da carga (0%, 0,5%, 1,0%, 2,0%, 3,0% e 5,0% m/m sobre a massa do pol?mero). Utilizou-se como reagentes iniciais: o Dimetil Tereftalato (DMT), o Politereftalato de Etileno (PET) e uma mistura de 1,4- butanodiol e 1,6- hexanodiol. Os nanocomp?sitos preparados foram caracterizados por Espectroscopia de Infravermelho por Transformada de Fourier (FTIR), Microscopia Eletr?nica de Varredura (MEV), Calorimetria Diferencial Explorat?ria (DSC), An?lise Termogravim?trica (TGA), Cromatografia em Permea??o em Gel (GPC), Dureza Shore D, ?ngulo de contato e Difra??o de Raios- X (DRX). Pelos resultados obtidos neste trabalho, pode-se ressaltar que houve intera??o carga/pol?mero comprovada pelas an?lises de DRX e FTIR onde as mesmas interferiram nas intensidades das bandas proporcionais a quantidade de carga adicionada. As propriedades t?rmicas do material analisadas por DSC e TGA n?o sofreram modifica??o significativa. Tamb?m foi poss?vel observar uma mudan?a na superf?cie do material sintetizado mostrando uma boa compatibilidade da carga com a matriz polim?rica e uma diminui??o da hidrofilicidade da superf?cie (avaliada atrav?s do ?ngulo de contato), al?m de um aumento na dureza do material quando comparado ao pol?mero puro.