Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-01-13T18:22:43Z No. of bitstreams: 1 nataliavelosomalta.pdf: 1376730 bytes, checksum: cdeb2bd74c09e4792776e296bd5f7f42 (MD5) / Approved for entry into archive by Diamantino Mayra (mayra.diamantino@ufjf.edu.br) on 2017-01-31T10:32:11Z (GMT) No. of bitstreams: 1 nataliavelosomalta.pdf: 1376730 bytes, checksum: cdeb2bd74c09e4792776e296bd5f7f42 (MD5) / Made available in DSpace on 2017-01-31T10:32:11Z (GMT). No. of bitstreams: 1 nataliavelosomalta.pdf: 1376730 bytes, checksum: cdeb2bd74c09e4792776e296bd5f7f42 (MD5) Previous issue date: 2016-06-09 / O objetivo desse estudo foi avaliar, a influência de duas diferentes técnicas de aplicação de glaze (pincél e spray) sobre a morfologia de superfície de uma cerâmica Y-TZP (IPS e.maxR®ZirCAD (IvoclarVivadent) antes e após a aplicação do ácido fluorídrico. Foram confeccionados 20 corpos de prova a partir de 4 blocos cerâmicos de zircônia parcialmente estabilizada por ítria pré-sinterizados, que foram divididos em 5 grupos (n=4) de acordo com o tratamento de superfície recebido: C= controle (nenhum tratamento de superfície); S: glaze spray VITA AKZENT( Vita Zanhfabrik )P/L: glaze pó/líquido VITA AKZENT (Vita Zanhfabrik,) S+HF: S + condicionamento com ácido fluorídrico 10% (HF)(FGM) (1min); P/L + HF: P/L + condicionamento com HF 10% (1min). As amostras forma então submetidas ao seguintes testes: 1) goniometria, para ánalise do ângulo de contato e da energia de superfície; 2) análise dos dados de rugosidade (Ra) por meio de um perfilômetro óptico digital; 3)identificação das fases cristalinas do material pela Difratometria de Raios X; 4) análise dos elementos químicos presentes no material cerâmico por Microscopia e espectrometria por energia dispersiva (EDS); 5) análise da superfície por meio de microscopia eletrônica de varredura (MEV). Os resultados demonstraram que: 1) a superfície das amostras tratadas com o glaze pó/líquido foram as que apresentaram uma camada mais espessa de glaze, com superfícies menos rugosas; 2)o grupo que recebeu o tratamento com o glaze pó/líquido foi o que apresentou a maior energia de superfície (69,83mN/m), e os demais grupos apresentaram elevados valores de ângulos de contato; 3) o tratamento térmico de vitrificação não causou alterações de fases na estrutura da zircônia; 4)As imagens de perfilometria e MEV revelaram um padrão irregular de disposição do glaze após o condicionamento com HF 10%, e um alto conteúdo de sílica foi observado somente nos grupos P/L e P/L + HF. O estudo concluiu que a utilização do glaze pó/líquido pela técnica do pincel promoveu uma maior padronização da camada de glaze e foi método de tratamento de superfície que apresentou uma maior energia de superfície e um maior conteúdo vítreo. Pelas imagens de microscopia, pode-se observar que a aplicação do ácido fluorídrico a 10% criou microretenções sobre a camada de glaze pó-liquido que podem favorecer a adesão a esta superfície. / The present study evaluated qualitatively the influence of two different types of glaze (brush and spray) on the surface of Y-TZP ceramics (IPS e.maxR® ZirCAD (IvoclarVivadent,) before and after use of hydrofluoric acid. Twenty specimens were made from 4 zirconia ceramic blocks partially stabilized by pre-sintered yttria, which were divided into 5 groups (n=5) according to the surface treatment received: C = Zirconia (control) (no surface treatment); S: glaze spray VITA AKZENT; P/L: glaze powder/liquid VITA AKZENT, S+HF: S + etching with hidrofluoridric acid 10% (HF)(FGM) (1min); P/L + HF: P/L + etching with HF 10% (1min).Samples were then subjected to the following tests: 1) Goniometry for analysis of the contact angle and the surface energy ; 2) Analysis of roughness data (Ra) by means of a digital optical profilometer; 3) Identification of the crystalline phases of the material by X-ray diffraction;4) Analysis of the chemical elements present in the ceramic material by microscopy and energy dispersive spectrometry (EDS); 5) analysis of the surface after each surface treatment by means of scanning electron microscopy (SEM).Partial results showed that: 1) The surface of the samples treated with glaze powder/liquid showed a thicker layer of glaze with less rough surfaces; 2) the group receiving treatment with glaze powder/liquid presented higher surface energy (69,83mN/m), while the other groups showed high values of contact angles; 3) thermal treatment of vitrification did not change the phases of zirconia surface; 4) The SEM and profilometry images revealed a glaze irregular pattern layout after etching with 10% HF, and a high silica content was observed only in GP / L and GP / L + HF groups. The study concluded that use of the glaze powder / liquid by brush technique promoted a greater standardization of the glaze layer and this surface treatment method was the one that showed a higher surface energy and a higher glassy content. For microscopy images, it can be seen that the application of hydrofluoric acid 10% created micro retentions on the glaze powder-liquid layer that can promote adhesion to this surface.

