Randdichtheit und Randqualität von Kl. II-Füllungen aus einem Siloran bzw. konventionellen Kompositen unter Verwendung eines selbstkonditionierenden Dentinhaftvermittlers ohne vorherige Schmelz- oder Dentinätzung in vitro. / Microleakage and marginal integrity of class II restorations using a silorane compared to methacrylate based resin composites luted with self-etch or an etch and rinse adhesive in vitroGura [geb. Küstermann], Katharina January 2013 (has links) (PDF)
Um die Schrumpfung von Kompositen weiter zu verringern, wechselten die Hersteller von der herkömmlichen methacrylatbasierten Harzmatrix zur Siloranchemie. Durch kationische, ringöffnende Polymerisation anstatt radikalischer Polymerisation wird die räumliche Annäherung der Monomere verringert und eine Schrumpfung von weniger als 1% ermöglicht.
In der vorliegenden in vitro Studie wurde die Randqualität und die Randdichtigkeit eines Silorans untersucht und mit klinisch bereits erfolgreich eingesetzten methacrylatbasierten Kompositen (Filtek™Supreme, Clearfil AP-X, Tetric®EvoCeram) verglichen. Lediglich in einer Kontrollgruppe (Filtek™Supreme/Scotchbond 1XT) wurde eine Konditionierung nach der total-etch Technik angewandt, in den anderen Gruppen wurde mit den markeneigenen selbstätzenden Adhäsivssystemen gearbeitet (Siloran/ Siloran System Adhesive; Filtek™Supreme/Scotchbond SE; Clearfil AP-X/ Clearfil SE; Tetric®EvoCeram/AdheSE).
Insgesamt 100 menschliche, kariesfreie dritte Molaren wurden in 10 Gruppen aufgeteilt, gereinigt und gesockelt. Es wurden standardisierte MOD-Kavitäten von 4 mm Tiefe und 3,5 mm Breite präpariert. Auf einer Seite reichte der approximale Kasten bis in das Wurzeldentin unterhalb der Schmelz-Zement-Grenze, auf der anderen Seite endete er im Schmelz. Die approximalen Kästen wurden mit Hilfe einer Bevelshape Feile ca. 1mm breit angeschrägt. Zum Füllen wurden die Zähne in ein Gerät zur Simulation der Nachbarzahnsituation eingespannt und entsprechend den Herstellerangaben konditioniert. In der Kontrollgruppe erfolgte zusätzlich eine Schmelzätzung von insgesamt 30 Sekunden und 15 Sekunden Dentinätzung. In insgesamt 8 Schichten wurden anschließend die Füllungen gelegt, in der Hälfte der Gruppen wurde dabei mit markeneigenen fließfähigen Kompositen im Sinne der lining-Technik gearbeitet. Zum Ausarbeiten wurden die Zähne aus dem Approximalkontaktsimulator herausgenommen, sichtbare Überschüsse mit dem Scaler entfernt und die Restaurationen anschließen mit Silikonspitzen poliert. Insgesamt 28 Tage wurden die Testzähne bei 37 Grad Celsius in physiologischer Kochsalzlösung gelagert, nach der Hälfte der Zeit wurden sie 2500 Zyklen Temperaturwechselbelastung (5°/55° jeweils 30 Sekunden) unterzogen.
Für die Untersuchung unter dem Rasterelektronenmikroskop wurden Kunstharzreplika hergestellt, auf REM-Träger aufgeklebt und mit Gold bedampft. Bei 100-1000facher Vergrößerung wurden diese dann auf kontinuierlichen Rand, Randspalt, Überschuss, Unterschuss und (im Dentin) auf kontinuierlichen Randanteil mit Wasserblasen hin untersucht.
Nach der Farbstoffpenetration mit Silbernitrat wurden die Zähne geschnitten und die Diffusionsstrecke am Füllungsrand entlang unter einem Auflichtmikroskop fotografiert und mit einer Bildverarbeitungssoftware vermessen.
