<p>Bridge deck deterioration due to chloride-induced pitting corrosion of steel reinforcement is a common occurrence. Because rust decreases the cross-sectional area of reinforcing bars, corrosion of bridge deck reinforcement directly reduces the structural capacity of the bridge deck. A typical NDT method for assessing the possibility of corrosion at the top reinforcement level is ground-penetrating radar (GPR). The goal of the study is to investigate the effect of reducing the cross-sectional area of the reinforcing bar on deck strength due to corrosion. Flexural and shear failure were considered in the analysis. In conclusion, typical corrosion of reinforcement was not found to cause a bridge deck to collapse after testing the flexure with the yield line method, the one-way and two-way shears with AASHTO LRFD Bridge Design Specifications (2020), and the one-way shear with ACI 318 (2019). </p>

This thesis reports on the research outcome of corrosion mechanism and corrosion rate of mild steel in different environments (saline, alkaline solutions and concrete media) using potentiodynamic polarization technique. The study also included the effect of corrosion on bond strength between reinforcing steel and concrete using pull-out test. Corrosion of mild steel and 316L stainless steel with different surface conditions in 1, 3 and 5% saline (NaCl + Distilled water) was investigated. Specimens ground with 200 and 600 grit silicon carbide grinding paper as well as 1μm surface finish (polished with 1μm diamond paste) were tested. In case of mild steel specimens, reduction in surface roughness caused increase in corrosion rate, while in 316L stainless steel corrosion rate decreased as the surface roughness improved. Metallographic examination of corroded specimens confirmed breakdown of passive region due to pitting corrosion. Corrosion of mild steel was also investigated in alkaline solution (saturated calcium hydroxide, pH =12.5) contaminated with 1, 3 and 5% saline. A series of corrosion experiments were also conducted to examine the efficiency of various concentrations of calcium nitrite (CN) on corrosion behaviour of both as-received and polished mild steel in alkaline solution containing 3% saline after 1 hour and 28 days of exposure. Corrosion rate was higher for the as-received than polished mild steel surface under the same testing conditions in NaCl alkaline solution with and without nitrites due to the effect of surface roughness. Morphology investigation of mild steel specimens in alkaline solution ii containing chlorides and nitrites showed localized pits even at nitrite concentration equal to chloride concentration. Corrosion of steel bars embedded in concrete having compressive strengths of 20, 30 and 46MPa was also investigated. The effect of 2 and 4% CN by weight of cement on corrosion behaviour of steel bar in low and high concrete strengths specimens were also studied. All reinforced concrete specimens were immersed in 3% saline solution for three different periods of 1, 7 and 15 days. In order to accelerate the chemical reactions, an external current of 0.4A was applied. Corrosion rate was measured by retrieving electrochemical information from polarization tests. Pull-out tests of reinforced concrete specimens were then conducted to assess the corroded steel/concrete bond characteristics. Experimental results showed that corrosion rate of steel bars and bond strength were dependent on concrete strength, amount of CN and acceleration corrosion period. As concrete strength increased from 20 to 46MPa, corrosion rate of embedded steel decreased. First day of corrosion acceleration showed a slight increase in steel/concrete bond strength, whereas severe corrosion due to 7 and 15 days corrosion acceleration significantly reduced steel/concrete bond strength. Addition of only 2% CN did not give corrosion protection for steel reinforcement in concrete with 20MPa strength at long time of exposure. However, the combination of good quality concrete and addition of CN appear to be a desirable approach to reduce the effect of chloride induced corrosion of steel reinforcement. At less time of exposure, specimens without CN showed higher bond strength in both concrete mixes than those with CN. After 7 days of corrosion acceleration, the higher concentration of CN gave higher bond strength in both concrete mixes. The same trend was observed at 15 days of corrosion acceleration except for the specimen with 20MPa compressive strength and 2% CN which recorded the highest deterioration in bond strength.

This thesis reports on the research outcome of corrosion mechanism and corrosion rate of mild steel in different environments (saline, alkaline solutions and concrete media) using potentiodynamic polarization technique. The study also included the effect of corrosion on bond strength between reinforcing steel and concrete using pull-out test. Corrosion of mild steel and 316L stainless steel with different surface conditions in 1, 3 and 5% saline (NaCl + Distilled water) was investigated. Specimens ground with 200 and 600 grit silicon carbide grinding paper as well as 1¿m surface finish (polished with 1¿m diamond paste) were tested. In case of mild steel specimens, reduction in surface roughness caused increase in corrosion rate, while in 316L stainless steel corrosion rate decreased as the surface roughness improved. Metallographic examination of corroded specimens confirmed breakdown of passive region due to pitting corrosion. Corrosion of mild steel was also investigated in alkaline solution (saturated calcium hydroxide, pH =12.5) contaminated with 1, 3 and 5% saline. A series of corrosion experiments were also conducted to examine the efficiency of various concentrations of calcium nitrite (CN) on corrosion behaviour of both as-received and polished mild steel in alkaline solution containing 3% saline after 1 hour and 28 days of exposure. Corrosion rate was higher for the as-received than polished mild steel surface under the same testing conditions in NaCl alkaline solution with and without nitrites due to the effect of surface roughness. Morphology investigation of mild steel specimens in alkaline solution ii containing chlorides and nitrites showed localized pits even at nitrite concentration equal to chloride concentration. Corrosion of steel bars embedded in concrete having compressive strengths of 20, 30 and 46MPa was also investigated. The effect of 2 and 4% CN by weight of cement on corrosion behaviour of steel bar in low and high concrete strengths specimens were also studied. All reinforced concrete specimens were immersed in 3% saline solution for three different periods of 1, 7 and 15 days. In order to accelerate the chemical reactions, an external current of 0.4A was applied. Corrosion rate was measured by retrieving electrochemical information from polarization tests. Pull-out tests of reinforced concrete specimens were then conducted to assess the corroded steel/concrete bond characteristics. Experimental results showed that corrosion rate of steel bars and bond strength were dependent on concrete strength, amount of CN and acceleration corrosion period. As concrete strength increased from 20 to 46MPa, corrosion rate of embedded steel decreased. First day of corrosion acceleration showed a slight increase in steel/concrete bond strength, whereas severe corrosion due to 7 and 15 days corrosion acceleration significantly reduced steel/concrete bond strength. Addition of only 2% CN did not give corrosion protection for steel reinforcement in concrete with 20MPa strength at long time of exposure. However, the combination of good quality concrete and addition of CN appear to be a desirable approach to reduce the effect of chloride induced corrosion of steel reinforcement. At less time of exposure, specimens without CN showed higher bond strength in both concrete mixes than those with CN. After 7 days of corrosion acceleration, the higher concentration of CN gave higher bond strength in both concrete mixes. The same trend was observed at 15 days of corrosion acceleration except for the specimen with 20MPa compressive strength and 2% CN which recorded the highest deterioration in bond strength.