Submitted by Geandra Rodrigues (geandrar@gmail.com) on 2017-12-20T11:21:00Z No. of bitstreams: 1 brenofortesbittar.pdf: 2144210 bytes, checksum: e81cc0440d6624e220a83357474498f4 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2017-12-22T11:56:27Z (GMT) No. of bitstreams: 1 brenofortesbittar.pdf: 2144210 bytes, checksum: e81cc0440d6624e220a83357474498f4 (MD5) / Made available in DSpace on 2017-12-22T11:56:27Z (GMT). No. of bitstreams: 1 brenofortesbittar.pdf: 2144210 bytes, checksum: e81cc0440d6624e220a83357474498f4 (MD5) Previous issue date: 2017-08-14 / Este estudo avaliou a influência da pigmentação extrínseca na degradação hidrotérmica e resistência à flexão biaxial de cerâmica de zircônia Y-TZP (InCoris TZI – Sirona – EUA) submetidas a diversos tipos de tratamento de superfície. Foram confeccionados discos seguindo a norma ISO 6872 (12x1,2 mm) a partir de blocos de zircônia Y-TZP pré-sinterizados. As amostras foram pigmentadas (InCoris TZI Coloring Liquid A3,5 – Sirona – EUA) pela técnica da imersão por 5 minutos. Foram, então, separadas em grupos de acordo com o critério de se receberam (P), ou não (S), pintura extrínseca (n=60) e posteriormente, de acordo com o tipo de tratamento de superfície a que foram submetidas (n=15): 1 – (C) controle (sem tratamento de superfície); 2 – (R) Rocatec®; 3 – (G) Glazeamento; 4 – (GA) Glazeamento e condicionamento com ácido fluorídrico 10%. Duas amostras adicionais foram, também, analisadas via (1) perfilômetro ótico, para se determinar a influência dos tratamentos de superfície na rugosidade superficial; (2) análise em difração de raio-X (DRX) para se avaliar possíveis transformações de fase; (3) espectrometria por energia dispersiva (EDS) para se avaliar a composição química das amostras; e (4) microscopia eletrônica de varredura (MEV) para caracterização superficial e quantificação do tamanho médio dos grãos. As amostras foram submetidas à ciclagem mecânica (1,2x106, carga de 200N e frequência de 3.8Hz) e ensaio de resistência à flexão biaxial (1mm/min e célula de 1000kg até a fratura catastrófica). A análise dos dados obtidos pela perfilometria permitem afirmar que a pigmentação extrínseca e os tratamentos superficiais empregados alteraram de forma significativa a rugosidade superficial. A análise do DRX permite concluir que o subgrupo SR sofreu alteração de fase T → M (3,5%) e o subgrupo PR apresentou fase cúbica. A análise dos dados permite afirmar que, no grupo S, o tratamento de superfície influenciou de maneira estatisticamente significante a resistência à flexão biaxial (p=0,014), sendo que o subgrupo SR apresentou maior resistência (642,8±112,1 MPa) e o grupo SGF, a menor (542,9±80,96 MPa). O mesmo não ocorre em P, onde não foi observado diferenças estatisticamente significantes (p=0,113). Desta forma, é possível afirmar que a pigmentação extrínseca promove alterações na estrutura do material analisado. / This study evaluated the influence of extrinsic pigmentation on the hydrothermal degradation and biaxial flexural strength of zirconia ceramics Y-TZP (InCoris TZI - Sirona - USA) submitted to several surface treatments. Discs-shape specimens (ISO 6872 - 12x1.2 mm) were prepared from pre-sintered Y-TZP zirconia blocks. The specimens received pigmentation (InCoris TZI Colouring Liquid A3,5 – Sirona – USA) by immersion technique for 5 minutes. Then they were separated into groups according to the criteria of whether they received (P) or not (N), extrinsic pigmentation (n = 60) and then according to the surface treatment they were submitted to (n = 15): 1 - (C) control (as sintered); 2 - (R) Rocatec®; 3 - (G) Glaze; 4 - (GA) Glaze and conditioning with 10% hydrofluoric acid. Two additional samples were also analyzed via (1) optical profilometer to determine the influence of surface treatments on surface roughness; (2) X-ray diffraction (XRD) analysis to evaluate possible phase transformations; (3) dispersive energy spectrometry (EDX) to evaluate the chemical composition of the samples; And (4) scanning electron microscopy (SEM) for surface characterization and quantification of the mean grain size. The samples were submitted to mechanical cycling (1.2x106, 200N load and 3.8Hz) and biaxial flexural strength test (1mm / min and 1000kg cell until catastrophic fracture). The analysis of the data obtained by the profilometer allows to state that the extrinsic pigmentation and the surface treatments employed significantly altered the surface roughness. The XRD analysis allows to conclude that the subgroup SR underwent T → M phase change (3.5%) and the subgroup PR presented also cubic phase. Data analysis allowed us to state that, in the N group, the surface treatment had a statistically significant influence on biaxial flexural strength (p = 0.014), and the SR subgroup presented higher resistance (642.8 ± 112.1 MPa) and the SGF group, the lowest (542.9 ± 80.96 MPa). The same does not occur in P, where no statistically significant differences were observed (p = 0.113). Thus, it is possible to conclude that the extrinsic pigmentation promotes changes in the structure of the analyzed material.

