Orientador: Flávio Henrique Baggio Aguiar / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T02:49:00Z (GMT). No. of bitstreams: 1 Soares_GiullianaPanfiglio_D.pdf: 64597032 bytes, checksum: e11e3cff0a47e90986ae7f73605e5aa2 (MD5) Previous issue date: 2013 / Resumo: A manutenção da integridade entre a interface dente e restauração é importante para o sucesso clínico de restaurações adesivas, influenciando significativamente na longevidade das mesmas. Assim, o objetivo deste trabalho in vitro, foi avaliar o efeito de diferentes sistemas adesivos na resistência de união à dentina e ao esmalte de uma resina composta a base de silorano, após 24 horas e 6 meses de armazenamento. Para este estudo, setenta terceiros molares humanos hígidos, recém-extraídos e não restaurados, foram usados em um dos dois testes de resistência de união. Para a resistência à microtração à dentina, vinte e oito terceiros molares humanos, sem raízes, tiveram a superfície oclusal planificada a fim de expor a dentina superficial. Os dentes foram aleatoriamente divididos em 8 grupos experimentais (n=7): Adper Single Bond 2 (3M ESPE); Adper Scotchbond Multiuso (3M ESPE); Adper SE Plus (3M ESPE) e sistema adesivo P90 (3M ESPE), sendo os palitos obtidos de cada grupo divididos entre os testes envelhecidos ou não. Após a aplicação do sistema adesivo relacionado com cada um dos grupos, foi aplicada uma camada do adesivo da resina à base de silorano e fotopolimerizado por 10 segundos. O passo seguinte foi à inserção da resina composta Filtek P90 (3M ESPE) e fotoativação por 40 segundos com aparelho LED de segunda geração, o mesmo utilizado para a fotoativação dos sistemas adesivos. Para a resistência de união ao microcisalhamento ao esmalte, oitenta e quatro fragmentos foram obtidos a partir de superfícies proximais de quarenta e dois terceiros molares humanos (n=7). Os grupos foram os mesmos que os utilizados no ensaio de microtração acrescido de quatro grupos experimentais com condicionamento ácido prévio com ácido fosfórico 35% (3M ESPE) para os grupos que utilizaram os adesivos auto condicionantes, resultando em 12 grupos experimentais. As amostras foram testadas em 24 horas ou após 6 meses de envelhecimento. Os dados foram analisados estatisticamente por meio xii da análise de variância (ANOVA) com medidas repetidas e Teste de Tukey (p = 0,05) Os resultados mostraram que, para o teste de resistência à microtração, não houve diferença estatística significativa entre os grupos, nem para a interação (p > 0,05). No teste de microcisalhamento, o grupo condicionado com ácido fosfórico 35% + Adper SE Plus apresentou a maior resistência de união, no entanto, nenhuma diferença estatística entre o grupo condicionado com ácido fosfórico 35% + Sistema adesivo Silorano (p = 0,051) foi observada. O sistema Adesivo Silorano apresentou a menor resistência de união, sem diferença estatística entre o Adper SE Plus (p = 0,972). Para ambos os testes não houve diferença entre 24 horas e 6 meses (p> 0,05) de armazenamento. Pode concluir-se que os sistemas adesivos apresentaram comportamentos semelhantes na resistência de união à dentina; para o esmalte, o condicionamento ácido prévio aumentou os valores de resistência de união dos adesivos auto-condicionantes, promovendo um padrão de condicionamento que favorece a adesão a este substrato. O armazenamento por 24 horas e 6 meses não foi significativo para a resistência de união ao esmalte ou dentina / Abstract: The maintenance of the bond integrity between tooth and dental restoration is important for the clinical success of adhesive restorations, influencing their durability. Thus, the aim of this in vitro study was to evaluate the effect of different adhesive systems on the microtensile bond strength to dentin and microshear bond strength to enamel of silorane based resin after 24 hours and 6 months of storage. For this study seventy freshly extracted non-carious, unrestored human third molars were assigned to one of two bond strength test. For the microtensile bond strength, twenty-eight third human molars, with no roots, had their oclusal surface flattened in order to expose superficial dentin. Teeth were randomly assigned to 8 experimental groups (n=7): Adper Single Bond 2 (3M ESPE); Adper Scotchbond Multi-Purpose (3M ESPE); Adper SE Plus (3M ESPE) and P90 adhesive system (3M ESPE), the sticks being obtained from each group divided between tests aged or not. After application of the adhesive system related to each group, was applying only the silorane adhesive bond and then light cured for 10 seconds. The next step was the insertion of silorane composite resin Filtek P90 (3M ESPE) and light cured for 40 seconds with second-generation light-emitting diode, the same used for the light cured of the adhesive systems. For the microshear bond strength, eighty four fragments were obtained from proximal surfaces of forty two third human molars. Groups were the same as those used in the microtensile test increasing two more experimental groups with etching previous with phosphoric acid 35% (3M ESPE) for the self etch adhesive systems, resulting in 12 experimental groups (n=7). The samples were tested after 24 hours or after 6 months of aging. The data were statistically analyzed by repeated measure analysis of Variance (ANOVA) and Tukey's test (p=0.05). Results showed that for the microtensile bond strength there was no statistical difference for all groups, neither for interaction (p>0.05). For microshear bond strength, Etching with xiv phosphoric acid 35% + Adper SE Plus presented the highest bond strength, however no statistical difference between Etching with phosphoric acid 35% + Silorane System Adhesive (p=0.051) was observed. Silorane System Adhesive presented the lowest bond strength, without statistical difference from Adper SE Plus (p=0.972). There was no statistical difference between 24 hours and 6 months (p > 0.05). It can be concluded that there was no difference for the dentin bond strength group; for microshear bond strength, acid etching increases the bond strength values of the self-etching adhesive to enamel, promoting a conditioning pattern that favors the adhesion to this substrate. There was no statistical difference between the periods of 24 hours and 6 months of storage for enamel or dentin / Doutorado / Dentística / Doutora em Clínica Odontológica

