Made available in DSpace on 2014-12-17T14:07:01Z (GMT). No. of bitstreams: 1 GenaroZC_partes_autorizadas_pelo_autor.pdf: 1229479 bytes, checksum: 5495990b3c8d250f3f3eb0d7bcc6bbd4 (MD5) Previous issue date: 2009-05-29 / In this work, mixed oxides were synthesized by two methods: polymeric precursor and gel-combustion. The oxides, Niquelate of Lanthanum, Cobaltate of Lanthanum and Cuprate of Lanthanum were synthesized by the polymeric precursor method, and treated at 300 ? C for 2 hours, calcined at 800 ? C for 6h in air atmosphere. In gel-combustion method were produced and oxides using urea and citric acid as fuel, forming for each fuel the following oxides Ferrate of Lanthanum, Cobaltato of Lanthanum and Ferrato of Cobalt and Lanthanum, which were submitted to the combustion process assisted by microwave power maximum of 10min. The samples were characterized by: thermogravimetric analysis, X-ray diffraction; fisisor??o of N2 (BET method) and scanning electron microscopy. The reactions catalytic of depolymerization of poly (methyl methacrylate), were performed in a reactor of silica, with catalytic and heating system equipped with a data acquisition system and the gas chromatograph. For the catalysts synthesized using the polymeric precursor method, the cuprate of lanthanum was best for the depolymerization of the recycled polymer, obtaining 100% conversion in less time 554 (min), and the pure polymer, was the Niquelate of Lanthanum, with 100% conversion in less time 314 (min). By gel-combustion method using urea as fuel which was the best result obtained Ferrate of Lanthanum for the pure polymer with 100% conversion in less time 657 (min), and the recycled polymer was Cobaltate of Lanthanum with 100 % conversion in less time 779 (min). And using citric acid to obtain the best result for the pure polymer, was Ferrate of Lanthanum with 100% conversion in less time 821 (min and) for the recycled polymer, was Ferrate of Lanthanum with 98.28% conversion in less time 635 (min) / Neste trabalho, foram sintetizados ?xidos mistos por dois m?todos: precursores polim?ricos e gel-combust?o. Os ?xidos, Niquelato de Lant?nio, Cobaltato de Lant?nio e Cuprato de Lant?nio, foram sintetizados pelo m?todo dos precursores polim?ricos, sendo tratados termicamente a 300 ?C por 2h, calcinados a 800 ?C por 6h, em atmosfera de ar. No m?todo gel-combust?o foram produzidos os ?xidos utilizando como combust?vel Ur?ia e ?cido C?trico, formando para cada combust?vel os seguintes ?xidos Ferrato de Lant?nio, Cobaltato de Lant?nio e Ferrato de Cobalto e Lant?nio, que foram submetidos ao processo de combust?o assistida por microondas ? pot?ncia m?xima por 10min. As amostras foram caracterizadas por: an?lise termogravim?trica; difra??o de raio-X; fisisor??o de N2 (m?todo de B.E.T.) e microscopia eletr?nica de varredura. As rea??es catal?ticas de despolimeriza??o do Poli (metacrilato de metila), foram realizadas em um reator de s?lica, com sistema catal?tico e aquecimento munido de um sistema de aquisi??o de dados e o cromat?grafo a g?s. Para os catalisadores sintetizados utilizando o m?todo dos precursores polim?ricos, o Cuprato de Lant?nio, foi melhor para a despolimeriza??o do pol?mero reciclado, obtendo 100 % de convers?o em menor tempo 554 (min), e para o pol?mero puro, foi o Niquelato de Lant?nio, com 100 % de convers?o em menor tempo 314 (min). Pelo m?todo de gel-combust?o utilizando Ur?ia como combust?vel o que obteve melhor resultado foi o Ferrato de Lant?nio, para o pol?mero puro com 100 % de convers?o em menor tempo 657 (min), e para o pol?mero reciclado foi o Cobaltato de Lant?nio com 100 % de convers?o em menor tempo 779 (min). E utilizando ?cido C?trico o que obteve melhor resultado para o pol?mero puro, foi o Ferrato de Lant?nio com 100 % de convers?o em menor tempo 821 (min) e para o pol?mero reciclado, foi o Ferrato de Lant?nio com 98,28 % de convers?o em menor tempo 635 (min)

No presente trabalho produziu-se amostras de flexão em três pontos, SENB, a partir de placas moldadas por compressão feitas de uma resina de Poli(metacrilato de metila) comercial. Dois conjuntos contendo 6 amostras cada foram então pré-trincados por meio de uma lamina afiada de aço adotando-se dois métodos diferentes propostos pela literatura técnica: através de batidinhas (gentle tapping) e através da inserção controlada a velocidade constante da lâmina, ambas usando um dispositivo especialmente desenhado para este fim. Estas amostras foram então submetidas ao ensaio de tenacidade à fratura em deformação plana, KIc, com o intuito de se testar a hipótese de que os diferentes métodos introduzem diferentes padrões de dano na matriz próxima à região da ponta da pré-trinca, o que, por sua vez, influência os resultados obtidos. Adotou-se a norma ASTM D 5045 como padrão do ensaio. Todas as amostras produziram resultados válidos para KIc, considerando-se os critérios da norma. Os resultados confirmam a hipótese inicial mostrando que os diferentes métodos de introdução da pré-trinca influenciam o valor medido de KIc a um nível de significância de 5% para a diferença das médias obtidas nos dois grupos, sendo que o valor mais conservador é obtido quando as pré-trincas são introduzidas pelo método das batidinhas (KIc = 1,15 ± 0,11 MPa m1/2). Com base nestes resultados novas amostras com geometria auto-similar às anteriores foram produzidas e usadas para a investigação do estado de tensão desenvolvido nas amostras pelo método da fotoelasticidade. Os resultados confirmam que os diferentes métodos de pré-trincamento produzem diferentes padrões de Moiré próximos à ponta da trinca, o que prova que os estados de tensão são efetivamente afetados e que o método da inserção controlada produz a