No description available.

Pool oscillations in tungsten inert gas welding pools have been used in a closed-loop control system for orbital welding of ultra high purity tubing, determining a target level of penetration by altering the welding current in real-time. The technique is ideally suited to this application since it is does not contravene the cleanliness requirements for the inner bore and can be implemented outside the small orbital heads that are commonly used. The results presented in this thesis show how clear pool oscillation signals in extremely small molten pools can be monitored by optimising the welding conditions and signal processing of the arc voltage signal. As an indicator of the likely variation in cast behaviour present particularly in austenitic stainless steels, a 'time-to-penetrate' characterisation was made of the materials, using the time of the transition from the Mode 1 to the Mode 3 oscillation behaviour as the measured variable. By applying the test across a range of welding currents, significant insight was obtained into the cast and associated penetration behaviour. Late transitions indicated casts that exhibited significantly different responses to the more usually applied welding procedures, especially at the lower levels of welding current (highlighting their potentially more problematic penetration behaviour). It was shown that the established theoretical models were difficult to apply with certainty to moving weld pools, and consequently a fuzzy logic model was used in the control strategy. The closed-loop system comprised a user-interface PC, a control rack and commercial welding power source - control signals were applied every 2 to 3 Hz. Mode 3 pool oscillations were found to offer a more than satisfactory sensitivity to the inner bead width created for the various casts of 1.65 mm wall thickness materials studied.

Wear resistant surfaces with high toughness and impact resistant properties are to be created to improve the life cycle cost of brake discs for trains. A potential solution to this industrial problem is to use an arc cladding process. This work describes the application of gas tungsten arc welding (GTAW) for a structural ceramic Metal Matrix Composite (MMC) on steel. The structure of the two ceramics examined indicates the possibility of development of a wear resistant surface, which would extend the life of the brake disc. Silicon Carbide (SiC) and Tungsten Carbide (WC) ceramics were studied to embed them in a steel matrix by an advanced GTAW method. WC particles penetrated the liquid weld pool and also partially dissolved in the steel matrix, whereas, SiC because of the physical properties never penetrated deeper into the weld pool but segregated on the surface. Successful embedding and bonding of WC led to the decision to exercise an in-depth analysis of the bonding between the WC particles and the matrix. Chemical analysis of the matrix revealed more WC dissolution as compared to particle form within the clad. It was observed that WC reinforcement particles built a strong chemical bond with the steel matrix. This was shown by electron backscatter diffraction (EBSD) analysis. The hard clad layer composed of WC reinforced steel matrix gave an matching friction coefficient to high-strength steel in cold wear conditions through Pin-on-Disc wear and friction testing. A prototype railway brake disc was created with the established GTAW parameters to find out the difficulties of producing industrial scale components.

