This dissertation focuses on improving the chromatographic efficiency of polymeric organic monoliths by characterizing and optimizing the bed morphology. In-situ characterization techniques such as capillary flow porometry (CFP), 3-dimensional scanning electron microscopy (3D SEM) and conductivity measurements were developed and implemented to quantitatively characterize the morphology of poly(ethylene glycol) diacrylate (PEGDA) monoliths. The CFP measurements for monoliths prepared by the same procedure in capillaries with different diameters (i.e., 75, 150, and 250 μm) clearly showed a change in average through-pore size with capillary diameter, thus, certifying the need for in-situ measurement techniques. Serial sectioning and imaging of PEGDA monoliths using 3D SEM gave quantitative information about the average pore size, porosity, radial heterogeneity and tortuosity of the monolith. Chromatographic efficiency was better for a monolith with smaller average pore size (i.e., 5.23 μm), porosity (i.e., 0.49), radial heterogeneity (i.e., 0.20) and tortuosity (i.e., 1.50) compared to another monolith with values of 5.90 μm, 0.59, 0.50 and 2.34, respectively. Other than providing information about monolith morphology, these techniques also aided in identifying factors governing morphological changes, such as capillary diameter, polymerization method, physical/chemical properties of the pre-polymer constituents and weight proportion of the same. A statistical model was developed for optimizing the weight proportion of pre-polymer constituents from their physical/chemical properties for improved chromatographic efficiency. Fabricated PEGDA columns were used for liquid chromatography of small molecules such as phenols, hydroxyl benzoic acids, and alkyl parabens. The chromatographic retention mechanism was determined to be principally reversed-phase (RP) with additional hydrogen bonding between the polar groups of the analytes and the ethylene oxide groups embedded in the monolith structure. The chromatographic efficiency measured for a non-retained compound (uracil) was 186,000 plates/m when corrected for injector dead volume. High resolution gradient separations of selected pharmaceutical compounds and phenylurea herbicides were achieved in less than 18 min. Column preparation was highly reproducible, with relative standard deviation (RSD) values less than 2.1%, based on retention times of the phenol standards (3 different columns). A further improvement in chromatographic performance was achieved for monoliths fabricated using a different polymerization method, i.e., living free-radical polymerization (LFRP). The columns gave an unprecedented column performance of 238, 000 plates/m for a non-retained compound under RP conditions.

Rigid poly[hydroxyethyl acrylate-co-poly(ethylene glycol) diacrylate] (Poly(HEA-co-PEGDA) monoliths were synthesized inside 75-µm i.d. capillaries by one-step UV-initiated copolymerization using methanol and ethyl ether as porogens. The optimized monolithic column was evaluated for hydrophobic interaction chromatography (HIC) of standard proteins. Six proteins were separated within 20 min with high resolution using a 20 min elution gradient, resulting in a peak capacity of 54. The performance of this monolithic column for HIC was comparable or superior to the performance of columns packed with small particles. Monoliths synthesized solely from PEGDA were also found to show excellent performance in HIC of proteins. Continuing efforts showed that rigid monoliths could be synthesized from PEGDA or poly(ethylene glycol) dimethacrylates (PEGDMA) containing different ethylene glycol chain lengths for HIC of proteins. Effects of PEG chain length, bi-porogen ratio and reaction temperature on monolith morphology and back pressure were investigated. Monoliths prepared from PEGDA 258 were found to provide the best chromatographic performance with respect to peak capacity and resolution. An optimized PEGDA 258 monolithic column was able to separate proteins using a 20-min elution gradient with a peak capacity of 62. The preparation of these in situ polymerized single-monomer monolithic columns was highly reproducible. The single-monomer synthesis approach clearly improves column-to-column reproducibility.The highly crosslinked monolith networks resulting from single crosslinking monomers were found to enhance the surface area of the monolith and concentrations of mesopores. Thus, monolithic columns were developed from four additional crosslinking monomers, i.e., bisphenol A dimethacrylate (BADMA), bisphenol A ethoxylate diacrylate (BAEDA, EO/phenol = 2 or 4) and pentaerythritol diacrylate monostearate (PDAM) for RPLC of small molecules. Gradient elution of alkyl benzenes and alkyl parabens was achieved with high resolution using all monolithic columns. Porogen selection for the BADMA and PDAM was investigated in detail with the intention of obtaining data that could possiblly lead to a rational method for porogen selection.