Dissolution of soluble substrates such as gypsum presents a major hazard to dams in many parts of the world. This research simulates hypothesised conditions beneath the Mosul Dam, northwest Iraq, where collapse of a karstic system associated with continuous fresh water supply from its massive reservoir water is a recognised problem. The gypsum substrates at Mosul Dam vary in purity and thickness. Experimental work used gypsum rocks and gypseous soils. Gypsum rocks from northern Iraq and similar rocks from Bantycock gypsum mine, UK, were analysed for short-term mechanical response following immersion (5 to 50 weeks) and long-term loading during immersion (maximum 50 weeks). New experimental devices were developed from a conventional oedometer. Cylinder samples (NX, standard diamond drill core size = 54mm diameter, length/diameter ratio equal to 2.5) provided a proxy for massive gypsum strata, while thin samples (NX = 54mm in diameter, 20mm thickness) represented thin layers and lenses. Rectangular bar samples (240 x 40 x 20 mm and 140 x 40 x 20 mm) were tested for short-and long-term mechanical four-point bending behaviour. Samples were permanently submerged at a variety of water pressures, with the influence of groundwater recharge and flow on dissolution simulated by regular changes of water. Stress on each sample was progressively increased to a maximum of 2688 kPa. Small increases in strain were recorded by the end of each test but no failures occurred within 60 days of tests. However, notable failure due to water pressure and axial stress over long time periods of 166 and 238 days occurred. Visible physical changes were observed, notably a decrease in sample mass and volume. Similar change was recorded in ultrasonic velocities. These indicate that gypsum collapse risk beneath dams requires prolonged exposure to dissolution. Gypseous soils from Iraq and similar artificially-prepared soils were also tested. Gypseous soil samples (diameter = 50mm and length = 20mm) and box model strata results showed that gypseous soils are significantly weakened by dissolution over 15 weeks and 50 weeks respectively. Dams built on gypsum substrates are likely to experience ongoing weakening of their foundations, with a progressively increasing risk of failure. This is expected to be enhanced for dams with a large and deep reservoir that induces high ground water pressure.

Gelžbetonis yra kompozitinė medžiaga, kurios komponentai yra betonas ir plieninė armatūra. Kaip žinoma, betono stipris tempiant yra 1020 kartų mažesnis nei stipris gniuždant. Atrodytų, kad tempiamojo betono įtaka, atlaikant įrąžas skerspjūvyje, yra nereikšminga. Iš tiesų, nustatant lenkiamųjų elementų stiprumą normaliniame pjūvyje, tempiamo betono įtempių galima nevertinti. Kita vertus, skaičiuojant įlinkius, neįvertinus tempiamojo betono įtakos, gali būti daroma didesnė nei 100 % paklaida. Adekvatus supleišėjusio tempiamojo betono įtakos įvertinimas, nustatant trumpalaike apkrova veikiamų gelžbetoninių elementų deformacijas, yra bene svarbiausia ir sudėtingiausia problema. Plyšio vietoje betonas negali atlaikyti tempimo įtempių, todėl visą įrąžą atlaiko armatūra. Kadangi plyšyje ir gretimuose pjūviuose armatūra praslysta betono atžvilgiu, kontakto zonoje atsiranda tangentiniai įtempiai. Šie įtempiai perduodami betonui, todėl jis atlaiko tempimo įtempius. Armatūros ir betono sąveika ruožuose tarp plyšių standina gelžbetoninį elementą. Supleišėjusio betono gebėjimas atlaikyti tempimo įtempius vadinama tempimo sustandėjimu (angl. tension stiffening). Šis efektas dažniausiai modeliuojamas supleišėjusio betono įtempių ir deformacijų diagrama, taikant vidutinių plyšių koncepciją. Tuomet neatsižvelgiama į diskrečius plyšius, o supleišėjęs betonas traktuojamas kaip ortotropinė medžiaga su pakitusiomis savybėmis. Dauguma tempimo sustandėjimo modelių įvertina betono įtempių... [toliau žr. visą tekstą] / Modelling behaviour of cracked tensile concrete is a complicated issue. Due to bond with reinforcement, the cracked concrete between cracks carries a certain amount of tensile force normal to the cracked plane. Concrete adheres to rein-forcement bars and contributes to overall stiffness of the structure. The phe-nomenon, called tension-stiffening, has significant influence on the results of short-term deformational analysis. Assumption of a tension-stiffening law has great influence on numerical results of load – deflection behaviour of reinforced concrete members subjected to short – term loading. Under wrong assumption of this law, errors in calculated deflections, particularly for lightly members, may exceed 100 %. Most known tension-stiffening relationships relate average stresses to average strains. However, some experimental and theoretical investi-gations have shown that tension-stiffening may be affected by other parameters. The scientific supervisor of the thesis has proposed a tension-stiffening model depending on reinforcement ratio. This model has been developed using experi-mental data reported in the literature. Besides, concrete shrinkage effect was not taken into account. The main objective of this PhD dissertation is to propose a tension-stiffening law for bending RC members subjected to short-term loading with eliminated concrete shrinkage effect.

