Quantitative characterization of microstructure in high strength microalloyed steelsLi, Xiujun Unknown Date
No description available.
|
2 |
Quantitative characterization of microstructure in high strength microalloyed steelsLi, Xiujun 11 1900 (has links)
X-ray diffraction (XRD) profile fitting (Rietveld method) was used in this study to characterize the microstructure for seven microalloyed steels, which were produced through thermomechanical controlled processing (TMCP). Microstructure characterization was conducted through the strip thickness. The microstructural variables studied include subgrain size, dislocation density, texture index and weight percent of retained austenite. The subgrain size was also analyzed by electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). The effects of processing parameters, including coiling temperature, cooling rate and alloying elements, on the microstructure were also investigated. It was found that decreasing the coiling temperature resulted in a finer subgrain size and higher dislocation densities. The texture index was observed to increase with decreasing coiling temperature. The subgrain size decreased and dislocation density increased as the amount of alloying elements (Ni, Mo and Mn) were increased. The amount of retained austenite increased at the strip center with increasing coiling temperature and increasing C and Ni content. / Materials Engineering
|
Page generated in 0.0536 seconds