Aproveitamento de resíduo de soja para produção de painéis MDP (Medium Density Particleboard) / Use of soybean residue for production of MDP panels (Medium Density Particleboard)Guimarães, Íngrid Luz 23 March 2017 (has links)
Submitted by Erika Demachki (erikademachki@gmail.com) on 2017-06-29T22:20:43Z
No. of bitstreams: 2
Dissertação - Ingrid Luz Guimarães - 2017.pdf: 1402447 bytes, checksum: 7d2b3bc12c14d9a3bd34392e4f9d7049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2017-07-10T10:46:04Z (GMT) No. of bitstreams: 2
Dissertação - Ingrid Luz Guimarães - 2017.pdf: 1402447 bytes, checksum: 7d2b3bc12c14d9a3bd34392e4f9d7049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-07-10T10:46:05Z (GMT). No. of bitstreams: 2
Dissertação - Ingrid Luz Guimarães - 2017.pdf: 1402447 bytes, checksum: 7d2b3bc12c14d9a3bd34392e4f9d7049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Previous issue date: 2017-03-23 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Soybean pre-cleaning residue is found in large quantities in the processing and processing
dryers' farms, resulting in serious inconvenience if it is not removed to farther places before the
fermentation process begins. Among the residues generated at the time of harvesting and cleaning
of the grains are soybean pods, which presents as an alternative lignocellulosic material to be used
in the production of Agglomerated panels of the MDP type. The objective of this work was to
verify the effect of the use of soybean pods in the production of eucalyptus MDP panels. The
panels, with a nominal density of 0.70 g / cm³, were composed of three layers, the thin layers of
eucalyptus wood were used in the covers and the core was composed of a mixture of eucalyptus
particles and soybean pods. The proportions used of soybean residue particles in relation to those
of eucalyptus in the kernels were 0, 25, 50, 75 and 100%. For the glueing of the particles the
adhesive urea formaldehyde, in the proportion of 12%, was used for both the covers and the crumb.
The pressing cycle had a temperature of 160 ° C for a period of 15 minutes at a pressure of 4MPa.
To evaluate the quality of the panels produced, their physical and mechanical properties of
apparent density; Compaction ratio; Water absorption and swelling in thickness at 2 and 24 hours
of immersion were determinater; Perpendicular traction; Modulus of elasticity and modulus of
rupture in the static bending. To meet the requirements of Brazilian standard (NBR 14.810 / 2002),
for the properties of swelling in thickness (2h) and modulus of rupture, the maximum amount of
soybean recommended for MDP panels is 20%. / O resíduo da pré-limpeza de soja é encontrado em grande quantidade no pátio das
indústrias de beneficiamento e dos secadores das fazendas, acarretando sérios transtornos
caso não seja removido para locais mais afastados antes que o processo de fermentação se
inicie. Dentre os resíduos gerados no momento da colheita e limpeza dos grãos estão às
vagens de soja, que se apresenta como um material lignocelulósico alternativo para ser
utilizado na produção de painéis aglomerados do tipo MDP. Este trabalho teve como objetivo
verificar o efeito da utilização de vagens de soja na produção de painéis MDP de eucalipto. Os
painéis, com densidade nominal de 0,70 g/cm³, foram constituídos por três camadas, de
modo que nas capas foram utilizadas finas partículas de madeira de eucalipto e o miolo foi composto por uma mistura de partículas de eucalipto e de vagens soja. As proporções
utilizadas de partículas de resíduo de soja em relação às de eucalipto no miolo foram de 0,
25, 50, 75 e 100%. Para o encolamento das partículas foi utilizado o adesivo uréia
formaldeído, na proporção de 12%, tanto para as capas como para o miolo. O ciclo de
prensagem teve temperatura de 160°C, por um período de 15 minutos a uma pressão de
4MPa. Para avaliar a qualidade dos painéis produzidos, foram determinadas suas propriedades
físicas e mecânicas de densidade aparente; razão de compactação; absorção de água e
inchamento em espessura em 2 e 24 horas de imersão; tração perpendicular; módulo de
elasticidade e módulo de ruptura na flexão estática. Para atender as exigências da norma
brasileira (NBR 14.810/2002), para as propriedades de inchamento em espessura (2h) e
módulo de ruptura, a quantidade máxima de vagem de soja recomendada para painéis MDP é
de 20%.
|