Orientadores : Saide Sarckis Domitti, Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T14:40:33Z (GMT). No. of bitstreams: 1 Abreu_RicardoTeixeira_M.pdf: 17366541 bytes, checksum: 52e9fa145d98172f597b993bba61e992 (MD5) Previous issue date: 2003 / Mestrado

Orientador: Celia Marisa Rizzatti Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-24T14:48:28Z (GMT). No. of bitstreams: 1 Fraga_MarcoAurelio_M.pdf: 2300241 bytes, checksum: b3d505b92d41270efebc5938157fa89c (MD5) Previous issue date: 1998 / Resumo: O objetivo do presente trabalho foi estudar a sorção de água de amostras de resina acrílica termopolimerizável, submetidas a alterações de pressão e temperatura em função do tempo. Foram confeccionadas 45 amostras de acordo com a especificação n° 12, da 'American Dental Association POT. 13¿. As amostras foram subdivididas em 9 grupos com 5 repetições cada um. As 5 amostras do Grupo I foram consideradas controle, e após confeccionadas, foram submetidas ao seguinte tratamento (GI): imersão em água destilada a 37 ' + OU ¿ ' 2 °C, à pressão ambiente durante 30 dias. Os demais grupos receberam os seguintes tratamentos: imersão em água destilada a 70 ' + OU ¿ ' 2 °C, à pressão de 40 Lb. por 60 minutos (GIl ), à pressão de 60 Lb. por 60 minutos (GIII), à pressão de 40 Lb. por 90 minutos (GIV), à pressão de 60 Lb. por 90 minutos (GV); imersão em água destilada a 90 ' + OU ¿ ' 2 °C à pressão de 40 Lb. por 60 minutos (GVI), à pressão de 60 Lb. por 60 minutos (GVII) , à pressão de 40 Lb. por 90 minutos (GVIII), e à pressão de 60 Lb. por 90 minutos (GIX). Após estes tratamentos, as amostras foram submetidas ao teste de sorção de água descrito na especificação n° 12, da 'American Dental Association POT. 13¿. Os resultados, após terem sido submetidos à análise estatística, permitiram concluir que os índices de sorção de água apresentados pelas amostras de resina polimerizada a 73 °C por 9 horas, armazenadas em água à temperatura de 90 ' + OU ¿ ' 2 °C, apresentaram valores compatíveis aos das amostras do grupo controle, não havendo influência da pressão de 40 ou 60 Lb. sobre estes índices / Abstract: The aim of this study was to observe the water sorption by heat-eured polymethyl methaerylate resin samples, submitted to pressure and temperature alterations, according to timing. Forty-five samples were made in aeeordanee to Specification #12 of the 'American Dental Association POT. 13¿. The samples were divided in 09 groups with 05 samples each one . The five samples to Group 1 ( GI) were taken as control group and after being crafted they were submitted to the following treatment: immersion in distilled water at 37 ' + OU ¿ ' 2 °C, at ambient pressure, for 30 days. The other groups were given the following treatment: immersion in distilled water at 70 ' + OU ¿ ' 2 °C, under a 40 Lb. pressure for 60 minutes (GII), under a 60 Lb. pressure for 60 minutes (GIll), under a 40 Lb. pressure for 90 minutes (GIV), under a 60 Lb. pressure for 90 minutes (GV); immersion in distilled water at 90 ' + OU ¿ ' 2 °C under a 40 Lb. Pressure for 60 minutes (GVI), under a 60 Lb. pressure for 60 minutes (GVII), under a 40 Lb. pressure for 90 minutes (GVIIl), and under a 60 Lb. pressure for 90 minutes (GIX). After this procedures the samples were submitted to the water sorption test described by Specification # 12 of 'Ameriean Dental Association POT. 13¿ . The results, after statisties analysis permitted to, conclude that the water sorption presented by the resin polymethyl samples, cured by 73°C by 9 hours, stored in water under 90 ' + OU ¿ ' 2 °C, presented the same values of the control group, not occuring influence by pressure of 40 or 60 Lb. on this scores / Mestrado / Protese / Mestre em Clínica Odontológica

Orientador: Dalton Belmudes de Toledo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-20T15:29:36Z (GMT). No. of bitstreams: 1 Battistuzzo_JosedoCarmo_D.pdf: 2253826 bytes, checksum: 3d6e01d2567ca6d90714b0ddb50416e4 (MD5) Previous issue date: 1968 / Resumo: Não informado / Abstract: Not informed. / Doutorado / Dentística Operatoória / Doutor em Ciências

