Spelling suggestions: "subject:"waste time recycled"" "subject:"waste tir recycled""
1 |
Preparation and Properties of Bio-Based Polyurethane Foam Prepared from Modified Natural Rubber and Poly(ε-caprolactone) / Préparation et Caractérisation des propriétés de mousses polyuréthane biobasées synthétisées à partir du caoutchouc naturel modifié et de la poly(ε-caprolactone)Rattanapan, Suwat 27 June 2016 (has links)
L’objectif de ces travaux de recherche était de synthétiser de mousses polyuréthane (PUF) bio-basées à partir d’oligomères hydroxytéléchéliques issus du caoutchouc naturel (HTNR) ou à partir de poudrettes de pneus usagés (HTWT) et du diol de la polycaprolactone (PCL) comme segments soft. Les paramètres étudiés ont été le type de polyol et le rapport molaire entre HTNR/PCL et HTWT/PCL. La masse molaire de HTNR, HTWT et PCL étaient respectivement 1,800, 1400 et 2000 g/mol. L’effet du rapport molaire HTNR/PCL et HTWT/PCL (1/0, 1/0/5/, 1/1, et 0.5/1) sur la vitesse de formation des mousses et sur les propriétés chimiques et physiques a été étudié. Les structures chimiques de HTNR, HTWT et PUF ont été confirmées par FTIR et 1H-RMN. Le diol de la PCL était le plus réactif donc augmentant le contenu de PCL-diol la vitesse de formation des mousses a augmenté. La densité des mousses a changé légèrement avec le rapport molaire cependant la résistance à la traction reste dans la même gamme. Le diamètre moyen des cellules a augmenté en fonction du contenu de PCL-diol et la tendance inverse a été observée pour l’allongement à la rupture et la résistance à la compression. L’observation au microscope électronique à balayage (MEB) a montré que les mousses basées sur les HTNR étaient alvéolées et fermées. La biodégradabilité a été évaluée selon le test de Sturm. Polyéthylène à baisse densité et benzoate de sodium ont été utilisés respectivement comme témoins négatif et positif. Les mousses ont montré une période d’induction de 33 jours dans lequel le pourcentage de dégradation était ~ 7-10%. La biodégradation de PUF contenant seulement HTNR a été 8.4% après 28 jours et 31.89% après 60 jours ; les PUF contenants 1/0.5 HTNR/PCL ont montré un pourcentage supérieure : 11.31% après 28 jours et 45.6% après 60 jours. Le rapport molaire HTWT/PCL a influencé beaucoup la vitesse de formation des mousses et leur morphologie. Cellules fermées de forme polyédrique ont été observé par microscopie électronique à balayage. Les résultats de l’analyse thermogravimétrique ont montré que l’addition du diol de la PCL a augmenté la température de dégradation. Il a été observé qu’une basse vitesse de réaction génère des mousses à haute densité, petit diamètre de cellule et haute distribution des diamètres. La biodégradation des PUF contenant seulement HTWT a été 31.2% après 28 jours et 51.3% après 60 jours, tandis que les PUF contenant 1/0.5 HTWT/PCL ont montré une dégradation plus élevée : 39.1% après 28 jours et 64.3% après 60 jours. La vitesse de formation des mousses basées sur les HTWT était supérieure à celle des mousses basées sur les HTNR. Toutes les mousses basées sur les HTWT ont une densité supérieure et une taille de cellule inférieure à celles basées sur HTNR. La structure des cellules des mousses basées sur les HTNR ou HTWT était différente cependant toutes les mousses ont montré des cellules quasi complètement fermées. Les mousses basées sur les HTWT ont montré des propriétés thermiques et de biodégradation meilleures par rapport aux mousses basées sur les HTNR. / The aim of this research was to prepare a bio-based polyurethane foam (PUF) containing hydroxyl telechelic oligomers from natural rubber (HTNR) and waste tire crumbs (HTWT) and polycaprolactone diol (PCL) as soft segments. The studied parameters included type of polyols and molar ratio between HTNR/PCL and HTWT/PCL. The molecular weight of HTNR and HTWT derived from 1H-NMR spectra were 1,800 and 1,400 g/mol, respectively. The molecular weight of PCL diol was 2000 g/mol. The effect of HTNR/PCL and HTWT/PCL molar ratio (1/0, 1/0.5, 1/1 and 0.5/1) on the foam formation rate and physical and chemical properties of the resulting PUF was investigated. The chemical structure of HTNR, HTWT and PUF were confirmed by FTIR and 1H-NMR. PCL diol provided faster reaction, thus higher PCL diol content showed higher