As ceramicas a base de zirconia (Y-TZP) apresentam propriedades mecanicas superiores as das demais ceramicas odontologicas. Entretanto, o aumento do conteudo cristalino modificou suas caracteristicas de adesao a cimentos resinosos, tornando necessario o desenvolvimento de metodos mais efetivos de uniao a estes materiais. Este trabalho in vitro pretende, portanto, avaliar a influencia de diferentes tratamentos de superficie e de diferentes agentes de uniao na resistencia ao cisalhamento entre uma zirconia estabilizada por itrio e um agente cimentante autoadesivo (RelyX U100®/3M ESPE). Para tal, cilindros de PROCERA® Allzircon receberam como tratamento de superficie jateamento com oxido de aluminio (Al2O3 - 50 m) ou jateamento com o sistema Rocatec. Sobre a superficie tratada dos cilindros foram aplicados, de acordo com os diferentes grupos experimentais, o sistema adesivo Clearfil SE Bond® (Kuraray Co.), e os primers Metal Zirconia Primer (Ivoclar Vivadent) e Alloy Primer (Kuraray Co.) e, finalmente, o cimento resinoso adotado. Cada especime foi, entao, submetido ao teste de cisalhamento (0,05 mm/min), por meio da acao de uma alca de fio ortodontico passando o mais próximo possivel da interface adesiva. A analise de variancia a um criterios (ANOVA) e o teste de Tukey (p<0,05) mostraram que a realizacao do tratamento de superfície aumentou os valores de resistencia de uniao entre a ceramica e o cimento resinoso. O jateamento com o sistema Rocatec (15,33 MPa) apresentou valores significantemente maiores que o jateamento com Al2O3 (11,93 MPa). A aplicacao dos agentes de uniao resultou em uma maior resistencia adesiva, sendo que o sistema adesivo Clearfill SE Bond (17,07 MPa) teve um comportamento estatisticamente superior aos demais materiais. Entre os primers, o Metal Zirconia Primer (11,26 MPa) apresentou maior valor de resistencia de uniao que o Alloy Primer (10,01 MPa). Portanto, a associacao de um tratamento superficial com um agente de união e valida, ja que promoveu os maiores valores de resistencia adesiva. / Yttrium-stabilized tetragonal zircon polycrystal (Y-TZP) ceramics show better mechanical properties than other dental ceramics. However, the high crystalline content modified their adhesiveness to resin cements, making it extremely necessary to develop a more effective adhesive strategy between them. This in vitro study intends to evaluate the influence of different surface treatments and different bond agents on the shear bond strength between a Y-TZP and self-adhesive resin cement. PROCERA® Allzircon cylinders (3.5 mm in diameter) received a surface airborne abrasion treatment with 50 m aluminum-oxide (Al2O3) particles or with the Rocatec system. According to the experimental groups, the adhesive system Clearfil SE Bond® (Kuraray Co.), and the primers Metal Zirconia Primer (Ivoclar Vivadent) and Alloy Primer (Kuraray Co.) were applied on the treated surface of the cylinders, before the application of the adopted resin cement (RelyX U100®/3M ESPE). Each specimen was submitted to the shear bond strength test (0.5 mm/min), by the action of an orthodontic stainless steel ligature wire (0.5 mm in diameter) loop, wrapped around the resin cement, as close as possible to the adhesive interface. One way-ANOVA and Tukey´s post hoc tests (p<0.05) revealed that surface treatment increased bond strength between the ceramic and the resin cement. Silica coating with the Rocatec system (15.33 MPa) showed significantly higher values than airborne abrasion with Al2O3 (11.93 MPa). Application of all bond agents improved shear bond strength: adhesive system Clearfil SE Bond (17.07 MPa) showed better performance than the other evaluated materials, and Metal Zirconia Primer (11.26 MPa) showed higher bond strength values than Alloy Primer (10.01 MPa). Therefore, the association of a surface treatment with a bond agent is suitable, once it resulted in higher values of adhesive strength.

