Concrete, the major construction material used in the civil industry worldwide, displays remarkable performance and economic benefits. Yet, it also presents a huge environmental impact producing about 7% of the global carbon dioxide (CO2). Given the rise of global warming concerns, studies have been focusing on alternatives to reduce the amount of Portland cement (PC), which is the least sustainable ingredient of the mixture, for example by adopting particle packing model (PPM) techniques. Although a promising alternative, there is currently a lack of studies regarding the efficiently use of PPMs to reduce PC without compromising the fresh and hardened properties of the material. This work appraises the influence of PPMs and advanced mix-design techniques on the fresh (rheological behaviour) and hardened (compressive strength, modulus of elasticity, porosity, and permeability) state behaviours of systems with reduced amount of PC, the so-called low cement content (LCC) concrete. Results show that is possible to produce eco-efficient concrete maintaining and/or enhancing fresh and hardened properties of the material. Nevertheless, further durability and long-term behaviour must be performed on LCC systems.

The construction industry is closely tied to economic development economies, and increasing demand also presents a significant contribution to environmental degradation. The construction industry’s impact to climate change is led by the 8% contribution from the production of concrete mixtures, more specifically, the production of cement. The combination of using advanced mixdesign techniques (e.g., particle packing models -PPM) and more sustainable ingredients poses as a promising alternative to overcome concrete environmental impact. However, there is a lack of studies regarding the fresh state difficulties arising from the aforementioned combination. Therefore, this work appraises the use of mobility parameters to overcome the fresh state issue raised when mix-designing mortar mixtures through PPM and with high volume of limestone filler. Twelve mixtures were developed with distinct cement content ranging from 150 kg/m3 to 320 kg/m3. To produce sustainable mortar, besides using PPM, cement content was replaced by limestone filler. Time dependent fresh state analysis was performed using mortar slump flow and a rheological profile. In the hardened states, the compressive strength, porosity, surface electrical resistivity tests were performed. The main findings of the project observed a strong correlation between mobility parameters and five distinct rheological parameters: flow behaviour parameter, high shear rate viscosity and shear stress, low shear rate viscosity and shear stress. Additionally, in the hardened state, a dilution parameter IPScement was used to appraise the dilution and filler effect of the mortar mixtures. The works highlighted a promising method to produce eco-efficient mortars.

Concrete, the second most used material in the world, presents great performance and economic benefits. Yet, it is often characterized by a brittle behaviour, low tensile strength, and toughness. Fibers are usually added to concrete to counteract its brittle behaviour, increasing ductility and toughness, controlling crack propagation and delaying concrete failure. However, their addition significantly worsens the fresh state performance of the material. To improve fresh state of the so-called Fiber Reinforced Concrete (FRC), conventional mix-design methods recommend the use of high paste content, which results in a significant increase of Portland cement (PC) content and raises the carbon footprint of the material. The latter is responsible for 8% of the global annual carbon dioxide (CO2) anthropogenic emissions. Given the current worldwide concerns on global warming, the construction industry is in a need to lessen the demand, and thus production of PC. Recent studies have been focusing on the use of advanced mix-design techniques (i.e. particle packing models- PPMs) along with Inert Fillers (IF) as an alternative to reduce PC content in concrete. However, the latter was not applied to conventional FRC. In this work, advanced mix design techniques (i.e. PPMs) are used to overcome the aforementioned issues and mix-proportion eco-efficient FRC with low cement content (< 300 kg/m3). Fresh (i.e. VeBe time, slump, rheological behaviour) and hardened (i.e. compressive strength, and flexural behaviour) state tests were performed on the proposed mixtures and compared with control high PC content (375 kg/m3) FRC mixes. Results show that PPM designed mixes presented higher minimum torque (yield stress) but quite comparable apparent viscositiy when compared to conventionally designed mixtures. Moreover, the flowability (i.e. VeBe time, and slump) tends to decrease as fiber content, length, and/or as the amount of fillers increase in the mixtures. In addition, PPM mixes exhibited a shear thinning behaviour following the Herschel-Bulkley model, which enables the design of FRC PPM mix-proportioned mixtures for applications requiring high torque regimes such as vibrated and/or pumped concrete. Finally, results show that the use of PPMs to mix proportion eco-efficient low cement FRC mixtures produced improved hardened (i.e. compressive strength, and flexural performance) state behaviour with lower environmental impact than conventional ACI designed FRC mixtures.

Concrete is the most widely used construction material worldwide, yet, it presents major sustainability drawbacks due to the CO2 released during the manufacturing of its main constituent, cement. Several approaches are used to improve concrete’s eco-efficiency and reduce the binder intensity index, a metric used to measure the eco-efficiency of concrete, to a value below that of conventional concrete mixtures (i.e., 10 kg/m3.MPa-1 for 25-40 MPa mixtures). Particle Packing Models (PPM) is consequently an approach that can be used to enhance system packing density, reducing cement content while increasing hardened state properties and durability (i.e., reducing porosity). However, packed mixtures normally present issues in the fresh state while their hardened state performance is not fully comprehended. Therefore, this Ph.D. project proposes a new mix-design method called PPM-MP approach to develop eco-efficient mixtures. First, a detailed laboratory investigation was conducted on mixtures developed using the proposed approach in order to understand their fresh and hardened state performance. Concrete samples containing distinct ranges of cement content (320, 250, 200, 150 kg/m3) and slump (180, 90, and 20 +/- 20 mm) were fabricated and a wide range of fresh state tests (pH, temperature, fresh density, air content, slump and rheology over time) and hardened state tests (apparent porosity, surface electrical resistivity, compressive strength, and modulus of elasticity) were performed over time. Then, its performance against the alkali-silica reaction (ASR) induced expansion and deterioration, which is one of the leading and most damaging distress mechanisms issues in durability, was evaluated. In this section of the project, four sustainable concrete mixtures developed with varying cement content (e.g., 325, 250, 200, and 150 kg/m3) were developed and compared to a control mixture containing 420 kg/m3 of cement content. The mixtures were tested over a year under Concrete prism test (CPT) setup, which is the current method used to evaluate concrete ASR and using three different non-boosted test setups (i.e., Wrapped - W, Soaked - S, and Encapsulated - E). Moreover, two distinct types of highly reactive aggregates (e.g., Springhill Greywacke coarse aggregate and Texas Polymictic sand) were selected. Microscopic analysis was used to better understand the impact of ASR on sustainable mixtures, as well as the differences in ASR-damage and crack propagation under different test protocols. The results show the feasibility of producing an eco-efficient mixture in a more efficient manner which may contribute to the Net Zero Concrete targets. The proposed PPM-MP approach improves the sustainability of concrete mixtures and can be used for specific projects requiring 28-day compressive strength ranging from 18 to 45 MPa and slumps (180, 90, and 20 +/- 20 mm).