SÃntese e caracterizacÃes de nanopartÃculas de FeCo/(Fe,Co)304 com acoplamento magnÃtico tipo exchange spring sintetizadas pelo mÃtodo sol-gel Proteico. / Synthesis and characterization of FeCo/(Fe,Co)3O4 nanoparticles with magnetic couplings synthesized by Sol-gel protein methodDiego FÃlix Dias 21 December 2015 (has links)
Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / NanopartÃculas de FeCo recobertas com (Fe,Co)3O4 (Magnetita dopadas com cobalto) na estrutura casca caroÃo (Core-Shell), foram sintetizadas pela rota quÃmica conhecida como Sol-Gel Proteica. Os materiais sintetizados foram caracterizados por Termogravimetria (TG), DifraÃÃo de Raios-X (DRX), Magnetometria de Amostra Vibrante (VSM), Espectroscopia MÃssbauer, Microscopia EletrÃnica de Varredura (MEV) e Microscopia EletrÃnica de TransmissÃo (MET). Os resultados mostram que o aumento da temperatura de re-oxidaÃÃo influi diretamente no tamanho da casca (Shell) bem como o aumento da razÃo entre a magnetizaÃÃo remanente pela magnetizaÃÃo de saturaÃÃo. O efeito de Exchange Spring e Exchange Bias foram observados nas curvas de histerese. A estrutura Core-Shell foi formada de maneira nÃo homogÃnea, ou seja, nem todas as partÃculas foram recobertas pela magnetita. / FeCo Nanoparticles coated with (Fe,Co)3O4 (Magnetite doped with cobalt) were synthesized by the chemical route known as Sol-Gel Protein. The synthesized materials were characterized by thermogravimetry (TG), X-Ray Diffraction (XRD), Vibrating Sample Magnetometry (VSM), MÃssbauer spectroscopy, Scanning Electronic Miscroscopy (SEM) and Transmission Electronic Microscopy (TEM). The results show that the increase in temperature directly influences the size of the shell (Shell) and increased the ratio of remanent magnetization to the saturation magnetization. The effect of Exchange Spring and Exchange Bias were observed in the hysteresis curves. The Core-Shell structure was formed a non-homogeneous manner, ie not all the magnetite particles were coated.
|
2 |
Aglomerados de CayFe12-yO19(0 ≤ y ≤ 1,0) diluídos em uma matriz antiferromagnéticaPassos, José Cleverton da Conceição 25 February 2015 (has links)
In this dissertation were studied powders and pellets of the CayFe12-yO19-aFe2O3(0 ≤ y ≤ 1,0) obtained by the proteic sol-gel process having as precursor coconut water. Samples were
analyzed by techniques of X-ray diffraction, magnetometry and impedance. The impedance analysis showed that resistivity increased with the calcium concentration to 0.0 <y ≤ 0.2, but
decreased for y> 0.2 and reached saturation at 7.5×106 Ω.cm to y = 0.9. The magnetization curve as a function of the magnetic field presents high values of saturation magnetization (Ms
= 40 emu / g) with low remanent field (Mr = 6.7 emu / g) and coercive field (Hc = 320 Oe). By means of X- ray diffraction we have observed that agglomerates of the type hexaferrite
CaM were formed after the doping with hematite, i.e., there was the existence of the two phases occurring antiferromagnetic coupling confirmed by exchange bias field of 9.6 Oe. / Resumo : Nesta dissertação foram estudados os pós e pastilhas de CayFe12-yO19 - (0 ≤ y ≤ 1,0) obtidos por meio do processo sol-gel proteico que tem como precursor água de coco. As amostras foram analisadas através de técnicas de difratometria de raios X, magnetometria e impedanciometria. A análise de impedância mostrou que a resistividade aumentou com a concentração de cálcio para 0,0 < y 0,2, mas diminuiu para y> 0,2 e atingiu a saturação em 7,5×106 cm para y = 0,9. A curva de magnetização como uma função do campo magnético teve valores elevados de magnetização de saturação (Ms = 40 emu/g) com baixo campo remanente (Mr = 6,7 emu/g) e campo coercivo (Hc = 320 Oe). Por meio da difratometria de raios X observou-se que foram formados aglomerados da hexaferrita tipo CaM a partir da dopagem da hematita, ou seja, houve a existência das duas fases ocorrendo um acoplamento ferro-antiferro, confirmado pelo campo de exchange bias na curva de M x H de 9,6 Oe.
|