Orientador: Lafayette Nogueira Junior / Coorientador: Estevão Tomomitsu Kimpara / Banca: Tarcísio José de Arruda Paes Junior / Banca: João Maurício Ferraz da Silva / Banca: Fabíola Pessôa Pereira Leite / Banca: Júlio César Brigolini de Faria / Resumo: O objetivo deste estudo foi avaliar se há alteração no comportamento mecânico e na aderência microbiológica da cerâmica à base de dissilicato de lítio com a técnica de pigmentação extrínseca aplicada, após ser submetida a diferentes condições experimentais. Foram confeccionadas 160 amostras, divididas em grupos com e sem pigmentação (n=80). Destes, cada grupo foi subdividido em Controle, Desgate, Biodegradação e Desgaste com Biodegradação (n=20).15 amostras de cada subgrupo foram submetidas ao teste de resistência à flexão e 5 para o teste de aderência microbiológica. As amostras passaram anteriormente por testes complementares para caracterização da superfície (rugosidade, perfilometria volumétrica e microscopia eletrônica de varredura (MEV)). Os resultados foram submetidos a análise estatística descritiva (média e desvio padrão) e inferencial, mediante o teste paramétrico de análise de variância (ANOVA) dois fatores e teste de Tukey ( = 0,05). O fator pigmentação extrínseca influenciou negativamente no comportamento mecânico da cerâmica, apresentando significância estatística (p = 0,000), assim como a interação entre o tipo de condição experimental e a pigmentação (p = 0,020). Entretanto, na aderência microbiológica, foi a condição experimental que influenciou negativamente no comportamento microbiológico (p = 0,000), assim como a interação entre a condição experimental e a pigmentação (p = 0,000). Nas análises complementares, observou-se que a interação entre os fatores a... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to evaluate the mechanical and microbiological behavior of the ceramics based on lithium disilicate with extrinsic characterization. For this, 160 discs were made, divided into two large groups, with extrinsec characterization and without, after which each was divided into four groups (n = 20): Control, Wear, Biodegradation and Biodegradation with Wear. Fifteen samples from each group were submitted to the flexural strength test and 5 submitted to the microbiological adherence test. Prior to the destructive test of flexural strength, the representative samples of each group underwent complementary tests for surface characterization. The results were submitted to descriptive statistical analysis (mean and standard deviation) and inferential, using the parametric analysis of variance (ANOVA) two way and Tukey test ( = 0,05). The extrinsec characterization factor influenced the mechanical behavior of the ceramic, presenting statistical significance (p = 0.000), as well as the interaction between the type of experimental condition and the extrinsec characterization (p = 0.020). However, in the microbiological adherence, it was the experimental condition that influenced the microbiological behavior (p = 0.000), as well as the interaction between the experimental condition and the extrinsec characterization (p = 0.000). It was concluded that the makeup influenced the mechanical behavior of the ceramic, and the experimental condition influenced the m... (Complete abstract click electronic access below) / Doutor

Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-03-03Bitstream added on 2014-06-13T20:37:55Z : No. of bitstreams: 1 haddad_mf_me_araca.pdf: 2948188 bytes, checksum: 2fbab93d0b5d242f0543ea496a3c8a05 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Este estudo teve como objetivo avaliar a estabilidade dimensional, reprodução de detalhes e estabilidade de cor de silicone facial, com adição ou não de pigmento e opacificador; sob influência da desinfecção química e do envelhecimento acelerado. Para isso, foram obtidas 120 amostras, utilizando o silicone Silastic MDX 4-4210, divididas em 4 grupos contendo 30 amostras cada, sendo GI - incolor, GII - pigmentado com pó de cerâmica, GIII – com adição de sulfato de bário (opacificador) e GIV- pigmentado com pó de cerâmica e sulfato de bário. Dez amostras de cada grupo foram desinfetadas com uma das três substâncias a seguir: pastilhas efervescentes a base de peróxido alcalino, sabão neutro ou clorexidina. O processo de desinfecção química foi realizado três vezes por semana, durante 60 dias. Após esse período, todas as amostras foram submetidas ao envelhecimento acelerado. Os testes de estabilidade dimensional, reprodução de detalhes e estabilidade de cor foram realizados no período inicial, após 60 dias de desinfecção e, nos intervalos de 252, 504 e 1008 horas de envelhecimento acelerado. As amostras foram analisadas em computador pelo sistema AutoCAD para verificação da alteração dimensional linear; e observadas em lupa estereoscópica para a análise da reprodução de detalhes. A estabilidade de cor foi verificada por meio de espectrofotometria de reflexão. Os valores obtidos nos testes de estabilidade dimensional e estabilidade cromática foram submetidos à análise de variância e teste de Tukey (p<0,05). Para a análise da reprodução e manutenção de detalhes foi utilizado escore de 0 a 2. O fator desinfecção não influenciou estatisticamente nos valores de estabilidade dimensional, reprodução de detalhes e estabilidade de cor do silicone, independente da... / The aim of this study was to evaluate the dimensional stability, reproduction and maintenance of details and color stability of facial silicone, with different pigmentation, on the influence of the disinfection and accelerated aging. 