Factors such as water to cement ratio, moisture, mixture, presence and depth of rebar, and dimension of specimens, all of which affect apparent resistivity of concrete, were analyzed by experimental and modeling methods. Cylinder and rectangular prism concrete specimens were used in the experiments exposed in a high moisture room, laboratory room temperature, high humidity and outdoor weather environments. Single rebar and four rebar specimens were used to study the rebar effect on the apparent resistivity. Modeling analysis was employed to verify and explain the experimental results. Based on the results, concrete with fly ash showed higher resistivity than concrete with just ordinary Portland cement. Rebar presence had a significant effect on the measured apparent resistivity at some of the locations. The results could be used as a guide for field apparent resistivity measurements and provide a quick, more precise and easy way to estimate the concrete quality. / by Yanbo Liu. / Thesis (M.S.C.S.)--Florida Atlantic University, 2008. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2008. Mode of access: World Wide Web.

This investigation presents results of the temperature effect on durability properties (resistivity and diffusivity) and compressive strength of concrete with pozzolans, and the effect of pozzolanic admixtures on microstructure and chemical compositions of concrete pore solution. ... Temperature dependence of electrical resistivity and chloride diffusivity was studied by dynamic temperature tests. Accelerated curing regimes involving curing concrete specimens in 35À C lime water with different durations were tested. Compressive strength test, resisivity measurement and rapid chloride migration (RCM) tests were performed. A leaching method was used to measure pH and conductivity of concrete pore solution. ... The accelerated curing regimes were found to increase the compressive strength and resistance to chloride ion penetration at short-term and long-term. With the developed correlation between resistivity and migration coefficients, it is possible to employ the resistivity measurement as an alternative or replacement of the RCM test to evaluate resistance of chloride ion penetration of concrete. Pozzolanic admixtures were found to decrease both pH and conductivity of concrete pore solution as the replacement ratio increased. Moreover, the migration coefficients were found to be greatly correlated to the microstructure properties of concrete, such as porosity, formation factor and tortuosity. / by Yanbo Liu. / Thesis (Ph.D.)--Florida Atlantic University, 2012. / Includes bibliography. / Mode of access: World Wide Web. / System requirements: Adobe Reader.

Prevention of the corrosion of steel reinforcement embedded in concrete is a constant challenge in engineering. A study of concrete surface resistivity versus elevation of partially immersed reinforced concrete structures in a marine splash zone has been developed and correlations made between concrete quality and chloride diffusion, i.e., aggressive ion permeability. A conditioning procedure was developed in which the concrete moisture content is increased by direct contact with fresh water for several days. The electrical resistivity of concrete is known to be primarily a function of the degree of water saturation. Correlations between field obtained concrete surface resistivity values versus chloride diffusivity, and between normalized resistivity measured on cores obtained from the field versus chloride diffusivity has been established. The resistivity values were measured on structures with different concrete mixes and various ages. / by Andres M. Suarez-Solano. / Thesis (M.S.C.S.)--Florida Atlantic University, 2009. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2009. Mode of access: World Wide Web.

This research is aimed at investigating the corrosion durability of polyolefin fiber-reinforced fly ash-based geopolymer structural concrete (hereafter referred to as GPC, in contradistinction to unreinforced geopolymer concrete referred to as simply geopolymer concrete), where cement is completely replaced by fly ash, that is activated by alkalis, sodium hydroxide and sodium silicate. The durability in a marine environment is tested through an electrochemical method for accelerated corrosion. The GPC achieved compressive strengths in excess of 6,000 psi. Fiber reinforced beams contained polyolefin fibers in the amounts of 0.1%, 0.3%, and 0.5% by volume. After being subjected to corrosion damage, the GPC beams were analyzed through a method of crack scoring, steel mass loss, and residual flexural strength testing. Fiber reinforced GPC beams showed greater resistance to corrosion damage with higher residual flexural strength. This makes GPC an attractive material for use in submerged marine structures. / Includes bibliography. / Thesis (M.S.)--Florida Atlantic University, 2013.

The aim of this study was to investigate the diffusion of chloride ions into concrete samples that were exposed in scenarios that simulate the splash, tidal, atmospheric, and immersed portions of a marine structure. To study the atmospheric deposition, the project also investigated the relationship between chloride ion deposition on the wet candle and its accumulation into concrete samples. Results from the wet candle experiment indicated that between 2% and 45% of the chlorides deposited per square meter of exposed area could be found within the concrete samples. After 6 months, slag G1a blocks showed the most resistance to chloride penetration in the tidal and splash simulations. After 10 months of exposure, fly ash samples had the slowest rates of diffusion in the tidal simulation while the fly ash + silica fume samples and the slag samples measured similar rates of diffusion within the tidal zone. After 90 days of curing, cylinders composed of 20% fly ash & 8% silica fume measured the highest average resistivity values and were found to be less vulnerable to chloride ion penetration than the 20% fly ash and the 50% slag concrete through rapid migration tests. / by Victor Anthony Echevarria. / Thesis (M.S.C.S.)--Florida Atlantic University, 2012. / Includes bibliography. / Mode of access: World Wide Web. / System requirements: Adobe Reader.

The construction industry is increasingly turning to the use of environmentally friendly materials in order to meet the sustainable aspect required by modern infrastructures. Consequently, for the last two decades, the expansion of this concept, and the increasing global warming have raised concerns on the extensive use of Portland cement due to the high amount of carbon dioxide gas associated with its production. The development of geopolymer concretes offers promising signs for a change in the way of producing concrete. However, to seriously consider geopolymer binders as an alternative to ordinary Portland cement, the durability of this new material should be evaluated in any comparative analysis. The main purpose of this study was to evaluate the durability characteristics of low calcium fly ash-based geopolymer concretes subjected to the marine environment, compared to ordinary Portland cement concrete with similar exposure. To achieve this goal, 8 molar geopolymer, 14 molar geopolymer and ordinary Portland cement concrete mixes were prepared and tested for exposure in seawater. Compressive strengths in the range of 2900 to 8700 psi (20-60 MPa) were obtained. The corrosion resistance performance of steel-reinforced concrete beams, made of these mixes, was also studied, using an accelerated electrochemical method, with submergence in salt water. The test results indicated that the geopolymer concrete showed excellent resistance to chloride attack, with longer time to corrosion cracking, compared to ordinary Portland cement concrete. / by Jean-Baptiste Edouard. / Thesis (M.S.C.S.)--Florida Atlantic University, 2011. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2011. Mode of access: World Wide Web.