Made available in DSpace on 2014-12-17T15:41:41Z (GMT). No. of bitstreams: 1 GuymmannCS.pdf: 1754712 bytes, checksum: 731ccc6c9bb4f783f3a118094959297b (MD5) Previous issue date: 2008-02-29 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Latices based on acrylic acid and ethyl methacrylate, crosslinked with 1,6‐propoxylate‐hexanodiol diacrylate were synthesized via emulsion polymerization with different monomeric compositions. The resultant latices were thickened with different NaOH/(acrylic acid) molar ratios and were characterized by titrimetry, zeta potential measurements, turbidimetry, and capillary viscometry. Intrinsic viscosity was determined for an uncrosslinked copolymer, using toluene as solvent. All the latices were coagulated with NaCl and washed with water at 60?C analyzed by FTIR spectrophotometry, in order to characterize functional groups from the copolymer and crosslinking agent. / L?tices ? base de ?cido acr?lico e metacrilato de etila, reticulados com 1,6‐diacrilato de propoxilato hexanodiol, foram sintetizados via polimeriza??o em emuls?o, com diferentes composi??es monom?ricas. Os l?tices sintetizados foram espessados com diferentes raz?es molares NaOH/(?cido acr?lico) e caracterizados por titrimetria, medidas de potencial zeta, turbidimetria e viscometria capilar. Todos os l?tices foram coagulados com NaCl, lavados com ?gua destilada e em seguida secos a 60 0C, para a an?lise de FTIR. A viscosidade intr?nseca do l?tex n?o reticulado foi determinada utilizando tolueno como solvente. O potencial zeta foi usado para determinar a carga superficial das part?culas e o FTIR para caracterizar os grupos funcionais dos comon?meros.

Made available in DSpace on 2014-12-17T15:41:43Z (GMT). No. of bitstreams: 1 ZilvanMS.pdf: 850138 bytes, checksum: 377846a49fcf47805db83b68c5e1b5f7 (MD5) Previous issue date: 2007-07-31 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Latexes based on acrylic acid, acrylamide, ethyl methacrylate, and ethyl acrylate were synthesized via emulsion polymerization with different monomer compositions. The resultant latices were thickened with different molar ratios of NaOH to acrylic acid and were analyzed in terms of acid‐basis titrimetry, turbidimetry, rheology, and tensiometry. Titrimetry, turbidimetry, and rheometry were used to analyze factors such as carboxyl group availability and particle solubilization, tensiometry monitoring the influence of carboxyl neutralization on polymer‐surfactant interactions. For the acrylic acid content used in this work (20 wt%), the results indicated that as carboxyl groups distribution became more homogeneous, the process of latex thickening became more effective / L?tices baseados em ?cido acr?lico, acrilamida, acrilato de etila e metacrilato de etila foram sintetizados via polimeriza??o em emuls?o com diferentes composi??es monom?ricas. Os l?tices resultantes foram espessados a diferentes raz?es molares de NaOH/?cido acr?lico. Titrimetria ?cido‐base, turbidimetria, reometria e tensiometria foram usados para analisar fatores tais como a disponibilidade de grupos carboxila e a solubiliza??o de part?culas, a tensiometria sendo usada para monitorar a influ?ncia da neutraliza??o de grupos carboxilas nas intera??es pol?mero‐surfactante. Para o teor de ?cido acr?lico usado neste trabalho (20 m/m%), os resultados indicaram que, a medida em que a distribui??o de grupos carboxilas torna‐se mais homog?nea, o processo de espessamento tornou‐se mais efetivo