Conselho Nacional de Desenvolvimento Científico e Tecnológico / Epoxy paints are organic coatings applied on the metal surface and hindering the contact surface with the corrosive medium. The condition of curing a resin is of fundamental importance because it affects the mechanical behavior of crosslinked resin. This paper aims to present a study monitoring the curing process of two types of epoxy paints, primer and finishing with the variation of temperature and time, Since the polyamide as curing agent in paint primer and polyamine in paint topcoats. The technique of Raman spectroscopy was used to monitor the cure of epoxy resin and the technique of thermogravimetric analysis (TGA) was used only to verify the onset of degradation temperature of each specific component. The crosslinking process was monitored by Raman spectroscopy for 12 hours consecutive, obtained by heating in Raman spectrometer at temperatures of 50, 100, 125 and 150°C and room temperature for nine days. The monitoring results indicate that cure of the paint primer showed better cure temperature to 100°C with the best curing time around 4 hours and the topcoat with curing temperature of 50°C with the best curing time around 8 hours. / As tintas epóxi são revestimentos orgânicos aplicados sobre a superfície metálica e que dificultam o contato da superfície com o meio corrosivo. A condição de cura de uma resina é de fundamental importância, pois afeta o comportamento mecânico da resina reticulada. Esta dissertação tem por objetivo apresentar um estudo do monitoramento do processo de cura de dois tipos de tintas epóxi, primer e de acabamento, com variação da temperatura e do tempo, tendo a poliamida como agente de cura nas tintas primer e a poliamina nas tintas de acabamento. A técnica de espectroscopia Raman foi utilizada para monitorar a cura da resina epóxi e a técnica de análise termogravimétrica (TGA) foi utilizada apenas para verificar o início da temperatura de degradação de cada componente específico. O processo de reticulação foi monitorado por espectroscopia Raman por 12h consecutivas, obtidos com aquecimento no espectrômetro Raman nas temperaturas de 50, 100, 125 e 150°C e a temperatura ambiente por nove dias. Os resultados do monitoramento da cura indicam que a tinta primer mostrou melhor temperatura de cura a 100°C com melhor tempo de cura em torno de 4h, bem como a tinta de acabamento com temperatura de cura de 50°C com melhor tempo de cura em torno de 8h.

A utilização de produtos provenientes de fontes renováveis e livres de substâncias tóxicas é tendência global, prova disso é o constante aumento da demanda por produtos à base de madeira. Segundo o Forest Products Statistics (2015), a produção mundial de painéis de madeira reconstituída, em 2014, foi de 388 milhões de m³, um aumento de 5,5% em comparação com o ano anterior e um aumento de 34% quando comparado com 2010. No entanto, o setor industrial de painéis de madeira há décadas enfrenta um grande desafio com relação às emissões tóxicas vindas dos adesivos convencionais. Diante destes problemas, a proposta do presente trabalho foi testar a viabilidade da produção de painéis aglomerados e painéis OSB, com significativa redução da emissão de formaldeído, a partir de resíduos de madeira de Pinus sp. e Tectona grandis (Teca). Neste sentido, buscou-se contribuir para o aumento do conhecimento científico sobre a utilização do polímero natural polihidroxibutirato (PHB) e do resíduo de tinta à base de resina epóxi como adesivos alternativos. Os painéis foram fabricados variando-se os parâmetros de produção para obtenção de melhores condições de processo, sendo estes: densidade baixa, média e alta; teor de adesivo de 20, 30 e 40%; adição de partículas de Teca nas proporções de 0, 25, 50, 75, 100%. O desempenho físico-mecânico dos painéis foi avaliado com base nas normas ABNT NBR 14810 (2013) e ANSI A208.1 (2009). Realizou-se análise de variância (ANOVA) para testar a influência dos fatores individuais (densidade, percentual de adesivo e fração de Teca), além das interações entre tais fatores nas propriedades físico-mecânicas dos painéis. Os resultados apontaram para excelentes propriedades físicas e mecânicas dos painéis aglomerados de média e alta densidade, tendo resíduo de tinta, principalmente, nas proporções de 30 e 40%. Na maioria dos casos as propriedades de tais painéis foram superiores aos requisitos estipulados pela norma brasileira e pelas internacionais. Assim, ficou confirmada a viabilidade de produção dos aglomerados com pelo menos um dos insumos estudados bem como seu potencial de emprego para as finalidades compatíveis com produtos desta natureza. / The use of products from renewable sources and free of toxic substances is a global trend, the proof is the steady increase in demand for wood-based products. According to the Forest Products Statistics (2015), world production of reconstituted wood panels in 2014 was 388 million cubic meters, an increase of 5.5% compared to the previous year and an increase of 34% compared to 2010. However, the industrial sector of wood panels for decades faces a major challenge with regard to toxic emissions coming from conventional adhesives. Faced with these problems, the purpose of this study was to test the feasibility of production of panels and OSB panels, with significant reduction of formaldehyde emissions from wood waste Pinus sp. and teak (Teak). In this sense, we sought to contribute to the increase of scientific knowledge on the use of natural polymer polyhydroxybutyrate (PHB) and residual ink resin-based epoxy as alternative adhesives. The panels were manufactured by varying the production parameters to obtain the best processing conditions, namely: low density, medium and high; resin content of 20, 30 and 40%; adding particles of Teak in proportions of 0, 25, 50, 75, 100%. The physical-mechanical performance of the panels was evaluated based on the standards NBR 14810 (2013) and ANSI A208.1 (2009). Held analysis of variance (ANOVA) to test the influence of individual factors (density, adhesive percentage and fraction Teak), and the interactions among these factors in the physical-mechanical properties of the panels. The results showed excellent physical and mechanical properties of the panels average clusters and high density, and ink residue, mainly in the proportions of 30 and 40%. In most cases the properties of these boards were superior to the requirements set by the Brazilian and international standards. Thus, it was confirmed production of agglomerates with at least one viability of inputs studied as well as their potential for employment for purposes compatible with products of this nature.