Orientador: Luís Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T10:56:59Z (GMT). No. of bitstreams: 1 Bertaglia_PriscilaCamondy_M.pdf: 1765685 bytes, checksum: 8df88a23b4523a61343a7a780e9c4043 (MD5) Previous issue date: 2011 / Resumo: O objetivo deste estudo foi avaliar a resistência de união e grau de conversão de um compósito a base de silorano em associação a sistemas adesivos autocondicionantes e convencionais. Para a realização do teste de microtração, foram utilizados 50 terceiros molares humanos sem raiz e sem esmalte oclusal e com a superfície dentinária exposta. As amostras foram submetidas ao desgaste da superfície dentinária com lixas de carbeto de silício de granulação 600 para a padronização da lama dentinária e divididas aleatoriamente em cinco grupos de acordo com o sistema adesivo aplicado (n=10): 3 sistemas autocondicionantes G1 - P90; G2 - Adper Easy One Bond; G3 - Adper SE Bond; e dois convencionais G4 - Adper Single Bond 2; G5 - Adper Scotchbond Multi-Uso Plus. Em seguida, foram aplicados os sistemas adesivos e a resina composta a base de silorano de acordo com as instruções do fabricante. Após o procedimento restaurador, as amostras foram seccionadas, obtendo-se palitos com largura de 0,7 - 1mm. Foram selecionados aleatoriamente 5 palitos de cada dente para a realização do teste de microtração e fraturados em Máquina de Ensaio Universal. Os valores obtidos em KgF foram convertidos para MPa. Para a avaliação do grau de conversão, através da espectroscopia FT-Raman, foram confeccionados 25 amostras em uma matriz metálica com orifício circular com 2mm de diâmetro e 1mm de altura. Os grupos utilizados neste teste foram os mesmos daqueles usados no teste de microtração. Os sistemas adesivos foram aplicados em uma tira de poliéster, fotoativado e posicionados sobre a resina composta a base de silorano. O conjunto foi fotoativado e seus espectros analisados através da espectroscopia FT-Raman. Os dados foram estatisticamente analisados por meio de análise de variância (ANOVA) one way e teste de Tukey com nível de significância de 0,05 (p?0,05). O sistema adesivo Adper Scotchbond Multi-Uso Plus apresentou os maiores valores de resistência de união (26,07 MPa), porém sem diferença estatística para os sistemas adesivos Adper Single Bond 2 (23,24 MPa) e P90 (20,83 MPa). O sistema adesivo Adper SE Bond apresentou o menor valor de resistência de união (9,65 MPa), não diferindo estatisticamente do sistema Adper Easy One Bond (13,73 MPa), porém com diferença em relação ao sistema adesivo P90. Com relação ao grau de conversão, a resina composta da face de contato com os sistemas adesivos Adper Scotchbond Multi-Uso Plus e o Adper Single Bond 2 apresentaram maiores valores, porém sem diferença significante entre si. A resina composta da face em contato com o sistema adesivo P90 apresentou valores intermediários diferindo de todos os sistemas e os menores valores foram obtidos pelos sistemas Adper SE Bond e Easy One Bond, mas sem diferença estatística entre si. Os resultados obtidos nesta pesquisa sugerem que os sistemas adesivos convencionais podem ser utilizados como agentes de união em associação com a resina composta a base de silorano, em dentina / Abstract: This study evaluated bond strength values and degree of conversion of a Silorane composite in combination with self-etch and etch & rinse adhesive systems. Fifty human third molars with no roots and exposed occlusal dentine surface were used to evaluate microtensile bond strength. The samples were grounded flat using 600-grit silicon carbide papers to standardize the smear layer and they were randomly divided into five groups(n=10): three self-etch systems G1 - P90 adhesive system; G2 - Adper Easy One Bond system; G3 - Adper SE Bond system; and two etch&rinse systems G4 - Single Bond 2; G5 - Adper Scotchbond Multi-Purpose Plus. After that, the adhesive systems and resin-based Silorane were applied following to the manufacturer's instructions. After restorative procedure, samples were sectioned in sticks sectioned in 1X1mm. Five random sticks from each sample were submitted to microtensile test at 0,5mm/min in a Mechanical Testing Machine until fracture. FT-Raman spectroscopy was performed to evaluate degree of conversion 25 samples were produced in a metal matrix with a 2mm-circular hole of diameter and 1mm of height. Groups were the same as those used in the microtensile test. The adhesive systems were applied on a polyester strip, photocured and placed over the Silorane composite. The assembly was cured and their spectra analyzed by FT-Raman spectroscopy. The data was statistically analysed by analysis of variance (ANOVA) and Tukey Test (p?0,05). Adper Scotchbond Multi-Purpose Plus presented the highest bond strength (26.07 MPa), however no statistical difference between Single Bond 2 (23.24 MPa) and P90 (20.83 MPa) was observed. Adper SE Bond presented the lowest bond strength (9.65 MPa), without statistical diference neither from Adper Easy One Bond (13.73 MPa) nor P90 adhesive system (20,83 MPa).The composite presented higher values of conversion degree with Adper Scotchbond Multi-Purpose Plus and Single Bond 2 adhesive than the other tested adhesives, with P90 adhesive presented intermediate values with statistical difference among all the adhesive systems. The lowest values were obtained with Adper SE Bond and Easy One Bond, but no difference between them. The results of this research suggest the conventional adhesive systems can be used as coupling agents in combination with Silorane composite in dentin / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientadores: Mario Alexandre Coelho Sinhoreti, Americo Bortolazzo Corrrer / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-26T12:38:53Z (GMT). No. of bitstreams: 1 Felizardo_KlissiaRomero_D.pdf: 5538718 bytes, checksum: 380cb510516fc2b1b84875f344139970 (MD5) Previous issue date: 2015 / Resumo: O objetivo do estudo foi gerar uma nova metodologia restauradora, através de um compósito fluído fotopolimerizável com fosfatos de cálcio e incorporação de tri-metafosfato de sódio em primer autocondicionante para auto-produção de fosfoproteína biomineralizadora da matriz de colágeno na interface de união. A hipótese desse trabalho foi de que a inovadora metodologia irá recuperar as propriedades mecânicas, remineralizará e aumentará a