120 samples were obtained, using Silastic MDX 4-4210 elastomer, divided in 4 groups with 30 samples: GI - colorless, GII - pigmented with ceramics, GIII - pigmented with barium sulfate opacifier, and GIV - pigmented with ceramics and barium sulfate opacifier. Ten samples of each group was submitted to the disinfection with effervescent tablets, with neutral soap or 4% chlorhexidine, three times a week during 60 days. After this period all samples were taken to a chamber of accelerated aging for not metallic bodies. The tests of dimensional stability, maintenance of the details, and color stability were realized after the confection, disinfection and in the intervals of each cycle of accelerated aging (252, 504 e 1008 hours). Samples were analyzed, in computer by the AutoCAD system to verification of the linear dimensional alteration and observed, in stereoscopic magnifying glass for analysis of the reproduction of details. The color stability was analyzed by means of spectrophotometer. The dimensional alteration and color stability values had been submitted to the analysis of variance and Tukey test (p<0.05). For the analysis of detail reproduction, the 0 -2 scores were used It can be observed that the factor: chemical disinfection had no influenced statistically on dimensional stability, detail reproduction and color stability values. Accelerated aging had influenced statistically on dimensional stability values after 1008 hours. About detail reproduction, all samples exhibited score 2 for all analyzed periods. Pigment and opacifier association was more stable for chromatic stability test in all analyzed... (Complete abstract, click electronic address below)

Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-01-21Bitstream added on 2014-06-13T19:58:22Z : No. of bitstreams: 1 santos_dm_me_araca.pdf: 1205156 bytes, checksum: fffe6214d9a798b0c0b924994c235e30 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O maior problema enfrentado pelo protesista bucomaxilofacial é reproduzir a cor exata da pele do paciente, proporcionando uma estética agradável. Para alcançar este objetivo, o profissional deve ter materiais que possibilitem uma fácil caracterização, mantendo por um longo período de tempo a cor obtida. O propósito do presente estudo foi avaliar a estabilidade de cor de resinas acrílicas (Rapidaflex, Lentaflex e Resina Acrílica Termopolimerizável incolor e pigmentada) e de um silicone (Silastic MDX4-4210 incolor e com pigmentação) utilizados na confecção de próteses faciais, submetidos ao intemperismo natural ou artificial. Foram confeccionados 120 corpos-de-prova distribuídos em doze grupos. Metade dos corpos-de-prova foram submetidos ao envelhecimento natural por 180 dias, e a outra metade ao envelhecimento acelerado por 1008 horas. A alteração cromática dos corpos-de-prova foi verificada por meio da análise visual e da espectrofotometria de reflexão (Shimadzu, Kyoto, Japão). Os resultados foram submetidos à análise estatística pelos testes de Variância (ANOVA) de dois fatores e Tukey, com significância de 5%. Pode-se observar pela análise espectrofotométrica e visual que, independente do tipo de envelhecimento, ocorreu alteração de cor, estatisticamente significativa, entre alguns materiais. Os corpos-de-prova submetidos ao envelhecimento natural apresentaram maiores valores de alteração de cor do que aqueles submetidos ao envelhecimento acelerado. Todos os materiais sofreram alteração cromática pela influência da exposição ao meio ambiente ou pela ação do envelhecimento acelerado. / The great problem that confronts the maxillofacial prosthodontist is reproduces the accurate color of the patient’s skin, providing a satisfactory esthetic. Attempt to reach this purpose; the clinician should have materials to make an easy characterization, keeping the color by the time. The aim of this study was to evaluate the color stability of acrylic resins (Rapidaflex, Lentaflex and heat-cured colorless and pigmented acrylic resins) and a silicone (colorless and pigmented Silastic MDX4-4210) used to the confection of facial prostheses, submitted to natural or artificial weathering. 120 samples were made and distributed in twelve groups. 60 samples were submitted to the natural aging by 180 days, and the other half were submitted to the accelerated aging by 1008 hours. The chromatic differences were verified by means of the visual analysis and reflection spectrophotometer (Shimadzu, Kyoto, Japan). The results were analyzed by two-way analysis of variance (ANOVA) and Tukey tests (P<0,05). Color changes, between some materials, were observed by spectrophotometer and visual analysis, independently of the type of aging; it was statistically significant. The samples submitted to the natural aging showed higher values than the samples submitted to the accelerated aging. All materials suffered chromatic differences because to the environment exposure or the accelerated aging.

Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2004Bitstream added on 2014-06-13T19:16:54Z : No. of bitstreams: 1 fernandes_aur_me_araca.pdf: 952229 bytes, checksum: 8e65200d34f1586880d463d53baa7659 (MD5) / Universidade Estadual Paulista (UNESP) / A íris artificial é a estrutura da prótese ocular responsável pela sua dissimulação e estética. O propósito do presente trabalho foi avaliar a alteração de cor de tintas utilizadas na pintura de íris em próteses oculares polimerizadas por energia de microondas, variando-se tinta, cor e método de secagem. Para o estudo, foram confeccionados cinco discos em resina termopolimerizável por microondas para cada tinta analisada: acrílica hidrossolúvel, automotiva à base de nitrocelulose, guache hidrossolúvel e a óleo, nas cores marrom e azul, para os métodos de secagem natural e por radiação infravermelha, perfazendo um total de 80 corpos-de-prova. Cada corpo-de-prova foi constituído por um disco de resina acrílica incolor e outro, de igual dimensão, de resina acrílica de coloração branca de esclera e, entre os dois discos, a pintura. Os corposde- prova foram submetidos a uma câmara de envelhecimento acelerado sob radiação ultravioleta, por 1008 horas. Para avaliar as variações de cor foi usado um espectrofotômetro de reflexão. Os resultados foram analisados estatisticamente por Análise de Variância e teste de Tukey a 5% de significância. Todas as tintas sofreram alteração cromática. A tinta a óleo apresentou a maior resistência frente ao envelhecimento acelerado, independente da cor e do método de secagem. / The artificial iris is the structure of the ocular prosthesis responsible for its dissimulation and aesthetics. The objective of the present study was to evaluate the color stability of paint used for iris painting for ocular prosthesis polymerized with microwaves, varying painting, color and drying method. For the study, 80 discs in heat-curing for microwaves acrylic resin were made, five discs for each paint analyzed: acrylic water-soluble paints, automotive nitrocellulose paints, watercolor paints and oil paints, for the colors brown and blue, for both natural and infrared drying methods. Each specimen was constituted of one disc in colorless acrylic resin and another colored with a basic sclera pigment. The painting was accomplished in one of the surfaces of one of the discs. The specimens were submitted to an artificial aging chamber under ultraviolet light, during 1008 hours. To evaluate color changes a reflective spectrophotometer was used. The data were statistically analyzed by Variance Analysis and Tukey’s test. All paints suffered color alteration. The oil paints presented the highest resistance to artificial aging regardless the pigment and the drying method.

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-10-03Bitstream added on 2014-06-13T20:37:56Z : No. of bitstreams: 1 mancuso_dn_me_araca.pdf: 2113835 bytes, checksum: 27a105a29a2894608038cc448f18dd65 (MD5) / Universidade Estadual Paulista (UNESP) / O objetivo desta pesquisa foi o de avaliar a estabilidade de cor dos silicones faciais pigmentados e não pigmentados após o envelhecimento acelerado. Foram utilizados dois silicones, sendo um de fabricação estrangeira, próprio para próteses faciais, e um silicone acético de fabricação nacional, de uso industrial. Foram confeccionados 24 corpos-de-prova para cada silicone, divididos em grupos incolor e pigmentados intrinsecamente com: cerâmica; maquiagem; óxido de ferro. Os grupos foram submetidos ao sistema acelerado de envelhecimento para não-metálicos - ultravioleta B / condensação (Comexim, Brasil). Foi feita leitura inicial e após períodos correspondentes a 163, 351, 692 e 1000 horas de envelhecimento, através do método visual de comparação e da análise por espectrofotômetro de reflexão Color-Eye (MacBeth, USA), utilizando o Sistema CIE L*a*b*. Os valores foram submetidos à análise de variância e teste de Tukey em nível de 5% de probabilidade. Todos os grupos apresentaram estabilidade de cor no método visual de comparação. Mas, com relação à espectrofotometria de reflexão, após as 1000 horas de envelhecimento acelerado, tanto o 732 RTV, quanto o MDX, pigmentados com maquiagem, apresentaram alteração de cor. Para o grupo incolor, em 351 horas de envelhecimento, tanto o 732 RTV, quanto o MDX, apresentaram alteração. Conclui-se então que os dois silicones possuem boa estabilidade de cor em todos os grupos estudados, com exceção da maquiagem que foi considerada a mais instável dentre os pigmentos para os dois silicones. / The objective of this research was evaluating the color stability of the facial silicones pigmented and without pigmentation after the accelerated aging. A foreign silicone created specifically for facial prostheses and a national acetic silicon for industrial use were used in research. 