Die Untersuchung der Randdichtigkeit mittels Farbstoffpenetration ergab keine signifikanten Unterschiede zwischen den Gruppen mit und ohne fließfähiges Komposit. Die Analyse der Randqualität zeigte nur bei Filtek™Supreme mit Scotchbond SE mit Flowable in den axialen Randanteilen signifikant mehr kontinuierlichen Rand als ohne fließfähiges Komposit. Sonst hat die lining- Technik keinen Einfluss auf die Randqualität gezeigt.
Im Vergleich der verschiedenen methacrylatbasierten Komposite bei alleiniger Verwendung von selbstätzenden Adhäsivsystemen war Clearfil AP-X häufig überlegen. Bereits in anderen Studien wurde gezeigt, dass Clearfil AP-X und das Adhäsiv Clearfil SE Bond exzellente Randqualität liefern.
Das Siloran kann in dieser Studie gut mit klinisch erfolgreich eingesetzten Kompositen wie Filtek™Supreme und Tetric®EvoCeram mithalten. Die Ergebnisse von Clearfil AP-X sind aber zumindest bei der REM-Untersuchung häufig überlegen. Bei der Farbstoffpenetration erwiesen sich die Ränder der Siloranfüllung als ebenso dicht wie bei der Kontrollgruppe mit total-etch Technik. Auch andere Untersuchungen erbrachten bereits den Nachweis, dass Siloran mit dem selbstätzenden Siloran Systeme Adhesive ähnlich gute Ergebnisse erzielt wie methacrylatbasierte Komposite. Die Überlegenheit des neuen Materials, das sich durch seine niedrige Schrumpfung auszeichnet, konnte hier allerdings nicht gezeigt werden. Es gilt weitere Ergebnisse abzuwarten, ob zusätzliche Phosphorsäureätzung bei Verwendung des Silorans noch bessere Randqualität bringt.
Der direkte Vergleich zwischen Filtek™Supreme einmal mit den selbstätzenden Adhäsivsystem Scotchbond SE und einmal mit Scotchbond 1XT und Anwendung der total-etch Technik zeigte, dass sich im Schmelz durchaus eine signifikant bessere Randqualität ergeben kann als ohne Phosphorsäureätzung. / Microleakage and marginal integrity of class II restorations using a silorane compared to methacrylate based resin composites luted with self-etch or an etch and rinse adhesive in vitro
|
2 |
Randschluss von Klasse V Kavitäten nach neunmonatiger Lagerung der Adhäsivsysteme bei Raumtemperatur / Marginal gaps of class V cavities after Storage of the adhesives at room temperature for nine monthsSpelmanns, Dominik January 2011 (has links) (PDF)
Der entscheidende Faktor für den Langzeiterfolg einer Kompositfüllung ist der Verbund zwischen Zahnhartsubstanz und Füllungsmaterial. Ziel dieser Untersuchung war die In-Vitro-Evaluation der Randadaptation von Klasse V Kavitäten nach neunmonatiger Lagerung von 8 All-In-One Adhäsiven bei Raumtemperatur. Zu diesem Zweck wurden von 80 extrahierten Zähnen Klasse V Kavitäten hergestellt. Sie wurden in 8 Gruppen eingeteilt ( Adper Prompt L-Pop, 3M ESPE; iBond, Heraeus Kulzer; Clearfil S3 Bond, Kuraray Dental; Optibond Fl, Kerr; Xeno V, Densply; Filtek Silorane, 3M ESPE). Nach künstlicher Alterung wurden diese quantitativ und qualitativ mittels Farbstoffpenetration und unter dem Elektronenmikroskop untersucht. Ein negativer Einfluss der Lagerung der Adhäsive konnte sowohl für die All-In-One Adhäsive, als auch für die Etch-Rinse Systeme nachgewiesen werden. Verantwortlich hierfür sind vermutlich hydrolytische Prozesse, welche besonnders in den schwierigen Lösungszusammensetzungen der All-In-One Systeme zur Geltung kommen. Präparate wie Xeno V, welche lagerstabilere Methacrylamide verwenden, weisen zwar bessere Ergebnisse auf, lösen das Problem aber nicht vollständig. / Objectives : to evaluate the storage stability of eight adhesives after nine months. Methods : standardized class V cavities were prepared in 80 extracted human molars. These were filled with 8 different adhesives but the same composit (Adper Prompt L-Pop, 3M ESPE; iBond, Heraeus Kulzer; Clearfil S3 Bond, Kuraray Dental; Optibond Fl, Kerr; Xeno V, Densply; Filtek Silorane, 3M ESPE ). The adhesives were stored at room temperature for nine months. After water storage (12 weeks) and interuppted thermocycling, the margin quality was evaluated in the SEM using the replica technique. Marginal seal was studied using dye penetration (AgNo3 50%). Results : after storage, all adhesives show significant more marginal gaps than before. Even adhesives that use new methacrylamides, which were more stable against hydrolysis can not solve this problem to be satisfactory.