longevidade da interface de união. No Capítulo 1 foi realizado análise qualitativa em relação à presença de fosfato e apatita carbonata nas amostras de dentina desmineralizada e após contato com os compósitos experimentais (VSG1- 0% fosfato, VSG2- 10% fosfato, VSG3- 20% fosfato e VSG4- 30% fosfato) armazenados em água destilada e solução de PBS no período de 24h, 7 dias, 1 e 3 meses. As amostras foram analisadas por espectroscopia (ATR / FTIR) e análise microscópica (ESEM / EDX). Os dados foram submetidos à análise de variância de três fatores e teste de Tukey ('alfa'=0.05). Em 24h os maiores picos referentes às bandas de apatita carbonatada (CO32- - v2) fosfato (PO43- - v1,v3) e bruxita (DCPD- vO-H) foram para os grupos VSG2 (água destilada) e VSG3 (PBS). Em 7 dias esses picos diminuiram e ocorreu aumento dos picos para os grupos VSG1 (água destilada), VSG2 (PBS) e VSG4 (PBS). Após 1 mês, o material VSG2 (PBS) apresentou aumento do pico, por outro lado o grupo VSG4 (PBS) manteve-se similar ao do período de 7 dias. Aos 3 meses, nota-se aumento para o material VSG3 (água destilada) e grupo controle (VSG1) em PBS. A análise em EDX não mostrou diferença estatística entre os grupos no decorrer do tempo. No Capítulo 2, o objetivo foi avaliar a influência de fosfato de cálcio como partículas de carga em relação ao grau de conversão, dureza, resistência flexural e módulo elástico. O material experimental VSG4 mostrou maiores valores de dureza após 6 meses e maior grau de conversão nos períodos de 3 meses e 6 meses. Maiores valores de resistência à flexão foram encontrados para o material experimental VSG2 bem como para o material comercial Wave HV (SDI). Maior módulo de elasticidade foi obtido para o material VSG4, valores estes similares aos obtidos para o material comercial Filtek Z350XT (3M/ESPE). Assim, pode-se concluir que a utilização de fosfatos de cálcio não afetou as propriedades mecânicas após envelhecimento em solução de PBS. No Capítulo 3, o objetivo foi avaliar por microscopia de confocal e microscopia óptica a micropermeabilidade por penetração de corante fluoresceína e nanoinfiltração por nitrato de prata amoniacal na camada híbrida assim como a resistência adesiva nos períodos de 24 h e 6 meses em solução de PBS. Os dados referentes ao teste de união foram submetidos à análise de variância de dois fatores e teste de Tukey ('alfa'=0.05). Os resultados mostraram que em relação à resistência adesiva não houve diferença estatística entre os grupos e período de armazenamento. A inclusão de fosfato de cálcio e o uso de tri-metafosfato de sódio auxiliaram no processo de remineralização para o material experimental VSG3 e VSG4 os quais mostraram melhores resultados, reduzindo a permeabilidade dentinária após 6 meses / Abstract: The aim of this study was to generate a new therapeutic restorative methodology through a flowable composite with bioactive calcium phosphates and incorporation of sodium tri-metaphosphate in self-etching primer will serve as a biomimetic analogs to self-phosphoprotein biomineralization production of collagen within the matrix the bonded interface. The hypothesis is that the revolutionary biomineralisation will recover the biomechanical properties, remineralise and increase the longevity of the bonded interfaces. In the chapter 1 was designed to qualitatively compare the presence of phosphate and carbonated apatite between demineralized dentin samples and experimental composite (VSG1- 0% phosphate, VSG2- 10% phosphate, VSG3- 20% phosphate e VSG4- 30% phosphate) storage in distilled water and PBS solution in 24h, 7 days, 1 e 3 months. The samples were analyzed by (ATR/FTIR) and (ESEM/EDX). Data were subjected to variance analysis with three factors and Tukey ('alfa' = 0.05). The results showed that in 24 hours the higher peak related the bands of carbonated apatite (CO32- - v2), phosphate (PO43- - v1,v3) and brushite (DCPD- vO-H) was found to the experimental material VSG2 (distilled water) and VSG3 (PBS). After 7 days, these same peaks suffered a drop therefore having an increased peak to control group VSG1 (distilled water), VSG2 (PBS) and VSG4 (PBS) groups. At 1 month , the material VSG2 (PBS) showed an increase in their peak, on the other hand VSG4 group (PBS solution) was maintained as compared to results 7 days and after 3 months, was an increase in the peaks to VSG3 materials (distilled water) and control group (VSG1) in PBS solution. The EDX analysis showed no statistical difference between the groups over time. In the chapter 2, the objective was to evaluate the in?uence of calcium phosphate as a filler in experimental composite and their correlation with the degree of conversion, microhardness, flexural resistance and elastic modulus. The experimental material VSG4 showed higher hardness values after 6 months and higher degree of conversion at 3 months and 6 months. Further flexural strength values were found for the experimental material VSG2 well as the commercial material Wave HV (SDI). Higher elasticity modulus was obtained for the experimental material VSG4, similar values to the commercial Filtek Supreme (Z350XT- 3M/ESPE). Thus, it can be concluded that the use of calcium phosphate did not affect the mechanical properties after storage in PBS solution. In the chapter 3, the aim was evaluated by confocal microscopy and optcial microscopy the micropermeability by fluorescein dye penetration and the nanoleakage by ammoniacal silver nitrate as well as the adhesive strength over 24h and 6 months in buffer solution (PBS) by microtensile test. Data on microtensile test were subjected to variance analysis with two factors and Tukey ('alfa'= 0.05). The results showed that the bond strength was not statistically different between the experimental groups. The calcium phosphate inclusion as filler particles and the use of tri-sodium metaphosphate aided in the remineralization process mainly to the experimental material VSG3 and VSG4 which showed better micropermeability and nanoleakage reducing dentin permeability after 6 months. / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-26T13:35:05Z (GMT). No. of bitstreams: 1 Fugolin_AnaPaulaPiovezan_D.pdf: 4905643 bytes, checksum: 75a91fcf559fc00359be8feeeb2d2a0c (MD5) Previous issue date: 2015 / Resumo: Novos compósitos bulk-fill, autoadesivos e de menor contração foram desenvolvidos