Modelling behaviour of cracked tensile concrete is a complicated issue. Due to bond with reinforcement, the cracked concrete between cracks carries a certain amount of tensile force normal to the cracked plane. Concrete adheres to rein-forcement bars and contributes to overall stiffness of the structure. The phe-nomenon, called tension-stiffening, has significant influence on the results of short-term deformational analysis. Assumption of a tension-stiffening law has great influence on numerical results of load – deflection behaviour of reinforced concrete members subjected to short – term loading. Under wrong assumption of this law, errors in calculated deflections, particularly for lightly members, may exceed 100 %. Most known tension-stiffening relationships relate average stresses to average strains. However, some experimental and theoretical investi-gations have shown that tension-stiffening may be affected by other parameters. The scientific supervisor of the thesis has proposed a tension-stiffening model depending on reinforcement ratio. This model has been developed using experi-mental data reported in the literature. Besides, concrete shrinkage effect was not taken into account. The main objective of this PhD dissertation is to propose a tension-stiffening law for bending RC members subjected to short-term loading with eliminated concrete shrinkage effect. / Gelžbetonis yra kompozitinė medžiaga, kurios komponentai yra betonas ir plieninė armatūra. Kaip žinoma, betono stipris tempiant yra 10-20 kartų mažesnis nei stipris gniuždant. Atrodytų, kad tempiamojo betono įtaka, atlaikant įrąžas skerspjūvyje, yra nereikšminga. Iš tiesų, nustatant lenkiamųjų elementų stiprumą normaliniame pjūvyje, tempiamo betono įtempių galima nevertinti. Kita vertus, skaičiuojant įlinkius, neįvertinus tempiamojo betono įtakos, gali būti daroma didesnė nei 100 % paklaida. Adekvatus supleišėjusio tempiamojo betono įtakos įvertinimas, nustatant trumpalaike apkrova veikiamų gelžbetoninių elementų deformacijas, yra bene svarbiausia ir sudėtingiausia problema. Plyšio vietoje betonas negali atlaikyti tempimo įtempių, todėl visą įrąžą atlaiko armatūra. Kadangi plyšyje ir gretimuose pjūviuose armatūra praslysta betono atžvilgiu, kontakto zonoje atsiranda tangentiniai įtempiai. Šie įtempiai perduodami betonui, todėl jis atlaiko tempimo įtempius. Armatūros ir betono sąveika ruožuose tarp plyšių standina gelžbetoninį elementą. Supleišėjusio betono gebėjimas atlaikyti tempimo įtempius vadinama tempimo sustandėjimu (angl. tension stiffening). Šis efektas dažniausiai modeliuojamas supleišėjusio betono įtempių ir deformacijų diagrama, taikant vidutinių plyšių koncepciją. Tuomet neatsižvelgiama į diskrečius plyšius, o supleišėjęs betonas traktuojamas kaip ortotropinė medžiaga su pakitusiomis savybėmis. Dauguma tempimo sustandėjimo modelių įvertina betono įtempių... [toliau žr. visą tekstą]