Caracterização microestrutural e modelagem do amaciamento dinâmico a quente do aço inoxidável austenítico ASTM F 138, utilizado em implantes ortopédicos / Microtructural characterization and modeling of hot working dynamic softening of the ASTM F 138 austenitic stasinless steel biomaterialGeronimo, Fabio Henrique Casarini 10 July 2014 (has links)
Made available in DSpace on 2016-06-02T19:10:29Z (GMT). No. of bitstreams: 1
6680.pdf: 8910629 bytes, checksum: 2223220bfe27cba5df32a8d026e02fc8 (MD5)
Previous issue date: 2014-07-10 / Financiadora de Estudos e Projetos / Flow stress curves of ASTM F 138 austenitic stainless steel were obtained through isothermal hot torsion testing in the temperature range of 900- 1200oC and in the strain rate range of 0,01-10s-1, totaling 24 experiments. To understand the dynamic softening during hot working of this material, the shape of the flow stress curves and the parameters required to calculate activation energy for hot working were evaluated. Also, the semi-empirical equations describing these parameters as function of Zener-Hollomon parameter (Z) were obtained. Mathematical modeling of flow stress curves was developed taking into account the recovery parameter r and the Avrami exponent n. Processing maps were constructed using the Dynamic Materials Model. The attained microstructures were analyzed by optical microscopy and the microstructure evolutions under some processing conditions were evaluated by EBSD technique. These procedures were also used to obtain the recrystallized fraction, to identify what softening mechanism was operating and in which conditions it becomes more active. Due to the intermediate stacking fault energy level in this material (78mJ/m2), attained data indicate that dynamic softening occurs in a balance between dynamic recovery and dynamic recrystallization, with temperature having a determining role. At higher Z, extended dynamic recovery takes place and dynamic recrystallization becomes incomplete due to plastic instabilities such as localized flow. Lower Z values offer favorable conditions for complete dynamic recrystallization, even if were necessary to impose large straining. / As curvas de escoamento plástico do aço inoxidável austenítico ASTM F 138 foram obtidas por meio de ensaios de torção a quente isotérmicos contínuos, com temperaturas na faixa de 900 a 1200oC e taxas de deformação (&) variando entre 0,01 e 10s-1, totalizando 24 ensaios. Com o intuito de compreender o amaciamento dinâmico deste material em altas temperaturas, as curvas foram avaliadas quanto à forma e foram determinados os parâmetros necessários para calcular a energia de ativação aparente para a deformação a quente e as equações semi-empíricas em função do parâmetro Z, de Zener- Hollomon. Realizou-se a modelagem matemática das curvas de escoamento plástico em função do parâmetro de recuperação r e da cinética de recristalização de Avrami de acordo com o expoente n, e os mapas de processamento deste aço foram construídos. As microestruturas resultantes dos ensaios foram analisadas por microscopia óptica e avaliou-se a evolução microestrutural em algumas condições de processamento por meio da técnica de EBSD a fim de obter a fração recristalizada do material, além de identificar os mecanismos de amaciamento atuantes e em quais condições de processamento estes se tornam mais efetivos. Pelo fato deste material possuir um valor intermediário de energia de falha de empilhamento (78mJ/m2), os resultados, quando avaliados em conjunto, indicam que o amaciamento ocorre num balanço entre recuperação e recristalização dinâmica, com a temperatura exercendo um papel fundamental neste aspecto. Para os maiores valores de Z, a recuperação dinâmica avança até deformações elevadas e a recristalização dinâmica não se completa devido à instabilidade plástica causada por fluxo localizado, enquanto que para menores valores de Z, as condições tornam-se mais favoráveis à recristalização, mesmo que necessitando de altas deformações para se completar.
|
2 |
Estudo microestrutural em mineralização aurífera do tipo-veio hospedada em zona de cisalhamento: caso do depósito Sertãozinho, província Borborema, NE do BrasilAlmeida, Harrizon Lima de [UNESP] 15 August 2003 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:32:21Z (GMT). No. of bitstreams: 0
Previous issue date: 2003-08-15Bitstream added on 2014-06-13T20:23:37Z : No. of bitstreams: 1
almeida_hl_dr_rcla.pdf: 806140 bytes, checksum: 7940276ecd62a931d89c15464ccc97db (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / A zona de cisalhamento Itapetim (ZCI) desenvolveu foliação e lineação nos diferentes tipos de rochas, milonitos a ultramilonitos. Muitos dos tipos de microestruturas observadas na ZCI preservam evidências de condições metamórficas de alto grau e baixo grau de temperatura. O padrão das orientações preferenciais dos eixos [c] de quartzo, obtida a partir de agregados policristalinos deformados, mostra dois diferentes tipos de simetrias, guirlandas do tipo I e simples. A análise da textura sugere partição da deformação com cisalhamento coaxial e não coaxial na ZCI. Um veio de quartzo mineralizado em ouro encaixado em rocha ultramilonítica, constitui a zona de precipitação hidrotermal. O veio é bandado por segmentos de turmalina, o qual inclui agregados de grãos de quartzo maciço entre as bandas. Os grãos de quartzo mostram contatos poligonais e restritos limites intumescentes. O último sugere recristalização dinâmica por migração de limite de grão e os grãos poligonais (microestrutra em espuma) são melhor explicados por annealing. Os padrões de eixos [c] de quartzo obtido no veio aurífero é idêntico ao observado nos ultramilonitos da ZCI. Este padrão é interpretado como uma textura preservada formada durante o cisalhamento não coaxial. A estrutura bandada é interpretada como o resultado de variações da pressão de fluidos e a formação microfraturas, associadas a eventos de crack-seal. Mecanismos de crack-seal foram ativos antes ou durante a deformação da ZCI. As feições microestruturais suportam evidências para a última possibilidade. / The Itapetim shear zone(ISZ) developed both foliation and lineation in the different rock types, from mylonites to ultramylonites. Most of the microstructure types observed in the ISZ preserve evidence of high temperature metamorphic conditions. The quartz [c]-axis, of deformed polycrystalline aggregates, show two distinct symmetries, type I crossed girdles and single girdles. The geometrical analysis of texture, suggest non-coaxial shear for deformation in ISZ. A gold mineralized quartz vein hosted in ultramylonitic rocks, constitutes the hydrothermal precipitation zone. The vein is banded by tourmiline segments, which include massive quartz grains aggregates between the bands. The quartz grains show polygonal contacts and minor intumescent limits. These latter suggest grain boundary migration recrystallization and the polygonal grains seem to be best explained by the annealing after stopping the shear deformation. The quartz [c]-axis obtained in the auriferous vein shows the same single girdle pattern observed in the ultramylonites of the ISZ. This pattern is interpreted as a preserved texture formed during the shear deformation. The banded structure is interpreted as the result of variations of the fluid pressure and the formation of microfractures, associated the crack-seal events. Crack-seal mechanisms can have been active previous or during the deformation of the IZS. The microstructurals features supports evidences for the last possibility.