propondo mudanças na técnica restauradora incremental preconizada. Os objetivos desta pesquisa foram: 1) analisar os compósitos Tetric EvoCeram Bulk Fill (TEC), Surefil SDR (SDR), Vertise Flow (VF), Filtek Low Shrinkage (SIL) e compará-los com o compósito convencional Z100 (Z100) quanto à contração volumétrica, tensão de contração, grau de conversão, cinética, resistência à flexão e módulo de elasticidade; 2) avaliar a profundidade de polimerização e a resistência da união à tração de cavidades de Classe II restauradas com diferentes técnicas e diversas associações de materiais submetidas à ciclagem mecânica; e 3) analisar a adaptação marginal por microscopia eletrônica de varredura de restaurações de Classe II antes e após ciclagem mecânica e resistência coesiva. No capitulo 1, a contração volumétrica foi avaliada por dilatômetro de mercúrio e bonded disc (n=5) e a tensão de contração com Bioman (n=5). O grau de conversão foi analisado com espectroscopia de infravermelho próximo (NIR) (n=5) e a cinética por meio de optical bench (n=5). Resistência à flexão e módulo de elasticidade foram mensurados em ensaio com três pontos de apoio após 10 e 60 minutos da fotoativação. Os dados foram analisados por ANOVA e teste de Tukey (5%). VF apresentou os maiores valores de contração volumétrica e tensão de contração, enquanto que SIL obteve os menores. SDR apresentou a maior taxa de polimerização e os maiores valores de grau de conversão. VF apresentou os maiores valores de resistência à flexão após 10 e 60 minutos e Z100 os maiores valores de módulo de elasticidade. No capítulo 2, cavidades de Classe II ocluso-distais em terceiros molares humanos extraídos foram restauradas usando sistema adesivo convencional ¿ XP Bond (XP) ou à base de silorano (SSA) associado aos compósitos TEC, SDR, VF, SIL e Z100 inseridos por meio da técnica incremental (I) e bulk (B). Os grupos experimentais testados foram: XP-Z-B, XP-Z-I, SSA-Z-B, SSA-Z-I, XP-TEC-B, XP-TEC-I, XP-SDR-Z100, SSA-SDR-Z100, VF-Z-B e SSA-SIL-B (n=8). Metade do total das amostras foi preparada para obtenção de palitos e submetida ao teste de resistência da união à microtração após sete dias de armazenagem, enquanto outra metade foi submetida à ciclagem mecânica antes do ensaio de resistência da união. A profundidade de polimerização foi mensurada em restaurações com 4,0 mm de profundidade removidas da cavidade e submetidas ao ensaio de dureza Knoop (n=3). Os resultados foram analisados por ANOVA e teste de Tukey (5%). Quanto à resistência de união o grupo XP-SDR-Z apresentou os maiores valores em ambas as superfícies (oclusal e cervical) nos grupos ciclados ou não. Os menores valores foram exibidos por VF-Z-B em ambas as superfícies para os grupos não ciclados e SSA-SDR-Z para os ciclados. Em relação à profundidade de polimerização, VF apresentou a maior redução da dureza, enquanto os demais compósitos apresentaram valores de redução menores do que 20%. No capítulo 3, as cavidades de Classe II restauradas seguiram as mesmas etapas dos grupos experimentais apresentados no capítulo 2 (n=5) e foram submetidas ao ensaio de ciclagem mecânica; porém, foram previamente moldadas para obtenção de replicas para análise da integridade marginal em microscopia eletrônica de varredura. As imagens foram analisadas pelo software Image J para verificar a porcentagem de fendas. Os compósitos utilizados para restaurar as cavidades foram submetidos ao teste de resistência coesiva (n=5). Os resultados foram analisados por ANOVA e teste de Tukey (5%). A análise da adaptação marginal qualitativa e quantitativa mostrou alteração significativa antes e após a ciclagem mecânica apenas para todos o grupo SSA-Z-B. Os resultados de resistência coesiva mostraram que Z100, SDR e SIL apresentaram os maiores valores, seguido de TEC. VF apresentou os menores valores. Concluiu-se que os novos compósitos apresentam propriedades comparáveis e, em algumas situações, melhores quando comparado ao compósito convencional / Abstract: New bulk-fill, self-adhering and low shrinkage materials were developed and purposed significant changes in the preconized incremental restorative technique. The aims of this research were: 1) analyze the new composites represented by Tetric EvoCeram Bulk Fill (TEC), Surefil (SDR), Vertise Flow (VF), Filtek Low Shrinkage (SIL) and compare them with the conventional composite Z100 (Z100) in relation to volumetric shrinkage, stress of polymerization, degree of conversion, kinetics, flexural strength and modulus; 2) evaluate depth of cure of different composites and microtensile bond strength of Class II cavities filled by different restorative techniques and materials association submitted to mechanical fatigue-cycling test; and 3) analyze marginal adaptation by scanning electron microscopy (SEM) of Class II restoration before and after mechanical cycling, and ultimate tensile strength. In the charter 1, the volumetric shrinkage was evaluated by mercury dilatometer and bonded-disc techniques (n=5) and stress of polymerization by Bioman instrument (n=5). Degree of conversion was analyzed with NIR-spectroscopy (n=5) and the kinetics by the optical bench (n=5). Flexural strength and modulus were carried out using a three-point bending test after 10 and 60 minutes after photocuring. Results were analyzed by ANOVA and Tukey¿s test (5%). VF showed the highest values of volumetric shrinkage and stresses of polymerization and SIL the lowest ones. SDR obtained the highest rate of polymerization and the highest degree of conversion values. VF presented the highest values of flexural strength in both tested times, and Z100 the highest values of modulus. In the charter 2, Class II occluso-distal cavities (6 x 2 x 4 mm) in extracted human molars were restored using a etch-and-rinse adhesive system ¿ XP Bond (XP) or silorane-based (SSA) associated to TEC, SDR, VF, SIL and Z100 composites placed by incremental (I) or bulk (B) technique. The tested experimental groups were: XP-Z-B, XP-Z-I, SSA-Z-B, SSA-Z-I, XP-TEC-B, XP-TEC-I, XP-SDR-Z100, SSA-SDR-Z100, VF-Z-B e SSA-SIL-B (n=8). Half of the samples were prepared to obtain sticks and submitted to the microtensile bond strength test after 7 days of storage. The other samples were submitted to the mechanical fatigue-cycling test before the microtensile bond strength test. Depth of cure was carried out