foam formation rate. The foam density slightly changed with the molar ratio whereas the specific tensile strength of all samples was in the same range. The average diameter of cell increased with increasing contents of PCL diol. The addition of PCL diol resulted in reduced elongation at break and compressive strength. The cellular structure observed by SEM micrographs of HTNR based foams showed an almost closed cell. The biodegradability was assessed according to a modified Sturm test. Low density polyethylene and sodium benzoate were used as a negative and positive control sample, respectively. PUF samples showed an induction time of 33 days in which the percentage of biodegradation was 7-11%. The biodegradation of PUF containing only HTNR was 8.4% and 31.89% at 28 days and 60 days of testing respectively whereas the PUF containing 1/0.5 HTNR/PCL (by mole) showed a higher biodegradation: 11.31% and 45.6% at 28 days and 60 days of testing respectively. The molar ratio of HTWT/PCL strongly affected the kinetic rate of foam formation and foam morphology. According to SEM micrographs, polyhedral closed cells were observed. The addition of the PCL diol increased the thermal degradation temperature of the PUF based on TGA results. A low kinetic rate provided PUF with a high density, small cell size and a broad cell size distribution. The biodegradation of PUF containing only HTWT was 31.2% and 51.3% at 28 days and 60 days of testing respectively whereas the PUF containing 1/0.5 HTWT/PCL diols (by mole) showed a higher biodegradation: 39.1% and 64.3% at 28 days and 60 days of testing respectively. The foam formation rate of HTWT based PUF was higher than the one of HTNR based PUF. All HTWT based PUF have a higher density than HTNR based PUF. The HTWT based PUF had an inferior cell size in comparison to HTNR based PUF. The cellular structure of HTNR based and HTWT based PUF were different, but all PUFs showed almost closed cells. The HTWT based PUF had a higher thermal degradation temperature and biodegradation properties than foams from HTNR. / วัตถุประสงค์ของงานวิจัยนี้ เพื่อทำการเตรียมโฟมพอลิยูรีเทนชีวภาพ (PUF) จากยางธรรมชาติดัดแปรที่มีหมู่ปลายไฮดรอกซิล (HTNR) ยางคลัมบ์ดัดแปรที่มีหมู่ปลาย ไฮดรอกซิล (HTWT) และพอลิคาโปรแลคโทน (PCL) ศึกษาผลของชนิดพอลิออล และสัดส่วนโดยโมลระหว่าง HTNR/PCL และ HTWT/PCL ที่สัดส่วน 1/0, 1/0.5, 1/1 และ 0.5/1 โดยโมล นํ้าหนักโมเลกุลของ HTNR, HTWT และ PCL ที่ใช้สำหรับงานวิจัยนี้ คำนวณจาก 1H-NMR คือ 1,800, 1,400 และ 2,000 g/mol ตามลำดับ ลักษณะโครงสร้างทางเคมีของ HTNR, HTWT และPUF สามารถวิเคราะห์และยืนยันด้วยเทคนิค FTIR และ 1H-NMR รวมถึงทำการวัดอัตราการก่อโฟม (Foam formation rate) ทดสอบสมบัติทางกายภาพ ทางเคมี และสมบัติการย่อยสลายทางชีวภาพ พบว่าในกรณีของโฟมพอลิยูรีเทนจาก HTNR/PCL เมื่อใช้ PCL ในปริมาณที่มากขึ้นจะส่งผลให้อัตราการก่อโฟมเร็วขึ้น และขนาดของเซลโฟมมีขนาดใหญ่ขึ้นด้วย ในขณะที่ค่าความหนาแน่น และความต้านทานต่อแรงดึงจำเพาะมีการเปลี่ยนแปลงเล็กน้อย การเติม PCL ในส่วนผสมของโฟมยังส่งผลให้ความสามารถในการยืด ณ จุดขาด และความทนทานต่อการกดมีค่าลดลง การคืนตัวหลังการกดของโฟม PUF2 (สัดส่วนระหว่าง HTNR/PCL = 1/0.5) จะให้ค่าตํ่าที่สุดคือ 40% ลักษณะของโฟมที่ได้จากการทดลองนี้โดยส่วนใหญ่จะเป็นแบบเซลปิด ความสามารถในการย่อยสลายทางชีวภาพของโฟม ทดสอบโดยใช้วิธี Sturm Test มี LDPE เป็นตัวเปรียบเทียบเชิงลบ และใช้ Sodium benzoate เป็นตัวเปรียบเทียบเชิงบวก พบว่าโฟมเริ่มมีการย่อยสายเกิดขึ้นอย่างเห็นได้ชัดที่เวลา 33 วัน มีเปอร์เซ็นต์การย่อยสลายในช่วง 7-11 เปอร์เซ็นต์ เปอร์เซ็นต์การย่อยสลายของโฟมจาก HTNR (PUF1) อยู่ที่ระดับ 8.4 และ 31.89 เปอร์เซ็นต์ และเปอร์เซ็นต์การย่อยสลายของโฟมจาก HTNR/PCL (1/0.5) อยู่ที่ระดับ 11.31 และ 45.6 เปอร์เซ็นต์ ที่เวลาในการทดสอบ 28 และ 60 วัน ตามลำดับ กรณีของโฟมพอลิยูรีเทนจาก HTWT/PCL เมื่อใช้ PCL ในปริมาณที่มากขึ้นจะส่งผลให้ค่าความหนาแน่นสูงขึ้น ขนาดของเซลโฟมลดลงมีการกระจายของเซลในวงกว้างไม่สมํ่าเสมอ เปอร์เซ็นต์การย่อยสลายทางชีวภาพของโฟมจาก HTWT (PUF5) อยู่ที่ระดับ 31.2 และ 51.3 เปอร์เซ็นต์ และเปอร์เซ็นต์การย่อยสลายของโฟมจาก HTWT/PCL (1/0.5) อยู่ที่ระดับ 39.1 และ 64.3 เปอร์เซ็นต์ ที่เวลาในการทดสอบ 28 และ 60 วัน ตามลำดับ เมื่อทำการเปรียบเทียบโฟมที่ได้จากการเตรียมโดยใช้พอลิออลหลักเป็น HTNR และ HTWT พบว่าโฟมจากพอลิออลหลัก HTWT ให้อัตราการก่อตัวของโฟมเร็วกว่า ขนาดของเซลโฟมเล็กกว่า ความหนาแน่น ความต้านทานต่อความร้อน และเปอร์เซ็นต์การย่อยสลายทางชีวภาพสูงกว่า เมื่อเทียบกับโฟมจากพอลิออลหลัก HTNR
|
Page generated in 0.0693 seconds