|
3 |
Randdichtheit und Randqualität von Kl. II-Füllungen aus einem Siloran bzw. konventionellen Kompositen unter Verwendung eines selbstkonditionierenden Dentinhaftvermittlers bei vorheriger selektiver Schmelzätzung in vitro / Microleakage and marginal integrity of class II restorations using a silorane compared to methacrylate-based resin composites luted with self-etch adhesives after phosphoric acid etching of enamel in vitroSeidl, René January 2013 (has links) (PDF)
Die bei der Polymerisation adhäsiver Kompositrestaurationen unweigerlich auftretende Volumenschrumpfung und die damit verbundene Schrumpfungsspannung stellt ein bis heute grundlegendes Problem in der modernen Zahnerhaltung dar. Das Ziel dieser In-vitro-Untersuchung war es, die Randdichtheit und Randqualität von Klasse II - Füllungen aus dem schrumpfungsreduzierten Komposit FiltekTM Silorane mit denen konventioneller Komposite auf Methacrylatbasis unter Verwendung selbstkonditionierender Dentinhaftvermittler nach vorheriger selektiver Schmelzätzung zu vergleichen.
Hierzu wurden 80 extrahierte, menschliche Molaren mit standardisierten MOD-Kavitäten versehen und mit Hilfe einer Mehrschichttechnik gefüllt. Trotz Verwendung von Self-Etch-Adhäsivsystemen (Silorane System Adhesive (3M ESPE), AdheSE® (Ivoclar Vivadent), ClearfilTM SE Bond (Kuraray), AdperTM ScotchbondTM SE (3M ESPE)) wurde zusätzlich eine selektive Schmelzätzung mit 35%iger Phosphorsäure für 30 Sekunden durchgeführt. Als Füllungsmaterialien kamen das auf der Siloranchemie basierende Hybridkomposit FiltekTM Silorane (3M ESPE), sowie die konventionellen, methacrylatbasierten Komposite Tetric EvoCeram® (ein Nano-Hybridkomposit, Ivoclar Vivadent), ClearfilTM AP-X (ein Hybridkomposit, Kuraray) und FiltekTM Supreme XT (ein Nanokomposit, 3M ESPE) zum Einsatz. Eine vierwöchige Wasserlagerung bei 37°C und ein 2500 Zyklen umfassendes Thermocycling (5°C vs. 55°C) dienten der künstlichen Alterung. Zur Bewertung der Randdichtheit und der Randqualität wurden die Proben bzw. Replika der Füllungsflächen einer Farbstoffpenetration und einer Analyse unter dem Rasterelektronenmikroskop unterzogen. Die ermittelten Daten wurden mit Hilfe der nicht-parametrischen Rangvarianzanalyse (Kruskal-Wallis-Test) und dem Multiplen Mittelwertvergleich nach Nemenyi bei einem Signifikanzniveau von P < 0,05 ausgewertet.
Im Rahmen dieser Studie konnte kein signifikanter Unterschied bezüglich der Verwendung eines fließfähigen Komposits festgestellt werden.