O objetivo deste trabalho foi avaliar o efeito da soldagem TIG (\"tungsten inert gas\") e compará-la com soldagem a laser, em hastes cilíndricas e supra-estruturas implantosuportadas, confeccionadas em titânio comercialmente puro (Ti cp) por meio dos ensaios de resistência mecânica (tração e flexão) e desajuste marginal, respectivamente. Foram confeccionados noventa corpos-de-prova em titânio cp, sendo sessenta, na forma de hastes cilíndricas, obtidas por fundição de hastes de latão, e trinta na forma de supra-estruturas implanto-suportadas, obtidas por modelo de gesso com quatro análogos de implantes Microunit (Conexão), com dez repetições para cada grupo (controle, solda TIG, solda a Laser). Para a obtenção dos corpos-de-prova, foi realizada inclusão em revestimento Rematitan Plus, de acordo com as instruções fabricante. Os anéis foram submetidos aos ciclos térmicos e posicionados na máquina de fundição (Rematitan), sob arco voltaico, vácuo e atmosfera de argônio, com injeção de titânio sob vácuo-pressão. Após resfriamento, as fundições foram desincluídas e jateadas com óxido de alumínio. Os corpos-de-prova obtidos em forma de hastes cilíndricas foram distribuídos aleatoriamente, em três grupos, para ambos os ensaios, resistência à tração e flexão: grupo controle (sem solda), solda TIG e solda a Laser. As trinta supra-estruturas foram divididas aleatoriamente em três grupos: I- controle - monobloco; II-B- pós-soldagem TIG e III-B- pós-soldagem a Laser; os grupos II-A e III-A, foram constituídos dos espécimes antes do processo de soldagem: II-A- pré-soldagem TIG e III-A- pré-soldagem a Laser. Os dados obtidos para o Ensaio de Tração (MPa) foram analisados estatisticamente pelos testes ANOVA e Tukey (&alpha;= 0,05). O teste complementar de Tukey (p = 0,05) evidenciou que houve diferença entre o grupo controle (605,84 ± 19,83) e os métodos de soldagem TIG (514,90 ± 37,76) e Laser (515,85 ± 62,07). Para o Ensaio de Flexão (MPa), o teste não-paramétrico de Kruskal-Wallis mostrou que não houve diferença estatisticamente significante entre os processos de soldagem TIG (1559,66) e Laser (1621,64), contudo a diferença foi significante entre estes grupos e o controle (1908,75). Para análise dos resultados do desajuste marginal (&mu;m) das supra-estruturas implanto-suportadas, o teste nãoparamétrico de Kruskal-Wallis revelou que não houve diferença estatisticamente significante entre os grupos pós-soldagem TIG (250) e pós-soldagem Laser (241), entretanto, o grupo controle (770) apresentou o maior desajuste. Pelos resultados obtidos e dentro das limitações deste estudo, pode-se afirmar que a soldagem a TIG propicia a obtenção de resultados similares à soldagem a Laser. / The aim of this study was to evaluate the effect of TIG welding (tungsten inert gas) and compare it with Laser welding, of the cylindrical rods and implant-supported frameworks, obtained by in commercially pure titanium (cp) through the mechanical resistance (tensile and flexural strength) and misfit marginal, respectively. Ninety specimens have been fabricated titanium cp, and sixty, cylindrical rods, obtained by casting of the brass rods, and thirty implant-supported frameworks, obtained by plaster die with four similar - Microunit implants (Connection), with ten repetitions for each group (control, TIG welding, laser welding). The specimens were invested in Rematitan Plus, according to the manufacturer instructions. The rings were subjected to thermal cycling and positioned in the machine of casting (Rematitan) under voltaic arc, vacuum and atmosphere of argon, with injection of titanium vacuumpressure. After cooling, were manually and airbone-particle abraded with aluminum oxide. The specimes cylindrical rods were randomly distributed in three groups, for tests, tensile and flexural strength: the control group (without welding), TIG welding and soldering laser. The above thirty-structures were randomly divided into three groups: I- one-piece-cast (control)-, II-B-after-TIG welding and III-B-after-Laser welding, the Group II-A, III-A, consisted of specimens before the process of welding: II-A-before-TIG welding and III-A before-Laser welding. The results for the test Traction were submitted to variance analysis ANOVA (p < 0.05) being observed difference between groups. The supplementary Tukey test (p = 0.05) showed that there was a difference between the control group (605.84 ± 19.83) and the methods of welding TIG (514.90 ± 37.76) and laser (515.85 ± 62.07). To test the Flexion nonparametric test Kruskal-Wallis showed that there was no statistically significant difference between the processes of TIG welding (1559.66) and Laser (1621.64), but the difference was significant between these groups and control (1908.75). For analysis of the results of marginal misfit implant-supported frameworks, the non-parametric Kruskal-Wallis test revealed that there was no statistically significant difference between groups after-TIG welding (250) and after- Laser welding (241), however, the control group (770) showed the largest misfit. With these and the limitations of this study TIG welding in may be to Laser welding.