Orientador: Marcelo Coelho Goiato / Banca: Adriana Cristina Zavanelli / Banca: Mauro Antônio de Arruda Nóbilo / Resumo: O objetivo deste trabalho foi avaliar a desadaptação e a microdureza superficial de quatro tipos de resinas acrílicas para base de dentaduras, em função de período de armazenagem em água de seis meses. Foram confeccionados vinte e cinco conjuntos modelo de gesso-base de resina, utilizando-se quatro resinas acrílicas: QC-20 que foi submetida à polimerização convencional (de acordo com as instruções dos fabricantes) e por energia de microondas (840 W por três minutos), Vipi Cril submetida à polimerização convencional (fabricante), Vipi Wave e Onda Cryl que receberam polimerização por energia de microondas conforme as recomendações dos fabricantes. Após a polimerização, os conjuntos modelo de gesso-base de resina foram seccionados na região posterior correspondente a região de "post-dam" para a leitura da desadaptação, com auxílio de um microscópio comparador, em três pontos referenciais: crista dos rebordos direito e esquerdo e região mediana do palato. Os conjuntos seccionados foram, então, imersos em água destilada a 35 l 2ºC por período de noventa dias, após o qual uma segunda leitura da desadaptação foi realizada. Imediatamente, os conjuntos modelo-base de resina foram separados e a bases de resina retiradas para a remoção dos excessos grosseiros da borda até o limite estabelecido pelo modelo de gesso. Posteriormente, as bases de resina acrílica foram fixadas nos respectivos modelos com adesivo de presa rápida colocado na região correspondente à crista do rebordo alveolar e uma terceira leitura para analisar a desadaptação, nos pontos referenciais, foi realizada. Após a terceira leitura, os conjuntos ficaram novamente imersos em água destilada a 35 l 2ºC e armazenados em estufa por um período de mais noventa dias, findo o qual uma quarta leitura nos pontos previamente demarcados foi...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this work was to evaluate the missfitting and the superficial microhardness of four acrylic resins types for dentures base due to storage period in six months water. 25 model sets of resin plaster-base have been confectioned using four acrylic resins: QC-20, which was submitted to the conventional polymerization (in accordance with the manufacturer's instructions) and microwaves energy polymerization (840W for three minutes) and Vipi Wave and Onda Cryl, which have received microwaves energy polymerization also in accordance with the manufacturer's recommendations. After the polymerization process, the model sets of resin plaster-base were parted in the corresponding posterior region, the "post-dam" region, for the missfitting analysis. This was supported by a comparing microscope in three reference points: right and left crest of ridges and palate's middle region. The parted sets have been, then, immersed in distilled water about 35 to 2°C, for a 90-day period which was followed by a second missfitting analysis. The resin base-model sets were immediately separated and the resin bases were immediately removed to promote the edge coarse excesses' removal until the limit established by the plaster model. Later, the acrylic resin bases were fixed in the respective models with fast stick adhesive, which was placed in the corresponding region to the alveolar crest of ridges. A third analysis to study the missfitting in the reference points was carried through. After the third analysis the sets were immersed again in distilled water about 35 to 2ºC and stored in a stove for a certain period, which exceeded 90 days. As soon as this period was finished, a fourth analysis was carried through in the points previously outlined (180 days total analysis period...(Complete abstract, click electronic address below) / Mestre