in restorations with 4.0 mm of depth, removed and submitted to Knoop hardness test (n=3). Results were statistically analyzed by ANOVA and Tukey¿s test (5%). In relation to microtensile bond strength, in overall, XP-SDR-Z showed the highest values in both analyzed surfaces (occlusal and cervical) in cycling and no-cycling groups. The lowest values were exhibited by VF-Z-B in both analyzed surfaces in no-cycling groups and SSA-SDR-Z in cycling groups. In relation to depth of cure, VF obtained the lowest top-to-bottom ratio, while the other tested composites exhibited less than 20% of reduction. In the charter 3, Class II cavities were prepared following the same steps described in charter 2 (n=5) and were carried out to mechanical fatigue-cycling test. However, impressions were made before and after to obtain replicas to SEM analysis of the marginal integrity. The micrographs were analyzed by Image J software to measure the discontinuity percentage. The composites used in the cavities were submitted to the ultimate tensile strength (UTS) (n=5). Results were statistically analyzed by ANOVA and Tukey¿s test (5%). Marginal adaptation analysis did not show significant alteration before and after cycling for all groups except to SSA-Z-B where cracks and gaps were found in the adhesive interface. In relation to UTS results Z100, SDR and SIL showed the highest results, followed by TEC. VF exhibited the lowest values. It is possible to conclude that new composites show comparable properties and in some situation better than conventional material / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários

Orientadores: Simonides Consani, Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-14T12:05:44Z (GMT). No. of bitstreams: 1 Garcia_LucasdaFonsecaRoberti_D.pdf: 2236392 bytes, checksum: 81c798a6c0a3550904a44b971bdeaf20 (MD5) Previous issue date: 2009 / Resumo: A grande quantidade de matizes que os compósitos possuem permite ao dentista obter excelentes resultados estéticos na confecção de uma restauração. Porém, para a confecção desta restauração, pouco material é utilizado e, muitas vezes, devido ao uso não freqüente, o compósito atinge o prazo de validade e a embalagem ainda contém material. O objetivo neste estudo foi avaliar a influência do Envelhecimento Artificial Acelerado (EAA - Sistema C-UV, Comexim) sobre a similaridade e a estabilidade de cor (?E), a opacidade (?OP) e a conversão monomérica de compósitos (Tetric Ceram, Tetric Ceram HB e Tetric Flow - Ivoclar/Vivadent) com prazo de validade vencido por 180 dias, comparando com àqueles com validade em vigência. Para avaliação das propriedades ópticas foram confeccionados 15 corpos-de-prova (n=5) em matriz de teflon, com 2 mm de espessura por 14 mm de diâmetro. Depois do polimento com discos Sof-Lex (3M Dental Products) foram submetidos às leituras de cor e opacidade (Espectrofotômetro PCB 6087 BYK GARDNER), antes e depois do EAA por 384 horas. Os valores obtidos para similaridade foram submetidos à análise estatística (t Student, p<0,05) e demonstraram que todos os compósitos antes do EAA apresentaram diferença significante para todas as coordenadas com exceção do Tetric Flow para a* e Tetric Ceram HB para b* antes do EAA. Após o EAA, somente o Tetric Ceram apresentou diferença significante para as coordenadas a* e b*. Os valores para ?E e ?OP foram submetidos à ANOVA 2 fatores e teste de Bonferroni (p<0,05) e demonstraram que todos os compósitos apresentaram alteração de cor acima do clinicamente aceitável (?E = 3,3). Somente o Tetric Flow apresentou diferença estatisticamente significante quando os prazos de validade foram comparados (p<0,05). Todos os compósitos avaliados apresentaram aumento nos valores numéricos de ?OP após o EAA, independente do prazo de validade, mas sem diferença significante (p>0,05). Para avaliação da conversão monomérica, 6 corpos-de-prova, sendo 3 envelhecidos e 3 não envelhecidos de cada compósito foram submetidos à verificação da densidade de ligações cruzadas (DLC) (Shimadzu HMV-2 Series) e do grau de conversão (GC) (FTIR - Thermo Scientific). Os valores obtidos foram submetidos à ANOVA 2 fatores e teste de Bonferroni (p<0,05) e demonstraram que todos os compósitos apresentaram diminuição na DLC após o EAA, independente do prazo de validade. Para o GC, o Tetric Flow vencido antes do EAA apresentou a maior porcentagem (71,42%), porém, sem diferença significante em relação aos demais compósitos (p>0,05). Concluiu-se que o prazo de validade e o EAA exerceram influência sobre as propriedades estudadas dos compósitos. / Abstract: Presently, the excellent aesthetic results obtained with composites require the dentist to use several composite resin hues to make a restoration. Nonetheless, to do this, little material is used, and many times, due to this low usage, the composite reaches its expiration date with material remaining in the packaging. The purpose of this study was to evaluate the influence of Artificial Accelerated Aging (AAA - Sistema C-UV, Comexim) on similarity and color stability (?E), opacity (?OP), and monomeric conversion of composites (Tetric Ceram, Tetric Ceram HB and Tetric Flow - Ivoclar/Vivadent) with their validity date expired for 180 days, comparatively to those within their validity date. For optical properties evaluation, 15 samples (n=5) with 2 mm of thick X 14 mm in diameter were made in a Teflon matrix. After polishing with Sof-Lex discs (3M Dental Products), they were submitted to color and opacity readings (Spectrophotometer PCB 6087 BYK GARDNER), before and after AAA for 384 hours. The values obtained for similarity were submitted to statistical analysis (t Student, p<0.05) and showed that all composites presented statistical significant difference for all coordinates, except Tetric Flow for a* and Tetric Ceram HB for b* before AAA. After AAA, only Tetric Ceram presented statistical significant difference for a* and b*. The values of ?E and ?OP were submitted to 2 way-ANOVA and Bonferroni's test (p<0.05) and showed that all composites presented color alteration above of the clinically acceptable (?E = 3.3). Only Tetric Flow presented statistical significant difference when the validity dates were compared (p<0.05). All studied composites showed increase in the values of ?OP after AAA, irrespective of the validity date, but without significant difference (p>0.05). To monomeric conversion evaluation, 6 samples, being 3 before aging and 3 after aging, of each composite, were submitted to cross-links density (CLD) (Shimadzu HMV-2 Series) and conversion degree evaluation (CD) (FTIR - Thermo Scientific). The values obtained were submitted to 2 way-ANOVA and Bonferroni's test (p<0.05) and showed that all composites presented decrease in CLD after AAA, irrespective of the validity date. For CD, Tetric Flow with expired date before AAA, showed the highest value (71.42%), however, without significant difference (p>0.05). It was concluded that the validity date and the AAA exert influence on the studied properties of the composites. / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Eduardo Bresciani / Coorientadora: Ticiane Cestari Fagundes Tozzi / Banca: Taciana Marco Ferraz Caneppele / Banca: Lucas Silveira Machado / Resumo: O objetivo deste trabalho foi avaliar a influência de observadores sobre a percepção e aceitabilidade de brilho superficial de resinas compostas, sob diferentes iluminantes, em angulação livre e pré-determina em 60°. E ainda, determinar o limite de perceptibilidade e aceitabilidade da variação de unidade de brilho (∆UB) entre os espécimes. Foram confeccionados 8 espécimes cilíndricos de 6 mm de diâmetro e 1,5 mm de espessura de resina composta, bem como um espécime padrão de dente humano, com 0,5 mm de espessura em esmalte e 1 mm em dentina. Os espécimes receberam polimento a fim de que se obtivesse ao final do processo amostras com 10 UB, 20 UB, 30 UB, 40 UB, 50 UB, 60 UB, 70 UB e 80 UB e um padrão de dente humano de 80 UB. Foram selecionados 60 observadores (20 leigos, 20 alunos de graduação e 20 cirurgiões-dentistas). O estudo foi submetido e aprovado pelo comitê de ética local. Os participantes fizeram a qualificação do brilho superficial de resina composta em cabine de luz (Gti - Newburgh,NJ). Para tanto, as amostras foram posicionadas no interior da cabine, duas a duas de forma aleatória, de forma com que a luz incidisse sua superfície em um ângulo de 60°. Os observadores responderam perguntas específicas para se determinar o nível e limite de perceptibilidade das variações de brilho. Todas as análises foram realizadas em duas condições de iluminação, com iluminantes D65 e luz fluorescente. Cinquenta por cento dos observadores iniciaram as análises com ângulo de visuali... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of the present study was to assess the influence of observers on gloss perception and acceptability of resin composites, with different illuminant exposures, under non-determined visualization field or at 60°; and also to determine the limit of perceptibility and acceptability of gloss unit variation (∆GU) between specimens. Eight composite resin specimens presenting 6 mm in diameter and 1.5 mm thick were fabricated. A human tooth specimen (1 mm dentin and 0.5 mm enamel) was also obtained. Specimens were polished to obtain surface gloss, in gloss units (GU), at 10 GU, 20 GU, 30 GU, 40 GU, 50GU, 60 GU, 70 GU, and 80 GU; while human tooth specimen presented 80 GU. Sixty observers were selected for the analyses (20 laypersons, 20 students, and 20 dentists). The study was submitted to and approved bythe local Institutional Review Board. Subjects compared the surface gloss of specimens in a light booth (Gti - Newburgh, NJ). Specimens were randomly placed, two at a time, in the light booth with light incidence at 60°. Observers answered to specific questions to determine the levels and limits of perceptibility of surface gloss variations. All analyses were performed under two illuminant conditions, being D65 and fluorescent light. Fifty percent of observes started the analyses with nondetermined visualization field, followed by determined visualization field at 60o . The rest 50% performed observations in opposite order. The levels and limits of acceptability of surface gloss, were determined by individually comparing resin specimens and human enamel sample. Data were submitted to General linear/nonlinear model PROBIT and non-linear regression estimation PROBIT (5%). For the perceptibility, significant differences were observed for the gloss variation (Δ GU) (p <0.001), for the observers (p = 0.043) and for different illuminant exposures (p <0.001)...(Resumo completo, clicar acesso eletrônico abaixo) / Mestre

Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T12:22:23Z (GMT). No. of bitstreams: 1 MarinFronza_Bruna_M.pdf: 2159343 bytes, checksum: 39b3c9ade2395da11c531548d34be71d (MD5) Previous issue date: 2014 / Resumo: Os objetivos no presente estudo foram: (1) caracterizar o conteúdo inorgânico; (2) investigar a passagem de luz (PL) através de incrementos com diferentes espessuras; (3) avaliar a resistência à flexão biaxial (RFB) e módulo de elasticidade (MO) em função da profundidade de polimerização; (4) verificar o grau de conversão (GC) e microdureza (MD) e (5) correlacionar a tensão de polimerização (TP) com a formação de fenda marginal (FM) em cavidades classe I com materiais restauradores bulk-fill, comparando com um compósito resinoso tradicional. Quatro resinas bulk-fill foram avaliadas: Surefill SDR flow (SDR), Filtek Bulk Fill (FBF), Tetric EvoCeram Bulk Fill (TEC) e EverX Posterior (EXP). Herculite Classic (HER) foi utilizada como controle. Para a caracterização da morfologia e composição do conteúdo inorgânico, uma porção de cada material foi imersa em solventes para remoção da matriz resinosa e posteriormente analisada por EDX e MEV. A PL foi mensurada através de diferentes espessuras dos materiais (1, 2, 3 e 4 mm) utilizando radiômetro acoplado a esfera integrada (n=5). Para o teste de RFB e MF, discos de resina composta (0,5 mm de espessura) foram confeccionados em um conjunto de matrizes sobrepostas (n=8), simulando profundidade de polimerização de 4 mm. O GC obtido por espectroscopia Confocal Raman e MD Knoop foram determinados em cavidades classe I com 4 mm de profundidade, as quais foram restauradas com as resinas e respectivos adesivos (n=5). A partir dessas restaurações foram confeccionadas réplicas em resina epóxi para análise de formação de FM em MEV. A TP de cada material foi determinada por um extensômetro associado a uma máquina de ensaio universal (n=5). As partículas de carga das resinas bulk-fill apresentaram formato irregular, esferoidal