20 bodies-of-proof were made for each silicone, divided in colorless and intrinsically pigmented groups with: ceramic; make-up; oxide of iron. The groups were submitted to the accelerated System of aging for no-metallic - Ultraviolet B / condensation (Comexim, Brazil). An initial evaluation and evaluations after 163, 351, 692 and 1000 hours of aging were made. The visual method of comparison and the analysis for reflection spectrophotometer Color-Eye (MacBeth, USES) were used with the CIE L*a*b * System. The values were submitted to the variance analysis and Tukeyþs test in level of 5% of probability. All groups presented color stability in visual method. After 1000 hours of accelerated aging, Silastic 732 RTV and MDX, both pigmented with make-up presented color change in spectrophotometer analysis. The Silastic 732 RTV and MDX colorless groups presented color change in 351 hours of aging. It was concluded that all groups of both silicones had good color stability, except make-up group that was considered the most unstable pigment for both silicones.

Indiana University-Purdue University Indianapolis (IUPUI) / This study evaluated the color stability of bleach shade composites when activated by a high-intensity quartz tungsten-halogen (QTH) light source after 1 day, 7 days, and 30 days of exposure to different conditions. The color stability of bleach shade composites depends on various factors, namely, the resin material, the shade of the resin material, the storage method, and the storage time.

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-04-13Bitstream added on 2014-06-13T20:58:51Z : No. of bitstreams: 1 pesqueira_aa_me_araca.pdf: 540641 bytes, checksum: 5dfe2f80d73fb4a9cb52016d432619cf (MD5) / Este estudo teve como objetivo avaliar a estabilidade dimensional, reprodução e manutenção de detalhes, dureza “Shore A”, deterioração e estabilidade de cor, de um silicone facial, com distintas pigmentações, sob a influência da desinfecção e do envelhecimento acelerado. Para isso foram obtidos 60 corpos-de-prova, utilizando o silicone Silastic MDX 4- 4210, divididos em 3 grupos: sem pigmentação, pigmentado com pó de maquiagem e pigmentado com cerâmica. Metade dos corpos-de-prova de cada grupo foram submetidas à desinfecção com Efferdent e a outra metade com sabão neutro por 60 dias. Após esse período todos os corpos-de-prova (n=10) foram levados a uma câmara de envelhecimento acelerado para corpos não metálicos. Os ensaios de deterioração, estabilidade dimensional, reprodução e manutenção de detalhes, dureza Shore A e estabilidade de cor foram realizados após sua confecção, desinfecção e nos intervalos de cada ciclo de envelhecimento acelerado (252, 504 e 1008 horas). Os corpos-de-prova foram analisados, em computador pelo sistema AutoCAD para verificação da alteração dimensional linear e observados, em lupa estereoscópica para a análise da reprodução de detalhes. A dureza dos materiais foi analisada em durômetro Shore A e pesados em balança digital de precisão para análise da deterioração. A estabilidade de cor foi analisada por meio de espectrofotometria. Os valores encontrados dos testes de estabilidade dimensional, reprodução e manutenção de detalhes, dureza “Shore a“ e estabilidade de cor foram submetidos à análise de variância e teste de Tukey em nível de 1% de probabilidade. Para a análise da reprodução e manutenção de detalhes foi utilizado escore. Pôde-se observar que os fatores desinfecção química e o envelhecimento acelerado influenciaram estatisticamente na deterioração, estabilidade dimensional, dureza... / The aim of this study was to evaluate the dimensional stability, reproduction and maintenance of details, Shore A hardness, deterioration and color stability of facial silicone, with different pigmentation, on the influence of the disinfection and accelerated wheatering. 60 samples were obtained, using silicone Silastic MDX 4-4210, divided in 3 groups: nonpigmented, pigmented with make-up powder and pigmented with ceramics. The half of the samples of each group was submitted to the disinfection with Efferdent and another one with neutral soap per 60 days. After this period all the samples were taken to a chamber of accelerated wheatering for not metallic bodies (n=10). The tests of deterioration, dimensional stability, maintenance of the details, Shore A hardness and color stability were realized after the confection, disinfection and in the intervals of each cycle of accelerated wheatering (252, 504 e 1008 horas). Samples were weighty in digital balance for analysis of deterioration. Analyzed, in computer by the AutoCAD system to verification of the linear dimensional alteration and observed, in stereoscopic magnifying glass for analysis of the reproduction of details. Materials hardness was analyzed in Shore A durometer and the color stability by means of spectrophotometer. The values had been submitted to the analysis of variance and Tukey test (1%). It can be observed that the factors: chemical disinfection and the accelerated wheatering had influenced statistically in deterioration, dimensional stability, Shore A hardness and color stability of the materials independently of the pigmented. With relation to the reproduction and maintenance of details, the values did not change independently of the pigmented, disinfection and accelerated wheatering.