O comportamento termodinâmico, assim como as propriedades físicas e químicas da resina acrílica, podem ser diferentes quando termopolimerizadas por diferentes métodos, podendo ser analisado através do monitoramento da temperatura em função do tempo de termopolimerização, do grau de porosidade, dureza Knoop (0,015 Kg) e quantidade de monômero residual. No presente trabalho foram avaliados o comportamento termodinâmico e algumas propriedades físicas e químicas de duas resinas acrílicas, termopolimerizadas em água aquecida e por energia de microondas. As resinas acrílicas Clássico e Onda Cryl foram termopolimerizadas em água aquecida pelo método clássico de Tuckfield, Worner e Guerin64 em 1943 (TWG) e através da energia de microondas a 520 W – 10 minutos, segundo Nishi44 em 1968 (MW). A temperatura da termopolimerização em função do tempo foi monitorada por termopares de cobre / constantan conectados a aparelhos eletrônicos e computacionais. Os termopares foram instalados dentro da massa de resina acrílica, da água e do revestimento de gesso. Os 22 espécimes de resina acrílica, medindo 65 / 49 / 5 mm, foram analisados sobre o grau de porosidade, dureza Knoop e quantidade de monômero residual. Os resultados foram submetidos a análise estatística através dos testes Mann – Whitney e “t" de Student. Houve diferença significante na temperatura máxima das termopolimerizações TWG e MW, na incidência de porosidade e na quantidade de monômero residual, já a dureza Knoop não apresentou diferença significante. A resina acrílica quando termopolimerizada pelas microondas sofreu um rápido aquecimento, alcançando temperaturas de 155o C, com alta incidência de porosidade, enquanto na termopolimerização em água aquecida, a temperatura máxima foi de 101,2o C, com isenção de porosidade. A maior quantidade de monômero residual foi detectada nos espécimes termopolimerizados pelo método MW. O comportamento termodinâmico da resina acrílica no método MW foi inadequado, caracterizado pela alta incidência de porosidade, menor dureza Knoop e maior quantidade de monômero residual. / Acrylic resins of the methyl methacrylate present unsuitable thermodynamic behavior during thermal polymerization mainly if the temperature exceed boiling point (100.8o C), what brings about an increase to the degree of porosity. The thermodynamic study was carried out with acrylic resins Clássico and Onda Cryl, thermal polymerized by water bath (3 hours, Tuckfield, Worner and Guerin in 1943) and by microwave (520 W – 10 minutes, Nishi in 1968). The temperature of the thermal polymerization was recorded by thermocouples (copper / constantan) and monitored by electric - electronically equipment and computers. The 2.0 mm spherical thermocouples were placed into acrylic resin and gypsium investment and the thermal polymerization was monitored. Twenty-two specimens (65 / 49 / 5 mm) were obtained after finishing and polishing and the degree of porosity was analyzed stabilizing temperature parameters in thermal polymerizations. Was analysis to hardness Knoop, by hardness machine Testor (Otto Wolpert – Werke) and residual monomer was analysis in the spectrophotometer U.V. (Ultrospect 2000 U.V. Pharmacia – Biotech). Statistical analysis was performed using Mann - Whitney and “t" Student tests. Significant difference was observed in the degree of porosity. residual monomer and maximum temperature between thermal microwave polymerization and polymerization by water bath. The microwave thermal polymerized acrylic resin quickly heated to 155o C and showed high incidence of porosity, whereas in thermal polymerization by water bath the maximum temperature reached 101.2o C and specimens were porosity free. According to the power and time used in the present study, the thermal polymerization by microwave irradiation showed unsuitable thermodynamic behavior, characterized by high incidence of porosity, least hardness and greater amount residual monomer.