|
3 |
ESTUDO DA RECRISTALIZAÇÃO DINÂMICA DURANTE A DEFORMAÇÃO A QUENTE DE UM AÇO ISO 5832-9 / STUDY OF THE DYNAMIC RECRYSTALLIZATION DURING THE DEFORMATION THE HOT ONE OF A STEEL ISO 5832-9Nascimento, Luciene Araujo 25 February 2010 (has links)
Made available in DSpace on 2016-08-18T18:19:27Z (GMT). No. of bitstreams: 1
LUCIENE ARAUJO NASCIMENTO.pdf: 1402629 bytes, checksum: b9ce204098b2c4fe0362b6792a692744 (MD5)
Previous issue date: 2010-02-25 / FUNDAÇÃO DE AMPARO À PESQUISA E AO DESENVOLVIMENTO CIENTIFICO E TECNOLÓGICO DO MARANHÃO / Austenitic stainless steels have low economic value compared to titanium and its alloys,
considered the most resistant to corrosion in biological environment, and for over fifty
years are widely used in the manufacture of orthopedic implants, particularly in public
health service. Currently the ISO 5832-1 steel (ASTM F 138) is the most used in the
manufacture of orthopedic prosthesis, especially the temporary ones. However, because
it is susceptible to localized corrosion when in contact with human tissue, it is being
gradually replaced by austenitic stainless steel of low carbon and high nitrogen called ISO
5832-9. The same is already used extensively in Europe and the United States, while in
Brazil it's use is more recent and smaller scale. This work investigates the behavior of
dynamic recrystallization in an ISO 5832-9 steel through hot torsion tests and optical
microscopy, for different conditions of temperature, strain and strain rate. It was found
through the plastic flow curves of the studied material crystallizes dynamically and that the
high value of its apparent activation energy for deformation can be attributed to the
presence of a large amount of precipitated particles and nitrogen dissolved in the matrix.
Micrographs confirmed that tests carried out at low temperatures reveal a strong
retardation of dynamic recrystallization. Moreover, the presence of serrated grain
boundaries and nucleation of new grains in the old deformed grain boundaries, are strong
indications that the recrystallization occurred by a necklace mechanism. The behavior of
the average recrystallized grain size, DDRX, with temperature resembles the behavior of
the austenitic grain growth in microalloyed steels. The presence of a minimum in the
behavior of DDRX with the strain rate can be attributed to a minimum strain rate required
to cause the greatest amount of dynamics precipitation. / Os aços inoxidáveis austeníticos possuem um baixo valor econômico quando
comparados ao titânio e suas ligas, considerados os mais resistentes à corrosão em meio
biológico, e há mais de cinquenta anos são amplamente utilizados na confecção de
implantes ortopédicos, em especial no serviço de saúde pública. Atualmente o aço ISO
5832-1 (ASTM F 138) é o mais utilizado na confecção de próteses ortopédicas,
principalmente as temporárias. Entretanto, devido o mesmo ser suscetível à corrosão
localizada quando em contato com tecido humano, ele está sendo gradativamente
substituído pelo aço inoxidável austenítico de baixo teor de carbono e alto teor de
nitrogênio denominado de ISO 5832-9. O mesmo já é utilizado em larga escala na
Europa e nos Estados Unidos, enquanto no Brasil a sua utilização é mais recente e em
menor escala. Este trabalho investiga o comportamento da recristalização dinâmica em
um aço ISO 5832-9, através de ensaios de torção a quente e microscopia ótica, para
diferentes condições de temperatura, deformação e taxa de deformação. Foi constatado
através das curvas de escoamento plástico que o material estudado recristaliza
dinamicamente e, que o alto valor da sua energia de ativação aparente para a
deformação pode ser atribuído à presença de uma grande quantidade de partículas de
precipitados e ao nitrogênio em solução na matriz. Micrografias confirmam que ensaios
realizados a baixas temperaturas revelam um forte retardamento da recristalização
dinâmica. Além disso, a presença de contornos de grão serrilhados e nucleação de novos
grãos nos antigos contornos de grãos deformados, são fortes indícios de que a
recristalização ocorreu por mecanismo colar. O comportamento do tamanho de grão
médio recristalizado, DDRX, com a temperatura, se assemelha ao comportamento do
crescimento de grão austeníticos de aços microligados. A presença de um mínimo no
comportamento do DDRX com a taxa de deformação pode ser atribuído a uma taxa de
deformação mínima necessária para que ocorra a maior quantidade de precipitação
dinâmica.
|