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-05-27Bitstream added on 2014-06-13T19:44:51Z : No. of bitstreams: 1 santos_dm_dr_araca.pdf: 1533021 bytes, checksum: 248d1fb3f8ac9369529ebf0ea03f0654 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O presente estudo teve por objetivo avaliar a influência de dois pigmentos (pó de cerâmica e tinta a óleo) e um opacificador (sulfato de barium) sobre as propriedades físicas de estabilidade de cor, dureza, absorção e solubilidade do silicone facial MDX4-4210, submetido ao envelhecimento acelerado. Para a confecção das amostras, foram utilizadas 2 matrizes metálicas em alumínio, contendo em seu interior 10 compartimentos circulares com 45mm de diâmetro apresentando estes, em uma matriz, uma espessura de 2mm para os testes de estabilidade de cor e dureza e, na outra, 1mm para os ensaios de absorção e solubilidade. Foram confeccionadas 120 amostras, metade para os ensaios de análise cromática e dureza e, a outra metade, para o teste de absorção e solubilidade. As amostras destinadas para cada teste foram distribuídas em seis grupos, incolor (G1), incolor com opacificador (G2), cerâmica (G3), cerâmica com opacificador (G4), óleo (G5), óleo com opacificador (G6). Após a obtenção das amostras, a análise cromática inicial foi verificada por meio da análise visual e da espectrofotometria de reflexão. Os ensaios de dureza foram realizados com auxílio de um durômetro Shore A. Os testes de absorção e solubilidade foram realizados por meio de um dessecador no qual as amostras permaneceram neste ambiente em estufa à temperatura de 37±2°C, sendo pesadas diariamente até obtenção de massa constante (W1); posteriormente as amostras foram submetidas ao envelhecimento seguido de nova pesagem (W2), e nova dessecação com pesagem final (W3). As amostras foram submetidas ao envelhecimento acelerado por 1008 horas, sendo os ensaios realizados nos períodos correspondentes a 252, 504 e 1008 horas. Os dados obtidos foram submetidos à ANOVA e Tukey, com significância de 5%. Pode-se observar pela análise espectrofotométrica que os grupos com opacificador apresentaram melhor... / The aim of this study was to evaluate the influence of two pigments (ceramic powder and oil paint) and one opacifier (barium sulfate) on physical properties of color stability, hardness, absorption and solubility of the facial silicone MDX4-4210 submitted to artificial aging. The replicas were fabricated in two metallic matrixes in aluminum containing 10 circular compartments with 45mm in diameter. One matrix generated specimens with 2mm in thickness for color stability and hardness evaluations while the other matrix, specimens with 1mm in thickness for absorption and solubility tests. The replicas were divided into six groups: colorless (G1), colorless with opacifier (G2), ceramic (G3), ceramic with opacifier (G4), oil (G5) and oil with opacifier (G6). Initial chromatic evaluation was performed by visual analysis and reflection spectrophotometry. The hardness tests were carried out by a Shore A durometer. The evaluations of absorption and solubility were performed through a desiccator to maintain the replicas in a stove at 37±2°C. The specimens were weighed daily until obtaining a constant mass, (W1). Then, the replicas were submitted to aging followed by a new weighing (W2) and drying with final weighing (W3). The replicas were submitted to accelerated aging during 1008 hours with evaluation after 252, 504 and 1008 hours. Data were submitted to statistical analysis by ANOVA and Tukey’s test at 5% level of significance. According to spectrophotometry, the groups with opacifier presented statistically significant better chromatic stability than the other groups. The accelerated aging generated significant chromatic alterations in all groups, except for colorless and oil groups both with opacifier. There was no statistically significant difference among the groups after aging regarding hardness, absorption and solubility. According to the results, it may be concluded that... (Complete abstract, click electronic access below)