The rheological behavior analysis of Engineered Cementitious Composites (ECC) is key to understand how the different preparation techniques affect the composite mechanical performance. However, the rheological assessment of reinforced materials becomes more complex since fibers usually cause flow disturbances not found in nonreinforced cementitious materials. Besides that, simple workability measurement techniques are not able to fully understand the composite behavior in the fresh state creating the need for more precise techniques to be employed. The main objectives of this study were to evaluate the ECC rheological behavior using different rheometer devices (Vane system and Ball measuring system) and investigate the influence of mixing processes on the fiber homogenization and rheological behavior. Additionally to this, a link between rheological behavior and mechanical performance was investigated. In the end, the ball measuring system revealed to be more efficient than the vane system when evaluating the composite rheological behavior. In addition, the mixing process influenced the rheological behavior of PVA-ECC especially regarding the moment which fibers are added. Fiber addition after mortar mixture improved fibers homogenization and reduced mixing energy by around 8%. Moreover, a correlation between rheological and mechanical properties showed that a 2-times variation in either yield stress or viscosity can lead to a variation of more than 50% in flexural strength without significantly affecting the composite compressive strength. It was also found that the lower the composite yield stress and viscosity the higher was its ultimate strain. To conclude, all those parameters contributed to understand the composite rheological behavior and globally optimize its performance. / Sem resumo

The rheological behavior analysis of Engineered Cementitious Composites (ECC) is key to understand how the different preparation techniques affect the composite mechanical performance. However, the rheological assessment of reinforced materials becomes more complex since fibers usually cause flow disturbances not found in nonreinforced cementitious materials. Besides that, simple workability measurement techniques are not able to fully understand the composite behavior in the fresh state creating the need for more precise techniques to be employed. The main objectives of this study were to evaluate the ECC rheological behavior using different rheometer devices (Vane system and Ball measuring system) and investigate the influence of mixing processes on the fiber homogenization and rheological behavior. Additionally to this, a link between rheological behavior and mechanical performance was investigated. In the end, the ball measuring system revealed to be more efficient than the vane system when evaluating the composite rheological behavior. In addition, the mixing process influenced the rheological behavior of PVA-ECC especially regarding the moment which fibers are added. Fiber addition after mortar mixture improved fibers homogenization and reduced mixing energy by around 8%. Moreover, a correlation between rheological and mechanical properties showed that a 2-times variation in either yield stress or viscosity can lead to a variation of more than 50% in flexural strength without significantly affecting the composite compressive strength. It was also found that the lower the composite yield stress and viscosity the higher was its ultimate strain. To conclude, all those parameters contributed to understand the composite rheological behavior and globally optimize its performance. / Sem resumo

yes / In order to study the mechanical behaviors of engineered cementitious composites (ECC) reinforced with various types of polyvinyl alcohol (PVA) fibers and different fiber volume fractions after the freeze-thaw cycles, the rapid freeze-thaw method was used to test the mass loss ratios, longitudinal relative dynamic elastic modulus, compressive strength and flexural strength. The results showed that specimens incurred more serious damage with the increasing of freeze-thaw cycles; however their performance would be improved by fiber type and dosage. Mass loss rate of JPA (specimen with 2% volume content of JP fiber) was lower than JPB (specimen with 1% volume content of JP fiber). Furthermore, the mass loss rate of JPB was lower than that of CPB (specimen with 1% volume content of CP fiber). The longitudinal relative dynamic elastic modulus of JPA was higher than that of JPB while the longitudinal relative dynamic elastic modulus of JPB was higher than that of CPB. In addition, the compressive strength and flexural strength decreased with the increasing of freeze-thaw cycles. Mechanical behaviors of specimens with fiber exhibited better strength than specimens without fiber. Based on the SL 211-2006 code for the design of hydraulic structures against ice and freezing action, JPA and JPB specimens are adequate for use in severe cold regions, while specimen CPA and CPB can be used in cold regions, specimen JPC only can be used in warm regions.