Desweiteren zeigte FiltekTM Silorane abschnittsunabhängig die geringsten Penetrationstiefen. Möglicherweise ist hierfür die deutlich geringere Polymerisationsschrumpfung gegenüber den anderen Kompositen verantwortlich.
Hinsichtlich der Randqualität konnte FiltekTM Silorane jedoch nicht uneingeschränkt überzeugen. Während in den okklusalen und zervikalen Abschnitten noch überwiegend vergleichbare Ergebnisse erzielt wurden, zeigten sich insbesondere am axialen Füllungsrand häufiger Imperfektionen in Form von Randspalten. Möglicherweise ist das Silorane System Adhesive als essentielles Bindeglied aktuell noch nicht in der Lage eine ausreichende Haftwirkung am Zahn zu realisieren.
Zusammenfassend lässt sich sagen, dass FiltekTM Silorane mit seiner ringöffnenden Polymerisation in Kombination mit einem funktionierenden Adhäsivsystem durchaus das Potential besitzt, den nächsten Schritt auf dem Weg zum schrumpfungsfreien Komposit zu gehen. Maßgeblich für den klinischen Erfolg eines Restaurationsmaterials sind neben einer geringen oder gar fehlenden Volumenkontraktion allerdings noch zahlreiche andere material-, patienten- und behandlerabhängige Faktoren. Auch die Entwicklung eines mit der Siloranchemie kompatiblen Flowables wäre aus Sicht vieler potentieller Anwender sicherlich wünschenswert. / PURPOSE: Polymerization shrinkage is still a great problem in modern dentistry. This study aimed to analyze the microleakage and marginal integrity of class II restorations using a silorane compared to methacrylate based resin composites luted with self-etch adhesives after enamel etching.
METHODS: Eighty extracted caries-free human molars were used and evenly distributed into eight groups (N=10). Wide mod cavities were prepared in each molar. Four self-etching adhesives were used, after enamel etching with 35% phosphoric acid gel for 30 seconds. The adhesive materials were: Silorane System Adhesive (3M ESPE), AdheSE® (Ivoclar Vivadent), ClearfilTM SE Bond (Kuraray) and AdperTM ScotchbondTM SE (3M ESPE). The cavities were restored with a silorane-based microhybrid composite (FiltekTM Silorane (3M ESPE)) and three different methacrylate based composites (Tetric EvoCeram® (Ivoclar Vivadent), ClearfilTM AP-X (Kuraray), FiltekTM Supreme XT (3M ESPE)). Respectivly twenty cavities were filled with the same composite. One half with an additional flowable, one half without. The flowable composites were: FiltekTM Supreme XT Flowable (3M ESPE), Tetric EvoFlow® (Ivoclar Vivadent) and Clearfil MAJESTYTM Flow (Kuraray). Simulating clinical conditions the teeth were stored in water for four weeks at 37°C and subjected to 2500 thermal cycles of 5°C vs. 55°C in water with a 30-second dwell. After replicas were taken, two test procedures were carried out. Procedure A: a quantitative margin analysis in the scanning-electron microscopy (SEM) was performed at a magnification of 100 x using nine different criteria. Procedure B: the teeth were immersed in 50% AgNO3 solution at 37°C for two hours. Sectioned samples were examined under a stereomicroscope (EZ4 D, Leica Microsystems). Statistical analysis was performed with Kruskal-Wallis and Nemenyi’s test at 95% significance level.
RESULTS: FiltekTM Silorane exhibited the lowest values of dye penetration. Compared with methacrylat based resin composites FiltekTM Silorane showed a comparable due of continuous margins. No statistically significant difference was observed between groups filled with the same composite with and without an additional flowable composite.
