Spelling suggestions: "subject:"transparent transistor"" "subject:"ransparent transistor""
1 |
Materials Approaches for Transparent ElectronicsIheomamere, Chukwudi E. 12 1900 (has links)
This dissertation tested the hypothesis that energy transferred from a plasma or plume can be used to optimize the structure, chemistry, topography, optical and electrical properties of pulsed laser deposited and sputtered thin-films of ZnO, a-BOxNy, and few layer 2H-WS2 for transparent electronics devices fabricated without substrate heating or with low substrate heating. Thus, the approach would be compatible with low-temperature, flexible/bendable substrates. Proof of this concept was demonstrated by first optimizing the processing-structure-properties correlations then showing switching from accumulation to inversion in ITO/a-BOxNy/ZnO and ITO/a-BOxNy/2H-WS2 transparent MIS capacitors fabricated using the stated processes. The growth processes involved the optimization of the individual materials followed by growing the multilayer stacks to form MIS structures. ZnO was selected because of its wide bandgap that is transparent over the visible range, WS2 was selected because in few-layer form it is transparent, and a-BOxNy was used as the gate insulator because of its reported atomic smoothness and low dangling bond concentration. The measured semiconductor-insulator interfacial trap properties fall in the range reported in the literature for SiO2/Si MOS structures. X-ray photoelectron spectroscopy (XPS), Hall, photoluminescence, UV-Vis absorption, and X-ray diffraction (XRD) measurements investigated the low-temperature synthesis of ZnO. All films are nanocrystalline with the (002) XRD planes becoming more prominent in films grown with lower RF power or higher pressure. Low power or high chamber pressure during RF magnetron sputtering resulted in a slower growth rate and lower energetic conditions at the substrate. Stoichiometry improved with RF power. The measurements show a decrease in carrier concentration from 6.9×1019 cm-3 to 1.4×1019 cm-3 as power increased from 40 W to 120 W, and an increase in carrier concentration from 2.6×1019 cm-3 to 8.6×1019 cm-3 as the deposition pressure increased from 3 to 9 mTorr. The data indicates that in the range of conditions used, bonding, stoichiometry, and film formation are governed by energy transfer from the plasma to the growing film. XPS characterizations, electrical measurements, and atomic force microscopy (AFM) measurements reveal an increase in oxygen concentration, improved dielectric breakdown, and improved surface topography in a-BOxNy films as deposition pressure increased. The maximum breakdown strength obtained was ~8 MVcm-1, which is comparable to a-BN. Metal-Insulator-Metal (MIM) structures of a-BOxNy grown at 10 and 15 mTorr suggest a combination of field-enhanced Schottky emission and Frenkel-Poole emission are likely transport mechanisms in a-BOxNy. In comparison, better fitted data was gotten for field enhanced Schottky emission which suggests the more dominant mechanism. The static dielectric constant range is 3.26 – 3.58 for 10 and 15 mTorr films. Spectroscopic ellipsometry and UV-Vis spectroscopy measured a bandgap of 3.9 eV for 15 mTorr grown a-BOxNy. 2H-WS2 films were grown on both quartz and a-BOxNy which revealed that the XRD (002) planes became more prominent as substrate temperature increased to 400 oC. AFM shows nano-grains at lower growth pressure. Increasing the growth pressure to 1 Torr resulted in the formation of larger particles. XPS chemical analysis reveals improved sulfur to tungsten ratios as pressure increased. Sulfur deficient films were n-type, whereas sulfur rich conditions produced p-type films. Frequency dependent C-V and G-V measurements revealed an interface trap concentration (Nit) of 7.3×1010 cm-2 and interface state density (Nss) of 7.5×1012 eV-1cm-2 for the transparent ITO/a-BOxNy/ZnO MIS structures, and approximately 2 V was required to switch the a-BOxNy/ZnO interface from accumulation to inversion. Using 2H-WS2 as the channel material, the ITO/a-BOxNy/2H-WS2 required approximately 4 V to switch from inversion to accumulation in both n and p-channel MIS structures. Interface trap concentrations (Nit) of 1.6×1012 cm-2 and 3.2×1010 cm-2, and interface state densities (Nss) of 1.6×1012 eV-1cm-2 and 6.5×1012 eV-1cm-2 were calculated for n and p-channel 2H-WS2 MIS structures, respectively. The data from these studies validate the hypothesis and demonstrate the potential of ZnO, a-BOxNy, and few layer 2H-WS2 for transparent electronics.
|
Page generated in 0.1103 seconds