maior perturbação no campo de tensão próximo à ponta da pré-trinca. / Single-Edge-Notch Bending samples produced out of compression-molded plates obtained from a commercial Poly(methyl metacrylate), PMMA, resin were investigated concerning the influence of the adopted pre-cracking methodology on plane strain fracture toughness results according to ASTM D 5045 standard. Two sets of 6 samples each were pre-cracked using a sharp-edge scalpel steel blade using two methodologies proposed in the technical literature: by gentle tapping on the blade and by controlled insertion at constant velocity, both using a device specially designed for these purposes. These sample were, then, submitted to the plane strain fracture toughness (KIc) test based on the hypothesis that different pre-cracking methods result in different damage levels of the matrix near the pre-crack tip and, hence, in different measured values for KIc. All samples produced valid results for KIc based on the geometric criteria adopted by the standard. The results confirm the original hypothesis showing that the two pre-cracking methods influence the measured value at a significance level of 5% for the comparison of the averages obtained in both sets. The most conservative value for plane strain fracture toughness of the investigated resin is obtained by pre-cracks introduced by gentle tapping on the blade (KIc = 1.15 ± 0.11 MPa m1/2). Based on these results new samples with a self-similar geometry were produced and submitted to photoelasticity tests to investigate the influence of the pre-cracking methods on the strain-field developed during three-point bending loading. The results confirm that the different methods produce different Moiré patterns close to the pre-crack tip, proving that the developed stress fields are different and that pre-cracks introduced by controlled insertion of the blade produce the largest perturbations of the strain field close to the pre-crack tip.

No presente trabalho produziu-se amostras de flexão em três pontos, SENB, a partir de placas moldadas por compressão feitas de uma resina de Poli(metacrilato de metila) comercial. Dois conjuntos contendo 6 amostras cada foram então pré-trincados por meio de uma lamina afiada de aço adotando-se dois métodos diferentes propostos pela literatura técnica: através de batidinhas (gentle tapping) e através da inserção controlada a velocidade constante da lâmina, ambas usando um dispositivo especialmente desenhado para este fim. Estas amostras foram então submetidas ao ensaio de tenacidade à fratura em deformação plana, KIc, com o intuito de se testar a hipótese de que os diferentes métodos introduzem diferentes padrões de dano na matriz próxima à região da ponta da pré-trinca, o que, por sua vez, influência os resultados obtidos. Adotou-se a norma ASTM D 5045 como padrão do ensaio. Todas as amostras produziram resultados válidos para KIc, considerando-se os critérios da norma. Os resultados confirmam a hipótese inicial mostrando que os diferentes métodos de introdução da pré-trinca influenciam o valor medido de KIc a um nível de significância de 5% para a diferença das médias obtidas nos dois grupos, sendo que o valor mais conservador é obtido quando as pré-trincas são introduzidas pelo método das batidinhas (KIc = 1,15 ± 0,11 MPa m1/2). Com base nestes resultados novas amostras com geometria auto-similar às anteriores foram produzidas e usadas para a investigação do estado de tensão desenvolvido nas amostras pelo método da fotoelasticidade. Os resultados confirmam que os diferentes métodos de pré-trincamento produzem diferentes padrões de Moiré próximos à ponta da trinca, o que prova que os estados de tensão são efetivamente afetados e que o método da inserção controlada produz a maior perturbação no campo de tensão próximo à ponta da pré-trinca. / Single-Edge-Notch Bending samples produced out of compression-molded plates obtained from a commercial Poly(methyl metacrylate), PMMA, resin were investigated concerning the influence of the adopted pre-cracking methodology on plane strain fracture toughness results according to ASTM D 5045 standard. Two sets of 6 samples each were pre-cracked using a sharp-edge scalpel steel blade using two methodologies proposed in the technical literature: by gentle tapping on the blade and by controlled insertion at constant velocity, both using a device specially designed for these purposes. These sample were, then, submitted to the plane strain fracture toughness (KIc) test based on the hypothesis that different pre-cracking methods result in different damage levels of the matrix near the pre-crack tip and, hence, in different measured values for KIc. All samples produced valid results for KIc based on the geometric criteria adopted by the standard. The results confirm the original hypothesis showing that the two pre-cracking methods influence the measured value at a significance level of 5% for the comparison of the averages obtained in both sets. The most conservative value for plane strain fracture toughness of the investigated resin is obtained by pre-cracks introduced by gentle tapping on the blade (KIc = 1.15 ± 0.11 MPa m1/2). Based on these results new samples with a self-similar geometry were produced and submitted to photoelasticity tests to investigate the influence of the pre-cracking methods on the strain-field developed during three-point bending loading. The results confirm that the different methods produce different Moiré patterns close to the pre-crack tip, proving that the developed stress fields are different and that pre-cracks introduced by controlled insertion of the blade produce the largest perturbations of the strain field close to the pre-crack tip.