Orientador: Juliana Campos Junqueira / Banca: Célia Regina Gonçalves e Silva / Banca: Antonio Olavo Cardoso Jorge / Resumo: Leveduras do gênero Candida são patógenos oportunistas que podem causar infecções superficiais ou sistêmicas. A investigação de plantas medicinais contra Candida spp. tem aumentado significativamente nos últimos anos. O presente estudo teve como objetivos avaliar a ação antimicrobiana do extrato hidroalcoólico e do óleo essencial de Mentha piperita L. sobre isolados clínicos de Candida spp. e observar o efeito da infusão de Mentha piperita L. sobre a aderência de leveduras do gênero Candida à resina acrílica. O extrato hidroalcoólico e o óleo essencial de Mentha piperita L. foram avaliados quanto à atividade antimicrobiana sobre diferentes espécies do gênero Candida, sendo cinqüenta amostras de C. albicans, dez C. glabrata, dez C. tropicalis, oito C. parapsilosis e duas C. krusei. A concentração inibitória mínima (CIM) e concentração fungicida mínima (CFM) do extrato hidroalcoólico (500 g de planta fresca/1 L de etanol) foram determinadas pelo método da diluição em caldo. O grupo controle constituiu-se de etanol na mesma concentração do extrato (79°GL). A atividade antimicrobiana do óleo essencial foi realizada por meio do teste de difusão em ágar. Foi observado o efeito da infusão de Mentha piperita L. sobre a aderência de cepas padrão de C. albicans, C. glabrata, C. tropicalis e C. krusei à resina acrílica. Os resultados demonstraram que o extrato hidroalcoólico de Mentha piperita L. apresentou atividade fungistática para algumas cepas de C. albicans, C. tropicalis e C. glabrata e atividade fungicida sobre cepas de todas as espécies de Candida estudadas em relação ao grupo controle. O óleo essencial mostrou maior atividade inibitória para cepas de C. albicans, seguida por C. tropicalis e C. parapsilosis. A infusão de Mentha piperita L. não foi capaz... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Fungi belonging to Candida species are opportunistic pathogens that can cause local and systemic infections. The investigation of natural products against Candida spp. increased significantly in the last few years. In this present study, the ethanolic extract and essential oil from Mentha piperita L. were evaluated for antimicrobial activity against Candida spp., being fifty strains from C. albicans, ten from C. glabrata, ten from C. tropicalis, eight from C. parapsilosis and two C. krusei. The minimal inhibition concentration (MIC) and minimal fungicidal concentration (MFC) of the ethanolic extract (500 g of fresh plant / 1 L of ethanol) were determined by the broth dilution method. The control group was constituted by ethanol in the same proportion of the extract (79ºGL). The antimicrobial activity of the essential oil was performed by the agar diffusion method. Besides, it was observed the effect of Mentha piperita L. infusion on the adherence of standard strains of C. albicans, C. glabrata, C. tropicalis and C. krusei to the acrylic resin. The results showed that ethanolic extract of Mentha piperita L. presented fungistatic activity to some strains of C. albicans, C. glabrata and C. tropicalis, and also fungicidal activity on strains of all Candida species in comparison with the control group. The essential oil of Mentha piperita L.was more active to strains of C. albicans followed by C. tropicalis and C. parapsilosis. The infusion of Mentha piperita L. was not effective to inhibit the Candida adherence to the acrylic resin. It was concluded that Mentha piperita L. was more active to strains of C. albicans and C. tropicalis, but was not effective to have any effect on the adherence of these microorganisms to the acrylic resin. / Mestre

