Made available in DSpace on 2017-07-21T20:42:36Z (GMT). No. of bitstreams: 1 Andre Cesar Bento.pdf: 1732687 bytes, checksum: 53eb9d5eb1ee3aca52e7d78b1169f466 (MD5) Previous issue date: 2012-04-10 / In this work, the effect of sodium hydroxide as a glass foaming agent using glass waste in the foam formulation was performed. During the synthesis process, the variation of temperature, heating rate and sintering time was investigated. Sample density and average pore sizes were estimated using mercury porosimetry. The morphology of the glass foams were evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foam with hierarchical density. / Neste trabalho foi realizado um estudo sobre a ação do hidróxido de sódio como agente formador de espuma vítrea usando resíduos de vidro em sua composição. Para a síntese, investigou-se a variação da temperatura, da taxa de aquecimento e do tempo de sinterização. Utilizando-se a técnica de porosimetria de mercúrio, para estimar a densidade e o tamanho médio de poros. A morfologia das espumas vítreas foi avaliada através da microscopia eletrônica de varredura de alta resolução (FEG) e as fases das espumas vítreas foram caracterizadas pelas técnicas de difração de raios X e a composição química estimada usando fluorescência de raios X.