As ceramicas a base de zirconia (Y-TZP) apresentam propriedades mecanicas superiores as das demais ceramicas odontologicas. Entretanto, o aumento do conteudo cristalino modificou suas caracteristicas de adesao a cimentos resinosos, tornando necessario o desenvolvimento de metodos mais efetivos de uniao a estes materiais. Este trabalho in vitro pretende, portanto, avaliar a influencia de diferentes tratamentos de superficie e de diferentes agentes de uniao na resistencia ao cisalhamento entre uma zirconia estabilizada por itrio e um agente cimentante autoadesivo (RelyX U100®/3M ESPE). Para tal, cilindros de PROCERA® Allzircon receberam como tratamento de superficie jateamento com oxido de aluminio (Al2O3 - 50 m) ou jateamento com o sistema Rocatec. Sobre a superficie tratada dos cilindros foram aplicados, de acordo com os diferentes grupos experimentais, o sistema adesivo Clearfil SE Bond® (Kuraray Co.), e os primers Metal Zirconia Primer (Ivoclar Vivadent) e Alloy Primer (Kuraray Co.) e, finalmente, o cimento resinoso adotado. Cada especime foi, entao, submetido ao teste de cisalhamento (0,05 mm/min), por meio da acao de uma alca de fio ortodontico passando o mais próximo possivel da interface adesiva. A analise de variancia a um criterios (ANOVA) e o teste de Tukey (p<0,05) mostraram que a realizacao do tratamento de superfície aumentou os valores de resistencia de uniao entre a ceramica e o cimento resinoso. O jateamento com o sistema Rocatec (15,33 MPa) apresentou valores significantemente maiores que o jateamento com Al2O3 (11,93 MPa). A aplicacao dos agentes de uniao resultou em uma maior resistencia adesiva, sendo que o sistema adesivo Clearfill SE Bond (17,07 MPa) teve um comportamento estatisticamente superior aos demais materiais. Entre os primers, o Metal Zirconia Primer (11,26 MPa) apresentou maior valor de resistencia de uniao que o Alloy Primer (10,01 MPa). Portanto, a associacao de um tratamento superficial com um agente de união e valida, ja que promoveu os maiores valores de resistencia adesiva. / Yttrium-stabilized tetragonal zircon polycrystal (Y-TZP) ceramics show better mechanical properties than other dental ceramics. However, the high crystalline content modified their adhesiveness to resin cements, making it extremely necessary to develop a more effective adhesive strategy between them. This in vitro study intends to evaluate the influence of different surface treatments and different bond agents on the shear bond strength between a Y-TZP and self-adhesive resin cement. PROCERA® Allzircon cylinders (3.5 mm in diameter) received a surface airborne abrasion treatment with 50 m aluminum-oxide (Al2O3) particles or with the Rocatec system. According to the experimental groups, the adhesive system Clearfil SE Bond® (Kuraray Co.), and the primers Metal Zirconia Primer (Ivoclar Vivadent) and Alloy Primer (Kuraray Co.) were applied on the treated surface of the cylinders, before the application of the adopted resin cement (RelyX U100®/3M ESPE). Each specimen was submitted to the shear bond strength test (0.5 mm/min), by the action of an orthodontic stainless steel ligature wire (0.5 mm in diameter) loop, wrapped around the resin cement, as close as possible to the adhesive interface. One way-ANOVA and Tukey´s post hoc tests (p<0.05) revealed that surface treatment increased bond strength between the ceramic and the resin cement. Silica coating with the Rocatec system (15.33 MPa) showed significantly higher values than airborne abrasion with Al2O3 (11.93 MPa). Application of all bond agents improved shear bond strength: adhesive system Clearfil SE Bond (17.07 MPa) showed better performance than the other evaluated materials, and Metal Zirconia Primer (11.26 MPa) showed higher bond strength values than Alloy Primer (10.01 MPa). Therefore, the association of a surface treatment with a bond agent is suitable, once it resulted in higher values of adhesive strength.