TEMÓTEO, Guilherme de Alencar. Análise da contaminação microbiana de dispositivos acrílicos confeccionados em laboratórios de próteses dentárias. 2014. 53 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2014. / Submitted by denise santos (denise.santos@ufc.br) on 2014-07-21T11:40:44Z No. of bitstreams: 1 2014_dis_gatemoteo.pdf: 741240 bytes, checksum: 21d11cc77cd7f873fb211cafff0f6596 (MD5) / Approved for entry into archive by denise santos(denise.santos@ufc.br) on 2014-07-21T11:50:50Z (GMT) No. of bitstreams: 1 2014_dis_gatemoteo.pdf: 741240 bytes, checksum: 21d11cc77cd7f873fb211cafff0f6596 (MD5) / Made available in DSpace on 2014-07-21T11:50:50Z (GMT). No. of bitstreams: 1 2014_dis_gatemoteo.pdf: 741240 bytes, checksum: 21d11cc77cd7f873fb211cafff0f6596 (MD5) Previous issue date: 2014 / The possible presence of potentially pathogenic microorganisms in denture newly arrived from prosthetic laboratories should be considered. This study evaluated the level of bacterial and fungal contamination of specimens of acrylic resin made in 14 dental laboratories registered with the Regional Council of Dentistry of Ceará, Fortaleza. Each laboratory was asked to fabricate 10 specimens of acrylic resin, from standard models of sterile silicone addition, unaware of the research objectives. Specimens received from laboratories were placed in individual tubes containing BHI broth, incubated at 37°C for 48 hours and then removed, washed and placed in sterile saline and stirred for microbial detachment. The suspension obtained was diluted (1:100, 1:1000) and plated on blood agar plates, and Sabouraud Dextrose Agar and Agar HiCrome ICU by incubation for 48 hours at 37°C. The number of colony forming units (CFU) bacterial and fungal viable was obtained, besides the identification and quantification of some species of bacteria, comparing the laboratory by means of the Kruskal-Wallis and Dunn (α = 0.05) tests. There was contamination originating from all laboratories analyzed, with a mean CFU counts of 101438 bacteria and 71047 fungi. Pseudomonas spp was the most prevalent microorganism identified (p < 0.05). It was concluded that there is a risk of contamination with potentially pathogenic bacteria and fungi in prosthetic devices newly arrived from dental laboratories. / A possível presença de microorganismos potencialmente patogênicos em próteses dentárias recém-chegadas dos laboratórios protéticos deve ser considerada. Este estudo avaliou o nível de contaminação bacteriana e fúngica de espécimes de resina acrílica confeccionados em 14 laboratórios de prótese dentária, inscritos no Conselho Regional de Odontologia do Ceará, na cidade de Fortaleza. Cada laboratório foi solicitado a confeccionar 10 espécimes de resina acrílica, a partir de modelos padronizados de silicona de adição estéreis, desconhecendo os objetivos da pesquisa. Os espécimes recebidos dos laboratórios foram colocados em tubos individuais contendo BHI caldo e incubados a 37°C por 48 horas e, em seguida, removidos, lavados, colocados em solução salina estéril e agitados para desprendimento microbiano. A suspensão obtida foi diluída em 1:100, 1:1000 e semeada em placas com Ágar Sangue, Sabouraud Dextrose Ágar e HICrome UTI Ágar®, para incubação por 48 horas a 37°C. Foi obtido o número de unidades formadoras de colônias (UFC) bacterianas e fúngicas viáveis, além da identificação e quantificação de algumas espécies de bactérias, comparando-se os laboratórios por meio dos testes de Kruskall-Wallis e Dunn (α=0.05). Houve contaminação advinda de todos os laboratórios analizados, com uma contagem de UFC média de 101438 de bactérias e 71047 de fungos. Pseudomonas spp foi o microorganismo a mais prevalente identificado (p<0,05). Foi concluido que existe risco de contaminação por bactérias potencialmente patogênicas e fungos em dispositivos protéticos recém chegados dos laboratórios.

Orientador: Saide Sarckis Domitti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T09:40:54Z (GMT). No. of bitstreams: 1 Consani_RafaelLeonardoXediek_M.pdf: 5078942 bytes, checksum: 2b86e6de317dfb726f032a50b49bdb9d (MD5) Previous issue date: 2000 / Resumo: Este trabalho verificou a adaptação das bases de prótese total superior, confeccionadas com resina acrílica termicamente ativada Clássico, sob a influência das variáveis prensagem e polimerização. Foram confeccionados quarenta modelos em gesso pedra, e os conjuntos modelo-base de cera foram divididos em quatro grupos de dez elementos e incluídos em muflas pela técnica de rotina, recebendo os tratamentos: Grupo 1- prensagem da resina e polimerização imediata em banho de água aquecida a 74°C por nove horas; Grupo 2- prensagem da resina acrílica e polimerização após seis horas, em banho