|
4 |
Randdichtheit und Randqualität von Kl. II-Füllungen aus einem Siloran bzw. methacrylatbasierten Kompositen unter Verwendung eines selbstkonditionierenden Dentinhaftvermittlers bei vorheriger Schmelz- und Dentinätzung in vitro / Micro-leakage and marginal integrity of class II restorations using a silorane compared to methacrylate-based resin composites luted with self-etch adhesives after phosphoric acid etching of enamel and dentine in vitroHäfner [geb. Wagner], Daniela Claudia January 2017 (has links) (PDF)
Im Rahmen dieser In-vitro-Studie wurde Randdichtheit und Randqualität von plastischen Füllungsmaterialien aus einem schrumpfungsreduziertem Siloran (FiltekTM Silorane), zwei Hybridkompositen (Tetric EvoCeram® und ClearfilTM AP-X) und einem Nanokomposit (FiltekTM Supreme XT) mit den dazugehörigen Dentinadhäsivsystemen in Klasse II-Kavitäten mit einem von Schmelz und einem von Dentin begrenzten Füllungsrand untersucht. Obwohl die Hersteller die Dentinhaftvermittlermaterialien als selbstkonditionierend im Schmelz und Dentin vermarkten, wurde ein Total-Etching durchgeführt. Dessen Auswirkungen auf die Systeme sollte im Vergleich zu den früheren Arbeiten mit selektiver Schmelzätzung bzw. Selbstkonditionierung nach Herstellerangabe untersucht werden.
An 80 extrahierenten dentes sapientes wurden Klasse II-Kavitäten nach Black präpariert, die eine Ausdehnung von 3,5 mm in vestibulo-oraler Richtung und eine okklusale Tiefe von 4 mm besaßen. Mesial wurde die okklusale Tiefe von 4 mm beibehalten, distal endete die Kavität an der Schmelz-Zement-Grenze. Die approximalen Schmelzränder wurden auf einer Breite von 1 mm angeschrägt. Die okklusal-zervikale Ausdehnung variierte je nach Ausdehnung der klinischen Krone zwischen 5 und 7 mm.
In Inkrementtechnik wurden die Füllungen gelegt und ausgearbeitet. Die Materialien wurden wie folgt kombiniert: Silorane System Adhesive / FiltekTM Supreme XT / FiltekTM Silorane, Silorane System Adhesive / FiltekTM Silorane, AdperTM ScotchbondTM SE / FiltekTM Supreme XT Flow / FiltekTM Supreme XT Universalrestaurationsmaterial, AdperTM ScotchbondTM SE / FiltekTM Supreme XT Universalrestaurationsmaterial, ClearfilTM SE Bond / ClearfilTM AP-X, Clear-filTM SE Bond / Clearfil MajestyTM Flow / ClearfilTM AP-X, AdheSE® Bond / Tetric EvoFlow® / Tetric EvoCeram®, AdheSE® Bond / Tetric EvoCeram®.
Nach 15-tägiger Lagerung in 0,9 %-iger Kochsalzlösung bei 37°C wurden die Proben einer Temperaturwechselbelastung (2500 Zyklen bei 5°C und 55°C, Verweilzeit 30 s) unterzogen. Im Anschluss an das Thermocycling erfolgte eine weitere 15-tägige Lagerung in Kochsalzlösung bei 37°C.
Nach Herstellung von Replika zur Untersuchung der Randqualität unter dem Elektronenmikroskop wurde ein Farbstoffpenetrationstest zur qualitativen Randanalyse durchgeführt. Hierzu wurden die Zähne in 50 Gewichts-% AgNO3-Lösung eingelegt, belichtet und in zwei Ebenen (mesial-distal und bukkal-lingual) geschnitten. Die Auswertung erfolgt mit einem Auflichtmikroskop.
Die statistische Auswertung erfolgte mit nicht-parametrischen Testverfahren wie dem Wilcoxon-Vorzeichen-Rang-Test und dem Kruskal-Wallis-Test. Unter-schiede zwischen den einzelnen Versuchsgruppen wurden mit dem multiplen Mittelwertsvergleich nach Nemenyi ermittelt. Das Signifikanzniveau war p<0,05.
Filtek™ Silorane ist den anderen Kompositen nicht überlegen.