ou cilíndrico de tamanhos variados, de 0,1 ?m a 1 mm. Quanto a composição os principais elementos químicos identificados foram alumínio, bário e silício. Todos os materiais demonstraram menor passagem de luz com o aumento da espessura. Não houve diferença entre a PL para as resinas bulk-fill, porém apenas a SDR permitiu maior PL que HER. A atenuação da luz, entretanto, não teve influencia na RFB das resinas bulk-fill, enquanto para HER na maior profundidade houve redução da RFB. Embora, o MO ainda foi maior para HER. O GC foi uniforme em termos de profundidade para os materiais SDR, FBF e HER aplicado em incrementos. De modo contrário, os materiais TEC, EXP e HER em incremento único tiveram diminuição do GC com o aumento da profundidade. Para o teste de MD, resultados inferiores com o aumento da profundidade foram encontrados apenas para TEC, assim não houve correlação entre as análises de MD e GC. Com relação a TP, EXP apresentou os valores mais altos, enquanto TEC os menores. Correlação positiva foi detectada entre TP e formação de FM, as quais variaram entre os materiais. A técnica incremental demonstrou reduzir a FM para HER, SDR e TEC tiveram comportamento comparável a essa técnica convencional. As resinas bulk-fill apresentaram variações nos resultados, algumas demonstraram resultados semelhantes ou superiores à resina controle, podendo ser uma opção para os tradicionais procedimentos restauradores diretos / Abstract: The aims of this study were: (1) to characterize the inorganic content; (2) investigate light transmission (LT) through different thicknesses increments; (3) assess biaxial flexural strength (BFS) and modulus (MO) according to depth of cure; (4) verify degree of conversion (DC) and microhardness (MH) and (5) correlate polymerization stress (PS) and gap formation (GF) in class I cavities of bulk-fill restorative materials, compared to a regular composite resin. Four bulk-fill composites were tested: Surefill SDR flow (SDR), Filtek Bulk Fill (FBF), Tetric EvoCeram Bulk Fill (TEC) and EverX Posterior (EXP). Herculite Classic (HER) was used as control. To morphological and composition characterization of inorganic content, a portion of each material was immersed in solvents to remove resin matrix and then analyzed by energy-dispersive X-ray and scanning electron microscopy. The LT was measured through different material thicknesses (1, 2, 3 and 4 mm) by a laboratory-grade spectral radiometer spectroradiometer (n=5). To BFS and MO tests, discs (0.5 mm thick) were fabricated using a set of eight molds, to simulate polymerization depth of 4 mm. DC obtained by Confocal Raman spectroscopy and Knoop MH were measured in 4 mm depth class I cavities, which were placed with the composites and it respective adhesives (n=5). PS was determined for each material by an extensometer attached to a universal testing machine (n=5). Filler particles of bulk-fill composites presented irregular, spherical or cylindrical shape, which size varied from 0.1 ?m to 1 mm. Regarding composition analysis, aluminum, barium and silicon were identified in all composites. All materials demonstrated lower LT with increased increment thickness. No differences were found in translucency among bulk-fill composites, only SDR had higher light transmission than HER. However, light attenuation did not influence BFS of bulk-fill composites, while HER presented decreased BFS at deeper layers. Nevertheless, HER still had the highest MO. DC was uniform among depths for SDR, FBF and HER applied incrementally. Conversely, TEC, EXP and HER bulk-filling presented a decrease in DC with increased depth. To MH test, lower results with increased depth were detected only for TEC, indeed there was no correlation between DC and MH analyzes. Regarding PS, EXP had the highest values, whilst TEC the lowest ones. Positive correlation was detected between PS and GF, which varied according to materials. Incremental filling technique reduced GF percentage to HER, and only SDR and TEC had comparable results to this conventional technique. Some of the bulk-fill composites presented similar or superior outcomes compared to control, which may be an option for traditional direct restorative procedures / Mestrado / Dentística / Mestra em Clínica Odontológica

Orientador: Ticiane Cestari Fagundes Tozzi / Resumo: O objetivo desse estudo foi avaliar o desgaste, as propriedades mecânicas, topografia e composição química dos substratos dentários e materiais restauradores após ciclo erosivo/abrasivo, utilizando diferentes dentifrícios. Foram utilizados 244 blocos, sendo 122 de esmalte e 122 blocos de dentina, medindo 4 x 4 mm, obtidos a partir de incisivos bovinos que foram cortados e polidos. Cada amostra continha um bloco de esmalte e um de dentina, entre os blocos foram confeccionadas restaurações com cimento de ionômero de vidro modificado por resina (CIVMR) e resina composta (RC). Após as restaurações, a hemiface de cada amostra foi recoberta com verniz ácido-resistente, afim de produzir o lado controle. Esses dois grupos foram subdivididos em três grupos, de acordo com o dentifrício utilizado no processo de abrasão: SF - sem flúor (controle negativo), NaF - com fluoreto de sódio 1450 ppm de F (controle positivo) e SnF2 - com fluoreto de estanho 1100 ppm de F. O ácido cítrico a 0,05 M, pH= 3.2, foi utilizado nos ciclos de erosão, sendo realizados 4x/dia, 2 minutos cada, com intervalos de 1 hora entre cada ciclo. Os espécimes foram submetidos à abrasão (2x/dia, ao final do primeiro e último ciclo erosivo/dia), aplicando o slurry (1:3) sobre as amostras por 2 minutos, seguidos de 15 segundos de escovação por espécime (200 g por 15 s), ao longo de 5 dias. Na sequência, o verniz ácido resistente foi removido da hemiface de cada amostra e estas foram analisadas quanto ao desgaste das supe... (Resumo completo, clicar acesso eletrônico abaixo) / Doutor