O objetivo deste trabalho foi avaliar o efeito da soldagem TIG (\"tungsten inert gas\") e compará-la com soldagem a laser, em hastes cilíndricas e supra-estruturas implantosuportadas, confeccionadas em titânio comercialmente puro (Ti cp) por meio dos ensaios de resistência mecânica (tração e flexão) e desajuste marginal, respectivamente. Foram confeccionados noventa corpos-de-prova em titânio cp, sendo sessenta, na forma de hastes cilíndricas, obtidas por fundição de hastes de latão, e trinta na forma de supra-estruturas implanto-suportadas, obtidas por modelo de gesso com quatro análogos de implantes Microunit (Conexão), com dez repetições para cada grupo (controle, solda TIG, solda a Laser). Para a obtenção dos corpos-de-prova, foi realizada inclusão em revestimento Rematitan Plus, de acordo com as instruções fabricante. Os anéis foram submetidos aos ciclos térmicos e posicionados na máquina de fundição (Rematitan), sob arco voltaico, vácuo e atmosfera de argônio, com injeção de titânio sob vácuo-pressão. Após resfriamento, as fundições foram desincluídas e jateadas com óxido de alumínio. Os corpos-de-prova obtidos em forma de hastes cilíndricas foram distribuídos aleatoriamente, em três grupos, para ambos os ensaios, resistência à tração e flexão: grupo controle (sem solda), solda TIG e solda a Laser. As trinta supra-estruturas foram divididas aleatoriamente em três grupos: I- controle - monobloco; II-B- pós-soldagem TIG e III-B- pós-soldagem a Laser; os grupos II-A e III-A, foram constituídos dos espécimes antes do processo de soldagem: II-A- pré-soldagem TIG e III-A- pré-soldagem a Laser. Os dados obtidos para o Ensaio de Tração (MPa) foram analisados estatisticamente pelos testes ANOVA e Tukey (&alpha;= 0,05). O teste complementar de Tukey (p = 0,05) evidenciou que houve diferença entre o grupo controle (605,84 ± 19,83) e os métodos de soldagem TIG (514,90 ± 37,76) e Laser (515,85 ± 62,07). Para o Ensaio de Flexão (MPa), o teste não-paramétrico de Kruskal-Wallis mostrou que não houve diferença estatisticamente significante entre os processos de soldagem TIG (1559,66) e Laser (1621,64), contudo a diferença foi significante entre estes grupos e o controle (1908,75). Para análise dos resultados do desajuste marginal (&mu;m) das supra-estruturas implanto-suportadas, o teste nãoparamétrico de Kruskal-Wallis revelou que não houve diferença estatisticamente significante entre os grupos pós-soldagem TIG (250) e pós-soldagem Laser (241), entretanto, o grupo controle (770) apresentou o maior desajuste. Pelos resultados obtidos e dentro das limitações deste estudo, pode-se afirmar que a soldagem a TIG propicia a obtenção de resultados similares à soldagem a Laser. / The aim of this study was to evaluate the effect of TIG welding (tungsten inert gas) and compare it with Laser welding, of the cylindrical rods and implant-supported frameworks, obtained by in commercially pure titanium (cp) through the mechanical resistance (tensile and flexural strength) and misfit marginal, respectively. Ninety specimens have been fabricated titanium cp, and sixty, cylindrical rods, obtained by casting of the brass rods, and thirty implant-supported frameworks, obtained by plaster die with four similar - Microunit implants (Connection), with ten repetitions for each group (control, TIG welding, laser welding). The specimens were invested in Rematitan Plus, according to the manufacturer instructions. The rings were subjected to thermal cycling and positioned in the machine of casting (Rematitan) under voltaic arc, vacuum and atmosphere of argon, with injection of titanium vacuumpressure. After cooling, were manually and airbone-particle abraded with aluminum oxide. The specimes cylindrical rods were randomly distributed in three groups, for tests, tensile and flexural strength: the control group (without welding), TIG welding and soldering laser. The above thirty-structures were randomly divided into three groups: I- one-piece-cast (control)-, II-B-after-TIG welding and III-B-after-Laser welding, the Group II-A, III-A, consisted of specimens before the process of welding: II-A-before-TIG welding and III-A before-Laser welding. The results for the test Traction were submitted to variance analysis ANOVA (p < 0.05) being observed difference between groups. The supplementary Tukey test (p = 0.05) showed that there was a difference between the control group (605.84 ± 19.83) and the methods of welding TIG (514.90 ± 37.76) and laser (515.85 ± 62.07). To test the Flexion nonparametric test Kruskal-Wallis showed that there was no statistically significant difference between the processes of TIG welding (1559.66) and Laser (1621.64), but the difference was significant between these groups and control (1908.75). For analysis of the results of marginal misfit implant-supported frameworks, the non-parametric Kruskal-Wallis test revealed that there was no statistically significant difference between groups after-TIG welding (250) and after- Laser welding (241), however, the control group (770) showed the largest misfit. With these and the limitations of this study TIG welding in may be to Laser welding.

No description available.