Unabhängig vom verwendeten Material hat die Lage des Füllungsrandes im Zahn entscheidenden Einfluss auf die Randdichtheit und Randqualität bei Klas-se II-Füllungen. Die Anzahl der Randspalten und die Farbstoffpenetration sind okklusal am geringsten (im Mittel 2%), dafür aber der prozentuale Anteil der Überschüsse am größten (im Mittel 36%). Randdichtheit und Randqualität sind im Schmelz besser als im Dentin.
Weder unter dem Elektronenmikroskop, noch unter dem Auflichtmikroskop, konnte ein Unterschied von statistischer Signifikanz zwischen der Verwendung und der Nichtverwendung eines Flowables zur Verbesserung der marginalen Integrität aufgezeigt werden.
Das Hybridkomposit Tetric EvoCeram® schnitt beim Farbstoffpenetrationstest und der rasterelektronenmikroskopischen Untersuchung schlechter ab als das Filtek™ Silorane sowie als das Universalhybrid- und Nanokomposit. / Aim of this study was to analyse the micro-leakage and marginal integrity of class II restorations using a silorane compared to methacrylate-based resin composites luted with self-etch adhesives after phosporic acid etching of enamel and dentine in vitro.
Eighty extracted human molars were used, divided into eight groups at ten molars. After preparing mod cavities, the teeth were filled with: Silorane Systeme Adhesive and FiltekTM Silorane, AdperTM ScotchbondTM SE and FiltekTM Supreme XT, ClearfilTM SE Bond and ClearfilTM AP-X, AdheSE® Bond and Tetric EvoCeram®. In four groups, an additional flowable was used.
After artificial aging, a quantitative margin analysis was performed by means of a scanning electron microscope (SEM). After storage in AgNO3 solution, dye penetration was examinated under a stereomicroscope.
Results: FiltekTM Silorane is not better than the other composites. Tetric EvoCeram® showed the highest values of dye penetration. No statistically significant difference was observed between groups filled with the same composite with and without an additional flowable composite. The location of the restorative junction in the tooth strongly influence the marginal integrity and quality.
|
5 |
Untersuchung zur Passgenauigkeit CAD/CAM-gefertigter Kronengerüste in Abhängigkeit von den verwendeten Materialien / Marginal fit analysis of CAD/CAM fabricated crown frameworks depending on the used materialsGronau, Karin Christine 30 June 2015 (has links)
No description available.
|
6 |
Der Einfluss von Brauchwasserdesinfektionsmitteln zahnärztlicher Behandlungseinheiten auf das Randschlussverhalten von Kompositfüllungen mit selbstätzenden Dentinadhäsiven. / The influence of disinfectants in dental unit waterlines on the marginal adaption of direct composite resins with self-etching adhesives.Schäfer, Sabine 12 December 2011 (has links)
No description available.
|
7 |
Der Einfluss von Kavitätenvolumen, Polymerisationsschrumpfung und Schichttechnik auf die Randschlussqualität von Klasse-II-Kompositfüllungen / The influence of cavity depth, polymerization shrinkage and application technique on marginal seal and margin fidelity of class II resin-based composite restorationsZentgraf, Christian January 2008 (has links) (PDF)
Die Randspaltbildung adhäsiver Restaurationen stellt bis heute ein grundlegendes Problem dar. Ziel dieser Untersuchung war die In-vitro-Evaluation der Randadaptation von Klasse-II-Kompositfüllungen nach künstlicher Alterung in Abhängigkeit von Kavitätentiefe, Komposit und Schichttechnik. Zu diesem Zweck wurden an 48 extrahierten Weisheitszähnen mittels sonoabrasiven Präparationsinstrumenten zwei unterschiedlich standardisierte Klasse-II-Kavitäten (flache Kavität bzw. tiefe Kavität) hergestellt. Diese wurden mit Hilfe zweier Schichttechniken (Drei-Schicht-Technik bzw. Schalentechnik) und zweier Komposite (Hybridkomposit (Tetric Ceram, Ivoclar) bzw. Nano-Hybridkomposit (Grandio, Voco)) gefüllt. Nach künstlicher Alterung mittels Thermocycling und Wasserlagerung wurden die Proben zur Beurteilung der Randadaptation mittels Farbstoffpenetration und unter dem Rasterelektronenmikroskop qualitativ und quantitativ bewertet. Die Ergebnisse wurden mittels dreifaktorieller Varianzanalyse auf statistische Signifikanz untersucht. Ein Einfluss des Kavitätenvolumens auf die Randadaptation konnte in dieser Studie nicht eindeutig nachgewiesen werden. Es zeigte sich jedoch am vertikalen Rand eine signifikant schlechtere Randadaptation aufgrund der häufigeren Ausbildung eines Spalts bei großem Kavitätenvolumen. Bezüglich der Schichttechnik konnte ein Einfluss auf die Randqualität gezeigt werden: Bei beiden Auswertungsmethoden war die Schalentechnik signifikant gegenüber der Drei-Schicht-Technik überlegen. Ebenfalls konnte ein Einfluss des Komposits auf die Randadaptation nachgewiesen werden: Keines der beiden getesteten Komposite war generell überlegen; es zeigte sich vielmehr eine signifikante Abhängigkeit von Komposit und Schichttechnik. Das Hybridkomposit zeigte gegenüber dem Nano-Hybridkomposit bessere Randqualitäten bei den mit Hilfe der Schalentechnik gefüllten Kavitäten. Bei den mittels Drei-Schicht-Technik gefüllten Kavitäten schnitt hingegen das Nano-Hybridkomposit besser ab. Dies ist wahrscheinlich darauf zurückzuführen, dass das Hybridkomposit seine Fähigkeit zum Nachfließen während der Polymerisation, welche auf sein geringes E-Moduls zurückzuführen ist, in Schichten mit kleinem C-Faktor ausnutzen und so seine größere Volumenschrumpfung ausgleichen kann. Schichtungen mit großem C-Faktor verringern die Möglichkeit des Nachfließens und das Nano-Hybridkomposit zeigt dort bessere Randadaptation aufgrund seiner niedrigeren Volumenschrumpfung. Diese Studie konnte zeigen, dass sowohl Materialeigenschaften wie Volumenschrumpfung und E-Modul als auch der C-Faktor - und damit verbunden die Füllungstechnik - entscheidenden Einfluss auf die Randadaptation von in vitro gelegten Füllungen in standardisierten Klasse-II-Kavitäten haben. Die Studie stellte heraus, dass diese drei Faktoren (Volumenschrumpfung, E-Modul und C-Faktor) nicht getrennt voneinander betrachtet werden sollten. Es zeigte sich, dass für Klasse-II-Kavitäten die Schalentechnik signifikant überlegen in Bezug auf die Randschlussqualität ist; dies gilt insbesondere für das Hybridkomposit „Tetric Ceram“. / Objectives: To evaluate the influence of cavity depth, polymerization shrinkage and application technique on marginal seal and margin fidelity of class II resin-based composite restorations. Methods: Standardized MOD class II cavities were prepared in extracted human molars. Occlusal boxes were 3.5mm wide and either 3mm or 4.5mm deep. Standardized interproximal boxes (box size: 3.5x4.5mm, bevel size 5.5x5.5mm) were prepared using sonic shape preparation instruments (SonicSys Approx Size 3) and reciprocating files (Bevelshape B15C). After application of a 3-step etch&rinse adhesive (Optibond FL), the cavities were restored using a resin-based composite of high (Tetric Ceram, 2.8%) or low polymerization shrinkage (Grandio, 1.6%). Interproximal boxes were restored using either a centripetal or a horizontal layering technique. After water storage (30 days, 37°C) and thermocycling (2500x 5-55°C), margin quality was evaluated in the SEM using the replica technique. Marginal seal was studied using dye penetration (AgNO3 50%, 2h, 37°C). For each combination of parameters six specimens were prepared. Results were analyzed using 3-way ANOVA. Results:The centripetal layering technique produced less dye penetration (P<0.01) and margin gaps (P<0.001) than the horizontal layering technique. This difference was more pronounced for the high shrinkage composite (interaction: P<0.05 / P<0.001).
|