A utilização de produtos provenientes de fontes renováveis e livres de substâncias tóxicas é tendência global, prova disso é o constante aumento da demanda por produtos à base de madeira. Segundo o Forest Products Statistics (2015), a produção mundial de painéis de madeira reconstituída, em 2014, foi de 388 milhões de m³, um aumento de 5,5% em comparação com o ano anterior e um aumento de 34% quando comparado com 2010. No entanto, o setor industrial de painéis de madeira há décadas enfrenta um grande desafio com relação às emissões tóxicas vindas dos adesivos convencionais. Diante destes problemas, a proposta do presente trabalho foi testar a viabilidade da produção de painéis aglomerados e painéis OSB, com significativa redução da emissão de formaldeído, a partir de resíduos de madeira de Pinus sp. e Tectona grandis (Teca). Neste sentido, buscou-se contribuir para o aumento do conhecimento científico sobre a utilização do polímero natural polihidroxibutirato (PHB) e do resíduo de tinta à base de resina epóxi como adesivos alternativos. Os painéis foram fabricados variando-se os parâmetros de produção para obtenção de melhores condições de processo, sendo estes: densidade baixa, média e alta; teor de adesivo de 20, 30 e 40%; adição de partículas de Teca nas proporções de 0, 25, 50, 75, 100%. O desempenho físico-mecânico dos painéis foi avaliado com base nas normas ABNT NBR 14810 (2013) e ANSI A208.1 (2009). Realizou-se análise de variância (ANOVA) para testar a influência dos fatores individuais (densidade, percentual de adesivo e fração de Teca), além das interações entre tais fatores nas propriedades físico-mecânicas dos painéis. Os resultados apontaram para excelentes propriedades físicas e mecânicas dos painéis aglomerados de média e alta densidade, tendo resíduo de tinta, principalmente, nas proporções de 30 e 40%. Na maioria dos casos as propriedades de tais painéis foram superiores aos requisitos estipulados pela norma brasileira e pelas internacionais. Assim, ficou confirmada a viabilidade de produção dos aglomerados com pelo menos um dos insumos estudados bem como seu potencial de emprego para as finalidades compatíveis com produtos desta natureza. / The use of products from renewable sources and free of toxic substances is a global trend, the proof is the steady increase in demand for wood-based products. According to the Forest Products Statistics (2015), world production of reconstituted wood panels in 2014 was 388 million cubic meters, an increase of 5.5% compared to the previous year and an increase of 34% compared to 2010. However, the industrial sector of wood panels for decades faces a major challenge with regard to toxic emissions coming from conventional adhesives. Faced with these problems, the purpose of this study was to test the feasibility of production of panels and OSB panels, with significant reduction of formaldehyde emissions from wood waste Pinus sp. and teak (Teak). In this sense, we sought to contribute to the increase of scientific knowledge on the use of natural polymer polyhydroxybutyrate (PHB) and residual ink resin-based epoxy as alternative adhesives. The panels were manufactured by varying the production parameters to obtain the best processing conditions, namely: low density, medium and high; resin content of 20, 30 and 40%; adding particles of Teak in proportions of 0, 25, 50, 75, 100%. The physical-mechanical performance of the panels was evaluated based on the standards NBR 14810 (2013) and ANSI A208.1 (2009). Held analysis of variance (ANOVA) to test the influence of individual factors (density, adhesive percentage and fraction Teak), and the interactions among these factors in the physical-mechanical properties of the panels. The results showed excellent physical and mechanical properties of the panels average clusters and high density, and ink residue, mainly in the proportions of 30 and 40%. In most cases the properties of these boards were superior to the requirements set by the Brazilian and international standards. Thus, it was confirmed production of agglomerates with at least one viability of inputs studied as well as their potential for employment for purposes compatible with products of this nature.