de água aquecida a 74°C por nove horas; Grupo 3- prensagem da resina acrílica, utilização do dispositivo RS de contensão e polimerização imediata em banho de água aquecida a 74°C por nove horas; Grupo 4­prensagem da resina acrílica, utilização do dispositivo RS de contensão e polimerização após seis horas, em banho de água aquecida a 74°C por nove horas. As bases de resina foram fixadas nos modelos com adesivo. Foram efetuados três cortes transversais, correspondentes à distal dos caninos (A), mesial dos primeiros molares (B) e região palatina posterior (C). O desajuste foi verificado com microscópio comparador (Leitz), em cinco pontos referenciais para cada corte. Os dados obtidos foram submetidos à análise estatística e ao teste de Tukey (5%). O dispositivo RS de contensão produziu níveis médios de adaptação (0,168 mm) com diferença estatística significativa (p<0,05) quando comparado com a prensagem convencional (0,215 mm), independente dos demais fatores.O dispositivo RS de contensão produziu níveis médios de adaptação (imediata = 0,173 mm e seis horas = 0,164 mm) com diferença estatística significativa (p<0,05) quando comparado com a prensagem convencional (imediata= 0,213 mm e seis horas= 0,216 mm). No fator corte, o dispositivo RS de contensão produziu valores (A = 0,140 mm, B= 0,183 mm e C= 0,256 mm) com diferença estatística significativa (p<0,05) quando comparado com a prensagem convencional (A= 0,151mm, B= 0,207 mm e C= 0,286 mm). Dentro do fator corte, a polimerização imediata produziu valores (A= 0,140 mm, B= 0,183 mm e C= 0,256 mm) sem diferença estatística significativa (p>0,05) quando comparada com a após seis horas (A= 0,193 mm, B= 0,187 mm e C= 0,244 mm). Independente dos demais fatores, os cortes A (0,140 mm), B (0,185 mm) e C (0,250 mm) foram diferentes estatisticamente entre si (p<0,05) / Abstract: The purpose of this study was to verify the denture base adaptation, made with Clássico heat-cured acrylic resin influenced by packing (conventional and RS tension system) and polymerization time (immediate and after 6 hours) variables. Forty stone plaster-acrylic resin base sets were randomly assigned in 4 groups of 10 elements and inc1uded in metallic frasks by routine technique, in order to receive the following experimental treatments: Group 1- acrylic resin packing and immediate polymerization in heated water at 74°C during 9 hours. Group 2- acrylic resin packing and polymerization after 6 hours in heated water at 74°C during 9 hours. Group 3­acrylic resin packing using RS tension system and immediate polymerization in heated water at 74°C during 9 hours. Group 4- acrylic resin packing using RS contension system and polymerization after 6 hours in heated water at 74°C during 9 hours The resin bases were fixed on stone casts with instantaneous adhesive, and transversally cuts were made in the corresponding regions to distal of bicuspids (A), mesial of the first molars (B), and posterior palatal region (C). The dimensional alteration between acrylic resin base and stone plaster was verified with a comparator microscope at 5 referential points to each kind of cut. The data submitted to ANOV A and Turkey's test at 5% of significance level showed that the RS tension system produced better adaptation level (0.168 mm) with statistical significance (p<.05) when compared to conventional packing (0.215 mm), independently of other factors. For polymerization time, the RS tension system produced better adaptation level (immediate 0.173 mm and after 6 hours 0.164 mm) with statistical significance (p<.05) when compared to conventional packing (immediate 0.213 mm and after 6 hours 0.216 mm). In the cuts, the RS tension system produced values (A= 0.129 mm, B= 0.162 mm, and C= 0.214 mm) with statistical difference (p<.05) when compared to conventional packing (A= 0.151 mm, B= 0.207 mm, and C= 0.286 mm). The immediate cure showed values (A= 0.140 mm, B= 0.183 mm, and C= 0.256 mm) with no statistical difference (p>.05) when compared to those after 6 hours (A= 0.139 mm, B= 0.187 mm, and C= 0.244 mm). Independently ofthe other factors, the A (0.140 mm), B (0.185 mm), and C (0.250 mm) cuts showed values with significative statistical difference / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador : Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de odontologia de Piracicaba / Made available in DSpace on 2018-07-27T15:34:55Z (GMT). No. of bitstreams: 1 Rahal_JulianaSaab_M.pdf: 22535090 bytes, checksum: 39a809ca29df4141a4b253da61f9b1aa (MD5) Previous issue date: 2001 / Resumo: O objetivo deste estudo foi avaliar a influência das técnicas de polimento (mecânico e químico), sobre as propriedades (rugosidade superficial, absorção de água, e solubilidade) de 4 resinas acrilicas ativadas termicamente. Foram confeccionadas 80 amostras, medindo 50mm de diâmetro e 0,5mm de espessura, divididas em 4 grupos: 1) resina Clássico (CL) -banho de água a 74±1°C por 9h; 2) QC-20 (QC) - água em ebulição por 20min; 3) Acron MC (AC) - forno de microondas a 500W por 3min; e 4) Onda Cryl (ON) - forno de microondas por 3min a 40% da potência máxima, 4min à potência 0 e 3min a 60% da potência máxima. Após a polimerização e desinclusão, as amostras receberam acabamento. Em seguida, foram subdivididas em 2 grupos de polimento: 1) mecânico (PM) - pedra-pomes e água, com escova macia; branco de espanha e água, com roda de flanela, em tomo de bancada, e 2) químico (PQ) - fluido para polimento, em polidora química. As leituras de rugosidade superficial foram realizadas em rugosímetro Surf Corder SE 1700. As amostras foram então submetidas à 1ª dessecação seguida de armazenagem em água destilada a 37 ±1°C pelos períodos de: 1h, 1 dia, 1, 2, 3 e 4 semanas. Ao término de cada período, foi realizada a mensuração da absorção de água. Ao final das 4 semanas, foi realizada a 2ª dessecação para cálculo da solubilidade. Os dados obtidos foram analisados estatisticamente por Análise de Variância e aplicado o Teste de Tuckey. Os resultados médios obtidos para rugosidade superficial (µm), absorção de água (%) e solubilidade (%), respectivamente, foram: CL-PM: 0,0350, 1,92 e 0,02; CL-PQ: 0,2298, 1,98 e 0,52; QCPM: 0,0307, 2,31 e -0,05; QC-PQ: 0,1792, 2,32 e 0,25; AC-PM: 0,0312, 2,45 e -0,07; AC-PQ: 0,2700, 2,43 e 0,41; ON-PM: 0,0321, 2,32 e -0,06; ON-PQ: 0,2949,2,34 e 0,27. Estes valores pennitiram concluir que: o polimento mecânico promoveu rugosidade superficial e grau de solubilidade significativamente menor em resinas acrilicas que o polimento químico; a absorção de água foi inicialmente maior nas amostras polidas quimicamente, mas ao final de 4 semanas, as proporções de absorção para todos os grupos foram semelhantes / Abstract: The aim of the present study was to evaluate the polishing (mechanical and chemical) methods influence on properties (surface roughness, water sorption and solubility) of 4 heat cured denture base acryli c resins. 80 samples were prepared, with 50mm diameter and 0,5mm thickness. They were divided in 3 groups: 1) Clássico resin (CL) - water bath at 74±1°C for 9h; 2) QC 20 (QC) - boiling water for 20min; Acron MC (AC) - microwave oven at 500W for 3min; 4) Onda Cryl (ON) - microwave oven for 3min at 40% of greatest potency, 4min at 0 potency and 3min at 60% of greatest potency. After cured and deflasked, the samples were grounded and subdivided in 2 groups: mechanical polishing (PM) - purnice slurry, chalk powder, soft brush and felt cone, at a bench vise, and chemical one (PQ) - proper fluid at a chemical polisher. Surface roughness was measured in a Surf Corder SE 1700 rugosimeter. Thus, the samples were submitted to a first desiccationprocess followed by storage at 37±1°C distilled water for lh, 1 day, 1,2,3 and 4 weeks. Concluding each period, it was conduced the water sorption measurement. In the end of the fourth week, a second desiccation process was done to calculate the solubility values. Data collected were statistically analyzed by Variance Analysis followed by Tuckey's Test. Means of surface roughness (µm), water sorption (%) and solubility (%), respectively, were: CL-PM: 0,0350, 1,92 e 0,02; CL-PQ: 0,2298, 1,98 e 0,52; QC-PM: 0,0307,2,31 e -0,05; QC-PQ: 0,1792,2,32 e 0,25; AC-PM: 0,0312,2,45 e -0,07; AC-PQ: 0,2700,2,43 e 0,41; ON-PM: 0,0321,2,32 e -0,06; ON-PQ: 0,2949,2,34 e 0,27. It could be concluded that mechanical polishing promoted surface roughness and solubility of acrylic resins values significantly lowers than chemical polishing; besides the higher water sorption at chemically polished samples initially, after 4 weeks of storage the water sorption proportions for all groups were similar / Mestrado / Protese Dental / Mestre em Clínica Odontológica