Orientador: Juliano Pelim Pessan / Coorientador: Alberto Carlos Botazzo Delbem / Banca: Rogério de Castilho Jacinto / Banca: Douglas Roberto Monteiro / Banca: Daniela Rios / Banca: Thiago Cruvinel da Silva / Resumo: O objetivo do presente estudo foi realizar uma revisão sistemática e meta-análise (MA) sobre o desempenho clínico do cimento de ionômero de vidro (CIV) comparado ao de resina composta (RC) em restaurações classe II em dentes decíduos. Foi realizada uma busca abrangente nas bases PubMeb, Scopus, Web of Science, LILACS-BBO, Cochrane Library, Clinical Trials e OpenGrey, sem restrições de data ou idioma. Foram utilizados termos Mesh, sinônimos e palavras chave, adaptados para cada base de dados. Também foi feita busca manual na lista de referências dos artigos selecionados. Foram incluídos 5 ensaios clínicos controlados e randomizados e 3 estudos clínicos não randomizados, que compararam o desempenho clínico, avaliado pela presença de lesões de cárie secundária, descoloração marginal, adaptação marginal, forma anatômica e retenção e desgaste do material restaurador de restaurações de classe II realizadas com CIV em comparação com restaurações de RC em dentes decíduos. Quinze estudos completos foram lidos na íntegra, dos quais 8 foram incluídos na síntese qualitativa (risco de viés) e quantitativa (meta-análise). A heterogeneidade variou de baixa a moderada nas 12 MAs realizadas dos 8 estudos, com acompanhamento de 6 a 48 meses (38 a 73%), não havendo diferença significativa entre os dois materiais na análise final (overall effect). A diferença de risco (intervalo de confiança 95%; valor de p) entre RC e CIV quanto a falhas foi de -0,03 (-0,11 - 0,05; p= 0,41); quanto a adaptação ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of the present study was to perform a systematic review and meta - analysis (MA) on the clinical performance of glass ionomer cement (GIC) compared to composite resin (CR) in class II restorations in deciduous teeth. A comprehensive search was performed on the PubMeb, Scopus, Web of Science, LILACS - BBO, Cochrane Library, Clinical Trials and OpenGrey databases, without dat e or language restrictions. Mesh terms, synonyms and key words were used, adapted for each database. Manual search was also performed on the list of references of the selected articles. Five randomized controlled trials and three non - randomized clinical tr ials comparing the clinical performance (assessed by the presence of secondary caries lesions, marginal discoloration, marginal adaptation, anatomical shape, and retention and wear of restorative material) were included in class restorations II performed w ith GIC compared to RC restorations in deciduous teeth. Fifteen complete studies were read in full, of which 8 were included in qualitative (risk of bias) and quantitative synthesis (meta - analysis). The heterogeneity ranged from low to moderate in the 12 M As from the 8 studies, with a follow - up of 6 to 48 months (38 to 73%), with no significant difference between the two materials in the final analysis (overall effect). The risk difference (95% confidence interval, p value) between RC and GIC for failure wa s - 0.03 ( - 0.11 - 0.05; p = 0.41); for marginal adaptation was - 0.01 ( - 0.06 - 0.05; p = 0.8); for marginal discoloration it was 0.07 ( - 0.11 - 0.26, p = 0.44), and for the anatomical form it was 0.00 ( - 0.04 - 0.05; p = 0.84). Regarding the presence of seconda ry caries lesion, the corresponding value was 0.07 (0.02 - 0.12; p = 0.01). The overall risk difference for clinical performance was 0.03 ( - 0.01 - 0.06, p = 0.17). For all the analyzed...(Complete abstract click electronic access below) / Doutor

Orientador: José Geraldo Nery / Resumo: A busca por novos materiais, principalmente materiais que apresentem múltiplas aplicações, continua atraindo pesquisas ao redor do mundo. Dentre os materiais pesquisados com esse intuito, os compósitos ganham destaque. Compósitos são materiais mistos formados pela união de dois ou mais materiais diferentes com a finalidade de produzir um material novo com propriedades distintas, em relação aos seus materiais de origem. Os compósitos podem ser aplicados em diferentes áreas, entre elas encontram-se a remediação ambiental e a hemostasia. A remediação ambiental se faz necessária principalmente pelo fato de que muitas fontes hídricas acabam sendo poluídas por resíduos nocivos a saúde humana e animal, como metais pesados, e o consumo destas águas acaba causando sérias doenças. Devido a isso a busca por agentes capazes de retirar estes poluentes da água torna-se necessária. Outro grande problema de saúde publica são as hemorragias incontroladas que continuam sendo umas das principais causas de mortes no mundo. Neste contexto, o objetivo deste trabalho foi sintetizar um compósito que apresente a capacidade de atuar tanto como agente de remediação ambiental como agente hemostático. O compósito foi sintetizado utilizando zeólita e quitosana como suas matrizes. O material foi caracterizado por Difração de Raios-X; Espectroscopia de Infravermelho e Microscopia Eletrônica de Varredura. O potencial de ação ambiental foi testado analisando a absorção de cátions de cádmio e chumbo, presentes... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The search for new materials, especially materials with multiple applications, continues to attract research from around the world. Among the materials researched for this purpose, composites stand out. Composites are mixed materials formed by joining two or more different materials in order to produce a new material with distinct properties relative to their source materials. Composites can be applied in different areas, including environmental remediation and hemostasis. Environmental remediation is necessary mainly due to the fact that many water sources end up being polluted by waste harmful to human and animal health, such as heavy metals, and the consumption of these waters ends up causing serious diseases. Because of this the search for agents capable of removing these pollutants from water becomes necessary. Another major public health problem is uncontrolled bleeding, which remains one of the leading causes of death worldwide. In this context, the objective of this work was to synthesize a composite that presents the ability to act as both environmental remediation agent and hemostatic agent. The composite was synthesized using zeolite and chitosan as their matrices. The material was characterized by X-ray diffraction; Infrared Spectroscopy and Scanning Electron Microscopy. The environmental action potential was tested by analyzing the absorption of cadmium and lead cations present in aqueous solution by the material, and the possible hemostatic application of the ma... (Complete abstract click electronic access below) / Mestre