O comportamento termodinâmico, assim como as propriedades físicas e químicas da resina acrílica, podem ser diferentes quando termopolimerizadas por diferentes métodos, podendo ser analisado através do monitoramento da temperatura em função do tempo de termopolimerização, do grau de porosidade, dureza Knoop (0,015 Kg) e quantidade de monômero residual. No presente trabalho foram avaliados o comportamento termodinâmico e algumas propriedades físicas e químicas de duas resinas acrílicas, termopolimerizadas em água aquecida e por energia de microondas. As resinas acrílicas Clássico&#63194; e Onda Cryl&#63194; foram termopolimerizadas em água aquecida pelo método clássico de Tuckfield, Worner e Guerin64 em 1943 (TWG) e através da energia de microondas a 520 W – 10 minutos, segundo Nishi44 em 1968 (MW). A temperatura da termopolimerização em função do tempo foi monitorada por termopares de cobre / constantan conectados a aparelhos eletrônicos e computacionais. Os termopares foram instalados dentro da massa de resina acrílica, da água e do revestimento de gesso. Os 22 espécimes de resina acrílica, medindo 65 / 49 / 5 mm, foram analisados sobre o grau de porosidade, dureza Knoop e quantidade de monômero residual. Os resultados foram submetidos a análise estatística através dos testes Mann – Whitney e “t” de Student. Houve diferença significante na temperatura máxima das termopolimerizações TWG e MW, na incidência de porosidade e na quantidade de monômero residual, já a dureza Knoop não apresentou diferença significante. A resina acrílica quando termopolimerizada pelas microondas sofreu um rápido aquecimento, alcançando temperaturas de 155o C, com alta incidência de porosidade, enquanto na termopolimerização em água aquecida, a temperatura máxima foi de 101,2o C, com isenção de porosidade. A maior quantidade de monômero residual foi detectada nos espécimes termopolimerizados pelo método MW. O comportamento termodinâmico da resina acrílica no método MW foi inadequado, caracterizado pela alta incidência de porosidade, menor dureza Knoop e maior quantidade de monômero residual. / Acrylic resins of the methyl methacrylate present unsuitable thermodynamic behavior during thermal polymerization mainly if the temperature exceed boiling point (100.8o C), what brings about an increase to the degree of porosity. The thermodynamic study was carried out with acrylic resins Clássico&#63194; and Onda Cryl&#63194;, thermal polymerized by water bath (3 hours, Tuckfield, Worner and Guerin in 1943) and by microwave (520 W – 10 minutes, Nishi in 1968). The temperature of the thermal polymerization was recorded by thermocouples (copper / constantan) and monitored by electric - electronically equipment and computers. The 2.0 mm spherical thermocouples were placed into acrylic resin and gypsium investment and the thermal polymerization was monitored. Twenty-two specimens (65 / 49 / 5 mm) were obtained after finishing and polishing and the degree of porosity was analyzed stabilizing temperature parameters in thermal polymerizations. Was analysis to hardness Knoop, by hardness machine Testor (Otto Wolpert – Werke) and residual monomer was analysis in the spectrophotometer U.V. (Ultrospect 2000 U.V. Pharmacia – Biotech). Statistical analysis was performed using Mann - Whitney and “t” Student tests. Significant difference was observed in the degree of porosity. residual monomer and maximum temperature between thermal microwave polymerization and polymerization by water bath. The microwave thermal polymerized acrylic resin quickly heated to 155o C and showed high incidence of porosity, whereas in thermal polymerization by water bath the maximum temperature reached 101.2o C and specimens were porosity free. According to the power and time used in the present study, the thermal polymerization by microwave irradiation showed unsuitable thermodynamic behavior, characterized by high incidence of porosity, least hardness and greater amount residual monomer.